Styrene-acrylate latex with high glass transition temperature （T）, low minimum film forming temperature（MFT） and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, hig...Styrene-acrylate latex with high glass transition temperature （T）, low minimum film forming temperature（MFT） and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, high conversion rate of monomer and low gel rate were achieved. The weight ratio of core monomer to shell monomer was approximately 1.35. It is found that many factors such as emulsifiers, initiators, reaction temperature, pH value and polymerization technology have influences on the permormance of styrene-acrylate latex. The prepared latex was characterized by TEM and FTIR. The obtained latex with T of 20.57 ℃, MFT or5.0 ℃, and good stability, had good stability of film forming.展开更多
A series of near or monodisperse styrene-butyl acrylate (SBA) copolymer latex particles with different butyl acrylate contents were coated with polypyrrole. The struc- ture of the SBA/PPy composites was characterized ...A series of near or monodisperse styrene-butyl acrylate (SBA) copolymer latex particles with different butyl acrylate contents were coated with polypyrrole. The struc- ture of the SBA/PPy composites was characterized by trans- mission electron microscopy (TEM), scanning electron mi- croscopy (SEM), diffuse reflectance infrared Fourier trans- form spectroscopy (DRIFT), X-ray photoelectron spectros- copy (XPS), differential scanning calorimetry (DSC) and standard four-probe method. The core-shell morphology of the SBA/PPy composite particles was confirmed. The result of DSC showed that Tg of the composite is mainly determined by the core component. The effects of the concentration of polypyrrole, the butyl acrylate content in SBA copolymer and the nature of the counter-anion on the electrical conduc- tivity of compression-moulded samples were studied. It was first found that the electrical conductivity of the samples can be tuned by varying the butyl acrylate content in SBA co- polymer and the highest conductivity of the core-shell com- posite was 0.17 S·cm?1.展开更多
Nanosize styrene-acrylate micro-emulsion was synthesized using semi-continuous seed emulsion polymerization method,with hard monomers of styrene and methyl methacryiate,soft monomer of n-buty1 acryiate,function monome...Nanosize styrene-acrylate micro-emulsion was synthesized using semi-continuous seed emulsion polymerization method,with hard monomers of styrene and methyl methacryiate,soft monomer of n-buty1 acryiate,function monomers of acrylic,α-methyl acrylic acid and N-methyloacry amide,complex emulsifier of SDS and OP-10.The structure of the copolymer was characterized by IR and TEM.The influence of the main factors such as ratio of soft and hard monomers,function monomers,and ratio of an-ionic and non-ionicemulsifiers on properties of emulsion was investigated.The optimal emulsion polymerization conditions were determined.展开更多
文摘Styrene-acrylate latex with high glass transition temperature （T）, low minimum film forming temperature（MFT） and good stability was prepared via core-shell emulsion polymerization. With semicontinuous process, high conversion rate of monomer and low gel rate were achieved. The weight ratio of core monomer to shell monomer was approximately 1.35. It is found that many factors such as emulsifiers, initiators, reaction temperature, pH value and polymerization technology have influences on the permormance of styrene-acrylate latex. The prepared latex was characterized by TEM and FTIR. The obtained latex with T of 20.57 ℃, MFT or5.0 ℃, and good stability, had good stability of film forming.
基金This work was supported by the National Natural Science Foundation of China(Grant No.50373004).
文摘A series of near or monodisperse styrene-butyl acrylate (SBA) copolymer latex particles with different butyl acrylate contents were coated with polypyrrole. The struc- ture of the SBA/PPy composites was characterized by trans- mission electron microscopy (TEM), scanning electron mi- croscopy (SEM), diffuse reflectance infrared Fourier trans- form spectroscopy (DRIFT), X-ray photoelectron spectros- copy (XPS), differential scanning calorimetry (DSC) and standard four-probe method. The core-shell morphology of the SBA/PPy composite particles was confirmed. The result of DSC showed that Tg of the composite is mainly determined by the core component. The effects of the concentration of polypyrrole, the butyl acrylate content in SBA copolymer and the nature of the counter-anion on the electrical conduc- tivity of compression-moulded samples were studied. It was first found that the electrical conductivity of the samples can be tuned by varying the butyl acrylate content in SBA co- polymer and the highest conductivity of the core-shell com- posite was 0.17 S·cm?1.
文摘Nanosize styrene-acrylate micro-emulsion was synthesized using semi-continuous seed emulsion polymerization method,with hard monomers of styrene and methyl methacryiate,soft monomer of n-buty1 acryiate,function monomers of acrylic,α-methyl acrylic acid and N-methyloacry amide,complex emulsifier of SDS and OP-10.The structure of the copolymer was characterized by IR and TEM.The influence of the main factors such as ratio of soft and hard monomers,function monomers,and ratio of an-ionic and non-ionicemulsifiers on properties of emulsion was investigated.The optimal emulsion polymerization conditions were determined.