Cyclic oligomers of phenolphthalein polyarylene ether sulfone(ketone) were prepared through cyclo-depolymerisation of corresponding polymers using CsF as the catalyst in dipolar aprotic solvent DMAc and DMF, and a fam...Cyclic oligomers of phenolphthalein polyarylene ether sulfone(ketone) were prepared through cyclo-depolymerisation of corresponding polymers using CsF as the catalyst in dipolar aprotic solvent DMAc and DMF, and a family of macrocycles containing from dimer up to at least heptamer were confirmed by GPC, HPLC and MALDI-TOF-MS. The yields of cyclics get as high as 86.3% and 87.9% respectively.展开更多
Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chlorometh...Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone （NMP）, N,N-dimethylacetamide （DMAc） and chloroform. Quaternized poly（phthalazinone ether sulfone ketone） （QAPPESK） was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid （98%） and swollen in N,N-dimethylformamide （DMF）. The vanadium redox flow battery （V-RFB） using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.展开更多
A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were...A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures （Tg） and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction （WAXD）.展开更多
Phenylseleno and sulfonyl substituted allyl alcohols were synthesized stereoselectively by the three-component reaction of acetylenic sulfone, phenylselenomagnesium bromide and ketones in one-pot.
A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacem...A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacement reaction of 4-(4-hydroxylphenyl)- 1 (2H)-phthalazinone with di(4-chlorophenyl) sulfone, 4,4'-difluoro-benzophenone and phenolphthalin in sulfolane in the presence of K2CO3 to produce high molecular weight polymers which can be dissolved in some polar solvents such as chloroform and nitrobenzene at room temperature and can be easily cast into flexible, yellowish and transparent films. PPESK is an amorphous polymer having a decomposition temperature above 400degreesC, which indicates that it has high thermal stability. At the same time, the thermal properties of PPESKs with dicyandiamide (DICY) as curing agent indicated that the heat-resistance properties of the PPESKs are improved after curing. The apparent activation energy (A-E) of the cross-linking reaction and the reaction order (n) of PPESK/DICY were found to be 52.2 kJ/mol and ca. 1.0, respectively. Therefore, the cross-linking reaction is approximately a first order reaction.展开更多
Prolonged hydrothermal treatment for sulfonated poly(ether ether ketone) membranes induces mechanical degradation and developing hydrophilic-hydrophobic phase separation, simultaneously. The enhanced phase separation ...Prolonged hydrothermal treatment for sulfonated poly(ether ether ketone) membranes induces mechanical degradation and developing hydrophilic-hydrophobic phase separation, simultaneously. The enhanced phase separation provides incremental proton conductivity to the membranes, whereas mechanical degradation drastically reduces device stability. On this basis, we describe here the effects of two different ex situ aging processes on sulfonated poly(ether ether ketone) membranes: hydrationdehydration cycling and prolonged hydrothermal treatment. Both aged membranes exhibited enhanced phase separation under the hydrated conditions, as characterized by small angle X-ray scattering.However, when the aged membranes were dried again, the nanostructure of the membranes aged via the hydration-dehydration cycling was recoverable, whereas that of the membranes aged via prolonged hydrothermal treatment was irreversible. Furthermore, the two differently aged membranes showed clear differences in thermal, mechanical, and electrochemical properties. Finally, we implemented both aged membranes in fuel cell application. The sample aged via hydration-dehydration cycling maintained its improved cell performance, whereas the sample aged via hydrothermal treatment showed drastically reduced cell performance after durability test for 50 h.展开更多
A novel poly (ether sulfone ketone) containing the phthalazinone moiety was prepared by the reaction of 4-)4-hydroxyphenyl) (2H) phthalazin-1-one with activated dichloro-monomers. The polymer was characterized by FT-I...A novel poly (ether sulfone ketone) containing the phthalazinone moiety was prepared by the reaction of 4-)4-hydroxyphenyl) (2H) phthalazin-1-one with activated dichloro-monomers. The polymer was characterized by FT-IR, H-1-NMR, DSC, TGA and X-ray diffraction.展开更多
Two kinds of macrocyclic oligomers containing aromatic sulfide linkages have been synthesized by the solution polycondensation in high yield. The cyclic compounds were characterized by H-1 and C-13 NMR, by and MALDI -...Two kinds of macrocyclic oligomers containing aromatic sulfide linkages have been synthesized by the solution polycondensation in high yield. The cyclic compounds were characterized by H-1 and C-13 NMR, by and MALDI - TOF MS.展开更多
Dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in con- centrated sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure...Dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in con- centrated sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure 1,2-dihydro-4-(4-hydroxyphenyl)(2H)phthalazin- 1-one, and 4,4-difluorodiphenylketone. The sulfonated monomer and sulfonated polymer were characterized with FT-IR and 1H-NMR.展开更多
Proton conducting composite membranes from sulfonated polyether ether ketone and SiO2 for direct methanol fuel cell （DMFC） application were prepared with sulfonated polyether ether ketone（SPEEK） and tetracethoxy s...Proton conducting composite membranes from sulfonated polyether ether ketone and SiO2 for direct methanol fuel cell （DMFC） application were prepared with sulfonated polyether ether ketone（SPEEK） and tetracethoxy silane（TEOS） by sol-gel method. The covalent crosslinking structure was formed between —SO3H of SPEEK via SiO2. The SEM images show that the interfacial compatibility of SPEEK and SiO2 is improved obviously and SiO2 disperses uniformly in the polymer matrix and the particle diameter of SiO2 does not exceed 40 nm. The proton conductivity of composite membranes decreases slightly compared with the SPEEK membrane while the methanol permeability and swelling of composite membrane are improved remarkablely owing to covalent cross-linking between —SO3H and SiO2 .展开更多
A sulfonated poly(ether ether ketone)(SPEEK) membrane with a fairly high degree of sulfonation(DS) can swell excessively and even dissolve at high temperature.To solve these problems,insolvable functionalized silica p...A sulfonated poly(ether ether ketone)(SPEEK) membrane with a fairly high degree of sulfonation(DS) can swell excessively and even dissolve at high temperature.To solve these problems,insolvable functionalized silica powder with sulfonic acid groups(SiOx-S) was added into the SPEEK matrix(DS = 55.1%) to prepare SPEEK/SiOx-S composite membranes.The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder.Pure SPEEK membrane swelled 52.6% at 80°C,whereas the SPEEK/SiOx-S(15%,by mass) membrane swelled only 27.3% at the same temperature.From room temperature to 80℃,all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about o ne order of magnitude lower than that of Nafion?115.Compared with pure SPEEK membranes,the addition of the SiOx-S powder not only leads to higher proton conductivity,but also increases the dimensional stability at higher temperatures,and greater proton conductivity can be achieved at higher temperature.The SPEEK/SiOx-S(20%,by mass) membrane could withstand temperature up to 145°C,at which in 100% relative humidity(RH) its proton conductivity exceeded slightly that of Nafion?115 membrane and reached 0.17 S·cm-1,while pure SPEEK membrane dissolved at 90°C.The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability,high proton conductivity,and low methanol permeability.展开更多
Polyoxometalates(POMs)are classified as solid superacids which can exhibit notable proton conductivity,making them a promising functional inorganic filler for enhancing the proton conductivity of proton exchange membr...Polyoxometalates(POMs)are classified as solid superacids which can exhibit notable proton conductivity,making them a promising functional inorganic filler for enhancing the proton conductivity of proton exchange membranes(PEMs).In this study,a series of hybrid membranes were obtained by molecular-level hybridization of Weakley-type POM Na_(7)H_(2)LaW_(10)O_(36)(LaW_(10))clusters into sulfonated poly(aryl ether ketone sulfone)(SPAEKS).All hybrid membranes exhibited greater proton conductivity than the pristine membrane in the 30–80℃temperature range.When the doping amount of LaW 10 reached 7 wt.%,the proton conductivity of M-LaW 10^(-7)achieved 64 mS·cm^(−1)at 80℃.Lanthanide ions'high coordination number property and variable coordination environment can aid to attract more water molecules from the environment.LaW 10 and these bound water can construct denser hydrogen bonds with–SO_(3)H of SPAEKS.These intensive hydrogen bonds will facilitate the constitution of more continuous proton transport channels,and improve the proton conductivity of the hybrid membrane.This work off ers a fresh approach to using POMs containing rare-earth components in PEMs.展开更多
Objective To evaluate the sensitivity of arterial ketone body ratio as an indicator for multiple organ failure.Materials and methods The experimental model of multiple organ failure was made in adult and old rats by h...Objective To evaluate the sensitivity of arterial ketone body ratio as an indicator for multiple organ failure.Materials and methods The experimental model of multiple organ failure was made in adult and old rats by hypoperfusion-induced hemorrhagic shock. After blood sampling, the arterial acetoacetate, β-hydroxybutyrate, total ketone body, ALT, AST, BUN, creatinine at 2, 4, 8 hr in hypoperfusion were examined to compare the differences of ketone body ratio and organ failure between adult and old rats. Hepatic and mitochondrial metabolism were assessed by comparing ketone body ratios (AcAc/β-OHB) and free NAD+/NADH ratios. Results Ketone body ratio in old rats at 2, 4, 8 hr after the induction of hemorrhagic shock decreased from 0.68 to 0.31, 0.27 and 0.22, respectively. In adult rats, it decreased from 1.12 to 0.17, 0.12 and 0.09, respectively. Changes of ketone body ratio in the adult group were larger than in the elderly group ( P ＜ 0.001). The development of multiple organ failure is associated with the time of hemorrhagic shock development. Conclusions There was a different ketone body ratio between multiple organ failure in the elderly (MOFE) and multiple organ failure (MOF) in general adults. Ketone body ratio is a better indicator than ALT and AST in reflecting hepatic function in the early status of MOF. (J Geriatr Cardiol 2004;1(2) :125-128. )展开更多
A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through ...A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through a facile solution casting approach. The simple, but effective monomer sulfonation was performed for SFMC to create compact and rigid hydrophobic backbone structures, while conventional random sulfonation was carried-out for SPEEK. Hydrophilic-hydrophobic-hydrophilic structure of SFMC enhances the compatibility with SPEEK and GO and allows for an unprecedented approach to alter me- chanical strength and proton conductivity of ternary hybrid membrane, as verified from universal test machine （UTM） curves and alternating current （AC） impedance plots. The impact of GO integration on the morphology and roughness of hybrid membrane was scrutinized using field emission scanning electron microscope （FE-SEM） and atomic force microscope （AFM）. Ternary hybrid showed uniform intercalation of GO nanosheets throughout the entire surface of membrane with an increased surface roughness of 8.91 nm. The constructed ternary hybrid membrane revealed excellent water absorption, ion exchange capacity and gas barrier properties, while retaining reasonable dimensional stability. The well-optimized ternary hybrid membrane containing 5 wt% GO revealed a maximum proton conductivity of 111.9 mS/cm, which is higher by a factor of two-fold with respect to that of bare SFMC membrane. The maximum PEMFC power density of 528.07mW/cm2 was yielded by ternary hybrid membrane at a load current density of 1321.1 mA/cm2 when operating the cell at 70 ℃ under 100% relative humidity （RH）. In comparison, a maximum power density of only 182.06 mW/cm2 was exhibited by the bare SFMC membrane at a load current density of 455.56 mA/cm2 under same operating conditions.展开更多
Novel poly（aryl ether sulfone ketone）s （PAESK） were synthesized from bisphenol A （BPA）, 9,9＇-bis（4-hydroxyphenyl） fluorene （BHPF）, 4,4＇-dichlorodiphenylsulfone （DCS） and 4,4＇-difluorobenzophenone （DFB...Novel poly（aryl ether sulfone ketone）s （PAESK） were synthesized from bisphenol A （BPA）, 9,9＇-bis（4-hydroxyphenyl） fluorene （BHPF）, 4,4＇-dichlorodiphenylsulfone （DCS） and 4,4＇-difluorobenzophenone （DFB） via nucleophilic substitution polymerization, which were subsequently used to fabricate ultrafiltration membrane by phase-inversion method for high temperature condensed water treatment. The obtained high molecular weight co-polymers with fluorene group with good solubility and good thermal stability, can be easily cast into flexible, white and non-transparent fiat films. The influence of molar ratio of BPA and BHPF on the properties of the prepared co-polymers and membranes was investigated in detail. SEM study of the morphology of the membranes indicated that the prepared membranes possessed homogeneous pores on the top surface and were sponge-like or finger-like in cross-section. Pure water flux of the membranes increased from 71.87 L·m-2.h-1 to 247.65 L·m-2.h-1, while the retention of BSA decreased slightly, and the water contact angle decreased from 82.1 ° to 55.6° with the PVP concentration from 0 wt% to 10 wt%. With increasing concentration of PVP, the mechanical properties of membranes decreased, while the thermal stability increased. The permeate flux measurement showed that the PAESK membrane had the potential for high temperature condensed water treatment.展开更多
文摘Cyclic oligomers of phenolphthalein polyarylene ether sulfone(ketone) were prepared through cyclo-depolymerisation of corresponding polymers using CsF as the catalyst in dipolar aprotic solvent DMAc and DMF, and a family of macrocycles containing from dimer up to at least heptamer were confirmed by GPC, HPLC and MALDI-TOF-MS. The yields of cyclics get as high as 86.3% and 87.9% respectively.
基金partly financed by the Major State Basic Research Development Program of China(No.2003 CB615700)the National Natural Science Foundation of China(No.20604005).
文摘Chloromethylated poly（phthalazinone ether sulfone ketone） （CMPPESK） was prepared from poly（phthalazinone ether sulfone ketone） （PPESK） using chloromethyl octyl ethers （CMOE） with lower toxicity as chloromethylated regent. CMPPESK was soluble in N-methyl-2-pyrrolidone （NMP）, N,N-dimethylacetamide （DMAc） and chloroform. Quaternized poly（phthalazinone ether sulfone ketone） （QAPPESK） was prepared from CMPPESK by quaternization. QAPPESK had excellent solvent resistance, which was only partly soluble in sulfuric acid （98%） and swollen in N,N-dimethylformamide （DMF）. The vanadium redox flow battery （V-RFB） using QAPPESK anion-exchange membrane had better performance with 88.3% of overall energy efficiency.
文摘A novel series of poly（aryl ether sulfone ketone）s （PPESKs） containing phthalazinone and biphenyl moieties were prepared by two-step nucleophilic polycondensation reaction. The ^-Mw values of these copolymers were between 38,330 and 67,900. The glass transition temperatures （Tg） and 5% decomposition temperatures were ranged in 253-269 ℃ and 488-500 ℃, respectively, The structures of these copolymers were confirmed by FT-IR and ^1H NMR. Moreover, all the resultant copolymers were amorphous determined by wide angle X-ray diffraction （WAXD）.
基金Supported by the State Key Development Program for Basic Research of China （2008CB617502）, the National Natural Science Foundation of China （20606025）, and Program for Changjiang Scholars and Innovative Research Team in University of China （IRT0641）.
基金This work was supported by National Science Foundation of China （No. 20264001 ）, National Science Foundation of Jiangxi Province, Innovation Fund for Technology Based Firms of China （No. 06C26213601342）.
基金supported by the National Natural Science Foundation of China(No.29772007)
文摘Phenylseleno and sulfonyl substituted allyl alcohols were synthesized stereoselectively by the three-component reaction of acetylenic sulfone, phenylselenomagnesium bromide and ketones in one-pot.
基金This project was supported by the National Ninth Five-Year-Plan Key Project "The pilot-scale production and the applied development of polyaryl ether concerning phthalazinone moiety" (No. 97-564-01-07).
文摘A kind of novel heat-resistant, high performance engineering thermoplastic phthalazinone poly(aryl ether sulfone ketone) (PPESK) containing a carboxyl group in its side chain was prepared by the nucleophilic displacement reaction of 4-(4-hydroxylphenyl)- 1 (2H)-phthalazinone with di(4-chlorophenyl) sulfone, 4,4'-difluoro-benzophenone and phenolphthalin in sulfolane in the presence of K2CO3 to produce high molecular weight polymers which can be dissolved in some polar solvents such as chloroform and nitrobenzene at room temperature and can be easily cast into flexible, yellowish and transparent films. PPESK is an amorphous polymer having a decomposition temperature above 400degreesC, which indicates that it has high thermal stability. At the same time, the thermal properties of PPESKs with dicyandiamide (DICY) as curing agent indicated that the heat-resistance properties of the PPESKs are improved after curing. The apparent activation energy (A-E) of the cross-linking reaction and the reaction order (n) of PPESK/DICY were found to be 52.2 kJ/mol and ca. 1.0, respectively. Therefore, the cross-linking reaction is approximately a first order reaction.
基金Byoungseok Min of Pohang Accelerator Laboratory for SAXS technical support at 4C beamline.All authors have read the manuscript and agreed to its contents。
文摘Prolonged hydrothermal treatment for sulfonated poly(ether ether ketone) membranes induces mechanical degradation and developing hydrophilic-hydrophobic phase separation, simultaneously. The enhanced phase separation provides incremental proton conductivity to the membranes, whereas mechanical degradation drastically reduces device stability. On this basis, we describe here the effects of two different ex situ aging processes on sulfonated poly(ether ether ketone) membranes: hydrationdehydration cycling and prolonged hydrothermal treatment. Both aged membranes exhibited enhanced phase separation under the hydrated conditions, as characterized by small angle X-ray scattering.However, when the aged membranes were dried again, the nanostructure of the membranes aged via the hydration-dehydration cycling was recoverable, whereas that of the membranes aged via prolonged hydrothermal treatment was irreversible. Furthermore, the two differently aged membranes showed clear differences in thermal, mechanical, and electrochemical properties. Finally, we implemented both aged membranes in fuel cell application. The sample aged via hydration-dehydration cycling maintained its improved cell performance, whereas the sample aged via hydrothermal treatment showed drastically reduced cell performance after durability test for 50 h.
文摘A novel poly (ether sulfone ketone) containing the phthalazinone moiety was prepared by the reaction of 4-)4-hydroxyphenyl) (2H) phthalazin-1-one with activated dichloro-monomers. The polymer was characterized by FT-IR, H-1-NMR, DSC, TGA and X-ray diffraction.
文摘Two kinds of macrocyclic oligomers containing aromatic sulfide linkages have been synthesized by the solution polycondensation in high yield. The cyclic compounds were characterized by H-1 and C-13 NMR, by and MALDI - TOF MS.
基金the National Natural Science Foundation of China for financial support.
文摘Dihydro-4-(4-hydroxyphenyl)(2H)phthalazin-1-one(DHPZ) was sulfonated in con- centrated sulfuric acid. Poly(phthalazinone ether ketone) containing pendant sodium sulfonate group was synthesized from sulfonated and pure 1,2-dihydro-4-(4-hydroxyphenyl)(2H)phthalazin- 1-one, and 4,4-difluorodiphenylketone. The sulfonated monomer and sulfonated polymer were characterized with FT-IR and 1H-NMR.
文摘Proton conducting composite membranes from sulfonated polyether ether ketone and SiO2 for direct methanol fuel cell （DMFC） application were prepared with sulfonated polyether ether ketone（SPEEK） and tetracethoxy silane（TEOS） by sol-gel method. The covalent crosslinking structure was formed between —SO3H of SPEEK via SiO2. The SEM images show that the interfacial compatibility of SPEEK and SiO2 is improved obviously and SiO2 disperses uniformly in the polymer matrix and the particle diameter of SiO2 does not exceed 40 nm. The proton conductivity of composite membranes decreases slightly compared with the SPEEK membrane while the methanol permeability and swelling of composite membrane are improved remarkablely owing to covalent cross-linking between —SO3H and SiO2 .
基金Supported by the State Key Development Program for Basic Research of China （2008CB617502）, the National Natural Science Foundation of China （20606025）, and Program for Changjiang Scholars and Innovative Research Team in University of China （IRT0641）.
文摘A sulfonated poly(ether ether ketone)(SPEEK) membrane with a fairly high degree of sulfonation(DS) can swell excessively and even dissolve at high temperature.To solve these problems,insolvable functionalized silica powder with sulfonic acid groups(SiOx-S) was added into the SPEEK matrix(DS = 55.1%) to prepare SPEEK/SiOx-S composite membranes.The decrease in both the swelling degree and the methanol permeability of the membranes was a dose-dependent result of addition of the SiOx-S powder.Pure SPEEK membrane swelled 52.6% at 80°C,whereas the SPEEK/SiOx-S(15%,by mass) membrane swelled only 27.3% at the same temperature.From room temperature to 80℃,all SPEEK/SPEEK/SiOx-S composite membranes had methanol permeability of about o ne order of magnitude lower than that of Nafion?115.Compared with pure SPEEK membranes,the addition of the SiOx-S powder not only leads to higher proton conductivity,but also increases the dimensional stability at higher temperatures,and greater proton conductivity can be achieved at higher temperature.The SPEEK/SiOx-S(20%,by mass) membrane could withstand temperature up to 145°C,at which in 100% relative humidity(RH) its proton conductivity exceeded slightly that of Nafion?115 membrane and reached 0.17 S·cm-1,while pure SPEEK membrane dissolved at 90°C.The SPEEK/SiOx-S composite membranes are promising for use in direct methanol fuel cells because of their good dimensional stability,high proton conductivity,and low methanol permeability.
基金financially supported by the National Natural Science Foundation of China(No.22271022)the Natural Science Foundation of Jilin Province(No.YDZJ202201ZYTS342)supported by the China Scholarship Council(CSC No.201802335014).
文摘Polyoxometalates(POMs)are classified as solid superacids which can exhibit notable proton conductivity,making them a promising functional inorganic filler for enhancing the proton conductivity of proton exchange membranes(PEMs).In this study,a series of hybrid membranes were obtained by molecular-level hybridization of Weakley-type POM Na_(7)H_(2)LaW_(10)O_(36)(LaW_(10))clusters into sulfonated poly(aryl ether ketone sulfone)(SPAEKS).All hybrid membranes exhibited greater proton conductivity than the pristine membrane in the 30–80℃temperature range.When the doping amount of LaW 10 reached 7 wt.%,the proton conductivity of M-LaW 10^(-7)achieved 64 mS·cm^(−1)at 80℃.Lanthanide ions'high coordination number property and variable coordination environment can aid to attract more water molecules from the environment.LaW 10 and these bound water can construct denser hydrogen bonds with–SO_(3)H of SPAEKS.These intensive hydrogen bonds will facilitate the constitution of more continuous proton transport channels,and improve the proton conductivity of the hybrid membrane.This work off ers a fresh approach to using POMs containing rare-earth components in PEMs.
文摘Objective To evaluate the sensitivity of arterial ketone body ratio as an indicator for multiple organ failure.Materials and methods The experimental model of multiple organ failure was made in adult and old rats by hypoperfusion-induced hemorrhagic shock. After blood sampling, the arterial acetoacetate, β-hydroxybutyrate, total ketone body, ALT, AST, BUN, creatinine at 2, 4, 8 hr in hypoperfusion were examined to compare the differences of ketone body ratio and organ failure between adult and old rats. Hepatic and mitochondrial metabolism were assessed by comparing ketone body ratios (AcAc/β-OHB) and free NAD+/NADH ratios. Results Ketone body ratio in old rats at 2, 4, 8 hr after the induction of hemorrhagic shock decreased from 0.68 to 0.31, 0.27 and 0.22, respectively. In adult rats, it decreased from 1.12 to 0.17, 0.12 and 0.09, respectively. Changes of ketone body ratio in the adult group were larger than in the elderly group ( P ＜ 0.001). The development of multiple organ failure is associated with the time of hemorrhagic shock development. Conclusions There was a different ketone body ratio between multiple organ failure in the elderly (MOFE) and multiple organ failure (MOF) in general adults. Ketone body ratio is a better indicator than ALT and AST in reflecting hepatic function in the early status of MOF. (J Geriatr Cardiol 2004;1(2) :125-128. )
基金supported by the Korea Institute of Energy Technology Evaluation and Planning(KETEP)the Ministry of Trade,Industry&Energy(MOTIE)of the Republic of Korea(No.20164030201070)supported by Basic Science Research Program through the National Research Foundation of Korea(NRF)funded by the Ministry of Science,ICT and future Planning(NRF-2017R1A2B4005230)
文摘A ternary hybrid membrane architecture consisting of sulfonated fluorinated multi-block copolymer （SFMC）, sulfonated （poly ether ether ketone） （SPEEK） and I or 5 wt% graphene oxide （GO） was fabricated through a facile solution casting approach. The simple, but effective monomer sulfonation was performed for SFMC to create compact and rigid hydrophobic backbone structures, while conventional random sulfonation was carried-out for SPEEK. Hydrophilic-hydrophobic-hydrophilic structure of SFMC enhances the compatibility with SPEEK and GO and allows for an unprecedented approach to alter me- chanical strength and proton conductivity of ternary hybrid membrane, as verified from universal test machine （UTM） curves and alternating current （AC） impedance plots. The impact of GO integration on the morphology and roughness of hybrid membrane was scrutinized using field emission scanning electron microscope （FE-SEM） and atomic force microscope （AFM）. Ternary hybrid showed uniform intercalation of GO nanosheets throughout the entire surface of membrane with an increased surface roughness of 8.91 nm. The constructed ternary hybrid membrane revealed excellent water absorption, ion exchange capacity and gas barrier properties, while retaining reasonable dimensional stability. The well-optimized ternary hybrid membrane containing 5 wt% GO revealed a maximum proton conductivity of 111.9 mS/cm, which is higher by a factor of two-fold with respect to that of bare SFMC membrane. The maximum PEMFC power density of 528.07mW/cm2 was yielded by ternary hybrid membrane at a load current density of 1321.1 mA/cm2 when operating the cell at 70 ℃ under 100% relative humidity （RH）. In comparison, a maximum power density of only 182.06 mW/cm2 was exhibited by the bare SFMC membrane at a load current density of 455.56 mA/cm2 under same operating conditions.
基金financial support under Heilongjiang Postdoctoral Fund (No.LBH-Z09175)
文摘Novel poly（aryl ether sulfone ketone）s （PAESK） were synthesized from bisphenol A （BPA）, 9,9＇-bis（4-hydroxyphenyl） fluorene （BHPF）, 4,4＇-dichlorodiphenylsulfone （DCS） and 4,4＇-difluorobenzophenone （DFB） via nucleophilic substitution polymerization, which were subsequently used to fabricate ultrafiltration membrane by phase-inversion method for high temperature condensed water treatment. The obtained high molecular weight co-polymers with fluorene group with good solubility and good thermal stability, can be easily cast into flexible, white and non-transparent fiat films. The influence of molar ratio of BPA and BHPF on the properties of the prepared co-polymers and membranes was investigated in detail. SEM study of the morphology of the membranes indicated that the prepared membranes possessed homogeneous pores on the top surface and were sponge-like or finger-like in cross-section. Pure water flux of the membranes increased from 71.87 L·m-2.h-1 to 247.65 L·m-2.h-1, while the retention of BSA decreased slightly, and the water contact angle decreased from 82.1 ° to 55.6° with the PVP concentration from 0 wt% to 10 wt%. With increasing concentration of PVP, the mechanical properties of membranes decreased, while the thermal stability increased. The permeate flux measurement showed that the PAESK membrane had the potential for high temperature condensed water treatment.