92WC-8Co puwder mixture with superfine-tungsten carbide was respectively sintered by spark plasma sintering（ SPS ） and sintering isostutic pressure （SIP）. Complete dense samples with 200 nm WC grains and 94.2HRA ...92WC-8Co puwder mixture with superfine-tungsten carbide was respectively sintered by spark plasma sintering（ SPS ） and sintering isostutic pressure （SIP）. Complete dense samples with 200 nm WC grains and 94.2HRA hardness were prepared by spark plasma sintering at 1 150 ℃ and under 4.5 kN for 5 minutes. SIP was carried out at 1 400 ℃ for 30 minutes with a result of 300-400 nm WC grains and 93 HRA hardness. The results show that sintering temperature is greatly decreased by SPS, sintering time is largely shortened and WC grain growth is effectively retarded. Micropores and drawb（wks in superfine-cemented carbide made by SPS are greatly declined, which is very useful to improving nwehanical properties.展开更多
Specially designed wire-drawing equipment with multiple electropulse generator was introduced. The influences of multiple electropulses processing on the microstructure and properties of the hardened steel wire were i...Specially designed wire-drawing equipment with multiple electropulse generator was introduced. The influences of multiple electropulses processing on the microstructure and properties of the hardened steel wire were investigated. Samples treated by direct current under the same current density as that in multiple electropulses processing were carried out for contrast analysis. The results show that the optimized parameters of multiple electropulses processing will be facilitated to increase the nucleation rate and slow down the growth rate of recrystallized grains. Consequently, massive superfine grains of micro and sub-micro scale could be found in the steel wire. Thereby, the elongation was significantly enhanced with a relatively small strength reduction in comparison with as-received cold-drawing steel wires. Outstanding mechanical properties of steel wire were obtained.展开更多
基金Funded by the Science Foundation of Shanghai , China ( No.0152nm046)
文摘92WC-8Co puwder mixture with superfine-tungsten carbide was respectively sintered by spark plasma sintering（ SPS ） and sintering isostutic pressure （SIP）. Complete dense samples with 200 nm WC grains and 94.2HRA hardness were prepared by spark plasma sintering at 1 150 ℃ and under 4.5 kN for 5 minutes. SIP was carried out at 1 400 ℃ for 30 minutes with a result of 300-400 nm WC grains and 93 HRA hardness. The results show that sintering temperature is greatly decreased by SPS, sintering time is largely shortened and WC grain growth is effectively retarded. Micropores and drawb（wks in superfine-cemented carbide made by SPS are greatly declined, which is very useful to improving nwehanical properties.
文摘Specially designed wire-drawing equipment with multiple electropulse generator was introduced. The influences of multiple electropulses processing on the microstructure and properties of the hardened steel wire were investigated. Samples treated by direct current under the same current density as that in multiple electropulses processing were carried out for contrast analysis. The results show that the optimized parameters of multiple electropulses processing will be facilitated to increase the nucleation rate and slow down the growth rate of recrystallized grains. Consequently, massive superfine grains of micro and sub-micro scale could be found in the steel wire. Thereby, the elongation was significantly enhanced with a relatively small strength reduction in comparison with as-received cold-drawing steel wires. Outstanding mechanical properties of steel wire were obtained.