Catalytic removal of volatile organic compounds using ordered porous transition metal oxide and supported noble metal catalysts

Most of volatile organic compounds （VOCs） are harmful to the atmosphere and human health. Cata‐lytic combustion is an effective way to eliminate VOCs. The key issue is the availability of high per‐formance catalysts. Many catalysts including transition metal oxides, mixed metal oxides, and sup‐ported noble metals have been developed. Among these catalysts, the porous ones attract much attention. In this review, we focus on recent advances in the synthesis of ordered mesoporous and macroporous transition metal oxides, perovskites, and supported noble metal catalysts and their catalytic oxidation of VOCs. The porous catalysts outperformed their bulk counterparts. This excel‐lent catalytic performance was due to their high surface areas, high concentration of adsorbed oxy‐gen species, low temperature reducibility, strong interaction between noble metal and support and highly dispersed noble metal nanoparticles and unique porous structures. Catalytic oxidation of carbon monoxide over typical catalysts was also discussed. We made conclusive remarks and pro‐posed future work for the removal of VOCs.

AgAuPd/meso-Co_3O_4: High-performance catalysts for methanol oxidation

The meso-Co3O4 and AgxAuyPd/meso-Co3O4 catalysts were prepared using the KIT-6-templating and polyvinyl alcohol-protected NaBH4 reduction methods,respectively.Various techniques were used to characterize physicochemical properties of these materials.Catalytic performance of the samples was evaluated for methanol combustion.The cubically crystallized Co3O4 support displayed a three-dimensionally ordered mesoporous structure.The supported noble metal nanoparticles(NPs)possessed a surface area of 115.125 m^2/g,with the noble NPs(average size=2.8.4.5 nm)being uniformly dispersed on the surface of meso-Co3O4.Among all of the samples,0.68 wt%Ag0.75Au1.14Pd/meso-Co3O4 showed the highest catalytic activity(T50%=100℃and T90%=112℃at a space velocity of 80000 mL(g^–1 h^–1).The partial deactivation of the 0.68 wt%Ag0.75Au1.14Pd/meso-Co3O4 sample due to water vapor or carbon dioxide introduction was reversible.It is concluded that the good catalytic performance of 0.68 wt%Ag0.75Au1.14Pd/meso-Co3O4 was associated with its highly dispersed Ag0.75Au1.14Pd alloy NPs,high adsorbed oxygen species concentration,good low-temperature reducibility,and strong interaction between Ag0.75Au1.14Pd alloy NPs and meso-Co3O4.

Rare earth oxides and their supported noble metals in application of environmental catalysis

Volatile organic compounds(VOCs),methane,carbon monoxide,soot,automotive exhaust,and nitrogen oxides are harmful to the atmosphere and human health.It is urgent to strictly control their emissions.Heterogeneous catalysis is an effective pathway for the removal of these pollutants,and the critical issue is the development of novel and high-performance catalysts.In this review,we briefly summarize the preparation methods,physicochemical properties,catalytic activities,and related reaction mechanisms for the above pollutants removal of the rare earth oxides,mixed rare earth oxide,rare earth oxidesupported noble metal,and mixed rare earth oxide-supported noble metal catalysts that have been investigated by our group and other researchers.It was found that catalytic performance was associated with the factors,such as specific surface area,pore structure,particle size and dispersion,adsorbed oxygen species concentration,reducibility,reactant activation ability or interaction between metal nanoparticles and support.Furthermore,we also envision the development trend of such a topic in future work.

Catalytic performance enhancement by alloying Pd with Pt on ordered mesoporous manganese oxide for methane combustion

Ordered mesoporous Mn2O3 (meso‐Mn2O3) and meso‐Mn2O3‐supported Pd, Pt, and Pd‐Pt alloy x(PdyPt)/meso‐Mn2O3; x = (0.10?1.50) wt%; Pd/Pt molar ratio (y) = 4.9?5.1 nanocatalysts were prepared using KIT‐6‐templated and poly(vinyl alcohol)‐protected reduction methods, respectively.The meso‐Mn2O3 had a high surface area, i.e., 106 m2/g, and a cubic crystal structure. Noble‐metalnanoparticles (NPs) of size 2.1?2.8 nm were uniformly dispersed on the meso‐Mn2O3 surfaces. AlloyingPd with Pt enhanced the catalytic activity in methane combustion; 1.41(Pd5.1Pt)/meso‐Mn2O3gave the best performance; T10%, T50%, and T90% (the temperatures required for achieving methaneconversions of 10%, 50%, and 90%) were 265, 345, and 425 °C, respectively, at a space velocity of20000 mL/(g?h). The effects of SO2, CO2, H2O, and NO on methane combustion over1.41(Pd5.1Pt)/meso‐Mn2O3 were also examined. We conclude that the good catalytic performance of1.41(Pd5.1Pt)/meso‐Mn2O3 is associated with its high‐quality porous structure, high adsorbed oxygen species concentration, good low‐temperature reducibility, and strong interactions between Pd‐Pt alloy NPs and the meso‐Mn2O3 support.