The corundum - spinel castables were prepared by six kinds of tabular corundum, as aggregates, respective- ly, and their linear change rate on heating, apparent porosity, bulk density, cold modulus of rupture, coht cr...The corundum - spinel castables were prepared by six kinds of tabular corundum, as aggregates, respective- ly, and their linear change rate on heating, apparent porosity, bulk density, cold modulus of rupture, coht crushing strength, hot modulus of rupture and thermal shock resistance were compared and studied. The results show that： 1） the six tabular corundum materials have similar main chemical composition but their physical properties vary for the different technical procedures which result in different properties of castables ; 2 ） the optimal properties of corundum - spinel castables corre- spotut to different tabular corundum types, so the corundum type shall be selected according to the application of the castables.展开更多
Dense corundum-mullite brick for blast furnace ceramic pad was prepared using white fused corundum and tabular corundum as aggregates,andalusite fine powder,sillimanite fine powder,zircon sand powder and Guangxi soil ...Dense corundum-mullite brick for blast furnace ceramic pad was prepared using white fused corundum and tabular corundum as aggregates,andalusite fine powder,sillimanite fine powder,zircon sand powder and Guangxi soil as the matrix,and phosphate as the binder,introducing different amounts ofα-alumina micropowder,tabular corundum fine powder and fused corundum powder.The properties of the prepared brick were studied.The results show that,the brick with 10 mass%of tabular corundum fine powder fired at 1560℃for 3 h in a tunnel kiln has the bulk density of 3.08 g·cm^(-3),the apparent porosity of 13.2%,the cold compressive strength of 178 MPa,the molten iron corrosion rate of 0.6%,the slag corrosion rate of 6.4%,the alkali resistance strength decreasing rate of 7.5%,and the thermal shock resistance of 32 cycles,which is both dense and of good thermal shock resistance.The slag resistance simulation test was performed,which proved that the prepared corundum-mullite brick is better than those currently supplied in the market.展开更多
Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner c...Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner castables to investigate their influences on the flow ability, linear change on heating, bulk density, apparent porosity, cold strength, hot modulus of rupture, therm, al shock resistance, slag resistance, oxidation resistance as well as wear resistance of Al2O3 - SiC - C iron runner castables. The results show that （ 1 ） compared with the specimens with fused dense corundum, the specimens with dense sintered alumina have equivalent installation property, slag resistance and oxidation resistance, equivalent or even higher cold modulus of rupture, cold crushing strength and hot modulus of rupture, exhibiting better thermal shock resistance and cold wear resistance ; （2） adopting bimodal alumina micropowder LISAL22RABL as well as water reducers ZX2 and ZD2 can well reduce the water requirement of silica fume free castables, solving the problem of deteriorated flow ability resulted from the lack of silica fume; since the lack of silica fume avoids the formation of low melting point liquid, the hot modulus of rupture and the thermal shock resistance of the silica fume free castables are both better than those of the silica fume containing castables ; （3） the density of the castable specimens with dense sintered alumina is 4% -6% lower than that of the castable specimens with Jhsed dense corundum so the refractories consumption of one iron runner reduces by 5% by using the tastable with dense sintered alumina, which obviously reduces the cost of refractories.展开更多
文摘The corundum - spinel castables were prepared by six kinds of tabular corundum, as aggregates, respective- ly, and their linear change rate on heating, apparent porosity, bulk density, cold modulus of rupture, coht crushing strength, hot modulus of rupture and thermal shock resistance were compared and studied. The results show that： 1） the six tabular corundum materials have similar main chemical composition but their physical properties vary for the different technical procedures which result in different properties of castables ; 2 ） the optimal properties of corundum - spinel castables corre- spotut to different tabular corundum types, so the corundum type shall be selected according to the application of the castables.
文摘Dense corundum-mullite brick for blast furnace ceramic pad was prepared using white fused corundum and tabular corundum as aggregates,andalusite fine powder,sillimanite fine powder,zircon sand powder and Guangxi soil as the matrix,and phosphate as the binder,introducing different amounts ofα-alumina micropowder,tabular corundum fine powder and fused corundum powder.The properties of the prepared brick were studied.The results show that,the brick with 10 mass%of tabular corundum fine powder fired at 1560℃for 3 h in a tunnel kiln has the bulk density of 3.08 g·cm^(-3),the apparent porosity of 13.2%,the cold compressive strength of 178 MPa,the molten iron corrosion rate of 0.6%,the slag corrosion rate of 6.4%,the alkali resistance strength decreasing rate of 7.5%,and the thermal shock resistance of 32 cycles,which is both dense and of good thermal shock resistance.The slag resistance simulation test was performed,which proved that the prepared corundum-mullite brick is better than those currently supplied in the market.
文摘Three different kinds of corundum aggregates-tabular sintered alumina, dense sintered alumina, and fused dense corundum-were introduced into the silica fume .free or silica fume containing Al2O3 -SiC - C iron runner castables to investigate their influences on the flow ability, linear change on heating, bulk density, apparent porosity, cold strength, hot modulus of rupture, therm, al shock resistance, slag resistance, oxidation resistance as well as wear resistance of Al2O3 - SiC - C iron runner castables. The results show that （ 1 ） compared with the specimens with fused dense corundum, the specimens with dense sintered alumina have equivalent installation property, slag resistance and oxidation resistance, equivalent or even higher cold modulus of rupture, cold crushing strength and hot modulus of rupture, exhibiting better thermal shock resistance and cold wear resistance ; （2） adopting bimodal alumina micropowder LISAL22RABL as well as water reducers ZX2 and ZD2 can well reduce the water requirement of silica fume free castables, solving the problem of deteriorated flow ability resulted from the lack of silica fume; since the lack of silica fume avoids the formation of low melting point liquid, the hot modulus of rupture and the thermal shock resistance of the silica fume free castables are both better than those of the silica fume containing castables ; （3） the density of the castable specimens with dense sintered alumina is 4% -6% lower than that of the castable specimens with Jhsed dense corundum so the refractories consumption of one iron runner reduces by 5% by using the tastable with dense sintered alumina, which obviously reduces the cost of refractories.