The effects of preheating temperature and W powder size on the Self propagating High temperature Synthesis(SHS) of Ti W C system were studied. Preheated mixtures and the decrease of W powder size can accelerate the fo...The effects of preheating temperature and W powder size on the Self propagating High temperature Synthesis(SHS) of Ti W C system were studied. Preheated mixtures and the decrease of W powder size can accelerate the formation of (W,Ti)C powders. The uniphase (W,Ti)C (WC∶TiC=5∶5) powders with 0.32% free carbon were synthesized from Ti, W, C powders by SHS. The powder size of the product was 3~5 μm.展开更多
Titanium diboride based composites, good candidates for contact materials, have high hardness, Young's modulus, high temperature stability, and excellent electrical, thermal conductivity. However a good interface of ...Titanium diboride based composites, good candidates for contact materials, have high hardness, Young's modulus, high temperature stability, and excellent electrical, thermal conductivity. However a good interface of TiB2/Cu is very difficult to achieve for oxidation of TiB2. To avoid this oxidation behavior, the in situ combusting synthesis technology, SHS, was used to prepare TiB2/Cu composite. The characters of Ti-B-xCu SHS were studied in detail, such as combustion temperature, products phases and grain size. Based on the experimental results a proper technology way of self-high temperature synthesis plus quick press (SHS/QP) was determined and compact TiB2/Cu composites with relative density over than 97 pct of the theoretical were fabricated by this method. The properties and microstructures of these TiB2 based composites were also investigated.展开更多
TiC-TiB2-Cu composites were produced by self-propagating high-temperature synthesis combined with pseudo hot isostatic pressing using Ti, B4C and Cu powders. The microstructure and mechanical properties of the composi...TiC-TiB2-Cu composites were produced by self-propagating high-temperature synthesis combined with pseudo hot isostatic pressing using Ti, B4C and Cu powders. The microstructure and mechanical properties of the composites were investigated. The X-ray diffraction (XRD) and scanning electron microscopy (SEM) results showed that the final products were only TiC, TiB2 and Cu phases. The clubbed TiB2 grains and spheroidal or irregular TiC grains were found in the microstructure of synthesized products. The reaction temperature and grain size of TiB2 and TiC particles decreased with increasing Cu content. The introduction of Cu into the composites resulted in a drastic increase in the relative density and flexual strength, and the maximum values were obtained with the addition of 20 wt pct, while the fracture toughness was the best when Cu content was 40 wt pct.展开更多
Influence of Fe addition on products of self-propagating high-temperature synthesis (SHS) reaction in 3Ti-Si-2C system was investigated in the present study. Without Fe addition, Ti5Si3 and TiC are the dominant phases...Influence of Fe addition on products of self-propagating high-temperature synthesis (SHS) reaction in 3Ti-Si-2C system was investigated in the present study. Without Fe addition, Ti5Si3 and TiC are the dominant phases along with a small amount of Ti3SiC2 phase and unreacted C left in the final products. As Fe content ranges from 10% to 30%, the products consist of TiC, Ti5Si3, Fe2Ti and unreacted C, but no trace of Ti3SiC2 phase is detected. Furthermore, the amounts of both Fe2Ti and C phases increase with Fe content increasing. Addition of Fe has a great effect on the reaction route and significantly restrains the formation of Ti3SiC2 during the combustion synthesis process, and therefore, the SHS is not an effective fabrication technique to synthesize the ternary Ti3SiC2 ceramic in either 3Ti-Si-2C or Fe-3Ti-Si-2C system. Besides, without Fe addition, Ti5Si3 presents as the coarse irregular appearance with an obviously sintered morphology. In contrast, the shape of Ti5Si3 exhibits more and more spherical (cobblestone-like) and the surface becomes increasingly smooth, because the amount of liquids formed during the SHS reaction increases with the increase of Fe content. On the other hand, with Fe content increasing from 0 to 30 wt.%, the particulate size of TiC decreases from more than 5 μm to 1 μm or less, mainly due to the fact that the combustion temperature decreases with the increase of Fe content in the preforms.展开更多
High quality nano-sized zirconium carbide (ZrC) powders were successfully fabricated via a developed chemical active dilution self-propagating high-temperature synthesis (SHS) method assisted by ball milling pretr...High quality nano-sized zirconium carbide (ZrC) powders were successfully fabricated via a developed chemical active dilution self-propagating high-temperature synthesis (SHS) method assisted by ball milling pretreatment process using traditional cheap zirconium dioxide powder (ZrO2), magnesium powder (Mg) and sucrose (C12H22Oll) as raw materials. FSEM, TEM, HRTEM, SAED, XRD, FTIR and Raman, ICP- AES, laser particle size analyzer, oxygen and nitrogen analyzer, carbon/sulfur determinator and TG-DSC were employed for the characterization of the morphology, structure, chemical composition and thermal stability of the as-synthesized ZrC samples. The as-synthesized samples demonstrated high purity, low oxygen content and evenly distributed ZrC nano-powders with an average particle size of 50nm. In addition, the effects of endothermic rate and the possible chemical reaction mechanism were also discussed.展开更多
Using KClO3 as an inner oxidant, MnZn-ferrite powder was synthesized by a self-propagating high-temperature synthesis (SHS) process in normal air atmosphere. The effects of the inner oxidant on combustion temperature,...Using KClO3 as an inner oxidant, MnZn-ferrite powder was synthesized by a self-propagating high-temperature synthesis (SHS) process in normal air atmosphere. The effects of the inner oxidant on combustion temperature, combustion velocity, microstructure and the phase of the product were investigated by XRD and SEM,respectively. The results show that a highly ferritized powder can be obtained as well as the highest combustion temperature and the highest combustion velocity when the inner oxidant content m equals 54(k-16).展开更多
MoSi2 is presently regarded as the most important material for electrical heating and as one with huge potential for high temperature structural uses. MoSi2 and MoSi2 matrix composites were prepared by self-propagatin...MoSi2 is presently regarded as the most important material for electrical heating and as one with huge potential for high temperature structural uses. MoSi2 and MoSi2 matrix composites were prepared by self-propagating high temperature synthesis (SHS). Pure MoSi2 was obtained and a compound of MoSi2 and WSi2was synthesized in the form of predominant solid solution (Mo,W)Si2. By adding aluminum of 5.5 at.% to Mo-Si, the crystal structure of MoSi2 changed into a mixture of tetragonal Cllb MoSi2and hexagonal C40 Mo(Si,Al)2. The (Mo,W)Si2-Mo(Si,Al)2-W(Si,Al)2 composite materials were synthesized by adding aluminum of 5.5 at.% to Mo-W-Si. However, if the amount of the added aluminum was not larger than 2.5 at.%, it did not have any significant effect. SHS is an effective technology for synthesis of MoSi2 and MoSi2 matrix composites.展开更多
ZrB2 ceramics were prepared by self-propagating high-temperature synthesis(SHS) and were sintered by hot pressing(HP).The effects of the granularities and doses of raw materials in Zr-B2O3-Mgon SHS process and pro...ZrB2 ceramics were prepared by self-propagating high-temperature synthesis(SHS) and were sintered by hot pressing(HP).The effects of the granularities and doses of raw materials in Zr-B2O3-Mgon SHS process and product were investigated.XRD and combustion temperature curves prove that the ideal SHS reactants of Zr-B2O3-Mg are 50μm Zr powder,75μm B2O3 powder and 400μm Mg powder with 45% excessive.The particle sizes of SHS product,acid-leached product,sintered product are 2-5μm,0.5-2μm,2-10μm respectively.Chemical analysis indicates that the acid-leached product consists of ZrB2(94.59%),ZrO2(3.87%),and H3BO3(1.54%),The sintered product has a relative density of 95.4%.展开更多
The mechanism of self-propagating high-temperature synthesis (SHS) of TiC-Cu cermets was studied using a combustion front quenching method. Microstructural evolution in the quenched sample was observed using scannin...The mechanism of self-propagating high-temperature synthesis (SHS) of TiC-Cu cermets was studied using a combustion front quenching method. Microstructural evolution in the quenched sample was observed using scanning electron microscope (SEM) with energy dispersive X-ray (EDX) spectrometry, and the combustion temperature was measured. The results showed that the combustion reaction started with local formation of Ti-Cu melt and could be described with the dissolution-precipitation mechanism, namely, Ti, Cu, and C particles dissolved into the Ti-Cu solution and TiC particles precipitated in the saturated Ti-Cu-C liquid solution. The local formation of Ti-Cu melt resulted from the solid diffusion between Ti and Cu particles.展开更多
A method of estimating the safe storage life (τ), self-accelerating decomposition temperature (TsADT) and critical temperature of thermal explosion (Tb) of double-base propellant using isothermal and non-isothe...A method of estimating the safe storage life (τ), self-accelerating decomposition temperature (TsADT) and critical temperature of thermal explosion (Tb) of double-base propellant using isothermal and non-isothermal decomposition behaviours is presented. For double-base propellant composed of 56±1wt% of nitrocellulose (NC), 27±0.5wt% of nitroglycerine (NG), 8.15±0.15wt% of dinitrotoluene (DNT), 2.5±0.1wt% of methyl centralite, 5.0±0.15wt% of catalyst and 1.0±0.1wt% of other, the values of r of 49.4 years at 40℃, of TSAOT of 151.35℃ and of Tb of 163.01℃ were obtained.展开更多
Self-propagating high-temperature synthesis(SHS) method was used to synthesize ZrB2/Al2O3 composite powders from B2O3-ZrO2-Al system. X-ray diffractometry(XRD) and scanning electron microscopy(SEM) analyses show...Self-propagating high-temperature synthesis(SHS) method was used to synthesize ZrB2/Al2O3 composite powders from B2O3-ZrO2-Al system. X-ray diffractometry(XRD) and scanning electron microscopy(SEM) analyses show the presence of ZrB2 and Al2O3 as the primary phases in the composite powders, while the presence of a very small amount of ZrO2 is thought to be unreacted zirconium oxide. Transmission electron microscopy(TEM) and high resolution electron microscopy(HREM) observations of microstructure of the composite powders indicate that the interfaces of ZrB2/Al2O3 bond well without any interfacial reaction products. It is proposed that the good interfacial bonding of composite powders results from the ZrB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.展开更多
The effect of trace elements with zero self-interaction coefficient on crystallization temperature of iron carbon alloys was studied and the mathematic equation was developed based on thermodynamics in the present res...The effect of trace elements with zero self-interaction coefficient on crystallization temperature of iron carbon alloys was studied and the mathematic equation was developed based on thermodynamics in the present researeh. With the equation developed in this paper, the effects of nitrogen on crystallization temperature of Fe-3.45C-2.15Si0. 16Mn and Fe-3.45C-2. 15Si-0. 80Mn alloys were discussed.展开更多
In order to investigate the microstructural evolution during self-propagating high-temperature synthesis (SHS) of Ti-Al powder mixture with an atomic ratio of Ti: Al=1:1, a combustion front quenching method (CFQM...In order to investigate the microstructural evolution during self-propagating high-temperature synthesis (SHS) of Ti-Al powder mixture with an atomic ratio of Ti: Al=1:1, a combustion front quenching method (CFQM) was used for extinguishing the propagating combustion wave, and the microstructures on the quenched sample were observed with scanning electron microscope (SEM) and analyzed with energy dispersive spectrometry (EDS). In addition, the combustion temperature of the reaction was measured, and the phase constituent of the synthesized product was inspected by X-ray diffraction (XRD). The results showed that the combustion reaction started from melting of the Al particles, and the melting resulted in dissolving of the Ti particles and forming of Al3Ti grains. As the Al liquid was depleted, the combustion reaction proceeded through solid-state diffusion between the solid Al3Ti and the solid Ti. This led to the forming of TiAl and Ti3Al diffusing layers. In addition, the combustion reaction is incomplete besides TiAl, there are a large amount of Ti3Al and TiAl3 and a small amount of Ti in the final product. This incompleteness chiefly results from the using of coarser Ti powder.展开更多
Self-propagating high-temperature synthesis(SHS)was used to fabricate a Fe(Cr)–Al2O3 nanocomposite.The composite was fabricated by the reactions between the powders of Fe,Fe2O3,Cr2O3,and Al.The effect of blending rat...Self-propagating high-temperature synthesis(SHS)was used to fabricate a Fe(Cr)–Al2O3 nanocomposite.The composite was fabricated by the reactions between the powders of Fe,Fe2O3,Cr2O3,and Al.The effect of blending ratio and mechanical activation of the initial powders and the precursor compressing pressure on the microstructure of the final product was studied by optical microscopy,scanning electron microscopy,transmission electron microscopy,and X-ray diffraction.The significance of the effect of each of the aforementioned parameters on the quality of the composite(assessed by measuring the compressive strength and wear resistance)was determined using a full-factorial design of experiments method.The results showed that the best molar powder ratio that produced the most homogeneous product through a sustainable SHS reaction was Fe:Fe2O3:Cr2O3:Al=10:1:1:4.A lower Fe content caused the Fe(Cr)phase to melt and separate from the rest of the materials.展开更多
In the present work, we have studied the temporal evolution of aluminum alloy plasma produced by the fundamental (1064 nm) of a Q-switched Nd:YAG laser by placing the target material in air at atmospheric pressure. Th...In the present work, we have studied the temporal evolution of aluminum alloy plasma produced by the fundamental (1064 nm) of a Q-switched Nd:YAG laser by placing the target material in air at atmospheric pressure. The four Al I-neutral lines at 308.21, 309.27, 394.40 and 369.15 nm as well as Al II-ionic lines at 281.61, 385.64 and 466.30 nm are used for the determination of the electron temperature Te using Saha-Boltzmann plot method. The neutral aluminum lines were found to suffer from optical thickness which manifested itself on the form of scattered points around the Saha-Boltzmann line. The isolated optically thin hydrogen Hα-line at 656.27 nm appeared in the spectra under the same experimental conditions was used to correct the Al I-lines which contained some optical thickness. The measurements were repeated at different delay times ranging from 1 to 5 μs. The comparison between the deduced electron temperatures from aluminum neutral lines before correction against the effect self-absorption to that after correction revealed a precise value in temperature. The results sure that, in case of the presence of self-absorption effect the temperature varies from (1.4067 - 1.2548 eV) as the delay time is varied from 0 to 5 μs. Whereas, in the case of repairing against the effect, it varies from (1.2826 - 0.8961 eV) for the same delay time variation.展开更多
The relationship between the electrical resistivity of carbon fiber reinforced concrete(CFRC) containing different carbon fiber contents and temperature was studied.it is found that carbon fiber contents influence gre...The relationship between the electrical resistivity of carbon fiber reinforced concrete(CFRC) containing different carbon fiber contents and temperature was studied.it is found that carbon fiber contents influence greatly on the temperature sensibility of CFRC road material.Only with a certain amount of carbon fiber can CFRC show a sensitive and stable temperature sensibility.展开更多
文摘The effects of preheating temperature and W powder size on the Self propagating High temperature Synthesis(SHS) of Ti W C system were studied. Preheated mixtures and the decrease of W powder size can accelerate the formation of (W,Ti)C powders. The uniphase (W,Ti)C (WC∶TiC=5∶5) powders with 0.32% free carbon were synthesized from Ti, W, C powders by SHS. The powder size of the product was 3~5 μm.
基金the National Natural Science Foundation of China(No.59925207)the State Key Lab-oratory of New Nonferrous Metal Materials,Gansu University of Technology(No.2004016)for their financial support to this work.
文摘Titanium diboride based composites, good candidates for contact materials, have high hardness, Young's modulus, high temperature stability, and excellent electrical, thermal conductivity. However a good interface of TiB2/Cu is very difficult to achieve for oxidation of TiB2. To avoid this oxidation behavior, the in situ combusting synthesis technology, SHS, was used to prepare TiB2/Cu composite. The characters of Ti-B-xCu SHS were studied in detail, such as combustion temperature, products phases and grain size. Based on the experimental results a proper technology way of self-high temperature synthesis plus quick press (SHS/QP) was determined and compact TiB2/Cu composites with relative density over than 97 pct of the theoretical were fabricated by this method. The properties and microstructures of these TiB2 based composites were also investigated.
基金The work was supported by the Foundation of Aerospace Innovation Fund and the National Natural Science Foundation of China(No.90505015)the Foundation of National Key Laboratory for Remanufacturing.
文摘TiC-TiB2-Cu composites were produced by self-propagating high-temperature synthesis combined with pseudo hot isostatic pressing using Ti, B4C and Cu powders. The microstructure and mechanical properties of the composites were investigated. The X-ray diffraction (XRD) and scanning electron microscopy (SEM) results showed that the final products were only TiC, TiB2 and Cu phases. The clubbed TiB2 grains and spheroidal or irregular TiC grains were found in the microstructure of synthesized products. The reaction temperature and grain size of TiB2 and TiC particles decreased with increasing Cu content. The introduction of Cu into the composites resulted in a drastic increase in the relative density and flexual strength, and the maximum values were obtained with the addition of 20 wt pct, while the fracture toughness was the best when Cu content was 40 wt pct.
基金Support by the NNSFC (50671044 and 50531030)the NCET (06-0308)+1 种基金the Science and Technology Development Planning of Jilin Province (20070110)the Project 985-Automotive Engineering of Jilin University
文摘Influence of Fe addition on products of self-propagating high-temperature synthesis (SHS) reaction in 3Ti-Si-2C system was investigated in the present study. Without Fe addition, Ti5Si3 and TiC are the dominant phases along with a small amount of Ti3SiC2 phase and unreacted C left in the final products. As Fe content ranges from 10% to 30%, the products consist of TiC, Ti5Si3, Fe2Ti and unreacted C, but no trace of Ti3SiC2 phase is detected. Furthermore, the amounts of both Fe2Ti and C phases increase with Fe content increasing. Addition of Fe has a great effect on the reaction route and significantly restrains the formation of Ti3SiC2 during the combustion synthesis process, and therefore, the SHS is not an effective fabrication technique to synthesize the ternary Ti3SiC2 ceramic in either 3Ti-Si-2C or Fe-3Ti-Si-2C system. Besides, without Fe addition, Ti5Si3 presents as the coarse irregular appearance with an obviously sintered morphology. In contrast, the shape of Ti5Si3 exhibits more and more spherical (cobblestone-like) and the surface becomes increasingly smooth, because the amount of liquids formed during the SHS reaction increases with the increase of Fe content. On the other hand, with Fe content increasing from 0 to 30 wt.%, the particulate size of TiC decreases from more than 5 μm to 1 μm or less, mainly due to the fact that the combustion temperature decreases with the increase of Fe content in the preforms.
基金Funded by the Program for New Century Excellent Talents in University(No.NCET-12-0655)the Guangxi Natural Science Foundation(No.2014GXNSFFA118004)the Self-determined and Innovative Research Funds of WUT(Nos.136643002 and No.2013IV058)
文摘High quality nano-sized zirconium carbide (ZrC) powders were successfully fabricated via a developed chemical active dilution self-propagating high-temperature synthesis (SHS) method assisted by ball milling pretreatment process using traditional cheap zirconium dioxide powder (ZrO2), magnesium powder (Mg) and sucrose (C12H22Oll) as raw materials. FSEM, TEM, HRTEM, SAED, XRD, FTIR and Raman, ICP- AES, laser particle size analyzer, oxygen and nitrogen analyzer, carbon/sulfur determinator and TG-DSC were employed for the characterization of the morphology, structure, chemical composition and thermal stability of the as-synthesized ZrC samples. The as-synthesized samples demonstrated high purity, low oxygen content and evenly distributed ZrC nano-powders with an average particle size of 50nm. In addition, the effects of endothermic rate and the possible chemical reaction mechanism were also discussed.
文摘Using KClO3 as an inner oxidant, MnZn-ferrite powder was synthesized by a self-propagating high-temperature synthesis (SHS) process in normal air atmosphere. The effects of the inner oxidant on combustion temperature, combustion velocity, microstructure and the phase of the product were investigated by XRD and SEM,respectively. The results show that a highly ferritized powder can be obtained as well as the highest combustion temperature and the highest combustion velocity when the inner oxidant content m equals 54(k-16).
基金This project was financially supported by the National Natural Science Foundation of China (No. 50025412)
文摘MoSi2 is presently regarded as the most important material for electrical heating and as one with huge potential for high temperature structural uses. MoSi2 and MoSi2 matrix composites were prepared by self-propagating high temperature synthesis (SHS). Pure MoSi2 was obtained and a compound of MoSi2 and WSi2was synthesized in the form of predominant solid solution (Mo,W)Si2. By adding aluminum of 5.5 at.% to Mo-Si, the crystal structure of MoSi2 changed into a mixture of tetragonal Cllb MoSi2and hexagonal C40 Mo(Si,Al)2. The (Mo,W)Si2-Mo(Si,Al)2-W(Si,Al)2 composite materials were synthesized by adding aluminum of 5.5 at.% to Mo-W-Si. However, if the amount of the added aluminum was not larger than 2.5 at.%, it did not have any significant effect. SHS is an effective technology for synthesis of MoSi2 and MoSi2 matrix composites.
文摘ZrB2 ceramics were prepared by self-propagating high-temperature synthesis(SHS) and were sintered by hot pressing(HP).The effects of the granularities and doses of raw materials in Zr-B2O3-Mgon SHS process and product were investigated.XRD and combustion temperature curves prove that the ideal SHS reactants of Zr-B2O3-Mg are 50μm Zr powder,75μm B2O3 powder and 400μm Mg powder with 45% excessive.The particle sizes of SHS product,acid-leached product,sintered product are 2-5μm,0.5-2μm,2-10μm respectively.Chemical analysis indicates that the acid-leached product consists of ZrB2(94.59%),ZrO2(3.87%),and H3BO3(1.54%),The sintered product has a relative density of 95.4%.
基金This work was financially supported by the Natural Science Foundation of Shaanxi Province, China (No.2004E107)
文摘The mechanism of self-propagating high-temperature synthesis (SHS) of TiC-Cu cermets was studied using a combustion front quenching method. Microstructural evolution in the quenched sample was observed using scanning electron microscope (SEM) with energy dispersive X-ray (EDX) spectrometry, and the combustion temperature was measured. The results showed that the combustion reaction started with local formation of Ti-Cu melt and could be described with the dissolution-precipitation mechanism, namely, Ti, Cu, and C particles dissolved into the Ti-Cu solution and TiC particles precipitated in the saturated Ti-Cu-C liquid solution. The local formation of Ti-Cu melt resulted from the solid diffusion between Ti and Cu particles.
基金We are grateful to the National Natural Science Foundation of China (No. 20573098)
文摘A method of estimating the safe storage life (τ), self-accelerating decomposition temperature (TsADT) and critical temperature of thermal explosion (Tb) of double-base propellant using isothermal and non-isothermal decomposition behaviours is presented. For double-base propellant composed of 56±1wt% of nitrocellulose (NC), 27±0.5wt% of nitroglycerine (NG), 8.15±0.15wt% of dinitrotoluene (DNT), 2.5±0.1wt% of methyl centralite, 5.0±0.15wt% of catalyst and 1.0±0.1wt% of other, the values of r of 49.4 years at 40℃, of TSAOT of 151.35℃ and of Tb of 163.01℃ were obtained.
基金Project(KNH2021005) supported by Industrialization Programof Economic Committee of Shanghai
文摘Self-propagating high-temperature synthesis(SHS) method was used to synthesize ZrB2/Al2O3 composite powders from B2O3-ZrO2-Al system. X-ray diffractometry(XRD) and scanning electron microscopy(SEM) analyses show the presence of ZrB2 and Al2O3 as the primary phases in the composite powders, while the presence of a very small amount of ZrO2 is thought to be unreacted zirconium oxide. Transmission electron microscopy(TEM) and high resolution electron microscopy(HREM) observations of microstructure of the composite powders indicate that the interfaces of ZrB2/Al2O3 bond well without any interfacial reaction products. It is proposed that the good interfacial bonding of composite powders results from the ZrB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.
文摘The effect of trace elements with zero self-interaction coefficient on crystallization temperature of iron carbon alloys was studied and the mathematic equation was developed based on thermodynamics in the present researeh. With the equation developed in this paper, the effects of nitrogen on crystallization temperature of Fe-3.45C-2.15Si0. 16Mn and Fe-3.45C-2. 15Si-0. 80Mn alloys were discussed.
文摘In order to investigate the microstructural evolution during self-propagating high-temperature synthesis (SHS) of Ti-Al powder mixture with an atomic ratio of Ti: Al=1:1, a combustion front quenching method (CFQM) was used for extinguishing the propagating combustion wave, and the microstructures on the quenched sample were observed with scanning electron microscope (SEM) and analyzed with energy dispersive spectrometry (EDS). In addition, the combustion temperature of the reaction was measured, and the phase constituent of the synthesized product was inspected by X-ray diffraction (XRD). The results showed that the combustion reaction started from melting of the Al particles, and the melting resulted in dissolving of the Ti particles and forming of Al3Ti grains. As the Al liquid was depleted, the combustion reaction proceeded through solid-state diffusion between the solid Al3Ti and the solid Ti. This led to the forming of TiAl and Ti3Al diffusing layers. In addition, the combustion reaction is incomplete besides TiAl, there are a large amount of Ti3Al and TiAl3 and a small amount of Ti in the final product. This incompleteness chiefly results from the using of coarser Ti powder.
文摘Self-propagating high-temperature synthesis(SHS)was used to fabricate a Fe(Cr)–Al2O3 nanocomposite.The composite was fabricated by the reactions between the powders of Fe,Fe2O3,Cr2O3,and Al.The effect of blending ratio and mechanical activation of the initial powders and the precursor compressing pressure on the microstructure of the final product was studied by optical microscopy,scanning electron microscopy,transmission electron microscopy,and X-ray diffraction.The significance of the effect of each of the aforementioned parameters on the quality of the composite(assessed by measuring the compressive strength and wear resistance)was determined using a full-factorial design of experiments method.The results showed that the best molar powder ratio that produced the most homogeneous product through a sustainable SHS reaction was Fe:Fe2O3:Cr2O3:Al=10:1:1:4.A lower Fe content caused the Fe(Cr)phase to melt and separate from the rest of the materials.
文摘In the present work, we have studied the temporal evolution of aluminum alloy plasma produced by the fundamental (1064 nm) of a Q-switched Nd:YAG laser by placing the target material in air at atmospheric pressure. The four Al I-neutral lines at 308.21, 309.27, 394.40 and 369.15 nm as well as Al II-ionic lines at 281.61, 385.64 and 466.30 nm are used for the determination of the electron temperature Te using Saha-Boltzmann plot method. The neutral aluminum lines were found to suffer from optical thickness which manifested itself on the form of scattered points around the Saha-Boltzmann line. The isolated optically thin hydrogen Hα-line at 656.27 nm appeared in the spectra under the same experimental conditions was used to correct the Al I-lines which contained some optical thickness. The measurements were repeated at different delay times ranging from 1 to 5 μs. The comparison between the deduced electron temperatures from aluminum neutral lines before correction against the effect self-absorption to that after correction revealed a precise value in temperature. The results sure that, in case of the presence of self-absorption effect the temperature varies from (1.4067 - 1.2548 eV) as the delay time is varied from 0 to 5 μs. Whereas, in the case of repairing against the effect, it varies from (1.2826 - 0.8961 eV) for the same delay time variation.
文摘The relationship between the electrical resistivity of carbon fiber reinforced concrete(CFRC) containing different carbon fiber contents and temperature was studied.it is found that carbon fiber contents influence greatly on the temperature sensibility of CFRC road material.Only with a certain amount of carbon fiber can CFRC show a sensitive and stable temperature sensibility.