Tensile strength and failure behavior of rock-mortar interfaces: Direct and indirect measurements

The tensile strength at the rock-concrete interface is one of the crucial factors controlling the failure mechanisms of structures,such as concrete gravity dams.Despite the critical importance of the failure mechanism and tensile strength of rock-concrete interfaces,understanding of these factors remains very limited.This study investigated the tensile strength and fracturing processes at rock-mortar interfaces subjected to direct and indirect tensile loadings.Digital image correlation(DIC)and acoustic emission(AE)techniques were used to monitor the failure mechanisms of specimens subjected to direct tension and indirect loading(Brazilian tests).The results indicated that the direct tensile strength of the rock-mortar specimens was lower than their indirect tensile strength,with a direct/indirect tensile strength ratio of 65%.DIC strain field data and moment tensor inversions(MTI)of AE events indicated that a significant number of shear microcracks occurred in the specimens subjected to the Brazilian test.The presence of these shear microcracks,which require more energy to break,resulted in a higher tensile strength during the Brazilian tests.In contrast,microcracks were predominantly tensile in specimens subjected to direct tension,leading to a lower tensile strength.Spatiotemporal monitoring of the cracking processes in the rock-mortar interfaces revealed that they show AE precursors before failure under the Brazilian test,whereas they show a minimal number of AE events before failure under direct tension.Due to different microcracking mechanisms,specimens tested under Brazilian tests showed lower roughness with flatter fracture surfaces than those tested under direct tension with jagged and rough fracture surfaces.The results of this study shed light on better understanding the micromechanics of damage in the rock-concrete interfaces for a safer design of engineering structures.

Pyridinic-N doping carbon layers coupled with tensile strain of FeNi alloy for activating water and urea oxidation

Exploitation of oxygen evolution reaction(OER)and urea oxidation reaction(UOR)catalysts with high activity and stability at large current density is a major challenge for energy-saving H_(2) production in water electrolysis.Herein,we use the pyridinic-N doping carbon layers coupled with tensile strain of FeNi alloy activated by NiFe_(2)O_(4)(FeNi/NiFe_(2)O_(4)@NC)for efficiently increasing the performance of water and urea oxidation.Due to the tensile strain effect on FeNi/NiFe_(2)O_(4)@NC,it provides a favorable modulation on the electronic properties of the active center,thus enabling amazing OER(η_(100)=196 mV)and UOR(E_(10)=1.32 V)intrinsic activity.Besides,the carbon-coated layers can be used as armor to prevent FeNi alloy from being corroded by the electrolyte for enhancing the OER/UOR stability at large current density,showing high industrial practicability.This work thus provides a simple way to prepare high-efficiency catalyst for activating water and urea oxidation.

Strengthening effect of prefabrication(10-12)tensile twinning on AZ80+0.4%Ce magnesium alloy and inhibition mechanism of discontinuous precipitation

This paper provided an effective method to further improve the mechanical properties of the AZ80+0.4%Ce magnesium alloy wheel spoke.The effect of high strength and ductility was obtained with a yield strength of 295.36 MPa,an elongation of 10%,by the combination of pre-deformation(7%deformation)and two-stage aging treatment(120℃/9 h+175℃/24 h).The evolution of the microstructure and properties of the alloy was explored under the coupling conditions of different pre-deformation degrees and multi-stage aging.The results show that,pre-deformation introduced a large number of(1012)tensile twinning and dislocations,which greatly promoted the probability of continuous precipitates(CPs)appearing.On the contrary,the discontinuous precipitates(DPs)were limited by the vertical and horizontal twin structure.As a result,the pre-nucleation method of two-stage aging increased the proportion of CPs by 34%-38%.Owing to the DPs was effectively suppressed,the alloy's yield strength has been greatly improved.Besides,under multi-stage aging,the twin boundaries induce protruding nucleation to form static recrystallization by hindering the migration of dislocations,and the matrix swallows the twins,then the texture gradually tilts from the two poles to the basal plane.As an important supplement,the grain refinement and oblique texture promoted the improvement of the yield strength of the component.

Effect of brazing temperature on microstructure and tensile strength ofγ-TiAl joint vacuum brazed with micro-nano Ti−Cu−Ni−Nb−Al−Hf filler

A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the relationships among brazing temperature,interfacial microstructure and joint strength were emphatically investigated.Results show that the TiAl joints brazed at 1160 and 1180℃ possess three interfacial layers and mainly consist of α_(2)-Ti_(3)Al,τ_(3)-Al_(3)NiTi_(2) and Ti_(2)Ni,but the brazing seams are no longer layered and Ti_(2)Ni is completely replaced by the uniformly distributed τ_(3)-Al_(3)NiTi_(2) at 1200 and 1220℃ due to the destruction of α_(2)-Ti_(3)Al barrier layer.This transformation at 1200℃ obviously improves the tensile strength of the joint and obtains a maximum of 343 MPa.Notably,the outward diffusion of Al atoms from the dissolution of TiAl substrate dominates the microstructure evolution and tensile strength of the TiAl joint at different brazing temperatures.

Tensile Strain Capacity Prediction of Engineered Cementitious Composites (ECC) Using Soft Computing Techniques

Plain concrete is strong in compression but brittle in tension,having a low tensile strain capacity that can significantly degrade the long-term performance of concrete structures,even when steel reinforcing is present.In order to address these challenges,short polymer fibers are randomly dispersed in a cement-based matrix to forma highly ductile engineered cementitious composite(ECC).Thismaterial exhibits high ductility under tensile forces,with its tensile strain being several hundred times greater than conventional concrete.Since concrete is inherently weak in tension,the tensile strain capacity(TSC)has become one of the most extensively researched properties.As a result,developing a model to predict the TSC of the ECC and to optimize the mixture proportions becomes challenging.Meanwhile,the effort required for laboratory trial batches to determine the TSC is reduced.To achieve the research objectives,five distinct models,artificial neural network(ANN),nonlinear model(NLR),linear relationship model(LR),multi-logistic model(MLR),and M5P-tree model(M5P),are investigated and employed to predict the TSCof ECCmixtures containing fly ash.Data from115 mixtures are gathered and analyzed to develop a new model.The input variables include mixture proportions,fiber length and diameter,and the time required for curing the various mixtures.The model’s effectiveness is evaluated and verified based on statistical parameters such as R2,mean absolute error(MAE),scatter index(SI),root mean squared error(RMSE),and objective function(OBJ)value.Consequently,the ANN model outperforms the others in predicting the TSC of the ECC,with RMSE,MAE,OBJ,SI,and R2 values of 0.42%,0.3%,0.33%,0.135%,and 0.98,respectively.

Effect of hot isostatic pressure on the microstructure and tensile properties of γ'-strengthened superalloy fabricated through induction-assisted directed energy deposition

The microstructure characteristics and strengthening mechanism of Inconel738LC(IN-738LC) alloy prepared by using induction-assisted directed energy deposition(IDED) were elucidated through the investigation of samples subjected to IDED under 1050℃ preheating with and without hot isostatic pressing(HIP,1190℃,105 MPa,and 3 h).Results show that the as-deposited sample mainly consisted of epitaxial columnar crystals and inhomogeneously distributed γ’ phases in interdendritic and dendritic core regions.After HIP,grain morphology changed negligibly,whereas the size of the γ’ phase became increasingly even.After further heat treatment(HT,1070℃,2 h + 845℃,24 h),the γ’ phase in the as-deposited and HIPed samples presented a bimodal size distribution,whereas that in the as-deposited sample showed a size that remained uneven.The comparison of tensile properties revealed that the tensile strength and uniform elongation of the HIP + HTed sample increased by 5% and 46%,respectively,due to the synergistic deformation of bimodal γ’phases,especially large cubic γ’ phases.Finally,the relationship between phase transformations and plastic deformations in the IDEDed sample was discussed on the basis of generalized stability theory in terms of the trade-off between thermodynamics and kinetics.

Effect of slow shot speed on externally solidified crystal,porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy

The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).

Size effects on the tensile strength and fracture toughness of granitic rock in different tests

This study investigates the tensile failure mechanisms in granitic rock samples at different scales by means of different types of tests.To do that,we have selected a granitic rock type and obtained samples of different sizes with the diameter ranging from 30 mm to 84 mm.The samples have been subjected to direct tensile strength(DTS)tests,indirect Brazilian tensile strength(BTS)tests and to two fracture toughness testing approaches.Whereas DTS and fracture toughness were found to consistently grow with sample size,this trend was not clearly identified for BTS,where after an initial grow,a plateau of results was observed.This is a rather complete database of tensile related properties of a single rock type.Even if similar databases are rare,the obtained trends are generally consistent with previous scatter and partial experimental programs.However,different observations apply to different types of rocks and experimental approaches.The differences in variability and mean values of the measured parameters at different scales are critically analysed based on the heterogeneity,granular structure and fracture mechanics approaches.Some potential relations between parameters are revised and an indication is given on potential sample sizes for obtaining reliable results.Extending this database with different types of rocks is thought to be convenient to advance towards a better understanding of the tensile strength of rock materials.

Effect of the mineral spatial distribution heterogeneity on the tensile strength of granite:Insights from PFC3D-GBM numerical analysis

The mechanical characteristics of crystalline rocks are affected by the heterogeneity of the spatial distribution of minerals.In this paper,a novel three-dimensional(3D)grain-based model(GBM)based on particle flow code(PFC),i.e.PFC3D-GBM,is proposed.This model can accomplish the grouping of mineral grains at the 3D scale and then filling them.Then,the effect of the position distribution,geometric size,and volume composite of mineral grains on the cracking behaviour and macroscopic properties of granite are examined by conducting Brazilian splitting tests.The numerical results show that when an external load is applied to a sample,force chains will form around each contact,and the orientation distribution of the force chains is uniform,which is independent of the external load level.Furthermore,the number of high-strength force chains is proportional to the external load level,and the main orientation distribution is consistent with the external loading direction.The main orientation of the cracks is vertical to that of the high-strength force chains.The geometric size of the mineral grains controls the mechanical behaviours.As the average grain size increases,the number of transgranular contacts with higher bonding strength in the region connecting both loading points increases.The number of high-strength force chains increases,leading to an increase in the stress concentration value required for the macroscopic failure of the sample.Due to the highest bonding strength,the generation of transgranular cracks in quartz requires a higher concentrated stress value.With increasing volume composition of quartz,the number of transgranular cracks in quartz distributed in the region connecting both loading points increases,which requires many high-strength force chains.The load level rises,leading to an increase in the tensile strength of the numerical sample.

Correction of dynamic Brazilian disc tensile strength of rocks under preloading conditions considering the overload phenomenon and invoking the Griffith criterion

Dynamic tensile failure is a common phenomenon in deep rock practices,and thus accurately evaluating the dynamic tensile responses of rocks under triaxial pressures is of great significance.The Brazilian disc(BD)test is the suggested method by the International Society for Rock Mechanics and Rock Engineering(ISRM)for measuring both the static and dynamic tensile strengths of rock-like materials.However,due to the overload phenomenon and the complex preloading conditions,the dynamic tensile strengths of rocks measured by the BD tests tend to be overestimated.To address this issue,the dynamic BD tensile strength(BTS)of Fangshan marble(FM)under different preloading conditions were measured through a triaxial split Hopkinson pressure bar(SHPB).The fracture onset in BD specimen was captured through a strain gage around the disc center.The discrepancy between the traditional tensile strength(TTS,determined by the peak load P_(f) of the BD specimen)and the nominal tensile strength(NTS,obtained from the load P_(i) when the diametral fracture commences in the tested BD specimen)was applied to quantitatively evaluating the overload phenomenon.The Griffith criterion was used to rectify the calculation of the tensile stress at the disc center under triaxial stress states.The results demonstrate that the overload ratio(s)increases with the loading rate(σ)and decreases with the hydrostatic pressure(σ_(s)).The TTS corrected by the Griffith criterion is independent of theσ_(s)due to the overload phenomenon,while the NTS corrected by the Griffith criterion is sensitive to both the andσ.Therefore,it is essential to modify the tensile stress in dynamic confined BD tests using both the overload correction and the Griffith criterion rectification to obtain the accurate dynamic BTS of rocks.

Effects of magnesium and copper additions on tensile properties of Al-Si-Cr die casting alloy under as-cast and T5 conditions

Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.

Effect of Cooling Rates on Solidification Microstructures and Tensile Property of a Novel Wrought Superalloy

The effects of cooling rates on solidification behaviors,segregation characteristics and tensile property of GH4151 alloy were investigated using microstructure characterization and tensile test.Firstly,a relationship between the secondary dendrite arm spacing and cooling rate was determined and it was confirmed to be valid.Secondly,it can be found from microstructure observations that the morphology of(Nb,Ti)C carbides transits from blocky and script type to fine script type and spotty type,and the refinedγ'phase was observed due to decrease of segregation with increasing cooling rates.Thirdly,the solidification microstructures of the industrial-scale samples were analyzed.The morphology ofηphase changes from indistinguishable shape,fine needle-like shape to large block-like shape with increasing ingot diameter.As a result,the mechanical properties of alloy decrease due to increase of brittle precipitations.The experimental results show that the precipitation behavior of GH4151 is affected by segregation degree of elements,and the segregation degree is determined by solute distribution process and solid back-diffusion process.

Experimental study on tensile deformation behaviors under room and elevated temperatures induced by microstructure inhomogeneity of ZK60 Mg with a longitudinal weld

The tensile tests of the extruded ZK60 Mg containing a longitudinal weld seam were carried out at room and elevated temperatures, and the effects of induced microstructure inhomogeneity on tensile deformation behavior was clarified. The results show that the deformation mode, dynamic recrystallization(DRX), texture evolution and mechanical properties are strongly affected by the longitudinal weld seam,temperature, and loading direction. The room temperature(RT) deformation of welding zone is controlled by the dislocation slips with the association of some twins, while twinning plays significant roles in the accommodation of c-axis strain of the coarse grains on matrix zone.The deformation at RT stretched along extrusion direction(ED) and transverse direction(TD) are controlled by basal slip/twinning and basal slip/prismatic slip/twinning, respectively. During high temperature tension, the dislocation cross slip of pyramidal slip is activated, and grain boundary sliding occurred in welding zone, leading to the superplastic behavior. With the increase of tensile temperature, the predominant DRX mode is transformed from continuous DRX to discontinuous DRX. Moreover, the basal poles of the grains spread from TD towards ED with the decrease of maximum pole intensity when stretched along ED, while non-basal textures are transformed to (10-10) fiber texture when stretched along TD. The slip-dominated flow is seen during RT tension along ED, while twinning becomes predominant during RT tension along TD. The fine grain structure causes the superior RT tensile properties along ED of welding zone with ultimate tensile strength of 315 MPa and elongation to failure of 13.8%. With the increase of tensile temperature, the slipping-dominated deformation is transformed into twinning-dominated, causing the decrease of strength and increase of elongation.

Tensile Properties and Prediction Model of Recombinant Bamboo at Different Temperatures

The destruction of recombinant bamboo depends on many factors,and the complex ambient temperature is an important factor affecting its basic mechanical properties.To investigate the failure mechanism and stress–strain relationship of recombinant bamboo at different temperatures,eighteen tensile specimens of recombinant bamboo were tested.The results showed that with increasing ambient temperature,the typical failure modes of recombinant bamboo were flush fracture,toothed failure,and serrated failure.The ultimate tensile strength,ultimate strain and elastic modulus of recombinant bamboo decreased with increasing temperature,and the ultimate tensile stress decreased from 154.07 to 96.55 MPa,a decrease of 37.33%,and the ultimate strain decreased from 0.011 to 0.008,a decrease of 26.57%.Based on the Ramberg-Osgood model and the pseudo‒elastic design method,a predictive model was established for the tensile stress–strain relationship of recombinant bamboo considering the temperature level.The model can accurately evaluate the tensile stress–strain relationship of recombinant bamboo under different temperature conditions.

A Fuzzy Logic Approach to Predict Tensile Strength in TIG Mild Steel Welds

Welding defects influence the desired properties of welded joints giving fabrication experts a common problem of not being able to produce weld structures with optimal strength and quality. In this study, the fuzzy logic system was employed to predict welding tensile strength. 30 sets of welding experiments were conducted and tensile strength data was collected which were converted from crisp variables into fuzzy sets. The result showed that the fuzzy logic tool is a highly effective tool for predicting tensile strength present in TIG mild steel weld having a coefficient of determination value of 99%.

Effect of Strain Rate on Tensile Behavior of Sn-9Zn-xAg-ySb;{(x, y) = (0.2, 0.6), (0.2, 0.8), (0.6, 0.2), (0.8, 0.2)} Lead-Free Solder Alloys

The tensile properties of Sn-9Zn-xAg-ySb;{(x, y) = (0.2, 0.6), (0.2, 0.8), (0.6, 0.2), (0.8, 0.2)} lead-free solders were investigated. All the test samples were annealed at 150°C for 1 hour. The tests are carried out at room temperature at the strain rate of 4.17 × 10-3 s-1, 20.85 × 10-3 s-1, and 208.5 × 10-3 s-1. It is seen that the tensile strength increases and the ductility decrease with increasing the strain rate over the investigated range. From the strain rate change test results, the strain sensitivity values are found in the range of 0.0831 to 0.1455 due to the addition of different alloying elements.

Mesoscopic modelling of UHPCC material under dynamic tensile loadings

This paper presents a new 3D mesoscopic model of ultra-high performance cement-based composite(UHPCC)to investigate its dynamic tensile behavior.In this model,the UHPCC is regarded as a two-phase material composed of cementitious matrix and randomly distributed fibers.The model is established using the commercial software LS-DYNA and involves generating the randomly distributed fiber elements with considerations of diameter,length,orientation and volume fraction,and then fully constraining them with the matrix.In particular,to capture the slipping effect between fibers and matrix that has a strong influence on the dynamic tensile behavior,the fibers are modelled by a fictitious material represented by the load-slip relation.The strain-rate effect of slipping force neglected in most of previous studies is considered by calibrating constitutive parameters of the fictitious material under different strain-rates based on the single fiber pullout tests.Finally,the 3D mesoscopic model is validated against three sets of tension-dominated experiments covered a wide range of loading intensity.Numerical predictions demonstrate that strain-rate effect of slipping force must be considered,and the neglect of it may lead to a great underestimation of the dynamic tensile strength of UHPCC material and would unavoidably underestimate the blast resistance of UHPCC components.

Multiscale tensegrity model for the tensile properties of DNA nanotubes

DNA nanotubes(DNTs)with user-defined shapes and functionalities have potential applications in many fields.So far,compared with numerous experimental studies,there have been only a handful of models on the mechanical properties of such DNTs.This paper aims at presenting a multiscale model to quantify the correlations among the pre-tension states,tensile properties,encapsulation structures of DNTs,and the surrounding factors.First,by combining a statistical worm-like-chain(WLC)model of single DNA deformation and Parsegian's mesoscopic model of DNA liquid crystal free energy,a multiscale tensegrity model is established,and the pre-tension state of DNTs is characterized theoretically for the first time.Then,by using the minimum potential energy principle,the force-extension curve and tensile rigidity of pre-tension DNTs are predicted.Finally,the effects of the encapsulation structure and surrounding factors on the tensile properties of DNTs are studied.The predictions for the tensile behaviors of DNTs can not only reproduce the existing experimental results,but also reveal that the competition of DNA intrachain and interchain interactions in the encapsulation structures determines the pre-tension states of DNTs and their tensile properties.The changes in the pre-tension states and environmental factors make the monotonic or non-monotonic changes in the tensile properties of DNTs under longitudinal loads.

Improved continuous precipitation kinetics and tensile properties of extruded AZ80 alloy through {10-12} twin formation

This study investigates the effect of{10-12}deformation twins on the continuous precipitation behavior of an extruded Mg-8.0Al-0.5Zn-0.2Mn(AZ80)alloy during aging.The extruded AZ80 alloy is compressed along the transverse direction to introduce{10-12}twins,followed by an aging treatment at 300℃.The extruded material exhibits a twin-free microstructure with low internal strain energy,whereas the pre-twinned material possesses abundant{10-12}twins and has high internal strain energy.The aging results reveal that the peak-aging time of the pre-twinned material(1 h)is one-eighth of that of the extruded material(8 h).Although Mg_(17)Al_(12)continuous precipitates(CPs)are observed in both the peak-aged materials,these CPs are much smaller and more densely distributed in the pre-twinned material despite the significantly shorter aging time.The CPs size in the peak-aged materials increases in the following order:twinned region in the pre-twinned material(0.47μm)<residual matrix region in the pre-twinned material(1.71μm)<matrix region in the extruded material(2.55μm).Moreover,the CPs number density in the twinned region of the pre-twinned material is approximately 11 times higher than that in the matrix region of the extruded material.The peak-aged pre-twinned material exhibits significantly higher tensile strength and ductility than the peak-aged extruded material.These results demonstrate that the formation of{10-12}twins in the extruded AZ80 alloy substantially accelerates the static precipitation of CPs during aging at 300℃and improves the tensile properties of the peak-aged material.

Influence of uniaxial tensile pre-strain on forming limit curve by using biaxial tensile test

This paper focused on the effect of pre-strain on forming limit curves(FLC)of 5754-O aluminum alloy sheet through utilizing biaxial tensile approach.Based on Swift model and Yld2000-2 d yield criterion,the dimensions of cruciform specimen was optimized through applying finite element method for increasing the strain at specimen center.After that,with the recommended specimen size,the cruciform specimen was tested under various stroke ratios to experimentally characterize the limit strains under different pre-strain levels.Subsequently,the biaxial tensile tests were simulated by Abaqus to obtain the limit strains and validate the material models.It can be observed in both experiments and simulations that the pre-strained uniaxial tension followed by plane tension or equi-biaxial tension can improve the formability of sheet metals.Besides,the strain path change affects the trend of first derivative of strain rate difference between neighboring points with respect to time.An early increase occurred and then fell back to the stable value,the steady evolution continued until to a new increase reaching the critical value.The M–K prediction approach was simulated to verify the influence of pre-strain on FLC.It can be found that the early increase peaks of the major strain incremental ratio rose with the amplitude of pre-strain.Finally,the phenomenon of pseudolocalization caused by the strain path change was explained through evolution of stress state inside the groove.