低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度...低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度因子、J积分塑性因子、J积分与CTOD转换因子、裂纹尺寸测量方法、数字图像相关方法等关键问题进行对比分析,总结需要深入研究的问题,为低约束试件断裂韧性测试发展提供一定依据。展开更多
Fracture toughness measurement is an integral part of structural integrity assessment of pipelines. Traditionally, a single-edge-notched bend （SE（B）） specimen with a deep crack is recommended in many existing pipe...Fracture toughness measurement is an integral part of structural integrity assessment of pipelines. Traditionally, a single-edge-notched bend （SE（B）） specimen with a deep crack is recommended in many existing pipeline structural integrity assessment procedures. Such a test provides high constraint and therefore conservative fracture toughness results. However, for girth welds in service, defects are usually subjected to primarily tensile loading where the constraint is usually much lower than in the three-point bend case. Moreover, there is increasing use of strain-based design of pipelines that allows applied strains above yield. Low-constraint toughness tests represent more realistic loading conditions for girth weld defects, and the corresponding increased toughness can minimize unnecessary conservatism in assessments. In this review, we present recent developments in low-constraint fracture toughness testing, specifically using single-edge- notched tension specimens, SENT or SE（T）. We focus our review on the test procedure development and automation, round-robin test results and some common concerns such as the effect of crack tip, crack size monitoring techniques, and testing at low temperatures. Examples are also given of the integration of fracture toughness data from SE（T） tests into structural integrity assessment.展开更多
文摘低约束试件断裂韧性测试对油气管道安全运营具有重要意义。本文回顾了低约束试件断裂韧性测试方法及发展过程,介绍了裂纹尖端张开位移(crack tip opening displacement,CTOD)和J积分等常用断裂韧性表征参数,并对断裂韧性测试中应力强度因子、J积分塑性因子、J积分与CTOD转换因子、裂纹尺寸测量方法、数字图像相关方法等关键问题进行对比分析,总结需要深入研究的问题,为低约束试件断裂韧性测试发展提供一定依据。
文摘Fracture toughness measurement is an integral part of structural integrity assessment of pipelines. Traditionally, a single-edge-notched bend （SE（B）） specimen with a deep crack is recommended in many existing pipeline structural integrity assessment procedures. Such a test provides high constraint and therefore conservative fracture toughness results. However, for girth welds in service, defects are usually subjected to primarily tensile loading where the constraint is usually much lower than in the three-point bend case. Moreover, there is increasing use of strain-based design of pipelines that allows applied strains above yield. Low-constraint toughness tests represent more realistic loading conditions for girth weld defects, and the corresponding increased toughness can minimize unnecessary conservatism in assessments. In this review, we present recent developments in low-constraint fracture toughness testing, specifically using single-edge- notched tension specimens, SENT or SE（T）. We focus our review on the test procedure development and automation, round-robin test results and some common concerns such as the effect of crack tip, crack size monitoring techniques, and testing at low temperatures. Examples are also given of the integration of fracture toughness data from SE（T） tests into structural integrity assessment.