Three kinds of tetrapod-like ZnO nanostructures have been synthesized simultaneously via pure Zn chemical vapor deposition on silicon wafers with (111) orientation (Si (111)) at 920 ℃. X-ray diffraction indicat...Three kinds of tetrapod-like ZnO nanostructures have been synthesized simultaneously via pure Zn chemical vapor deposition on silicon wafers with (111) orientation (Si (111)) at 920 ℃. X-ray diffraction indicates that the nanotetrapods are of wurtzite structure. The morphology and the microstructure of the nanotetrapods are investigated by the scanning electron microscopy. Selected area electron diffraction shows the growth direction, and energy dispersive X-ray spectroscopy reveals the atomic composition ratio of Zn/O. The growth process is briefly discussed. The optical property of the products was also recorded by means of photoluminescence spectroscopy.展开更多
Large and uniform tetrapod-like ZnO whiskers (T-ZnO) were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The...Large and uniform tetrapod-like ZnO whiskers (T-ZnO) were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The products are pure hexagonal wurtzite crystals with tetrapod shape and edge size of center body 56 μm and needle length of 100130 μm. The size and shape of ZnO particles are fully controlled by the growth conditions and T-ZnO can be obtained only at 8501 000 ℃ and total gas flow rate ranging from 40 to 250 L·h-1 in which the size of the T-ZnO particles varies slightly with temperature. The process of the formation of T-ZnO is that T-ZnO may nucleate at the initial stage with a complete tetrapod shape and develop to the large size, but not the process of (preferential) growth of octahedral nuclei and subsequent growth of the needles. The experiment presents a new method to prepare T-ZnO economically by using the waste hot dipping zinc.展开更多
文摘Three kinds of tetrapod-like ZnO nanostructures have been synthesized simultaneously via pure Zn chemical vapor deposition on silicon wafers with (111) orientation (Si (111)) at 920 ℃. X-ray diffraction indicates that the nanotetrapods are of wurtzite structure. The morphology and the microstructure of the nanotetrapods are investigated by the scanning electron microscopy. Selected area electron diffraction shows the growth direction, and energy dispersive X-ray spectroscopy reveals the atomic composition ratio of Zn/O. The growth process is briefly discussed. The optical property of the products was also recorded by means of photoluminescence spectroscopy.
文摘Large and uniform tetrapod-like ZnO whiskers (T-ZnO) were prepared from waste hot dipping zinc by vapor oxidation and examined by means of X-ray diffraction and ICP-AES analysis and scanning electron microscope. The products are pure hexagonal wurtzite crystals with tetrapod shape and edge size of center body 56 μm and needle length of 100130 μm. The size and shape of ZnO particles are fully controlled by the growth conditions and T-ZnO can be obtained only at 8501 000 ℃ and total gas flow rate ranging from 40 to 250 L·h-1 in which the size of the T-ZnO particles varies slightly with temperature. The process of the formation of T-ZnO is that T-ZnO may nucleate at the initial stage with a complete tetrapod shape and develop to the large size, but not the process of (preferential) growth of octahedral nuclei and subsequent growth of the needles. The experiment presents a new method to prepare T-ZnO economically by using the waste hot dipping zinc.