Preparation and Magnetic Properties of Mn-Zn Ferrites by the Co-precipitation Method

Mn-Zn ferrites （Mn1-xZnxFe2O4） with different compositions were prepared by the coprecipitation method, and the influences of such synthesis conditions as pH value, composition and volume ratio （R） of the mixed solution and NH4HCO3 solution on their microstructures and magnetic properties were discussed. The samples were characterized by X-ray diffraction （XRD） and magnetization measurement instrument. Lattice parameters and average crystalline size of the synthesized materials were calculated from the corresponding XRD patterns with the related software Jade.5. For samples of different pH values, only one phase was found when pH values were 7.0, 8.0 and 9.0. The sample with pH value of 7.0 exhibited the highest saturation magnetic induction, the lowest coercive force, and crystallized best. For samples of different R values with pH value of 7.0, only one phase was observed in all samples, and the sample with R value of 2.3 exhibited the highest saturation magnetic induction and the lowest coercive force. The composition has mainly afected the magnetic properties, and the saturation magnetic induction increases with the increase of the content of Zn （x）, but decreases when x is beyond 0.6. The trend of coercive force is on the contrary. However, no magnetism is exhibited when the x value is up to 0.8.

Formation Mechanism of Impure Phases and Crystallinity Investigation of YAG Powders Synthesized via the Co-precipitation Method

We investigated the impure phase problem and summarized its two formation mechanisms of YAG powders synthesized via the co-precipitation method.The ions loss problem caused by high concentration reaction solution in the titration process was emphatically studied,and the corresponding thermodynamic explanation was carried out.In addition,influence of powder crystallinity and its new qualitative and quantitative standards were studied.One reason of impure phase is the local nonuniform mixture of Y and Al elements in precursor,which easily causes intermediate phases during calcination and difficulty of high pure powders at low temperatures.The other reason is the precipitation dissolution during titration and then the Y^(3+)/Al^(3+) loss,caused by high concentration of reaction solution.The powder crystallinity can be promoted by increasing calcination temperature or holding time of precursor.Besides the routine XRD method,the TEM-EDX method should be also introduced to directly determine the quality of crystallinity.

Effects of synthesis conditions on layered Li[Ni_(1/3)Co_(1/3)Mn_(1/3)]O_2 positive-electrode via hydroxide co-precipitation method for lithium-ion batteries

Layered Li[Ni1/3Co1/3Mn1/3]O2 was synthesized with complex metal hydroxide precursors that were prepared by a co-precipitation method.The influence of coordination between ammonia and transition-metal cations on the structural and electrochemical properties of the Li[Ni1/3Co1/3Mn1/3]O2 materials was studied.It is found that when the molar ratio of ammonia to total transition-metal cations is 2.7：1,uniform particle size distribution of the complex metal hydroxide is observed via scanning electron microscopy.The average particle size of Li[Ni1/3Co1/3Mn1/3]O2 materials was measured to be about 500 nm,and the tap-density was measured to be approximately 2.37 g/cm3,which is comparable with that of commercialized LiCoO2.XRD analysis indicates that the presently synthesized Li[Ni1/3Co1/3Mn1/3]O2 has a hexagonal layered-structure.The initial discharge capacity of the Li[Ni1/3Co1/3Mn1/3]O2 positive-electrode material is determined to be 181.5 mA·h/g using a Li/Li[Ni1/3Co1/3Mn1/3]O2 cell operated at 0.1C in the voltage range of 2.8-4.5 V.The discharge capacity at the 50th cycle at 0.5C is 170.6 mA·h/g.

Preparation of MnxNi0.5-xZn0.5Fe2O4 Nanorods by the Co-precipitation Method

MnxNi0.5-xZn0.5Fe2O4 nanorods were successfully synthesized by the thermal treatment of rod-like precursors that were fabricated by the co-precipitation of Mn2＋, Ni2＋, and Fe2＋ in the lye. The phase, morphology, and particle diameter were examined by the X-ray diffraction and transmission electron microscopy. The magnetic properties of the samples were studied using a vibrating sample magnetometer. nanorods with a diameter of 35 nm and an The results indicated that pure Ni0.5-xZn0.5Fe2O4 aspect ratio of 15 were prepared. It was found that the diametei of the MnxNi0.5-xZn0.5Fe2O4（0≤x≤0.5） samples increased, the length and the aspect .ratio decreased, with an increase in x value. When x=0.5, the diameter and the aspect ratio of the sample reached up to 50 nm and 7-8, respectively. The coercivity of the samples first increased and then decreased with the increase in the x value. The coercivity of the samples again increased when the x value was higher than 0.4. When x=0.5, the coercivity of the MnxNi0.5-xZn0.5Fe2O4 sample reached the maximal value （134.3 Oe） at the calcination temperature of 600 ℃. The saturation magnetization of the samples first increased and then. decreased with the increase in the x value. When x=0.2, the saturation magnetizat：ion of the sample reached the maximal value （68.5 emu/g） at the calcination temperature of 800 ℃.

Fluorescence and preparation of Sr_2(P_2O_7 ):Ce,Tb phosphate by co-precipitation method

The micron-sized Sr2（P2OT）：Ce,Tb green phosphors were prepared by being annealed at different temperatures with its precursors synthesized by co-pre-cipitates of （NH4）2HPO4 at ambient temperature. The phase structure, grain size, surface morphology, and luminescent properties of phosphors were investigated by X-ray diffraction, scanning electron microscope, trans-mission electron microscope, and fluorescence spectrum. The results show that the product of precursor annealed at 1,100 ℃ is Sr2（P2O7）：Ce,Tb, which belongs to ortho-rhombic phase. The powder is spherical and the size dis-tribution is in micron grade. The sample with the molar ratio of Sr/Tb/Ce of 100.0：0.4：0.6 shows the best fluores-cence effect annealed at 1,100 ℃ for 3 h. The phosphors produce green fluorescence by being excitated with ultra-violet radiation of 254 nm wavelength, and the main emission peak is at 547 nm. The Sr2（P2O7）：Ce,Tb phos-phors synthesized by co-precipitation method of precursors at ambient temperature is a kind of efficient green-emitting phosphors.

Effects of synthesis conditions on the structural and electrochemical properties of layered LiNi_(1/3)Co_(1/3)Mn_(1/3)O_2 cathode material via oxalate co-precipitation method

The uniform layered LiNi1/3Co1/3Mn1/3O2 cathode material for lithium ion batteries was prepared by using （Ni1/3Co1/3Mn1/3）C2O4 as precursor synthesized via oxalate co-precipitation method in air. The effects of calcination temperature and time on the structure and electrochemical properties of the LiNi1/3Co1/3Mn1/3O2 were systemically studied. XRD results revealed that the optimal calcination conditions to prepare the layered LiNi1/3Co1/3Mn1/302 were 950℃ for 15 h. Electrochemical measurement showed that the sample prepared under the such conditions has the highest initial discharge capacity of 160.8 mAh/g and the smallest irreversible capacity loss of 13.5% as well as stable cycling performance at a constant current density of 30 mA/g between 2.5 and 4.3 V versus Li at room temperature.

Electrochemical performance of Ti^(4+)-doped LiFePO_4 synthesized by co-precipitation and post-sintering method

Ti4+-mixed FePO4·xH2O precursor was prepared by co-precipitation method,with which Ti4+ cations were added in the process of preparing FePO4·xH2O to pursue an effective and homogenous doping way.Ti4+-doped LiFePO4 was prepared by an ambient-reduction and post-sintering method using the as-prepared precursor,Li2CO3 and oxalic acid as raw materials.The samples were characterized by scanning electron microscopy (SEM),X-ray diffractometry (XRD),electrochemical impedance spectroscopy (EIS),and electrochemical charge/discharge test.Effects of Ti4+-doping and sintering temperature on the physical and electrochemical performance of LiFePO4 powders were investigated.It is noted that Ti4+-doping can improve the electrochemical performance of LiFePO4 remarkably.The Ti4+-doped sample sintered at 600 ℃ delivers an initial discharge capacity of 150,130 and 125 mA·h/g with 0.1C,1C and 2C rates,respectively,without fading after 40 cycles.

Oxidative coupling of methane over LaAlO3 perovskite catalysts prepared by a co-precipitation method: Effect of co-precipitation pH value

Oxidative coupling of methane(OCM) was conducted over LaAlO3X catalysts that were prepared by a coprecipitation method using different co-precipitation pH values(X = 6–10). The aim is to investigate the effect of p H values on the catalytic activity of La AlO3 catalysts in this reaction. The results showed that the co-precipitation pH value affected greatly on the formation of chemical species of precipitate precursors in the co-precipitation step, leading to different phases of the finally obtained LaAlO3 catalysts.When the co-precipitation pH value increased up to 8, the lanthanum-related phases such as La2 O3 and La(OH)3 were gradually formed as by-products, preventing the formation of LaAlO3 perovskite crystalline structure and facilitating the formation of oxygen vacancies on catalyst surface. However, at pH value of9 or higher, the lanthanum content in the precipitate precursor was increased greatly. Not LaAlO3 perovskite but lanthanum-related phases were developed as main phases, reducing their catalytic activities in this reaction. Among LaAlO3 catalysts, the one prepared at pH = 8 showed the highest C2 yield due to its well-developed oxygen vacancies and electrophilic lattice oxygen. Therefore, the co-precipitation pH value strongly affected the LaAlO3 catalyst activity in OCM reaction. A precious pH control should be required to prepare various perovskite catalysts for the OCM.

Preparation and Characterization of Y_3Sc_2Ga_3O_(12) Nano-Polycrystalline Powders by Co-Precipitation Method

In order to grow high-quality gallium garnet crystals,polycrystalline materials were used as starting materials.YSGG precursor was synthesized by co-precipitation method using aqueous ammonia as a precipitator,and the precursor was then sintered at different temperatures.The results showed that the feasible pH range was 8.3～9.84 in the process of co-precipitation reaction.The YSGG precursor and the powders sintered at different temperatures were characterized by IR,XRD and TEM methods.It was found that the precursor transformed to pure YSGG polycrystalline phase at 800 ℃.YSGG nano-polycrystalline powders sintered at 800～1000 ℃ were well dispersed and the sizes of the YSGG grains were about 40～100 nm.

Yttrium-Doped SnO_2 Prepared by Co-Precipitation Method for Lithium-Ion Battery Anodes

SnO2 doped with Y were prepared by co-precipitation method and tested in lithium-ion cells. The structure and morphology of the materials were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). XRD patterns presented that the all the as-prepared materials had tetragonal rutile structure but a second phase (Y2O3) was observed when Y content reached 4%. TEM micrograph indicated that Y doped SnO2 had a small particle size ranging from 20 to 25 nm. The electrochemical properties for an anode active material in lithium-ion batteries were investigated at room temperature, including the observed capacity involved in the first-discharge and the reversible capacity values during subsequent charge-discharge cycles. The as-prepared Y-doped SnO2 exhibited promising electrochemical properties as anodes for lithium-ion batteries.

Synthesis of LaPO_4:Ce,Terbium by Co-Precipitation Method

The synthesis of precursor of green phosphors, LaPO4: Ce, Tb, by means of co-precipitation with cocurrent flow feed was studied. The effects of the reaction temperature, the kind and concentration of the acid in the bottom water, and the charging rate on the physical properties, such as particle size, were investigated. It is found that the particle size of the powder is controllable by adjusting acidity in bottom water and charging rate. The powder with diameter size of 3 to 5μm was obtained. Its XRD and SEM were analyzed. XRD patterns of the as-prepared green phosphor powders display the typical peaks of CePO4. SEM shows that the morphology of powders is ball-shaped.

Characterization and ultraviolet-visible shielding property of samarium-cerium compounds containing Sm_(2)O_(2)S prepared by co-precipitation method

Since ultraviolet(UV)light,as well as blue light,which is part of visible light,is harmful to skin,samarium-cerium compounds containing Sm_(2)O_(2)S were synthesized by co-precipitation method.This kind of compounds blocks not only UV light,but also blue light.The minimum values of average transmittance(360-450 nm)and band gap of samarium-cerium compounds were 8.90%and 2.76 eV,respectively,which were less than 13.96%and 3.01 eV of CeO_(2).Elemental analysis(EA),X-ray diffraction(XRD),Fourier transformation infrared(FTIR),and Raman spectra determined that the samples contained Ce_(4)O_(7),Sm_(2)O_(2)S,Sm_(2)O_(3),and Sm_(2)O_(2)SO_(4).The microstructure of samples was analyzed by scanning and transmission electron microscopies(SEM and TEM).X-ray photoelectron spectrum(XPS)showed that cerium had Ce^(3+)and Ce^(4+) valence states,and oxygen was divided into lattice oxygen and oxygen vacancy,which was the direct cause of the decrease of average transmittance and band gap.

Synthesis and electrochemical properties of LiNi_(0.8)Al_(0.2-x)Ti_xO_2 cathode materials by an ultrasonic-assisted co-precipitation method

A new co-precipitation route was proposed to synthesize LiNi0.8A10.2-xTixO2 （x=0.0-0.20） cathode materials for lithium ion batteries, with Ni（NO3）2, Al（NO3）3, LiOH·H2O, and TiO2 as the starting materials. Ultrasonic vibration was used during preparing the precursors, and the precursors were protected by absolute ethanol before calcination in the air. The influences of doped-Ti content, calcination temperature and time, additional Li content, and ultrasonic vibration on the structure and properties of LiNi0.8A10.2-xTixO2 were investigated by X-ray diffraction （XRD）, scanning electron microscopy （SEM）, and charge-discharge tests, respectively. The results show that the optimal molar fraction of Ti, calcination temperature and time, and additional molar fraction of Li for LiNi0.8A10.2-xTixO2 cathode materials are 0.1,700℃, 20 h, and 0.05, respectively. Ti doping facilitates the formation of the α-NaFeO2 layered structure, and ultrasonic vibration improves the electrochemical performance of LiNi0.8A10.2-xTixO2.

Nanostructured yttrium aluminum garnet powders synthesized by co-precipitation method using tetraethylenepentamine

Tetraethylenepentamine(C8H23N5,TEPA) has been used as a novel precipitant to synthesize yttrium aluminum garnet(Y3Al5O12,YAG) precursor from a mixed solution of aluminum and yttrium nitrates via a normal-strike co-precipitation method without controlling the pH value during precipitation process.The original precursor was analyzed by thermogravimetry/differential scanning calorimetry(TG/DSC).The evolution of phase composition and micro-structure of the as-synthesized YAG powders were characterized by X-ray ...

Synthesis of LiNi_(0.8)Co_(0.1)Mn_(0.1)O_2 cathode material by chloride co-precipitation method

LiNi0.8Co0.1Mn0.1O2 was prepared by a chloride co-precipitation method and characterized by thermogravimetric analysis, X-ray diffractometry with Rietveld refinement,electron scanning microscopy and electrochemical measurements.Effects of lithium ion content and sintering temperature on physical and electrochemical performance of LiNi0.8Co0.1Mn0.1O2 were also investigated. The results show that the sample synthesized at 750℃with 105%lithium content has fine particle sizes around 200 nm and homogenous sizes distribution.The initial discharge capacity for the powder is 184 mA·h/g between 2.7 and 4.3 V at 0.1C and room temperature.

An efficient nano-adsorbent via surfactants/dual surfactants assisted ultrasonic co-precipitation method for sono-removal of monoazo and diazo anionic dyes

To preserve the environment for civilization,we should remove the pollutants like toxic dyes by friendly and cost efficacious method.In this study,the effect of surfactants or mixed surfactants on physicochemical,optical and adsorption properties of ternary mixed oxide CeO_(2)-ZrO_(2)-Al_(2) O_3(CZA) are investigated.The ternary mixed oxide CZA was prepared by surfactants or mixed surfactants assisted ultrasonic coprecipitation method.The physicochemical and optical properties are estimated by different techniques like XRD,TEM,EDX,FTIR,S_(BET) and UV-Vis/DR.The CZA_T and CZA_C have hybrid shapes and high surface area.The adsorption properties of ternary mixed oxides adsorbents were characterized by sono-removing anionic dyes such as Congo red(CR) and Remazol red RB-133(RR).The different factors like contact time,different dye concentrations and temperatures also studied.The kinetics and isotherms applications showed that,the adsorption process was followed pseudo second order kinetics and the Freundlich isotherm model.Also,the adsorption is spontaneous and endothermic process through the thermodynamic study.Finally,the results showed that the ternary mixed oxide nano-adsorbent(CeO_(2)-ZrO_(2)-Al_(2) O_3) is promising and functional materials for anionic dye sweep from wastewater.

Characterization of ZnS nanoparticles synthesized by co-precipitation method

ZnS nanoparticles are prepared by homogeneous chemical co-precipitation method using EDTA as a stabilizer and capping agent. The structural, morphological, and optical properties of as-synthesized nanoparticles are investigated using x-ray diffraction, scanning electron microscopy, Fourier transform infrared spectroscopy, ultraviolet-visible （UV-Vis） absorption, and photoluminescence spectroscopy. The x-ray diffraction pattern exhibits a zinc-blended crystal structure at room temperature. The average particle size of the nanoparticles from the scanning electron microscopy image is about 50 nm. The ultraviolet absorption spectrum shows the blue shift in the band gap due to the quantum confinement effect. The photoluminescence spectrum of ZnS nanoparticles shows a blue visible spectrum.

Neodymium-doped Yttrium Aluminum Garnet Transparent Laser Ceramics Prepared by Co-precipitation Method

Transparent polycrystaUine neodymiumdoped yttrium aluminum garnet ceramics （Nd：YAG） with better chemical stability, excellent optical and high temperature mechanical property is becoming a new laser host material. The Nd：YAG precursor powders with loosely dispersed, slightly agglomerated and YAG cubic crystal phase were synthesized at 1100 ℃ by the co-precipitation method combined with the reverse strike,

Recovery of magnetite from FeSO_4·7H_2O waste slag by co-precipitation method with calcium hydroxide as precipitant

Proper utilization of the FeSO4·7H2O waste slag generated from TiO2 industry is an urgent need, and Fe3O4 particles are currently being widely used in the wastewater flocculation field. In this work, magnetite was recovered from ferrous sulphate by a novel co-precipitation method with calcium hydroxide as the precipitant. Under optimum conditions, the obtained spherical magnetite particles are well crystallized with a Fe304 purity of 88.78%, but apt to aggregate with a median particle size of 1.83 μm. Magnetic measurement reveals the obtained Fe304 particles are soft magnetic with a saturation magnetization of 81.73 A-m2/kg. In addition, a highly crystallized gypsum co-product is obtained in blocky or irregular shape. Predictably, this study would provide additional opportunities for future application of low-cost Fe3O4 particles in water treatment field.

Preparation and Characterization of Gd_3Sc_2Ga_3O_(12) Polycrystalline Material by Co-Precipitation Method

Gd3Sc2Ga3O12 polycrystalline material for single crystal growth was prepared with Ga, Gd2O3 and Sc2O3 as starting materials and aqueous ammonia as the precipitator by co-precipitation method. The precursors sintered at various temperatures were characterized by infrared spectra （IR）, X-ray diffractometry （XRD） and transmitted electron microscopy （TEM）. The results showed that pure GSGG phase could be obtained at 900 ℃. The sintered powders were well-dispersed and less-aggregated in the sintered temperature range of 900 - 1000 ℃. XRD and TEM show that the polycrystalline particle sizes of the polycrystalline powders were about 20 - 50 nm. Compared with the method that Ga2O3, Gd2O3 and Sc2O3 were mixed directly and sintered to get polycrystalline materials, the synthesized temperature was lower and sintered time was shorter. Thus co-precipitation was a good method to synthesize GSGG polycrystalline material.