A method for recycling AZ91D magnesium alloy scraps directly by hot extrusion was studied.Various microstructural analyses were performed using the techniques of optical microscopy,scanning electron microscopy(SEM)and...A method for recycling AZ91D magnesium alloy scraps directly by hot extrusion was studied.Various microstructural analyses were performed using the techniques of optical microscopy,scanning electron microscopy(SEM)and energy dispersive spectroscopy(EDS).Microstructural observations revealed that all the recycled specimens consisted of fine grains due to the dynamic recrystallization.The main strengthening mechanism of the recycled specimen was grain refinement strengthening and homogeneous distribution of oxide precipitates.The interfaces of individual scraps of extruded materials were not identified when the scraps were extruded with the extrusion ratio of 40-1.Oxidation layers of the scraps were broken into pieces by high compressive and shear forces under the extrusion ratio of 40-1.The ultimate tensile strength and elongation to failure increased with increasing the extrusion ratio.Recycled specimens with the extrusion ratio of 40:1 showed higher ultimate tensile strength of 342.61 MPa and higher elongation to failure of 11.32%,compared with those of the cast specimen.展开更多
For monomer reactivity ratios study, the copolymerization of D,L-3-methylglycolide (MG) with glycolide (GA) or D,L-lactide (LA) was carried out in bulk to a certain low conversion in the presence of stannous octoate a...For monomer reactivity ratios study, the copolymerization of D,L-3-methylglycolide (MG) with glycolide (GA) or D,L-lactide (LA) was carried out in bulk to a certain low conversion in the presence of stannous octoate at 140 degrees C. The copolymer compositions were determined by H-1 NMR spectroscopy. The monomer reactivity ratios were evaluated by Fineman-Ross method, Kelen-Tudos method and linear least-squares method. The monomer reactivity ratios of D,L-3-methylglycolide and glycolide or D,L-lactide are r(mg)= 0.73, r(ga)= 1.47; r(mg)= 1.71, r(la)= 0.92, respectively.展开更多
In order to predict the damage behaviours of 3D-printed continuous carbon fibre(CCF)reinforced composites,when additional short carbon fibre(SCF)composite components are employed for continuous printing or special fun...In order to predict the damage behaviours of 3D-printed continuous carbon fibre(CCF)reinforced composites,when additional short carbon fibre(SCF)composite components are employed for continuous printing or special functionality,a novel path-dependent progressive failure(PDPF)numerical approach is developed.First,a progressive failure model using Hashin failure criteria with continuum damage mechanics to account for the damage initiation and evaluation of 3D-printed CCF reinforced polyamide(PA)composites is developed,based on actual fibre placement trajectories with physical measurements of 3D-printed CCF/PA constituents.Meanwhile,an elastic-plastic model is employed to predict the plastic damage behaviours of SCF/PA parts.Then,the accuracy of the PDPF model was validated so as to study 3D-printed CCF/PA composites with either negative Poisson's ratio or high stiffness.The results demonstrate that the proposed PDPF model can achieve higher prediction accuracies in mechanical properties of these 3D-printed CCF/PA composites.Mechanism analyses show that the stress distribution is generally aggregated in the CCF areas along the fibre placement paths,and the shear damage and matrix tensile/compressive damage are the key damage modes.This study provides a new approach with valuable information for characterising complex 3D-printed continuous fibre-matrix composites with variable mechanical properties and multiple constituents.展开更多
Inherent drawbacks associated with drug-eluting stents have prompted the development of bioresorbable cardiovascular stents.Additive manufacturing(3-dimentional(3D)printing)has been widely applied in medical devices.I...Inherent drawbacks associated with drug-eluting stents have prompted the development of bioresorbable cardiovascular stents.Additive manufacturing(3-dimentional(3D)printing)has been widely applied in medical devices.In this study,we develop a novel screw extrusion-based 3D printing system with a new designed mini-screw extruder to fabricate stents.A stent with a zero Poisson’s ratio(ZPR)structure is designed,and a preliminary monofilament test is conducted to investigate appropriate fabrication parameters.3D-printed stents with different geometric structures are fabricated and analyzed by observation of the surface morphology.An evaluation of the mechanical properties and a preliminary biological evaluation of 3D-printed stents with different parameters are carried out.In conclusion,the screw extrusion-based 3D printing system shows potential for customizable stent fabrication.展开更多
Raman spectroscopy-based temperature sensing usually tracks the change of Raman wavenumber,linewidth and intensity,and has found very broad applications in characterizing the energy and charge transport in nanomateria...Raman spectroscopy-based temperature sensing usually tracks the change of Raman wavenumber,linewidth and intensity,and has found very broad applications in characterizing the energy and charge transport in nanomaterials over the last decade.The temperature coefficients of these Raman properties are highly material-dependent,and are subjected to local optical scattering influence.As a result,Raman-based temperature sensing usually suffers quite large uncertainties and has low sensitivity.Here,a novel method based on dual resonance Raman phenomenon is developed to precisely measure the absolute temperature rise of nanomaterial(nm WS_(2) film in this work)from 170 to 470 K.A 532 nm laser(2.33 eV photon energy)is used to conduct the Raman experiment.Its photon energy is very close to the excitonic transition energy of WS_(2) at temperatures close to room temperature.A parameter,termed resonance Raman ratio(R3)Ω=I_(A1g)/IE_(2g) is introduced to combine the temperature effects on resonance Raman scattering for the A_(1g) and E_(2g) modes.Ω has a change of more than two orders of magnitude from 177 to 477 K,and such change is independent of film thickness and local optical scattering.It is shown that when Ω is varied by 1%,the temperature probing sensitivity is 0.42 K and 1.16 K at low and high temperatures,respectively.Based on Ω,the in-plane thermal conductivity(k)of a∼25 nm-thick suspended WS_(2) film is measured using our energy transport state-resolved Raman(ET-Raman).k is found decreasing from 50.0 to 20.0 Wm^(−1) K^(−1) when temperature increases from 170 to 470 K.This agrees with previous experimental and theoretical results and the measurement data using our FET-Raman.The R3 technique provides a very robust and high-sensitivity method for temperature probing of nanomaterials and will have broad applications in nanoscale thermal transport characterization,non-destructive evaluation,and manufacturing monitoring.展开更多
基金Projects(50674038, 50974048) supported by the National Natural Science Foundation of ChinaProject(200802140004) supported by Doctoral Fund of Ministry of Education of China
文摘A method for recycling AZ91D magnesium alloy scraps directly by hot extrusion was studied.Various microstructural analyses were performed using the techniques of optical microscopy,scanning electron microscopy(SEM)and energy dispersive spectroscopy(EDS).Microstructural observations revealed that all the recycled specimens consisted of fine grains due to the dynamic recrystallization.The main strengthening mechanism of the recycled specimen was grain refinement strengthening and homogeneous distribution of oxide precipitates.The interfaces of individual scraps of extruded materials were not identified when the scraps were extruded with the extrusion ratio of 40-1.Oxidation layers of the scraps were broken into pieces by high compressive and shear forces under the extrusion ratio of 40-1.The ultimate tensile strength and elongation to failure increased with increasing the extrusion ratio.Recycled specimens with the extrusion ratio of 40:1 showed higher ultimate tensile strength of 342.61 MPa and higher elongation to failure of 11.32%,compared with those of the cast specimen.
基金This work was supported by the Key Project of the National Natural Science Foundation of China!(59833 140).
文摘For monomer reactivity ratios study, the copolymerization of D,L-3-methylglycolide (MG) with glycolide (GA) or D,L-lactide (LA) was carried out in bulk to a certain low conversion in the presence of stannous octoate at 140 degrees C. The copolymer compositions were determined by H-1 NMR spectroscopy. The monomer reactivity ratios were evaluated by Fineman-Ross method, Kelen-Tudos method and linear least-squares method. The monomer reactivity ratios of D,L-3-methylglycolide and glycolide or D,L-lactide are r(mg)= 0.73, r(ga)= 1.47; r(mg)= 1.71, r(la)= 0.92, respectively.
基金Supported by National Natural Science Foundation of China (Grant No.12302177)Guangdong Provincial Basic and Applied Basic Research Foundation of China (Grant No.2024A1515010203)+1 种基金Shenzhen Science and Technology Program of China (Grant No.JCYJ20230807093602005)Shenzhen Key Laboratory of Intelligent Manufacturing for Continuous Carbon Fibre Reinforced Composites of China (Grant No.ZDSYS20220527171404011)。
文摘In order to predict the damage behaviours of 3D-printed continuous carbon fibre(CCF)reinforced composites,when additional short carbon fibre(SCF)composite components are employed for continuous printing or special functionality,a novel path-dependent progressive failure(PDPF)numerical approach is developed.First,a progressive failure model using Hashin failure criteria with continuum damage mechanics to account for the damage initiation and evaluation of 3D-printed CCF reinforced polyamide(PA)composites is developed,based on actual fibre placement trajectories with physical measurements of 3D-printed CCF/PA constituents.Meanwhile,an elastic-plastic model is employed to predict the plastic damage behaviours of SCF/PA parts.Then,the accuracy of the PDPF model was validated so as to study 3D-printed CCF/PA composites with either negative Poisson's ratio or high stiffness.The results demonstrate that the proposed PDPF model can achieve higher prediction accuracies in mechanical properties of these 3D-printed CCF/PA composites.Mechanism analyses show that the stress distribution is generally aggregated in the CCF areas along the fibre placement paths,and the shear damage and matrix tensile/compressive damage are the key damage modes.This study provides a new approach with valuable information for characterising complex 3D-printed continuous fibre-matrix composites with variable mechanical properties and multiple constituents.
基金funding support from the Beijing Municipal Natural Science Foundation,China(Z150001)supported by Beijing Anzhen Hospital.
文摘Inherent drawbacks associated with drug-eluting stents have prompted the development of bioresorbable cardiovascular stents.Additive manufacturing(3-dimentional(3D)printing)has been widely applied in medical devices.In this study,we develop a novel screw extrusion-based 3D printing system with a new designed mini-screw extruder to fabricate stents.A stent with a zero Poisson’s ratio(ZPR)structure is designed,and a preliminary monofilament test is conducted to investigate appropriate fabrication parameters.3D-printed stents with different geometric structures are fabricated and analyzed by observation of the surface morphology.An evaluation of the mechanical properties and a preliminary biological evaluation of 3D-printed stents with different parameters are carried out.In conclusion,the screw extrusion-based 3D printing system shows potential for customizable stent fabrication.
基金Support of this work by National Science Foundation(CBET1930866 and CMMI2032464 for X W)National Natural Science Foundation of China(No.52106220 for S X and No.51906161 for Y X)。
文摘Raman spectroscopy-based temperature sensing usually tracks the change of Raman wavenumber,linewidth and intensity,and has found very broad applications in characterizing the energy and charge transport in nanomaterials over the last decade.The temperature coefficients of these Raman properties are highly material-dependent,and are subjected to local optical scattering influence.As a result,Raman-based temperature sensing usually suffers quite large uncertainties and has low sensitivity.Here,a novel method based on dual resonance Raman phenomenon is developed to precisely measure the absolute temperature rise of nanomaterial(nm WS_(2) film in this work)from 170 to 470 K.A 532 nm laser(2.33 eV photon energy)is used to conduct the Raman experiment.Its photon energy is very close to the excitonic transition energy of WS_(2) at temperatures close to room temperature.A parameter,termed resonance Raman ratio(R3)Ω=I_(A1g)/IE_(2g) is introduced to combine the temperature effects on resonance Raman scattering for the A_(1g) and E_(2g) modes.Ω has a change of more than two orders of magnitude from 177 to 477 K,and such change is independent of film thickness and local optical scattering.It is shown that when Ω is varied by 1%,the temperature probing sensitivity is 0.42 K and 1.16 K at low and high temperatures,respectively.Based on Ω,the in-plane thermal conductivity(k)of a∼25 nm-thick suspended WS_(2) film is measured using our energy transport state-resolved Raman(ET-Raman).k is found decreasing from 50.0 to 20.0 Wm^(−1) K^(−1) when temperature increases from 170 to 470 K.This agrees with previous experimental and theoretical results and the measurement data using our FET-Raman.The R3 technique provides a very robust and high-sensitivity method for temperature probing of nanomaterials and will have broad applications in nanoscale thermal transport characterization,non-destructive evaluation,and manufacturing monitoring.