When heavy machines and large scaled receiver system of communication equipment are manufactured, it always needs to produce large-sized steel castings, aluminum castings and etc. Some defects of hot cracking by therm...When heavy machines and large scaled receiver system of communication equipment are manufactured, it always needs to produce large-sized steel castings, aluminum castings and etc. Some defects of hot cracking by thermal stress often appear during solidification process as these castings are produced, which results in failure of castings. Therefore predicting the effects of technological parameters for production of castings on the thermal stress during solidification process becomes an important means. In this paper, the mathematical models have been established and numerical calculation of temperature fields by using finite difference method (FDM) and then thermal stress fields by using finite element method (FEM) during solidification process of castings have been carried out. The technological parameters of production have been optimized by the results of calculation and the defects of hot cracking have been eliminated. Modeling and simulation of 3D thermal stress during solidification processes of large-sized castings provided a scientific basis, which promoted further development of advanced manufacturing technique.展开更多
In order to solve the thermal stress field around crack tip in metal die when crack prevention using electromagnetic heating, a metal die with a half-embedded round crack was selected as the study object. The complex ...In order to solve the thermal stress field around crack tip in metal die when crack prevention using electromagnetic heating, a metal die with a half-embedded round crack was selected as the study object. The complex function method was used as a basis for the theoretical model of the space crack prevention in metal dies using electromagnetic heating. The crack arrest was accomplished by a pulse current discharge through the inner and outer. The theoretical analysis results show that the temperature around the crack tip rises instantly above the melting point of the metal. Small welded joints are formed at a small sphere near the crack tip inside the metal die by metal melting as a result of the heat concentration effect when the current pulse discharged. The thermal compressive stress field appears around the crack tip at the moment. The research results show that the crack prevention using electromagnetic heating can decrease the stress concentration and forms a compressive stress area around the crack tip, and also prevents the main crack from propagating further, and the goal of crack preventing can be reached.展开更多
The physical model of temperature field and thermal stress field are established in this paper, on which the numerical simulation with the assuming physical and laser milling parameters have been finished. The laser m...The physical model of temperature field and thermal stress field are established in this paper, on which the numerical simulation with the assuming physical and laser milling parameters have been finished. The laser milling process can be explained.展开更多
A system for the numerical simulation of 3D temperature and stress fields during casting process was studied, developed and practiced based on finite difference method (FDM) in this paper. An approach where the stress...A system for the numerical simulation of 3D temperature and stress fields during casting process was studied, developed and practiced based on finite difference method (FDM) in this paper. An approach where the stress/strain and the heat transfer analysis use the same computational domain was presented, which avoided transferring temperature data between FDM and FEM nodes and elements. A slot-board steel casting was simulated and the calculated results are in agreements with those obtained from practical producing.展开更多
文摘When heavy machines and large scaled receiver system of communication equipment are manufactured, it always needs to produce large-sized steel castings, aluminum castings and etc. Some defects of hot cracking by thermal stress often appear during solidification process as these castings are produced, which results in failure of castings. Therefore predicting the effects of technological parameters for production of castings on the thermal stress during solidification process becomes an important means. In this paper, the mathematical models have been established and numerical calculation of temperature fields by using finite difference method (FDM) and then thermal stress fields by using finite element method (FEM) during solidification process of castings have been carried out. The technological parameters of production have been optimized by the results of calculation and the defects of hot cracking have been eliminated. Modeling and simulation of 3D thermal stress during solidification processes of large-sized castings provided a scientific basis, which promoted further development of advanced manufacturing technique.
基金Project supported by the National Natural Science Foundation of China (No.50275128)the Natural Science Foundation of Hebei Province of China (No.599255)
文摘In order to solve the thermal stress field around crack tip in metal die when crack prevention using electromagnetic heating, a metal die with a half-embedded round crack was selected as the study object. The complex function method was used as a basis for the theoretical model of the space crack prevention in metal dies using electromagnetic heating. The crack arrest was accomplished by a pulse current discharge through the inner and outer. The theoretical analysis results show that the temperature around the crack tip rises instantly above the melting point of the metal. Small welded joints are formed at a small sphere near the crack tip inside the metal die by metal melting as a result of the heat concentration effect when the current pulse discharged. The thermal compressive stress field appears around the crack tip at the moment. The research results show that the crack prevention using electromagnetic heating can decrease the stress concentration and forms a compressive stress area around the crack tip, and also prevents the main crack from propagating further, and the goal of crack preventing can be reached.
文摘The physical model of temperature field and thermal stress field are established in this paper, on which the numerical simulation with the assuming physical and laser milling parameters have been finished. The laser milling process can be explained.
文摘A system for the numerical simulation of 3D temperature and stress fields during casting process was studied, developed and practiced based on finite difference method (FDM) in this paper. An approach where the stress/strain and the heat transfer analysis use the same computational domain was presented, which avoided transferring temperature data between FDM and FEM nodes and elements. A slot-board steel casting was simulated and the calculated results are in agreements with those obtained from practical producing.