Bio-Based Waterborne Poly(Vanillin-Butyl Acrylate)/MXene Coatings for Leather with Desired Warmth Retention and Antibacterial Properties

This study presents a solvent-free,facile synthesis of a bio-based green antibacterial agent and aromatic monomer methacrylated vanillin(MV)using vanillin.The resulting MV not only imparted antibacterial properties to coatings layered on leather,but could also be employed as a green alternative to petroleum-based carcinogen styrene(St).Herein,MV was copolymerized with butyl acrylate(BA)to obtain waterborne bio-based P(MV-BA)miniemulsion via miniemulsion polymerization.Subsequently,MXene nanosheets with excellent photothermal conversion performance and antibacterial properties,were introduced into the P(MV-BA)miniemulsion by ultrasonic dispersion.During the gradual solidification of P(MV-BA)/MXene nanocomposite miniemulsion on the leather surface,MXene gradually migrated to the surface of leather coatings due to the cavitation effect of ultrasonication and amphiphilicity of MXene,which prompted its full exposure to light and bacteria,exerting the maximum photothermal conversion efficiency and significant antibacterial efficacy.In particular,when the dosage of MXene nanosheets was 1.4 wt%,the surface temperature of P(MV-BA)/MXene nanocomposite miniemulsioncoated leather(PML)increased by about 15℃ in an outdoor environment during winter,and the antibacterial rate against Escherichia coli and Staphylococcus aureus was nearly 100%under the simulated sunlight treatment for 30 min.Moreover,the introduction of MXene nanosheets increased the air permeability,water vapor permeability,and thermal stability of these coatings.This study provides a new insight into the preparation of novel,green,and waterborne bio-based nanocomposite coatings for leather,with desired warmth retention and antibacterial properties.It can not only realize zerocarbon heating based on sunlight in winter,reducing the use of fossil fuels and greenhouse gas emissions,but also improve ability to fight off invasion by harmful bacteria,viruses,and other microorganisms.

Adhesion property of AlCrNbSiTi high-entropy alloy coating on zirconium:experimental and theoretical studies

Experimental scratch tests and first-principles calculations were used to investigate the adhesion property of AlCrNbSiTi high-entropy alloy(HEA)coatings on zirconium substrates.AlCrNbSiTi HEA and Cr coatings were deposited on Zr alloy substrates using multi-arc ion plating technology,and scratch tests were subsequently conducted to estimate the adhesion property of the coatings.The results indicated that Cr coatings had better adhesion strength than HEA coatings,and the HEA coatings showed brittleness.The special quasi-random structure approach was used to build HEA models,and Cr/Zr and HEA/Zr interface models were employed to investigate the cohesion between the coatings and Zr substrate using first-principles calculations.The calculated interface energies showed that the cohesion between the Cr coating and the Zr substrate was stronger than that of the HEA coating with Zr.In contrary to Al or Si in the HEA coating,Cr,Nb,and Ti atoms binded strongly with Zr substrate.Based on the calculated elastic constants,it was found that low Cr and high Al content decreased the mechanical performances of HEA coatings.Finally,this study demonstrated the utilization of a combined approach involving first-principles calculations and experimental studies for future HEA coating development.

Corrosion and antimicrobial property of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)micro-arc oxidation coatings on Ti-6Al-4V alloys in natural seawater

Microarc oxidation is an effective surface treatment for improving certain properties of metals and their alloys.In this paper,TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were prepared on Ti-6Al-4V by microarc oxidation.Thecoatings exhibited good corrosion resistance and antimicrobial properties.X-ray diffraction(XRD),scanning electronmicroscopy(SEM),and 3D laser confocal were used to characterize the coatings.The properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings were analyzed,including microstructure,surface roughness,corrosion resistance,andantimicrobial properties.The electrochemical results showed that the coatings prepared by microarc oxidation hadenhanced corrosion resistance compared to the substrate.The antibacterial properties of TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coating against Pseudomonas aeruginosa were evaluated by fluorescence microscopy and plate counting.The antibacterial rate of TiO_(2)/Cu_(2)O@CeO_(2)coating was up to 99.70%.In summary,the TiO_(2)/Cu_(2)O and TiO_(2)/Cu_(2)O@CeO_(2)coatings prepared by microarc oxidation have a potential application background in the field of marine corrosionprotection and biofouling.

Preparation and property of seal coating for gas turbine compressor

Double-layer structure of seal coating which consisted of a Ni5Al bond coating and a Ni25 graphite top coating were prepared on steel substrate of gas turbine compressor cylinder block.Bond coating was prepared by atmospheric plasma spraying and top coating was prepared by flame spraying.The microstructure,mechanical properties and abradability of the coating were characterized by scanning elec-tron microscope(SEM),hardness tester,universal testing machine,thermal shock testing machine and abradability testing machine.The res-ults show that the overall spraying structure of the seal coating is uniform,the nickel metal phase is the skeleton supporting the entire coat-ing,and the coating is well bonded without separation.The seal coating has a bonding strength of not less than 7.7 MPa,excellent thermal stability,and thermal shock resistance cycle numbers at 500℃more than 50;the scratch length,deepest invasion depth and wear amount of the coating increase with rise of test temperature,with almost no coating adhesion,indicating that the seal coating has excellent abradability.

Anti-oxidation properties of ZrB_2 modified silicon-based multilayer coating for carbon/carbon composites at high temperatures

To improve the anti-oxidation ability of silicon-based coating for carbon/carbon （C/C） composites at high temperatures, a ZrB2 modified silicon-based multilayer oxidation protective coating was prepared by pack cementation. The phase composition, microstructure and oxidation resistance at 1773, 1873 and 1953 K in air were investigated. The prepared coating exhibits dense structure and good oxidation protective ability. Due to the formation of stable ZrSiO4-SiO2 compound, the coating can effectively protect C/C composites from oxidation at 1773 K for more than 550 h. The anti-oxidation performance decreases with the increase of oxidation temperature. The mass loss of coated sample is 2.44% after oxidation at 1953 K for 50 h, which is attributed to the decomposition of ZrSiO4 and the volatilization of SiO2 protection layer.

Structure and mechanical properties of thick Cr/Cr_2N/CrN multilayer coating deposited by multi-arc ion plating

A Cr/Cr2N/CrN multilayer coating with a thickness of 24.4 μm was deposited by multi-arc ion plating. The coating was systematically characterized by field emission scanning electron microscopy(FESEM), X-ray photoelectron spectrometry(XPS), energy dispersive spectroscopy(EDS), X-ray diffraction(XRD) and transmission electron microscopy(TEM). Hardness and adhesion were tested by nanoindentation and scratch tester, respectively. The friction properties were investigated by a reciprocating UMT-3MT ball-on-disk tribometer in air and seawater. The results showed that the multilayer coating consisted of three different layers, with Cr,Cr2N and CrN phases, respectively. Compared with CrN single layer coating, the adhesion of the multilayer coating was improved significantly, the hardness of the multilayer coating was(21±2) GPa. The corrosion resistance of the multilayer coating was also improved in artificial seawater. The friction coefficient of multilayer coating was lower than that of CrN single layer coating both in air and seawater.

Effect of wear conditions on tribological properties of electrolessly-deposited Ni-P-Gr-SiC hybrid composite coating

The friction and wear properties of the electrolessly-deposited Ni-P-Gr-SiC composites were investigated. The effects of graphite content, load and rotation speed on the friction coefficient and wear resistance of the composite coatings were mainly investigated. The worn surface and cross section of the coatings were characterized by scanning electron microscopy and energy-dispersive X-ray analysis. The results show that the composite coatings reveal good antifriction and wear resistance due to the synergic effect of graphite and SiC particles. The formation of graphite-rich mechanically mixed layer （GRMML） on the surface of Ni-P-Gr-SiC coating contributes to the good tribological behavior of the wear counterparts and SiC particles play a load bearing role in protecting GRMML from shearing easily.

Effects of current density on microstructure and properties of plasma electrolytic oxidation ceramic coatings formed on 6063 aluminum alloy

Plasma electrolytic oxidation (PEO) ceramic coatings were fabricated in a silicate-based electrolyte with the addition of potassium fluorozirconate (K2ZrF6) on 6063 aluminum alloy, and the effects of current density on microstructure and properties of the PEO coatings were studied. It was found that pore density of the coatings decreased with increasing the current density. The tribological and hardness tests suggested that the ceramic coating produced under the current density of 15 A/dm2showed the best mechanical property, which matched well with the phase analysis. Electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves proved that the coating obtained under 15 A/dm2 displayed the best anti-corrosion property, which was directly connected with morphologies of coatings.

Properties of Zn-Bi composite coatings prepared by ionic co-discharge deposition

Zn-Bi composite was synthesized by ionic co-discharge deposition and its properties were investigated. The results show that the Zn-Bi composite with the incorporation of Bi has a finer grain size than the pure Zn coating and improves the mechanical properties. The microhardness is increased by approximately two times simply by adding a small amount of Bi electrolyte into a Zn bath solution. A lower volume loss of the Zn-Bi composite coating compared with the pure Zn coating also indicates that the Zn-Bi coating has a better wear resistance.

Microstructure and mechanical properties of Ni-based composite coatings reinforced by in situ synthesized TiB_2 + TiC by laser cladding

A Ni-based composite coating reinforced by in situ synthesized TiB2 and TiC particles was fabricated on Ti6A14V by laser cladding. An attempt was made to correlate the thermodynamic predictions and experimental observation. The micro- structure and the microhardness profile across the coating were investigated by means of X-ray diffraction （XRD）, scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and a hardness tester. It is found that the coating mainly consists of a large number of reinforcements （black blocky TiB2, flower-like or equiaxial TiC, and fine acicular CrB） and the 7 matrix. The hardness of TiB2, TiC, and CrB reinforcements is much higher than that of the 7 matrix. The dispersive distribu- tion of such high hardness reinforcements causes the increase in hardness of the whole coating. The average value of the hard- ness is approximately Hv0.2 700 in the coating. The hardness of the coating is obviously higher than that of the substrate due to the dispersion strengthening of reinforcements.

Effect of rare earth doping on thermo-physical properties of lanthanum zirconate ceramic for thermal barrier coatings

The effect of rare earth doping on thermo-physical properties of lanthanum zirconate was investigated. Oxide powders of various compositions La2Zr2O7 were synthesized by coprecipitation-calcination method. High-temperature dilatometer, DSC, and laser thermal diffusivity methods were used to analyze thermal expansion coefficient （TEC）, specific heat, and thermal diffusivity. The results showed that CeO2 doped pyrochlores La2（Zr1.8Ce0.2）2O7 and La1.7（DyNd）0.15（Zr0.8Ce0.2）2O7 had higher TEC than La2Zr2O7 and La1.7Dy0.3Zr2O7. La2（Zr1.8Ce0.2）2O7, La1.7Dy0.3Zr2O7, and La1.7（DyNd）0.15（Zr0.8Ce0.2）2O7 had lower thermal conductivity than undoped La2Zr2O7. The Dy2O3, Nd2O3, and CeO2 codoped composition showed the lowest thermal conductivity and the highest TEC. Thermo-physical results also indicated that TEC of rare earth oxide doped La2Zr2O7 ceramic was slightly higher than that of conventional ZrO2-8Wt.% Y2O3 （8YSZ）, and its thermal conductivity was lower than that of 8YSZ.

Microstructure and mechanical properties of twin-wire arc sprayed Ni-Al composite coatings on 6061-T6 aluminum alloy sheet

We have systematically studied the microstructure and mechanical properties of Ni-5wt%Al and Ni-20wt%Al composite coat- ings fabricated on 6061-T6 aluminum alloy sheet by twin-wire arc spraying under different experimental conditions. The abrasive wear be- havior and interface diffusion behavior of the composite coatings were evaluated by dry/wet rubber wheel abrasive wear tests and heat treat- ment, respectively. Experimental results indicate that the composite coatings exhibit features of adhesive wear. Besides, the Vickers micro- hardness of NiA1 and Ni3AI intermetallic compounds is relatively larger than that of the substrate, which is beneficial for enhancing the wear resistance. With the increase of annealing temperature and time, the interface diffusion area between the Ni-Al coating and the substrate gradually expands with the formation of NiAl3 and Ni2Al3 phases, and is controlled by diffusion of aluminum atoms. The grain growth ex- ponent n of diffusion kinetics of the Ni-Al coating, calculated via a high-temperature diffusion model at 400, 480, and 550℃, is between 0.28 and 0.38. This satisfies the cubic law, which is consistent with the general theoretical relationship of high-temperature diffusion.

Crystalline texture evolution, control of the tribocorrosion behavior, and significant enhancement of the abrasion properties of a Ni-P nanocomposite coating enhanced by zirconia nanoparticles

This paper describes an investigation of the effect of ZrO2 nanoparticles on the abrasive properties,crystalline texture developments,and tribocorrosion behavior of Ni-P nanostructured coatings.In the investigation,Ni-P and Ni-P-ZrO2 nanostructured coatings are deposited on St52 steel via the electroless method.Transmission electron microscopy(TEM),field emission scanning electron microscopy(FE-SEM),X-ray diffraction(XRD),energy dispersive spectroscopy(EDS),cyclic-static polarization tests in 3.5wt%NaCl solution,the tribocorrosion test(by back-and-forth wear in electrochemical cell),and the microhardness test using the Vickers method were performed to characterize and analyze the deposited coatings.The results of this study showed that the addition of ZrO2 nanoparticles to the Ni-P electroless bath produced the following:a sharp increase in wear and hardness resistance,the change of the wear mechanism from sheet to adhesive mode,the reduction of pitting corrosion resistance,significant reduction in the tribocorrosion protective properties,change in the preferred orientation of the crystalline texture coating from(111)to(200),increase in the sedimentation rate during the deposit process,and a sharp increase in the thickness of the Ni-P nanostructured coatings.

Study on microstructure and properties of high velocity arc sprayed Fe_3Al intermetallic coating

Coating structural materials with Fe 3Al based intermetallics may rapidly lead to industrial application of their environment and wear resistant features. In the present study, high velocity arc spraying (HVAS) was used to in situ synthesize Fe 3Al intermetallic coating. The microstructural characterization and properties of the coating have been investigated. The microstructure was found to consist of Fe 3Al based intermetallic (D0 3 and B2) and α Fe regions together with fine oxide (α Al 2O 3) layers. TEM images of coating show that the solidified lamellae are polycrystalline and have a grain size of the order of about 150 nm , and there also exists amorphous state in some areas. It can be concluded that a very high cooling rate has been obtained during HVAS process. Moreover, the coating has relatively higher adhesion strength and microhardness, as well as lower density and porosity.

Effect of Laser Power on the Microstructure and Mechanical Properties of TiN/Ti_3Al Composite Coatings on Ti6Al4V

Laser nitriding is one of the effective techniques to improve the surface properties of titanium alloys and has potential application in the life extension of last-stage steam turbine blades. However, cracking of surface coating is a common problem due to heat concentration in laser nitriding process. Conventionally, the cracks can be avoided through heat treatment, which may have an important influence on the mechanical properties of coating. Crack-free TiN/Ti3Al IMC coatings on Ti6Al4V are prepared by plasma spraying and laser nitriding. The microstructures, phase constitutes and compositions of the coating are observed and analyzed with scanning electron microscopy(SEM), X-ray diffraction(XRD) and X-ray energy-dispersive spectroscopy(EDS). Microhardness, elastic modulus, fracture toughness of the coating are measured. The results show that the crackand pore-free IMC coatings can be made through the proposed method; with increasing laser power, the amount and density of TiN phase in the coating first increased and then decreased, leading to the similar trend of microhardness and elastic modulus and the reverse trend of fracture toughness of the coating. Both the average microhardness and elastic modulus of the coating increase three times higher than those of the substrate. The volume fraction of the TiN reinforced phase in composite can be controlled by varying the laser power and the cracking problem in laser nitriding process is successfully solved.

Thermal sprayed WC-Co coatings and their mechanical properties

HVOF thermal spraying tests were carried out for thermal spraying the coatings with two kinds of cermet powders,which are microstructured Sulzer Metco Diamalloy 2004 WC-12%Co powders and nanostructured WC-12%Co powders.The microstructures of the as-prepared WC-12%Co coatings were then characterized by using XRD analyzer and SEM.The mechanical properties of the two coatings were evaluated by microhardness test,bend test,cup test,tensile test and abrasive wear test.The results showed that the mechanical properties of WC-12%Co coatings sprayed with nanostructured WC-12%Co powder is higher than that of coatings sprayed with microstructured WC-12%Co powders,and the reasons were discussed.

Preparation and Tribological Properties of Ni-P Electroless Composite Coating Containing Potassium Titanate Whisker

Nickel-phosphorus （Ni-P） composite coatings containing potassium titanate （K2Ti6O13） whiskers （PTWs） were prepared by electroless plating. The surface morphology and component of coatings were investigated by scanning electron microscopy （SEM） and energy dispersive X-ray spectroscopy （EDX）, respectively before and after wear test. The tribological performance was evaluated using a pin-on-disk wear tester under dry conditions. It is found that the Ni-P-PTWs composite coatings exhibit higher wear resistance than Ni-P and Ni-P-SiC electroless coatings. The favorable effects of PTWs on the tribological properties of the composite coatings are attributed to the super-strong mechanical properties and the specific tunneling structures of PTWs. The PTWs greatly reinforce the structure of the Ni-P-based composite coatings and thereby greatly reduce the adhesive and plough wear of Ni-P-PTWs composite coatings.

Effects of addition of rare earth on properties and structures of Ni-W-B-SiC composite coatings

The effects of rare earth (RE) on the composition, phase structures, surface morphologies and hardness of electrodeposited RE Ni W B SiC composite coatings were discussed. The results show that W and SiC contents in the coatings increase with the increase of RE in the bath. When RE is added in the coatings, the grains are refined and the trend of formation of amorphous coatings is increased. Moreover, the thermal stability of the RE Ni W B SiC composite coatings is enhanced. The hardness of the coatings is increased with the increase of heat treatment temperature, and it reaches the peak value when heated at 400 ℃. Besides, the hardness of the RE Ni W B SiC coatings is higher than that of the Ni W B SiC coatings.

Microstructure and Mechanical Properties of an in situ Synthesized TiB and TiC Reinforced Titanium Matrix Composite Coating

A titanium-based composite coating reinforced by in situ synthesized TiB and TiC particles was fabricated on Ti6A14V by laser cladding. The microstructure and mechanical properties were investigated. The coating was mainly composed of a-Ti cellular dendrites and an eutectic in which a large number of rod/ needle-shaped TiB and a few equiaxial TiC particles were homogeneously embedded. The microstructural evolution could be divided into four stages： precipitation and growth of primary fl-Ti phase, formation of the binary eutectic fl-Ti＋TiB, formation of the ternary eutectic fl-Ti＋TiB＋TiC, and solid transformation from fl-Ti to a-Ti. Microhardness of the coating showed a gradient variation from the surface （about HV0.2 876） to the bottom （about HV0.2 660） and was prominently improved in comparison with that of the substrate. Fracture toughness of the coating also exhibited a gradient variation from the surface （6.3 MPa-m1/2） to the interface （11.9 MPa-mV2）. Wear resistance of the coating was significantly superior to that of Ti6A14V.

Influence of Si Content on Properties of Ti1-xSixN Coatings

To investigate the evolution of microstructure and wear behavior of TiSiN coatings with the variation of Si in targets and lays the foundation for its controllable mass production, Ti1-xSixN composite coatings were deposited onto Si(100) and cemented carbide substrates using TiSi targets with different Si content by cathodic arc ion plating. The influences of Si on the microstructure and mechanical properties were studied. Nano-amorphous composite structure appeared in the Ti1-xSixN coatings when Si content in TiSi target was higher than 5 at%. However, further increase of Si content in TiSi target exhibited a negligible effect on the microstructure of Ti1-xSixN coatings. Hardness and deformation resistance were correlated to the content of Si in TiSi targets. Maximum hardness was obtained as the Si content in target increased up to 20 at%. Friction coefficient and wear rate significantly decreased with addition of Si in TiN coating, and then dually increased with the increase of Si content in targets.