The paper presents the investigation of the effect of alkaline treatment of sodium hydroxide(NaOH) on physical and dynamic mechanical analysis(DMA) viscoelastic properties of kenaf fibre filled natural rubber(NR)/ther...The paper presents the investigation of the effect of alkaline treatment of sodium hydroxide(NaOH) on physical and dynamic mechanical analysis(DMA) viscoelastic properties of kenaf fibre filled natural rubber(NR)/thermoplastic polyurethane(TPU) composites.The treated kenaf fiber,NR and TPU were weighed and proportioned according to the required compositions and were blended using hot mixed Brabender machine.The polymer composites were then fabricated using the hot press to form a sample board.The sample was cut and prepared and water absorption,density,thickness swelling and DMA tests were performed.As far as physical properties are concerned,composites with the highest NR amount of shows the best results,which indicates good fiber bonding adhesion.The polymer composites with the highest amount of TPU shows the highest damping properties at high temperature.展开更多
The dispersion of magnetic nanoparticles in matrix is crucial to ensure optimum performance of the composite.The difficulty level of achieving good dispersion is further increase when a multi-phases of matrix is prese...The dispersion of magnetic nanoparticles in matrix is crucial to ensure optimum performance of the composite.The difficulty level of achieving good dispersion is further increase when a multi-phases of matrix is present.A pre-coating technique of magnetic nanoparticles with polypropylene using ball-mill prior to melt-blending process was employed to prepare a multi-phases thermoplastic natural rubber composite.The effect of filler loading(2 wt%-10 wt%) on morphology,structure,magnetic properties,thermal stability and dynamic mechanical properties of the composites were investigated.It was found that the NiZn ferrite nanoparticles act as nucleating agent to form beta isostatic polypropylene thermoplastic composites.The composites’ magnetic properties are directly dependent on the filler concentration.The dispersion of magnetic fillers in polymer matrix plays role in affecting the magnetic properties and thermal stability.The preference of filler to locate at amorphous phase has distorted the chain orientation of natural rubber and polypropylene.Hence,the polymorphism and crystallinity of the matrix varied as the filler loading increased,affecting the dynamic mechanical properties.It was found that 8 wt% NiZn nanocomposite exhibits highest E’ and tanδ,indicating the dynamic mechanical properties of NiZn nanocomposite are affected by β-phase degree.展开更多
Thermoplastic elastomeric blends prepared from blending of (10%, 20%, 30%, 40% and 50 wt%) high density polyethylene(HDPE) and (10%, 20%, 30%, 40% and 50 wt%) ground rubber tire (TPV-R). The blends prepared contain (H...Thermoplastic elastomeric blends prepared from blending of (10%, 20%, 30%, 40% and 50 wt%) high density polyethylene(HDPE) and (10%, 20%, 30%, 40% and 50 wt%) ground rubber tire (TPV-R). The blends prepared contain (HDPE)/polybutadiene (TPV-V). The two blends were successfully prepared through a dynamic vulcanization process, involving dicumyl peroxide (3%) as vulcanizing agent. The data of the mechanical (tensile strength at yield, %elongation and young modulus) and rheological properties (shear stress, shear rate, viscosity, flow behavior index and activation energy of melt flow) of the TPV-V and TPV-R showed that there was comparable results between the two blends.展开更多
基金Universiti Kuala Lumpur(UniKL)the Ministry of Education Malaysia for providing the scholarship award+1 种基金financially support through UniKL Grant Scheme(STRG 15144)to the principal author in this projectHiCOE grant(6369107)from the Ministry of Education,Malaysia。
文摘The paper presents the investigation of the effect of alkaline treatment of sodium hydroxide(NaOH) on physical and dynamic mechanical analysis(DMA) viscoelastic properties of kenaf fibre filled natural rubber(NR)/thermoplastic polyurethane(TPU) composites.The treated kenaf fiber,NR and TPU were weighed and proportioned according to the required compositions and were blended using hot mixed Brabender machine.The polymer composites were then fabricated using the hot press to form a sample board.The sample was cut and prepared and water absorption,density,thickness swelling and DMA tests were performed.As far as physical properties are concerned,composites with the highest NR amount of shows the best results,which indicates good fiber bonding adhesion.The polymer composites with the highest amount of TPU shows the highest damping properties at high temperature.
基金the support from the National Science Fund(NSF)MOSTI+1 种基金UKMUCSI
文摘The dispersion of magnetic nanoparticles in matrix is crucial to ensure optimum performance of the composite.The difficulty level of achieving good dispersion is further increase when a multi-phases of matrix is present.A pre-coating technique of magnetic nanoparticles with polypropylene using ball-mill prior to melt-blending process was employed to prepare a multi-phases thermoplastic natural rubber composite.The effect of filler loading(2 wt%-10 wt%) on morphology,structure,magnetic properties,thermal stability and dynamic mechanical properties of the composites were investigated.It was found that the NiZn ferrite nanoparticles act as nucleating agent to form beta isostatic polypropylene thermoplastic composites.The composites’ magnetic properties are directly dependent on the filler concentration.The dispersion of magnetic fillers in polymer matrix plays role in affecting the magnetic properties and thermal stability.The preference of filler to locate at amorphous phase has distorted the chain orientation of natural rubber and polypropylene.Hence,the polymorphism and crystallinity of the matrix varied as the filler loading increased,affecting the dynamic mechanical properties.It was found that 8 wt% NiZn nanocomposite exhibits highest E’ and tanδ,indicating the dynamic mechanical properties of NiZn nanocomposite are affected by β-phase degree.
文摘Thermoplastic elastomeric blends prepared from blending of (10%, 20%, 30%, 40% and 50 wt%) high density polyethylene(HDPE) and (10%, 20%, 30%, 40% and 50 wt%) ground rubber tire (TPV-R). The blends prepared contain (HDPE)/polybutadiene (TPV-V). The two blends were successfully prepared through a dynamic vulcanization process, involving dicumyl peroxide (3%) as vulcanizing agent. The data of the mechanical (tensile strength at yield, %elongation and young modulus) and rheological properties (shear stress, shear rate, viscosity, flow behavior index and activation energy of melt flow) of the TPV-V and TPV-R showed that there was comparable results between the two blends.