The addition of 2,5-pyridinedicarboxylic acid(2,5-PDCA)to the Mg-Al LDH coating,which was prepared by one-step hydrothermal synthesis,had extremely enhanced the corrosion protection of AZ31 Mg alloy,although the 2,5-P...The addition of 2,5-pyridinedicarboxylic acid(2,5-PDCA)to the Mg-Al LDH coating,which was prepared by one-step hydrothermal synthesis,had extremely enhanced the corrosion protection of AZ31 Mg alloy,although the 2,5-PDCA could not be intercalated into the interlayer spacing.The corrosion current density of 0.05 mol L^(−1)2,5-PDCA LDH containing LDH coating is 3.18 nA cm^(−2),reduced by two orders of magnitude compared to the LDH coating without inhibitor,and the corrosion inhibition efficiency of the coating is 98.05%.The coating formed on the surface of AZ31 was peeled off from the substrate by using a mechanical method and SEM observation of the cross-section showed that the coating consisted of three different layers.The innermost layer is a thick layer that consists of Mg(OH)_(2)and the intermediate layer is LDH,which is vertical to the substrate and the outmost layer is a thin but very dense deposit layer of LDH agglomerates with complexes of 2,5-PDCA and Mg.This kind of sediment/LDH/Mg(OH)_(2)three-layer composite structure was accountable for the increase in the corrosion resistance of AZ31 Mg alloy.展开更多
In this study,the effects of three different particle sizes of wood wastes(A=–8+12 mesh;B=–12+20 mesh;C=–20+30 mesh)and factory shavings(D)on the properties of particleboard were investigated.According to the test ...In this study,the effects of three different particle sizes of wood wastes(A=–8+12 mesh;B=–12+20 mesh;C=–20+30 mesh)and factory shavings(D)on the properties of particleboard were investigated.According to the test results,three-layer particleboard was designed.Particleboard face layers made with mixture of A,B,and C.The core layer made with D.The ratio of core layer to face layers is 50:50.Three-layer particleboard were fabricated with 12%urea-formaldehyde(UF)resins and three different high voltage electrostatic field intensities(0 kv,30 kv,60 kv).The internal bond(IB)strength,modulus of rupture(MOR),modulus of elasticity(MOE),thickness swelling(TS),and water absorption(WA)of particleboard were evaluated.The density distribution of the three-layer particleboard were examined by vertical density profiles(VDP),and the bonding mechanism and functional groups changes in the particles were analyzed by FTIR analysis.The results showed that HVEF treatment intensity play a remarkable role in properties of particleboard.The particleboard with higher electrostatic field intensities treatment has higher MOE,MOR,IB,and TS.Under HVEF treatment(60 kv),the MOR,modulus of MOE,and IB of three-layer particleboard were 23.61 N/mm^(2),2787.09 N/mm^(2),and 0.86 N/mm^(2),respectively.FTIR indicated that the surface activity of wood particles was increased electric field treatment.展开更多
文摘The addition of 2,5-pyridinedicarboxylic acid(2,5-PDCA)to the Mg-Al LDH coating,which was prepared by one-step hydrothermal synthesis,had extremely enhanced the corrosion protection of AZ31 Mg alloy,although the 2,5-PDCA could not be intercalated into the interlayer spacing.The corrosion current density of 0.05 mol L^(−1)2,5-PDCA LDH containing LDH coating is 3.18 nA cm^(−2),reduced by two orders of magnitude compared to the LDH coating without inhibitor,and the corrosion inhibition efficiency of the coating is 98.05%.The coating formed on the surface of AZ31 was peeled off from the substrate by using a mechanical method and SEM observation of the cross-section showed that the coating consisted of three different layers.The innermost layer is a thick layer that consists of Mg(OH)_(2)and the intermediate layer is LDH,which is vertical to the substrate and the outmost layer is a thin but very dense deposit layer of LDH agglomerates with complexes of 2,5-PDCA and Mg.This kind of sediment/LDH/Mg(OH)_(2)three-layer composite structure was accountable for the increase in the corrosion resistance of AZ31 Mg alloy.
基金The Authors acknowledge funding support by the National Key R&D Program of China(2017YFC0703501)The authors wish to acknowledge the National Natural Science Foundation of China(Grant No.32071700).
文摘In this study,the effects of three different particle sizes of wood wastes(A=–8+12 mesh;B=–12+20 mesh;C=–20+30 mesh)and factory shavings(D)on the properties of particleboard were investigated.According to the test results,three-layer particleboard was designed.Particleboard face layers made with mixture of A,B,and C.The core layer made with D.The ratio of core layer to face layers is 50:50.Three-layer particleboard were fabricated with 12%urea-formaldehyde(UF)resins and three different high voltage electrostatic field intensities(0 kv,30 kv,60 kv).The internal bond(IB)strength,modulus of rupture(MOR),modulus of elasticity(MOE),thickness swelling(TS),and water absorption(WA)of particleboard were evaluated.The density distribution of the three-layer particleboard were examined by vertical density profiles(VDP),and the bonding mechanism and functional groups changes in the particles were analyzed by FTIR analysis.The results showed that HVEF treatment intensity play a remarkable role in properties of particleboard.The particleboard with higher electrostatic field intensities treatment has higher MOE,MOR,IB,and TS.Under HVEF treatment(60 kv),the MOR,modulus of MOE,and IB of three-layer particleboard were 23.61 N/mm^(2),2787.09 N/mm^(2),and 0.86 N/mm^(2),respectively.FTIR indicated that the surface activity of wood particles was increased electric field treatment.