The severe erosion and inadequate mechanical strength are prominent challenges for high-energy gun propellants.To address it,novel PTW@PDA composites was prepared by polydopamine(PDA)-modifying onto potassium titanate...The severe erosion and inadequate mechanical strength are prominent challenges for high-energy gun propellants.To address it,novel PTW@PDA composites was prepared by polydopamine(PDA)-modifying onto potassium titanate whisker(PTW,K_(2)Ti_(6)O_(13)),and after was incorporated into gun propellant as erosion-reducing and mechanical-reinforcing fillers.The interfacial characterizations results indicated that as-prepared PTW@PDA composites exhibits an enhanced surface compatible with propellant matrix,thereby facilitating their dispersion into propellants more effectively than raw PTW materials.Compared to original propellants,PTW@PDA-modified propellants exhibited significant less erosion,with a Ti-Kbased protective coating being detected on the eroded steel.And 0.5 wt%and 1.0 wt%addition of PTW@PDA significantly improved impact,compressive and tensile strength of propellants.Despite the inevitably reduction in relative force,PTW@PDA slightly increase propellant burning rate while exerting little adverse impact on propellant dynamic activity.This strategy can provide a promising alternative to develop high-energy gun propellant with less erosion and more mechanical strength.展开更多
Solid oxide electrolysis cell(SOEC) could be a potential technology to afford chemical storage of renewable electricity by converting water and carbon dioxide.In this work,we present the Ni-doped layered perovskite ox...Solid oxide electrolysis cell(SOEC) could be a potential technology to afford chemical storage of renewable electricity by converting water and carbon dioxide.In this work,we present the Ni-doped layered perovskite oxides,(La_(4)Sr_(n-4))_(0.9)Ti_(0.9n)Ni_(0.1n)O_(3n+2) with n=5,8,and 12(LSTNn) for application as catalysts of CO_(2) electrolysis with the exsolution of Ni nanoparticles through a simple in-situ growth method.It is found that the density,size,and distribution of exsolved Ni nanoparticles are determined by the number of n in LSTNn due to the different stack structures of TiO_6 octahedra along the c axis.The Ni doping in LSTNn significantly improved the electrochemical activity by increasing oxygen vacancies,and the Ni metallic nanoparticles afford much more active sites.The results show that LSTNn cathodes can successfully be manipulated the activity by controlling both the n number and Ni exsolution.Among these LSTNn(n=5,8,and 12),LSTN8 renders a higher activity for electrolysis of CO_(2) with a current density of 1.50A cm^(-2)@2.0 V at 800℃ It is clear from these results that the number of n in(La_(4)Sr_(n-4))_(0.9)Ti_(0.9n)Ni_(0.1n)O_(3n+2)with Ni-doping is a key factor in controlling the electrochemical performance and catalytic activity in SOEC.展开更多
Tetragonal barium titanate was synthesized from barium hydroxide octahydrate and titanium tetrachloride through a simple one-step hydrothermal method.The effect of different solvents on the crystal structure and morph...Tetragonal barium titanate was synthesized from barium hydroxide octahydrate and titanium tetrachloride through a simple one-step hydrothermal method.The effect of different solvents on the crystal structure and morphology of barium titanate nanoparticles during the hy-drothermal process was investigated.Except for ethylene glycol/water solvent,impurity-free barium titanate was synthesized in pure water,methanol/water,ethanol/water,and isopropyl alcohol/water mixed solvents.Compared with other alcohols,ethanol promotes the formation of a tetragonal structure.In addition,characterization studies confirm that particles synthesized in methanol/water,ethanol/water,and isopropyl al-cohol/water mixed solvents are smaller in size than those synthesized in pure water.In the case of alcohol-containing solvents,the particle size decreases in the order of isopropanol,ethanol,and methanol.Among all the media used in this study,ethanol/water is considered the optimum reaction media for barium titanate with high tetragonality(defined as the ratio of two lattice parameters c and a,c/a=1.0088)and small aver-age particle size(82 nm),which indicates its great application potential in multilayer ceramic capacitors.展开更多
Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degra...Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degradation was done to investigate the removal efficiency of Oxytetracycline Dihydrate (OTC) using ZnO, ZnO/3%BaTiO<sub>3</sub> (3 BZ), ZnO/18%BaTiO<sub>3</sub> (18 BZ), ZnO/ 33%BaTiO3 (33 BZ) and ZnO/48%BaTiO<sub>3</sub> (48 BZ) under UV light. After the exposure time of 420 min, about 99.57% and 97.87% of OTC was degraded using ZnO and 3 BZ respectively. Further, increasing the amount of BaTiO<sub>3</sub> in ZnO prolongs the degradation time. Therefore, faster efficiency was found using ZnO nanoparticles. The observed reaction rate constant using ZnO was 0.00933 min<sup>-1</sup> which decreased to 0.00532 min<sup>-1</sup> using 48 BZ, indicating the decrease of reaction rate for increasing the amount of BaTiO<sub>3</sub>. Hence, the use of ZnO photocatalyst is anticipated to be a promising technique for the photocatalytic degradation of contaminated wastewater with oxytetracycline antibiotics using UV light.展开更多
基金the support of the instrument and equipment fund of the Key Laboratory of Special Energy,Ministry of Education,Nanjing University of Science and Technology,China.
文摘The severe erosion and inadequate mechanical strength are prominent challenges for high-energy gun propellants.To address it,novel PTW@PDA composites was prepared by polydopamine(PDA)-modifying onto potassium titanate whisker(PTW,K_(2)Ti_(6)O_(13)),and after was incorporated into gun propellant as erosion-reducing and mechanical-reinforcing fillers.The interfacial characterizations results indicated that as-prepared PTW@PDA composites exhibits an enhanced surface compatible with propellant matrix,thereby facilitating their dispersion into propellants more effectively than raw PTW materials.Compared to original propellants,PTW@PDA-modified propellants exhibited significant less erosion,with a Ti-Kbased protective coating being detected on the eroded steel.And 0.5 wt%and 1.0 wt%addition of PTW@PDA significantly improved impact,compressive and tensile strength of propellants.Despite the inevitably reduction in relative force,PTW@PDA slightly increase propellant burning rate while exerting little adverse impact on propellant dynamic activity.This strategy can provide a promising alternative to develop high-energy gun propellant with less erosion and more mechanical strength.
基金supported by the National Natural Science Foundation of China (51877173)the Key R&D Project of Shaanxi Province (2023-YBGY-057)+1 种基金the State Key Laboratory of Electrical Insulation and Power Equipment (EIPE22314, EIPE22306)the Natural Science Basic Research Program of Shaanxi (2023-JC-QN-0483)。
文摘Solid oxide electrolysis cell(SOEC) could be a potential technology to afford chemical storage of renewable electricity by converting water and carbon dioxide.In this work,we present the Ni-doped layered perovskite oxides,(La_(4)Sr_(n-4))_(0.9)Ti_(0.9n)Ni_(0.1n)O_(3n+2) with n=5,8,and 12(LSTNn) for application as catalysts of CO_(2) electrolysis with the exsolution of Ni nanoparticles through a simple in-situ growth method.It is found that the density,size,and distribution of exsolved Ni nanoparticles are determined by the number of n in LSTNn due to the different stack structures of TiO_6 octahedra along the c axis.The Ni doping in LSTNn significantly improved the electrochemical activity by increasing oxygen vacancies,and the Ni metallic nanoparticles afford much more active sites.The results show that LSTNn cathodes can successfully be manipulated the activity by controlling both the n number and Ni exsolution.Among these LSTNn(n=5,8,and 12),LSTN8 renders a higher activity for electrolysis of CO_(2) with a current density of 1.50A cm^(-2)@2.0 V at 800℃ It is clear from these results that the number of n in(La_(4)Sr_(n-4))_(0.9)Ti_(0.9n)Ni_(0.1n)O_(3n+2)with Ni-doping is a key factor in controlling the electrochemical performance and catalytic activity in SOEC.
基金supported by Chongqing Newcent New Materials Co.,Ltd.,China (No.2021GKF-0708).
文摘Tetragonal barium titanate was synthesized from barium hydroxide octahydrate and titanium tetrachloride through a simple one-step hydrothermal method.The effect of different solvents on the crystal structure and morphology of barium titanate nanoparticles during the hy-drothermal process was investigated.Except for ethylene glycol/water solvent,impurity-free barium titanate was synthesized in pure water,methanol/water,ethanol/water,and isopropyl alcohol/water mixed solvents.Compared with other alcohols,ethanol promotes the formation of a tetragonal structure.In addition,characterization studies confirm that particles synthesized in methanol/water,ethanol/water,and isopropyl al-cohol/water mixed solvents are smaller in size than those synthesized in pure water.In the case of alcohol-containing solvents,the particle size decreases in the order of isopropanol,ethanol,and methanol.Among all the media used in this study,ethanol/water is considered the optimum reaction media for barium titanate with high tetragonality(defined as the ratio of two lattice parameters c and a,c/a=1.0088)and small aver-age particle size(82 nm),which indicates its great application potential in multilayer ceramic capacitors.
文摘Traditional wastewater mostly contains pharmaceutical ingredients. Therefore, the wastewater must be completely free from antibiotics before its release into the environment. In the present study, photocatalytic degradation was done to investigate the removal efficiency of Oxytetracycline Dihydrate (OTC) using ZnO, ZnO/3%BaTiO<sub>3</sub> (3 BZ), ZnO/18%BaTiO<sub>3</sub> (18 BZ), ZnO/ 33%BaTiO3 (33 BZ) and ZnO/48%BaTiO<sub>3</sub> (48 BZ) under UV light. After the exposure time of 420 min, about 99.57% and 97.87% of OTC was degraded using ZnO and 3 BZ respectively. Further, increasing the amount of BaTiO<sub>3</sub> in ZnO prolongs the degradation time. Therefore, faster efficiency was found using ZnO nanoparticles. The observed reaction rate constant using ZnO was 0.00933 min<sup>-1</sup> which decreased to 0.00532 min<sup>-1</sup> using 48 BZ, indicating the decrease of reaction rate for increasing the amount of BaTiO<sub>3</sub>. Hence, the use of ZnO photocatalyst is anticipated to be a promising technique for the photocatalytic degradation of contaminated wastewater with oxytetracycline antibiotics using UV light.