A series of Al based alloys with low titanium contents (mass fraction) from 0.178% to 0.526% were directly produced in ordinary industrial electrolyzer. The electrolyzing results show that producing Al based alloys wi...A series of Al based alloys with low titanium contents (mass fraction) from 0.178% to 0.526% were directly produced in ordinary industrial electrolyzer. The electrolyzing results show that producing Al based alloys with titanium contents of less than 0.30% without great loss of electrolysis efficiency is possible. The quantitative analysis shows that this method has a great refining effect on transiting the coarse columnar grains in pure Al to equiaxed grains. The grain sizes decrease with the increase of titanium content and tend to a low limit at about 130 μm. During the solidification, the non equilibrium distribution of titanium leads to a great growth restricting effect and a constitutional under cooling zone in front of the growing liquid /solid interface.展开更多
Two linear regression models based on absorption features extracted from CE-1 IIM image data are presented to discuss the relationship between absorption features and titanium content. We computed five absorption para...Two linear regression models based on absorption features extracted from CE-1 IIM image data are presented to discuss the relationship between absorption features and titanium content. We computed five absorption parameters (Full Wave at Half Maximum (FWHM), absorption position, absorption area, absorption depth and absorption asymmetry) of the spectra collected at Apollo 17 landing sites to build two regression models, one with FWHM and the other without FWHM due to the low relation coefficient between FWHM and Ti content. Finally Ti content measured from Apollo 17 samples and Apollo 16 samples was used to test the accuracy. The results show that the predicted values of the model with FWHM have many singular values and the result of model without FWHM is more stable. The two models are relatively accurate for high-Ti districts, while seem inexact and disable for low-Ti districts.展开更多
On the basis of the thermodynamic analysis and fundamental study in the laboratory, the equilibrium of the Ti A10 system was investigated. The results showed that the equilibrium titanium content in the steel increase...On the basis of the thermodynamic analysis and fundamental study in the laboratory, the equilibrium of the Ti A10 system was investigated. The results showed that the equilibrium titanium content in the steel increased with the increase in the soluble aluminum content in the steel and the TiO2 content in the slag. Although the slag basicity decreased and Al2O3 content in the slag increased, the titanium content increased. Based on these results, the BOF smelting process of low titanium bearing steel was put forward.展开更多
A series of Ti–Al–V titanium alloy bars with nominal composition Ti–7Al–5V ELI,Ti–5Al–3V ELI,commercial Ti–6Al–4V ELI and commercial Ti–6Al–4V were prepared.These alloys were then heat treated to obtain bimo...A series of Ti–Al–V titanium alloy bars with nominal composition Ti–7Al–5V ELI,Ti–5Al–3V ELI,commercial Ti–6Al–4V ELI and commercial Ti–6Al–4V were prepared.These alloys were then heat treated to obtain bimodal or equiaxed microstructures with various contents of primary a phase.Dynamic compression properties of the alloys above were studied by split Hopkinson pressure bar system at strain rates from 2,000 to 4,000 s-1.The results show that Ti–6Al–4V alloy with equiaxed primary a(ap)volume fraction of 45 vol%or 67 vol%exhibits good dynamic properties with high dynamic strength and absorbed energy,as well as an acceptable dynamic plasticity.However,all the Ti53ELI specimens and Ti64ELI specimens with ap of 65 vol%were not fractured at a strain rate of4,000 s-1.It appears that the undamaged specimens still have load-bearing capability.Dynamic strength of Ti–Al–V alloy can be improved as the contents of elements Al,V,Fe,and O increase,while dynamic strain is not sensitive to the composition in the appropriate range.The effects of primary alpha volume fraction on the dynamic properties are dependent on the compositions of Ti–Al–V alloys.展开更多
The sintering of chromium-containing vanadium-titanium magnetite using different coke contents was studied through the sintering pot tests, X-ray diffraction analysis and mineralogical phase analysis. Results showed t...The sintering of chromium-containing vanadium-titanium magnetite using different coke contents was studied through the sintering pot tests, X-ray diffraction analysis and mineralogical phase analysis. Results showed that, as the coke content increased from 3.2% to 4.4%, the liquid phase and combustion zone thickness increased while the vertical sintering rate and ratio of sintered product decreased. In addition, the combustion ratio of exhaust gas also increased with increasing the coke content, indicating that combustion zone temperature also increased, and the excessive the coke content in the sintering process of vanadiumtitanium magnetite is harmful. As the coke content increased, the magnetite, silicates, and perovskite contents of the sintered ore increased while the contents of hematite and calcium ferrite of sintered ore decreased; drum strength decreased, and reduction degradation properties increased while reduction ability decreased. We found that the appropriate coke content for the sintering process is 3.6 wt%.展开更多
The influence of interstitial content on mechanical properties of a new type of near α titanium alloy(Ti-Zr-Mo-Nb-Sn) at cryogenic temperature was studied. The results show that interstitial content affects the mecha...The influence of interstitial content on mechanical properties of a new type of near α titanium alloy(Ti-Zr-Mo-Nb-Sn) at cryogenic temperature was studied. The results show that interstitial content affects the mechanical properties of the alloy at cryogenic temperature. Interstitial element atoms solving into lattice causes the increasing of degree of distortion,which limits the sliding and twinning of dislocations. Reducing interstitial content is beneficial to generation of dislocation sliding and deformation twins. With interstitial element content reducing,the impact toughness and the elongation of the alloy decrease rapidly while the strength decreases weakly. To obtain good over-all properties at cryogenic temperature,the interstitial element content in this alloy must be controlled to extra low grade.展开更多
To characterize the effects of alloying elements on inclusion dissolution of titanium nitride, the content profiles of elements around TiN/Ti boundary α phase regions in liquid titanium alloys have been experimentall...To characterize the effects of alloying elements on inclusion dissolution of titanium nitride, the content profiles of elements around TiN/Ti boundary α phase regions in liquid titanium alloys have been experimentally carried out. Four kinds of commercial alloys of CpTi, Ti64, Ti17 and Ti6242 containing different α stabilizing or β stabilizing elements are examined through artificially embedding the TiN sponge particle into liquid alloys in VAR conditions. The content profiles of nitrogen and alloying elements around TiN/Ti boundary were measured by WDX and microprobe for as cast samples. The content profiles of nitrogen and alloying elements around N containing solid in α Ti region of these alloys show a common features of a steep change. In particular, the content profiles of elements for Ti6242 demonstrate unique change of a more gentle change tendency and further deeper into the alloy matrix. The experiment results show that, the differences among composite effects of alloying elements in different alloys within nitrogen induced diffusion α region result in different dissolution and diffusion behaviors to overcome the α phase region barriers.展开更多
Metallic titanium film was deposited on H-13 steel substrate at 470°C - 530°C using plasma enhanced chemical vapor deposition (PECVD) method. In this paper, the effects of manufacturing parameters were inves...Metallic titanium film was deposited on H-13 steel substrate at 470°C - 530°C using plasma enhanced chemical vapor deposition (PECVD) method. In this paper, the effects of manufacturing parameters were investigated on deposited titanium coating characteristics. XRD, FESEM, XPS and AFM were used in order to study coating characteristics. Increasing hydrogen flow rate from 200 to 360 sccm, resulted in a 72% decrease in oxygen content and 38% decrease in chlorine content of the film. Applied plasma voltage has a severe effect on nanohardness of coating. Pressure of the deposition chamber has a negative effect on titanium characteristics.展开更多
文摘A series of Al based alloys with low titanium contents (mass fraction) from 0.178% to 0.526% were directly produced in ordinary industrial electrolyzer. The electrolyzing results show that producing Al based alloys with titanium contents of less than 0.30% without great loss of electrolysis efficiency is possible. The quantitative analysis shows that this method has a great refining effect on transiting the coarse columnar grains in pure Al to equiaxed grains. The grain sizes decrease with the increase of titanium content and tend to a low limit at about 130 μm. During the solidification, the non equilibrium distribution of titanium leads to a great growth restricting effect and a constitutional under cooling zone in front of the growing liquid /solid interface.
基金supported by the Research Foundation of Science and Technology, China University of Geosciences (Wuhan) (Grant No. CUGXGF0901),the Special Fund for Basic Scientific Research of Central Colleges, China University of Geosciences (Wuhan) (Grant No. CUGL090228)the National College Students Innovation Foundation of China (Grant No. 091049130)
文摘Two linear regression models based on absorption features extracted from CE-1 IIM image data are presented to discuss the relationship between absorption features and titanium content. We computed five absorption parameters (Full Wave at Half Maximum (FWHM), absorption position, absorption area, absorption depth and absorption asymmetry) of the spectra collected at Apollo 17 landing sites to build two regression models, one with FWHM and the other without FWHM due to the low relation coefficient between FWHM and Ti content. Finally Ti content measured from Apollo 17 samples and Apollo 16 samples was used to test the accuracy. The results show that the predicted values of the model with FWHM have many singular values and the result of model without FWHM is more stable. The two models are relatively accurate for high-Ti districts, while seem inexact and disable for low-Ti districts.
文摘On the basis of the thermodynamic analysis and fundamental study in the laboratory, the equilibrium of the Ti A10 system was investigated. The results showed that the equilibrium titanium content in the steel increased with the increase in the soluble aluminum content in the steel and the TiO2 content in the slag. Although the slag basicity decreased and Al2O3 content in the slag increased, the titanium content increased. Based on these results, the BOF smelting process of low titanium bearing steel was put forward.
基金supported by the China–Korea Joint Research Program of Ministry of Science and Technology of China (No. 2012DFG51540)
文摘A series of Ti–Al–V titanium alloy bars with nominal composition Ti–7Al–5V ELI,Ti–5Al–3V ELI,commercial Ti–6Al–4V ELI and commercial Ti–6Al–4V were prepared.These alloys were then heat treated to obtain bimodal or equiaxed microstructures with various contents of primary a phase.Dynamic compression properties of the alloys above were studied by split Hopkinson pressure bar system at strain rates from 2,000 to 4,000 s-1.The results show that Ti–6Al–4V alloy with equiaxed primary a(ap)volume fraction of 45 vol%or 67 vol%exhibits good dynamic properties with high dynamic strength and absorbed energy,as well as an acceptable dynamic plasticity.However,all the Ti53ELI specimens and Ti64ELI specimens with ap of 65 vol%were not fractured at a strain rate of4,000 s-1.It appears that the undamaged specimens still have load-bearing capability.Dynamic strength of Ti–Al–V alloy can be improved as the contents of elements Al,V,Fe,and O increase,while dynamic strain is not sensitive to the composition in the appropriate range.The effects of primary alpha volume fraction on the dynamic properties are dependent on the compositions of Ti–Al–V alloys.
基金Funded by the National Natural Science Foundation of China(Nos.51604065,51674084)the Fundamental Funds for the Program of the Science Foundation of Liaoning Province(No.20170540316)
文摘The sintering of chromium-containing vanadium-titanium magnetite using different coke contents was studied through the sintering pot tests, X-ray diffraction analysis and mineralogical phase analysis. Results showed that, as the coke content increased from 3.2% to 4.4%, the liquid phase and combustion zone thickness increased while the vertical sintering rate and ratio of sintered product decreased. In addition, the combustion ratio of exhaust gas also increased with increasing the coke content, indicating that combustion zone temperature also increased, and the excessive the coke content in the sintering process of vanadiumtitanium magnetite is harmful. As the coke content increased, the magnetite, silicates, and perovskite contents of the sintered ore increased while the contents of hematite and calcium ferrite of sintered ore decreased; drum strength decreased, and reduction degradation properties increased while reduction ability decreased. We found that the appropriate coke content for the sintering process is 3.6 wt%.
基金Project(2007CB613807) supported by National Basic Research Program of China
文摘The influence of interstitial content on mechanical properties of a new type of near α titanium alloy(Ti-Zr-Mo-Nb-Sn) at cryogenic temperature was studied. The results show that interstitial content affects the mechanical properties of the alloy at cryogenic temperature. Interstitial element atoms solving into lattice causes the increasing of degree of distortion,which limits the sliding and twinning of dislocations. Reducing interstitial content is beneficial to generation of dislocation sliding and deformation twins. With interstitial element content reducing,the impact toughness and the elongation of the alloy decrease rapidly while the strength decreases weakly. To obtain good over-all properties at cryogenic temperature,the interstitial element content in this alloy must be controlled to extra low grade.
文摘To characterize the effects of alloying elements on inclusion dissolution of titanium nitride, the content profiles of elements around TiN/Ti boundary α phase regions in liquid titanium alloys have been experimentally carried out. Four kinds of commercial alloys of CpTi, Ti64, Ti17 and Ti6242 containing different α stabilizing or β stabilizing elements are examined through artificially embedding the TiN sponge particle into liquid alloys in VAR conditions. The content profiles of nitrogen and alloying elements around TiN/Ti boundary were measured by WDX and microprobe for as cast samples. The content profiles of nitrogen and alloying elements around N containing solid in α Ti region of these alloys show a common features of a steep change. In particular, the content profiles of elements for Ti6242 demonstrate unique change of a more gentle change tendency and further deeper into the alloy matrix. The experiment results show that, the differences among composite effects of alloying elements in different alloys within nitrogen induced diffusion α region result in different dissolution and diffusion behaviors to overcome the α phase region barriers.
文摘Metallic titanium film was deposited on H-13 steel substrate at 470°C - 530°C using plasma enhanced chemical vapor deposition (PECVD) method. In this paper, the effects of manufacturing parameters were investigated on deposited titanium coating characteristics. XRD, FESEM, XPS and AFM were used in order to study coating characteristics. Increasing hydrogen flow rate from 200 to 360 sccm, resulted in a 72% decrease in oxygen content and 38% decrease in chlorine content of the film. Applied plasma voltage has a severe effect on nanohardness of coating. Pressure of the deposition chamber has a negative effect on titanium characteristics.