The thermal stresses relaxation of Ni/NiFe2O4 system functionally graded cermet inert anode for aluminum electrolysis was optimally designed. The transient thermal stresses of the inert anode under complex boundary co...The thermal stresses relaxation of Ni/NiFe2O4 system functionally graded cermet inert anode for aluminum electrolysis was optimally designed. The transient thermal stresses of the inert anode under complex boundary condition during high-temp （955℃） electrolysis were calculated using the finite-element software ANSYS, the influence of different parameters on the distribution of the thermal stresses were analyzed. The results showed that, during the process of thermal shock, the thermal hoop tensile stress on the surface of the anode is very large, which is possibly the major cause of anode crack; when the radius of the anode is between 0.05-0.15m, a range that can be realized by recent manufacturing technology, the optimum composition distribution exponent p is 0.25; The hoop tensile stresses reduce with the decrease of anode scale and also decrease with the decrease of the convection coefficient between the electrolyte and the anode.展开更多
A comprehensive treatment of fracture of functionally gradedmaterials (FGMs) is provided. It is assumed that the materialproperties depend only on the coordinate perpendicular to the cracksurface And vary continuously...A comprehensive treatment of fracture of functionally gradedmaterials (FGMs) is provided. It is assumed that the materialproperties depend only on the coordinate perpendicular to the cracksurface And vary continuously along the crack faces. By using alaminated composite plate model to simulate the ma- Terialnon-homogeneity, an algorithm for solving the system based on Laplacetransform and Fourier transform Techniques is presented. Unlikeearlier studies that considered certain assumed propertydistributions and a Single crack problem, the current investigationstudies multiple crack problem in the FGMs with arbitrarily Varyingmaterial properties. Transient thermal stresses are presented.展开更多
The incorrect deduction of equations in the research works devoted to the studies of transient stress in cylindrically orthotropic tubes and done by Kardomateas (Journal of Applied Mechanics, 1989, 1990) leads to the ...The incorrect deduction of equations in the research works devoted to the studies of transient stress in cylindrically orthotropic tubes and done by Kardomateas (Journal of Applied Mechanics, 1989, 1990) leads to the wrong results. The errata (1991) correct the deduction error, but do not give the right numerical results. All errors are corrected, and the Mathematica is adopted to solve the large argument problem for Bessel function. A theoretical solution of the transient thermal stresses in tubes with uniform form is presented, and a numerical example is studied.展开更多
Based on the deep understanding of the requirements of cutting conditions on ceramic tools, a design model for functionally gradient ceramic tool materials with symmetrical composition distribution was presented in th...Based on the deep understanding of the requirements of cutting conditions on ceramic tools, a design model for functionally gradient ceramic tool materials with symmetrical composition distribution was presented in this paper, according to which an Al 2O 3-TiC functionally gradient ceramic tool material FG-1 was synthesized by powder-laminating and uniaxially hot-pressing technique. The thermal shock resistance of the Al 2O 3-TiC functionally gradient ceramics FG-1 was evaluated by water quenching and subsequent three-point bending tests of flexural strength diminution. Comparisons were made with results from parallel experiments conducted using a homogeneous Al 2O 3-TiC ceramics. Functionally gradient ceramics exhibited higher retained strength under all thermal shock temperature differences compared to homogeneous ceramics, indicating the higher thermal shock resistance. The experimental results were supported by the calculation of transient thermal stress field. The cutting performance of the Al 2O 3-TiC functionally gradient ceramic tool FG-1 was also investigated in rough turning the cylindrical surface of exhaust valve of diesel engine in comparison with that of a common Al 2O 3-TiC ceramic tool LT55. The results indicated that the tool life of FG-1 increased by 50 percent over that of LT55. Tool life of LT55 was mainly controlled by thermal shock cracking which was accompanied by mechanical shock. While tool life of FG-1 was mainly controlled by mechanical fatigue crack extension rather than thermal shock cracking, revealing the less thermal shock susceptibility of functionally gradient ceramics than that of common ceramics.展开更多
基金This work was supported by the National Basic Research Program of China(No.2005CB623703)National Natural Science Foundation(No.5047405I)+1 种基金Hunan Provincial Natural Science Foundation of China(No.03JJY3080)Trans-Century Excellent Persons Cultivation Project of Ministry of Education of China(in 2002).
文摘The thermal stresses relaxation of Ni/NiFe2O4 system functionally graded cermet inert anode for aluminum electrolysis was optimally designed. The transient thermal stresses of the inert anode under complex boundary condition during high-temp （955℃） electrolysis were calculated using the finite-element software ANSYS, the influence of different parameters on the distribution of the thermal stresses were analyzed. The results showed that, during the process of thermal shock, the thermal hoop tensile stress on the surface of the anode is very large, which is possibly the major cause of anode crack; when the radius of the anode is between 0.05-0.15m, a range that can be realized by recent manufacturing technology, the optimum composition distribution exponent p is 0.25; The hoop tensile stresses reduce with the decrease of anode scale and also decrease with the decrease of the convection coefficient between the electrolyte and the anode.
基金the National Natural Science Foundation of China (Nos.10102004 and 19902003).
文摘A comprehensive treatment of fracture of functionally gradedmaterials (FGMs) is provided. It is assumed that the materialproperties depend only on the coordinate perpendicular to the cracksurface And vary continuously along the crack faces. By using alaminated composite plate model to simulate the ma- Terialnon-homogeneity, an algorithm for solving the system based on Laplacetransform and Fourier transform Techniques is presented. Unlikeearlier studies that considered certain assumed propertydistributions and a Single crack problem, the current investigationstudies multiple crack problem in the FGMs with arbitrarily Varyingmaterial properties. Transient thermal stresses are presented.
文摘The incorrect deduction of equations in the research works devoted to the studies of transient stress in cylindrically orthotropic tubes and done by Kardomateas (Journal of Applied Mechanics, 1989, 1990) leads to the wrong results. The errata (1991) correct the deduction error, but do not give the right numerical results. All errors are corrected, and the Mathematica is adopted to solve the large argument problem for Bessel function. A theoretical solution of the transient thermal stresses in tubes with uniform form is presented, and a numerical example is studied.
文摘Based on the deep understanding of the requirements of cutting conditions on ceramic tools, a design model for functionally gradient ceramic tool materials with symmetrical composition distribution was presented in this paper, according to which an Al 2O 3-TiC functionally gradient ceramic tool material FG-1 was synthesized by powder-laminating and uniaxially hot-pressing technique. The thermal shock resistance of the Al 2O 3-TiC functionally gradient ceramics FG-1 was evaluated by water quenching and subsequent three-point bending tests of flexural strength diminution. Comparisons were made with results from parallel experiments conducted using a homogeneous Al 2O 3-TiC ceramics. Functionally gradient ceramics exhibited higher retained strength under all thermal shock temperature differences compared to homogeneous ceramics, indicating the higher thermal shock resistance. The experimental results were supported by the calculation of transient thermal stress field. The cutting performance of the Al 2O 3-TiC functionally gradient ceramic tool FG-1 was also investigated in rough turning the cylindrical surface of exhaust valve of diesel engine in comparison with that of a common Al 2O 3-TiC ceramic tool LT55. The results indicated that the tool life of FG-1 increased by 50 percent over that of LT55. Tool life of LT55 was mainly controlled by thermal shock cracking which was accompanied by mechanical shock. While tool life of FG-1 was mainly controlled by mechanical fatigue crack extension rather than thermal shock cracking, revealing the less thermal shock susceptibility of functionally gradient ceramics than that of common ceramics.