By means of hydration heat, XRD and SEM, effect of phosphorus and fluorine （P205 and F-） in phosphorous slag on hydration process of tricalcium silicate （C3S） and tricalcium aluminate （C3A） was explored. The res...By means of hydration heat, XRD and SEM, effect of phosphorus and fluorine （P205 and F-） in phosphorous slag on hydration process of tricalcium silicate （C3S） and tricalcium aluminate （C3A） was explored. The results indicated that the early hydration exothermic rate of C3S and C3A was obviously lowered by P205 and F- in phosphorous slag, the second peak occurring time of C3A was delayed by 0.9 h, the exothermal output of C3S was reduced by 25.04% and the time of accelerating stage was postponed by 0.86 h. The early hydration degree of C3S and C3A was also decreased. Due to the influence of P205 and F, more pores and thinner crystals can be observed in the microstructure of hardened paste and the chance of cracks was reduced.展开更多
The effect of addition of Zn, Cu, Pb and Cr chlorides as admixtures on the hydration reaction of the system 3CaO·Al2O3-gypsum with molar ratio 1：3 was studied. Different ratios of each salt were used, namely 0.5...The effect of addition of Zn, Cu, Pb and Cr chlorides as admixtures on the hydration reaction of the system 3CaO·Al2O3-gypsum with molar ratio 1：3 was studied. Different ratios of each salt were used, namely 0.5%, 2% and 4% by weight of the solid mixture. Hydration reaction was carried out at 35℃ for various time intervals from 0.5 h to up to 7 d. Hydration rate of the system 3CaO·Al2O3-CaSO4·2H2O in absence and presence of different salts was studied via the determination of the combined water contents. X-ray diffraction analysis showed that the ettringite was the only hydration product formed in the different mixes. The hydration products were investigated by scanning electron microscopy （SEM） and thermal gravimetric analysis. The results indicated that the rate of formation of ettringite and its microstructure depend on the admixture and its dosage.展开更多
基金Funded by the National Natural Science Foundation of China (No.50802067)
文摘By means of hydration heat, XRD and SEM, effect of phosphorus and fluorine （P205 and F-） in phosphorous slag on hydration process of tricalcium silicate （C3S） and tricalcium aluminate （C3A） was explored. The results indicated that the early hydration exothermic rate of C3S and C3A was obviously lowered by P205 and F- in phosphorous slag, the second peak occurring time of C3A was delayed by 0.9 h, the exothermal output of C3S was reduced by 25.04% and the time of accelerating stage was postponed by 0.86 h. The early hydration degree of C3S and C3A was also decreased. Due to the influence of P205 and F, more pores and thinner crystals can be observed in the microstructure of hardened paste and the chance of cracks was reduced.
文摘The effect of addition of Zn, Cu, Pb and Cr chlorides as admixtures on the hydration reaction of the system 3CaO·Al2O3-gypsum with molar ratio 1：3 was studied. Different ratios of each salt were used, namely 0.5%, 2% and 4% by weight of the solid mixture. Hydration reaction was carried out at 35℃ for various time intervals from 0.5 h to up to 7 d. Hydration rate of the system 3CaO·Al2O3-CaSO4·2H2O in absence and presence of different salts was studied via the determination of the combined water contents. X-ray diffraction analysis showed that the ettringite was the only hydration product formed in the different mixes. The hydration products were investigated by scanning electron microscopy （SEM） and thermal gravimetric analysis. The results indicated that the rate of formation of ettringite and its microstructure depend on the admixture and its dosage.