A non-destructive and in-situ technique for the measurement of tritium in materials, namely β-ray-induced X-ray spectrometry （BIXS）, has been developed recently. In the present study a V-4Cr-4Ti alloy was pre-heate...A non-destructive and in-situ technique for the measurement of tritium in materials, namely β-ray-induced X-ray spectrometry （BIXS）, has been developed recently. In the present study a V-4Cr-4Ti alloy was pre-heated at 1000℃ for 2 h to form a recrystallization structure before the tritium absorption experiments were conducted. Firstly the hydrogen isotope gas was charazterized by means of a quadrupole mass spectrometer （QMS） and a small-sized ionization chamber. Then hydrogen isotope absorption tests of V-4Cr-4Ti alloy were performed at 400 ℃ and the atomic concentration of hydrogen isotope in V-4Cr-4Ti alloy was estimated as 0.17% with a tritium content of approximately 2.5 ppm. Experimental results indicate that BIXS is a quite useful tool for quantitatively measuring the tritium content and tritium distribution in the surface layers of vanadium alloys and no strong trapping effects of tritium exist in the pre-heated V-4Cr-4Ti alloy.展开更多
基金supported by the China-Japan Core University Program(Task1-2A)
文摘A non-destructive and in-situ technique for the measurement of tritium in materials, namely β-ray-induced X-ray spectrometry （BIXS）, has been developed recently. In the present study a V-4Cr-4Ti alloy was pre-heated at 1000℃ for 2 h to form a recrystallization structure before the tritium absorption experiments were conducted. Firstly the hydrogen isotope gas was charazterized by means of a quadrupole mass spectrometer （QMS） and a small-sized ionization chamber. Then hydrogen isotope absorption tests of V-4Cr-4Ti alloy were performed at 400 ℃ and the atomic concentration of hydrogen isotope in V-4Cr-4Ti alloy was estimated as 0.17% with a tritium content of approximately 2.5 ppm. Experimental results indicate that BIXS is a quite useful tool for quantitatively measuring the tritium content and tritium distribution in the surface layers of vanadium alloys and no strong trapping effects of tritium exist in the pre-heated V-4Cr-4Ti alloy.