By means of ultra-violet(UV)irradiation with photoini-tiator and multifunctional crosslinking agent,thecrosslinking modification of ultrahigh molecular weightpolyethylene(UHMWPE)fibers prepared by gel-spin-ning was ca...By means of ultra-violet(UV)irradiation with photoini-tiator and multifunctional crosslinking agent,thecrosslinking modification of ultrahigh molecular weightpolyethylene(UHMWPE)fibers prepared by gel-spin-ning was carried out.Thermal properties of fiber sampleswere examined using differential scanning calorimetry(DSC),thermomechanical analysis(TMA)apparatusand a manual device.The results indicated that the opti-mal irradiation energy is 250-400 mJ/cm^2,heat-andcreep-resistant behaviors of modified fibers have beenimproved.展开更多
Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-...Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-lar Weight Polyethylene(UHMWPE)fiber reinforcedPE tape prepared with the method of powder impregnat-ion was studied.The effect of impregnate length and thetensile force of the yarn on the fiber content as well as on the strength and modulus of the tape were discussed.Calculation shows that the strength and the modulus ofthe ULMWPE fiber can keep about 85％ after it undergothe process.展开更多
Synthesis of a m m oniu m alu min u m carbonate hydroxide ( A A C H) w as investigated usinga m m oniu m alu min u m sulfate and a m moniu m hydro carbonate as the starting m aterials . Itw as found that A A C Hca...Synthesis of a m m oniu m alu min u m carbonate hydroxide ( A A C H) w as investigated usinga m m oniu m alu min u m sulfate and a m moniu m hydro carbonate as the starting m aterials . Itw as found that A A C Hcan be synthesized by adding a m m oniu m alu m inu m sulfate solution torapidly stirred a m moniu m hydro - carbonate solution at a tem perature of 30 ℃. A A C Hcantransfor m to α Al2 O3 co m pletely by calcining at 1100 ℃ for 1 hour , and the obtained po w ders , with a particle size of 100 n m , can be sintered to 98 99 % relative density at 1500 ℃for 2 hours .展开更多
This work explored the way to improve hot modulus q/＇ rupture （HMOR） and refractoriness under load （RUL） by adding mild-calcined coal gangue （MCG） in Al2O3 -SiO2 ultra low cement （ULC） castables, making use o...This work explored the way to improve hot modulus q/＇ rupture （HMOR） and refractoriness under load （RUL） by adding mild-calcined coal gangue （MCG） in Al2O3 -SiO2 ultra low cement （ULC） castables, making use of the in-situ effect of the MCG during heating-up. The influence of respective additions of 5%, 10% and 1.5% of the MCG powders calcined at 700℃ was investigated on HMOR at 1400 ℃ and RUL of the castables. With increased addition of the MCG, HMOR and RUL become significantly enhanced. At 10% of the MCG addition, HMOR reaches 3 MPa, as compared to 0. 3 MPa in the case of no MCG addition. RUL of the specimens dried at 110 ℃for 24 h can be increased by some 270 ℃ with 10% of the MCG addition. RUL 0.11 the specimens preheated at 1 500℃ for 3 h maintains the growth trend with the MCG addition increasing. The microstructure of the heated castable samples was investigated by means of SEM. The in-situ formed needle-like and interlaced mullite in the matrix is contributive to the tmprovement.展开更多
基金oral prepared in the Second East Asian Polymer Conference held in Hongkong,China,January 12-16,1999
文摘By means of ultra-violet(UV)irradiation with photoini-tiator and multifunctional crosslinking agent,thecrosslinking modification of ultrahigh molecular weightpolyethylene(UHMWPE)fibers prepared by gel-spin-ning was carried out.Thermal properties of fiber sampleswere examined using differential scanning calorimetry(DSC),thermomechanical analysis(TMA)apparatusand a manual device.The results indicated that the opti-mal irradiation energy is 250-400 mJ/cm^2,heat-andcreep-resistant behaviors of modified fibers have beenimproved.
文摘Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-lar Weight Polyethylene(UHMWPE)fiber reinforcedPE tape prepared with the method of powder impregnat-ion was studied.The effect of impregnate length and thetensile force of the yarn on the fiber content as well as on the strength and modulus of the tape were discussed.Calculation shows that the strength and the modulus ofthe ULMWPE fiber can keep about 85％ after it undergothe process.
文摘Synthesis of a m m oniu m alu min u m carbonate hydroxide ( A A C H) w as investigated usinga m m oniu m alu min u m sulfate and a m moniu m hydro carbonate as the starting m aterials . Itw as found that A A C Hcan be synthesized by adding a m m oniu m alu m inu m sulfate solution torapidly stirred a m moniu m hydro - carbonate solution at a tem perature of 30 ℃. A A C Hcantransfor m to α Al2 O3 co m pletely by calcining at 1100 ℃ for 1 hour , and the obtained po w ders , with a particle size of 100 n m , can be sintered to 98 99 % relative density at 1500 ℃for 2 hours .
文摘This work explored the way to improve hot modulus q/＇ rupture （HMOR） and refractoriness under load （RUL） by adding mild-calcined coal gangue （MCG） in Al2O3 -SiO2 ultra low cement （ULC） castables, making use of the in-situ effect of the MCG during heating-up. The influence of respective additions of 5%, 10% and 1.5% of the MCG powders calcined at 700℃ was investigated on HMOR at 1400 ℃ and RUL of the castables. With increased addition of the MCG, HMOR and RUL become significantly enhanced. At 10% of the MCG addition, HMOR reaches 3 MPa, as compared to 0. 3 MPa in the case of no MCG addition. RUL of the specimens dried at 110 ℃for 24 h can be increased by some 270 ℃ with 10% of the MCG addition. RUL 0.11 the specimens preheated at 1 500℃ for 3 h maintains the growth trend with the MCG addition increasing. The microstructure of the heated castable samples was investigated by means of SEM. The in-situ formed needle-like and interlaced mullite in the matrix is contributive to the tmprovement.