The influence of ultrasonic vibrations on microstructure and mechanical properties of the AZ91-C magnesium alloy after ultrasonic assisted friction stir welding(UaFSW)in comparison with conventional friction stir weld...The influence of ultrasonic vibrations on microstructure and mechanical properties of the AZ91-C magnesium alloy after ultrasonic assisted friction stir welding(UaFSW)in comparison with conventional friction stir welding(FSW)was investigated.The FSW was applied at the rotational speed of 1400 r/min and welding speed of 40 mm/min and no defects were observed.Using the same welding parameters,the process was carried out with inducing ultrasonic vibrations to the weld line at the amplitude of 15μm.The microstructure of the specimens was observed with optical and scanning electron microscopy.The results indicate that a very fine microstructure is obtained in UaFSW with respect to that of conventional FSW.Moreover,β-Mg17Al12 coarse dendrites are segregated to very fine and partly spherical particles that homogeneously distribute inα-Mg matrix.This remarkably-modified morphology of microstructure attributed to severe plastic deformation comes from ultrasonic vibration and friction stirring effect.Tensile and hardness tests were performed to evaluate the mechanical properties of the welds.According to the results,the vibration greatly improves the mechanical properties of the conventional FSW joint.The tensile strength and hardness are increased from 195 MPa and HV 79 in conventional FSW to 225 MPa and HV 87 in UaFSW,respectively.展开更多
Ultrasonic assisted friction stir welding （UAFSW） is a recent modification of conventional friction stir welding, which adds ultrasonic energy directly into the friction stir welding area by the pin. In this study, ...Ultrasonic assisted friction stir welding （UAFSW） is a recent modification of conventional friction stir welding, which adds ultrasonic energy directly into the friction stir welding area by the pin. In this study, 2A12 aluminum alloy was welded by this process and conventional, respectively. The tensile tests, microstructure and fracture surface of FSW joint and UAFSW joint were analyzed. The research results show that the surface forming texture of ultrasonic assisted friction stir welding joint, compared with conventional, is finer and more uniform, showing metallic matte color. The grains are much finer in weld nugget zone, thermo-mechanically affected zone and heat-affected zone; S-phase particles size is much smaller and distribution is more homogeneous in the matrix. The tensile strength of UAFSW joint is 94. 13% of base metal, and the elongation is 11.77%. The tensile strength of FSW joint is 83.15% of base metal, and the elongation is 8.81%. The tests results reveal that ultrasonic vibration can improve the tensile strength and the elongation of welded joints.展开更多
文摘The influence of ultrasonic vibrations on microstructure and mechanical properties of the AZ91-C magnesium alloy after ultrasonic assisted friction stir welding(UaFSW)in comparison with conventional friction stir welding(FSW)was investigated.The FSW was applied at the rotational speed of 1400 r/min and welding speed of 40 mm/min and no defects were observed.Using the same welding parameters,the process was carried out with inducing ultrasonic vibrations to the weld line at the amplitude of 15μm.The microstructure of the specimens was observed with optical and scanning electron microscopy.The results indicate that a very fine microstructure is obtained in UaFSW with respect to that of conventional FSW.Moreover,β-Mg17Al12 coarse dendrites are segregated to very fine and partly spherical particles that homogeneously distribute inα-Mg matrix.This remarkably-modified morphology of microstructure attributed to severe plastic deformation comes from ultrasonic vibration and friction stirring effect.Tensile and hardness tests were performed to evaluate the mechanical properties of the welds.According to the results,the vibration greatly improves the mechanical properties of the conventional FSW joint.The tensile strength and hardness are increased from 195 MPa and HV 79 in conventional FSW to 225 MPa and HV 87 in UaFSW,respectively.
文摘Ultrasonic assisted friction stir welding （UAFSW） is a recent modification of conventional friction stir welding, which adds ultrasonic energy directly into the friction stir welding area by the pin. In this study, 2A12 aluminum alloy was welded by this process and conventional, respectively. The tensile tests, microstructure and fracture surface of FSW joint and UAFSW joint were analyzed. The research results show that the surface forming texture of ultrasonic assisted friction stir welding joint, compared with conventional, is finer and more uniform, showing metallic matte color. The grains are much finer in weld nugget zone, thermo-mechanically affected zone and heat-affected zone; S-phase particles size is much smaller and distribution is more homogeneous in the matrix. The tensile strength of UAFSW joint is 94. 13% of base metal, and the elongation is 11.77%. The tensile strength of FSW joint is 83.15% of base metal, and the elongation is 8.81%. The tests results reveal that ultrasonic vibration can improve the tensile strength and the elongation of welded joints.