A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the rel...A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the relationships among brazing temperature,interfacial microstructure and joint strength were emphatically investigated.Results show that the TiAl joints brazed at 1160 and 1180℃ possess three interfacial layers and mainly consist of α_(2)-Ti_(3)Al,τ_(3)-Al_(3)NiTi_(2) and Ti_(2)Ni,but the brazing seams are no longer layered and Ti_(2)Ni is completely replaced by the uniformly distributed τ_(3)-Al_(3)NiTi_(2) at 1200 and 1220℃ due to the destruction of α_(2)-Ti_(3)Al barrier layer.This transformation at 1200℃ obviously improves the tensile strength of the joint and obtains a maximum of 343 MPa.Notably,the outward diffusion of Al atoms from the dissolution of TiAl substrate dominates the microstructure evolution and tensile strength of the TiAl joint at different brazing temperatures.展开更多
Ti-47Al-2Nb-2Cr-0.15B(mole fraction,%)alloy was vacuum brazed with amorphous and crystalline Ti.25Zr-12.5Cu-12.5Ni-3.0Co-2.0Mo(mass fraction,%)filler alloys,and the melting,spreading and gap filling behaviors of the a...Ti-47Al-2Nb-2Cr-0.15B(mole fraction,%)alloy was vacuum brazed with amorphous and crystalline Ti.25Zr-12.5Cu-12.5Ni-3.0Co-2.0Mo(mass fraction,%)filler alloys,and the melting,spreading and gap filling behaviors of the amorphous and crystalline filler alloys as well as the joints brazed with them were investigated in details.Results showed that the amorphous filler alloy possessed narrower melting temperature interval,lower liquidus temperature and melting active energy compared with the crystalline filler alloy,and it also exhibited better brazeability on the surface of the Ti.47Al.2Nb.2Cr.0.15B alloy.The TiAl joints brazed with crystalline and amorphous filler alloys were composed of two interfacial reaction layers and a central brazed layer.Under the same conditions,the tensile strength of the joint brazed with the amorphous filler alloy was always higher than that with the crystalline filler alloy.The maxmium tensile strength of the joint brazed at 1273 K with the amorphous filler alloy reached 254 MPa.展开更多
The ZrO2 ceranfic was successfully jointed to stainless steel by vacuum brazing with active filler metal. The AgCuTi active filler metal was used and the joining was performed at a temperature of 850 ℃ for 10 rain. T...The ZrO2 ceranfic was successfully jointed to stainless steel by vacuum brazing with active filler metal. The AgCuTi active filler metal was used and the joining was performed at a temperature of 850 ℃ for 10 rain. The microstructures of the joints were characterized by metallographic microscopy, scanning electron microscopy （SEM）, and energy dispersive spectroscopy （EDS）. Metallographic microscopy analysis shows that the morphology of the cross section was a sandwich structure and the TiO is observed in the surface of ZrO2/ stainless steel. The diffusion and enrichment of the elements are the key roles in the brazing of ZrO2 ceramic and stainless steel. The formation of TiCu compounds inhibited the further diffusion of titanium into stainless steel or the ZrO2 ceramic to form TiO compound. In the experimental conditions, the average tensile strength is 80MPa for the joint of ZrO2 ceramic / AgCuTi/ stainless steel systems. A complete joint is formed between the ZrO2 ceramic and stainless steel with the leakage rate at the degree of 10 ^-12 Pa · m^3/s.展开更多
Mo-Cu composite and Cr18-Ni8 stainless steel were brazed with Ni-Cr-P filler metal in a vacuum of 10-4 Pa and a Mo-Cu/Cr18-Ni8 joint was obtained. Microstructure in Mo-Cu/Cr18-Ni8 joint was investigated by field-emiss...Mo-Cu composite and Cr18-Ni8 stainless steel were brazed with Ni-Cr-P filler metal in a vacuum of 10-4 Pa and a Mo-Cu/Cr18-Ni8 joint was obtained. Microstructure in Mo-Cu/Cr18-Ni8 joint was investigated by field-emission scanning electron microscope( FE-SEM) with energy dispersive spectrometer( EDS). Shear strength of Mo-Cu/Cr18-Ni8 lap joint was measured by electromechanical universal testing machine. An excellent Mo-Cu/Cr18-Ni8 joint with a shear strength of 155 MPa was achieved at 980 ℃ for 20 min. Brazed joint was mainly comprised of eutectic structure in the center of brazing seam,matrix structure and lump structure. Ni-Cu( Mo) and Ni-Fe solid solution were at the interface beside Mo-Cu composite and Cr18-Ni8 stainless steel,respectively. Shear fracture exhibited mixed ductile-brittle fracture feature with trans-granular fracture,ductile dimples and tearing edges. Fracture originated from the interface between brazing seam and Mo-Cu composite.展开更多
In an attempt to develop low-silver brazing filler metals used for hermetic sealing materials in the vacuum interrupter industry,the ternary Ag-50Cu-5Ga low-silver vacuum brazing filler metal was investigated.The melt...In an attempt to develop low-silver brazing filler metals used for hermetic sealing materials in the vacuum interrupter industry,the ternary Ag-50Cu-5Ga low-silver vacuum brazing filler metal was investigated.The melting temperature was measured by differential scanning calorimetry(DSC),and the brazability of Ag-50Cu-5Ga alloy on copper and metallized copper/kovar were ascertained at 850℃under 1×10-4 Pa in this article.The microstructures of the filler metal and the joints have been analyzed by using scanning electron microscopy(SEM),equipped with an energy dispersive spectroscopy.The results show that vacuum brazing was success to join with copper or metallized copper/kovar using Ag-50Cu-5Ga filler and reliable joints were obtained.There were Ag-rich phase,Cu-rich phase and a fine eutectic structure of Ag-based solid solution and Cu-based solid solution in the copper joints and the width of brazing seam is about 60μm.The joints of kovar alloy to copper after surface nickel plating was composed of AgCu eutectic phase,Ag,Cu,Cu2Ga and CuNi2 phase.The tensile strength was 167 MPa and 150 MPa,respectively.The tensile results of joints show that the joint strengths were equivalent to the traditional brazing filler metals.展开更多
To explore the wide-frequency damping and vibration-attenuation performances in the application of aerospace components,the cylindrical sandwich shell structure with a gradient core of entangled wire mesh was proposed...To explore the wide-frequency damping and vibration-attenuation performances in the application of aerospace components,the cylindrical sandwich shell structure with a gradient core of entangled wire mesh was proposed in this paper.Firstly,the gradient cores of entangled wire mesh in the axial and radial directions were prepared by using an in-house Numerical Control weaving machine,and the metallurgical connection between skin sheets and the gradient core was performed using vacuum brazing.Secondly,to investigate the mechanical properties of cylindrical sandwich shells with axial or radial gradient cores,quasi-static and dynamic mechanical experiments were carried out.The primary evaluations of mechanical properties include secant stiffness,natural frequency,Specific Energy Absorption(SEA),vibration acceleration level,and so on.The results suggest that the vibration-attenuation performance of the sandwich shell is remarkable when the high-density core layer is at the end of the shell or abuts the inner skin.The axial gradient material has almost no influence on the vibration frequencies of the shell,whereas the vibration frequencies increase dramatically when the high-density core layer approaches the skin.Moreover,compared to the conventional sandwich shells,the proposed functional grading cylindrical sandwich shell exhibits more potential in mass reduction,stiffness designing,and energy dissipation.展开更多
基金the National Natural Science Foundation of China(No.51865012)the Natural Science Foundation of Jiangxi Province,China(No.20202BABL204040)+3 种基金the Open Foundation of National Engineering Research Center of Near-net-shape Forming for Metallic Materials,China(No.2016005)the Science Foundation of Educational Department of Jiangxi Province,China(No.GJJ170372)the GF Basic Scientific Research Project,China(No.JCKY2020205C002)the Civil Population Supporting Planning and Development Project,China(No.JPPT125GH038).
文摘A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the relationships among brazing temperature,interfacial microstructure and joint strength were emphatically investigated.Results show that the TiAl joints brazed at 1160 and 1180℃ possess three interfacial layers and mainly consist of α_(2)-Ti_(3)Al,τ_(3)-Al_(3)NiTi_(2) and Ti_(2)Ni,but the brazing seams are no longer layered and Ti_(2)Ni is completely replaced by the uniformly distributed τ_(3)-Al_(3)NiTi_(2) at 1200 and 1220℃ due to the destruction of α_(2)-Ti_(3)Al barrier layer.This transformation at 1200℃ obviously improves the tensile strength of the joint and obtains a maximum of 343 MPa.Notably,the outward diffusion of Al atoms from the dissolution of TiAl substrate dominates the microstructure evolution and tensile strength of the TiAl joint at different brazing temperatures.
基金Foundation item:Project(51865012)supported by the National Natural Science Foundation of ChinaProject(2016005)supported by the Open Foundation of National Engineering Research Center of Near-net-shape Forming for Metallic Materials,China+2 种基金Project(GJJ170372)supported by the Science Foundation of Educational Department of Jiangxi Province,ChinaProject(JCKY2016603C003)supported by the GF Basic Research Project,ChinaProject(JPPT125GH038)supported by the Research Project of Special Furnishment and Part,China
文摘Ti-47Al-2Nb-2Cr-0.15B(mole fraction,%)alloy was vacuum brazed with amorphous and crystalline Ti.25Zr-12.5Cu-12.5Ni-3.0Co-2.0Mo(mass fraction,%)filler alloys,and the melting,spreading and gap filling behaviors of the amorphous and crystalline filler alloys as well as the joints brazed with them were investigated in details.Results showed that the amorphous filler alloy possessed narrower melting temperature interval,lower liquidus temperature and melting active energy compared with the crystalline filler alloy,and it also exhibited better brazeability on the surface of the Ti.47Al.2Nb.2Cr.0.15B alloy.The TiAl joints brazed with crystalline and amorphous filler alloys were composed of two interfacial reaction layers and a central brazed layer.Under the same conditions,the tensile strength of the joint brazed with the amorphous filler alloy was always higher than that with the crystalline filler alloy.The maxmium tensile strength of the joint brazed at 1273 K with the amorphous filler alloy reached 254 MPa.
基金supported by the National Key R&D Program of China(Grant No.2017YFB0305700)
文摘The ZrO2 ceranfic was successfully jointed to stainless steel by vacuum brazing with active filler metal. The AgCuTi active filler metal was used and the joining was performed at a temperature of 850 ℃ for 10 rain. The microstructures of the joints were characterized by metallographic microscopy, scanning electron microscopy （SEM）, and energy dispersive spectroscopy （EDS）. Metallographic microscopy analysis shows that the morphology of the cross section was a sandwich structure and the TiO is observed in the surface of ZrO2/ stainless steel. The diffusion and enrichment of the elements are the key roles in the brazing of ZrO2 ceramic and stainless steel. The formation of TiCu compounds inhibited the further diffusion of titanium into stainless steel or the ZrO2 ceramic to form TiO compound. In the experimental conditions, the average tensile strength is 80MPa for the joint of ZrO2 ceramic / AgCuTi/ stainless steel systems. A complete joint is formed between the ZrO2 ceramic and stainless steel with the leakage rate at the degree of 10 ^-12 Pa · m^3/s.
基金supported by Shandong Natural Science Foundation(ZR2015EM040)
文摘Mo-Cu composite and Cr18-Ni8 stainless steel were brazed with Ni-Cr-P filler metal in a vacuum of 10-4 Pa and a Mo-Cu/Cr18-Ni8 joint was obtained. Microstructure in Mo-Cu/Cr18-Ni8 joint was investigated by field-emission scanning electron microscope( FE-SEM) with energy dispersive spectrometer( EDS). Shear strength of Mo-Cu/Cr18-Ni8 lap joint was measured by electromechanical universal testing machine. An excellent Mo-Cu/Cr18-Ni8 joint with a shear strength of 155 MPa was achieved at 980 ℃ for 20 min. Brazed joint was mainly comprised of eutectic structure in the center of brazing seam,matrix structure and lump structure. Ni-Cu( Mo) and Ni-Fe solid solution were at the interface beside Mo-Cu composite and Cr18-Ni8 stainless steel,respectively. Shear fracture exhibited mixed ductile-brittle fracture feature with trans-granular fracture,ductile dimples and tearing edges. Fracture originated from the interface between brazing seam and Mo-Cu composite.
基金the National Key R&D Program of China(Grant No.2017YFB0305702).
文摘In an attempt to develop low-silver brazing filler metals used for hermetic sealing materials in the vacuum interrupter industry,the ternary Ag-50Cu-5Ga low-silver vacuum brazing filler metal was investigated.The melting temperature was measured by differential scanning calorimetry(DSC),and the brazability of Ag-50Cu-5Ga alloy on copper and metallized copper/kovar were ascertained at 850℃under 1×10-4 Pa in this article.The microstructures of the filler metal and the joints have been analyzed by using scanning electron microscopy(SEM),equipped with an energy dispersive spectroscopy.The results show that vacuum brazing was success to join with copper or metallized copper/kovar using Ag-50Cu-5Ga filler and reliable joints were obtained.There were Ag-rich phase,Cu-rich phase and a fine eutectic structure of Ag-based solid solution and Cu-based solid solution in the copper joints and the width of brazing seam is about 60μm.The joints of kovar alloy to copper after surface nickel plating was composed of AgCu eutectic phase,Ag,Cu,Cu2Ga and CuNi2 phase.The tensile strength was 167 MPa and 150 MPa,respectively.The tensile results of joints show that the joint strengths were equivalent to the traditional brazing filler metals.
基金Supports from the National Natural Science Foundation of China(Grant No.12272094,No.52205185 and No.51975123)the Natural Science Foundation of Fujian Province of China(Grant No.2022J01541 and No.2020J05102)the Key Project of National Defence Innovation Zone of Science and Technology Commission of CMC(Grant No.XXX-033-01)。
文摘To explore the wide-frequency damping and vibration-attenuation performances in the application of aerospace components,the cylindrical sandwich shell structure with a gradient core of entangled wire mesh was proposed in this paper.Firstly,the gradient cores of entangled wire mesh in the axial and radial directions were prepared by using an in-house Numerical Control weaving machine,and the metallurgical connection between skin sheets and the gradient core was performed using vacuum brazing.Secondly,to investigate the mechanical properties of cylindrical sandwich shells with axial or radial gradient cores,quasi-static and dynamic mechanical experiments were carried out.The primary evaluations of mechanical properties include secant stiffness,natural frequency,Specific Energy Absorption(SEA),vibration acceleration level,and so on.The results suggest that the vibration-attenuation performance of the sandwich shell is remarkable when the high-density core layer is at the end of the shell or abuts the inner skin.The axial gradient material has almost no influence on the vibration frequencies of the shell,whereas the vibration frequencies increase dramatically when the high-density core layer approaches the skin.Moreover,compared to the conventional sandwich shells,the proposed functional grading cylindrical sandwich shell exhibits more potential in mass reduction,stiffness designing,and energy dissipation.
基金Project(22A0117)supported by Hunan Provincial Department of Education,ChinaProject(AWJ-20-M02)supported by State Key Laboratory of Advanced Welding and Joining,Harbin Institute of Technology,China。