WC- 10Co nanocomposite powder produced by spray pyrolysis-continuoas reduction and carbonization technology was used, and the vacuum sinteriag plus sinterhip process was cdopted to prepare ultrafine WCCo cemented carb...WC- 10Co nanocomposite powder produced by spray pyrolysis-continuoas reduction and carbonization technology was used, and the vacuum sinteriag plus sinterhip process was cdopted to prepare ultrafine WCCo cemented carbide. The microstructure, grain size, porosity, density, Rockwell A hardness （ HRA ）, transverse rupture strength （ TRS ） , saturated magnetization and coercivity force were studied. The experimental results show that average grain size of the sample prepared by vacuum sintering plas sinterhip technology was about 420 nm, transverse rupture strength was more than 3460 MPa, and Rockwell A hardness of sintered specimen was more than 92.5. Ultrafine WC- 10Co cemented carbide with high strength and high hardness is obtained.展开更多
基金Funded by he National Natural Science Foundation of China(50502026) , Key Project for Science and Technology Developmentof Wuhan City (20041003068-04) ,andthe Key Project forthe Sci .&Tech. Research of Chinese Ministry of Education (105123)
文摘WC- 10Co nanocomposite powder produced by spray pyrolysis-continuoas reduction and carbonization technology was used, and the vacuum sinteriag plus sinterhip process was cdopted to prepare ultrafine WCCo cemented carbide. The microstructure, grain size, porosity, density, Rockwell A hardness （ HRA ）, transverse rupture strength （ TRS ） , saturated magnetization and coercivity force were studied. The experimental results show that average grain size of the sample prepared by vacuum sintering plas sinterhip technology was about 420 nm, transverse rupture strength was more than 3460 MPa, and Rockwell A hardness of sintered specimen was more than 92.5. Ultrafine WC- 10Co cemented carbide with high strength and high hardness is obtained.