Oxidation Kinetics,Structural Changes and Element Migration during Oxidation Process of Vanadium-titanium Magnetite Ore

The oxidation kinetics, structural changes, and elements migration during the oxidation process of the va- nadium-titanium magnetite （VTM） ore were analyzed. Kinetics analysis indicated that the oxidation process was con- trolled by diffusion control and could be divided into interface diffusion and lattice diffusion with apparent activation energy of 99.69 kJ/mol and 144.08 kJ/mol in the range of 800--1000℃, respectively. The surface structure changed with the oxidization temperature as follows： dense surface→nano sized sheets→submicron particles→molten particles. The compact structure changed into porous one because of the elements migration and enrichment. Both Fe and Ti elements migrated in the opposite direction during the oxidation process. The V etement in the raw ore stably existed in the form of V^5＋ state, some vanadium migrated and occupied the tetrahedral sites of the hematite during the oxidation process.

High-chromium vanadium-titanium magnetite all-pellet integrated burden optimization and softening-melting behavior based on flux pellets

High-chromium vanadium-titanium magnetite(HVTM)is a crucial polymetallic-associated resource to be developed.The allpellet operation is a blast furnace trend that aims to reduce carbon dioxide emissions in the future.By referencing the production data of vanadium-titanium magnetite blast furnaces,this study explored the softening-melting behavior of high-chromium vanadium-titanium magnetite and obtained the optimal integrated burden based on flux pellets.The results show that the burden with a composition of 70wt%flux pellets and 30wt%acid pellets exhibits the best softening-melting properties.In comparison to that of the single burden,the softening-melting characteristic temperature of this burden composition was higher.The melting interval first increased from 307 to 362℃and then decreased to 282℃.The maximum pressure drop(ΔPmax)decreased from 26.76 to 19.01 kPa.The permeability index(S)dropped from 4643.5 to 2446.8 kPa·℃.The softening-melting properties of the integrated burden were apparently improved.The acid pellets played a role in withstanding load during the softening process.The flux pellets in the integrated burden exhibited a higher slag melting point,which increased the melting temperature during the melting process.The slag homogeneity and the TiC produced by over-reduction led to the gas permeability deterioration of the single burden.The segregation of the flux and acid pellets in the HVTM proportion and basicity mainly led to the better softening-melting properties of the integrated burden.

Effect of basicity on sintering behavior of low-titanium vanadium-titanium magnetite

Basicity has an important effect on the sinter quality, especially for low-titanium vanadium-titanium sinter. The effect of basieity on sintering behavior of low-titanium vanadium-titanium mixture, and the transference and distribution of element in sintering process were researched by sinter pot test, mineralogical analysis, scanning electron microscopy （SEM） and energy dispersive spectroscopy （EDS） analysis. The results show that CaO preferentially reacts with TiO2, generating pervoskite, so that the total liquid phase content of the sinter is low. There is an increase in the perovskite concentration of the sinter with the basicity ranging from 1.9：1 to 2.7：1. With increasing the basicity, the calcium ferrite content increases slightly and then rises rapidly, while the silicate content decreases and the metallurgical property of the sinter is improved. As for the distribution of these elements in the sinter, Ti occurs mainly in perovskite, V occurs mainly in silicate, and Fe occurs mainly in magnetite and hematite. The most abundant occurrence of Ca and Si occurs in silicate and perovskite. With increasing the basicity, the contents of A1 and Mg increase in calcium ferrite, while they decrease in other minerals.

Solid-state reduction kinetics and mechanism of pre-oxidized vanadium-titanium magnetite concentrate

The solid-state reduction kinetics of pre-oxidized vanadium-titanium magnetite concentrate was studied. The phase and microstructure of the reduction product were characterized by XRD, SEM and EDS methods, based on which the mechanism of the solid-state reduction was investigated. The results showed that using coal as reductant at 950-1100 °C, the solid-state reduction of the pre-oxidized vanadium-titanium magnetite concentrate was controlled by interface chemical reaction and the apparent activation energy was 67.719 k J/mol. The mineral phase transformation during the reduction process can be described as follows： pre-oxidized vanadium-titanium magnetite concentrate → ulvospinel → ilmenite → Fe Ti2O5 →（FenTi1-n）Ti2O5. M3O5-type（M can be Fe, Ti, Mg, Mn, etc） solid solutions would be formed during the reduction process of the pre-oxidized vanadium-titanium magnetite concentrate at 1050 °C for 60 min. The poor reducibility of iron in M3O5 solid solutions is the main reason to limit the reduction property of pre-oxidized vanadium-titanium magnetite concentrate.

Some basic properties of granules from ore blends consisting of ultrafine magnetite and hematite ores

Some basic properties of granules,including the granule size distribution,packed-bed permeability,and chemical composition of the adhering layer,were investigated in this study for four iron ore blends consisting of 5wt%,25wt%,and 45wt%ultrafine magnetite and 25wt%ultrafine hematite concentrates.The effects of varying the sinter basicity(CaO/SiO2 mass ratio=1.4 to 2.2)and adding ultrafine concentrates on the variation of the adhering-layer composition and granule microstructure were studied.Moreover,the effect of adhering-layer compositional changes on sintering reactions was discussed in combination with pot sintering results of ore blends.Increasing sinter basicity led to an increase in the basicities of both the adhering layer and the fine part of the sinter mix,which were higher than the overall sinter basicity.When the sinter chemistry was fixed and fine Si-bearing materials(e.g.,quartz sand)were used,increasing the amount of ultrafine ores in the ore blends tended to reduce the adhering-layer basicity and increase the SiO2 content in both the adhering layer and the fine part of the sinter mix,which will induce the formation of low-strength bonding phases and the deterioration of sinter strength.The adhering-layer composition in granules can be estimated in advance from the compositions of the-1 mm fractions of the raw materials.

Major and Trace Elements of Magnetite from the Qimantag Metallogenic Belt: Insights into Evolution of Ore–forming Fluids

Magnetite, as a genetic indicator of ores, has been studied in various deposits in the world. In this paper, we present textural and compositional data of magnetite from the Qimantag metallogenic belt of the Kunlun Orogenic Belt in China, to provide a better understanding of the formation mechanism and genesis of the metallogenic belt and to shed light on analytical protocols for the in situ chemical analysis of magnetite. Magnetite samples from various occurrences, including the ore-related granitoid pluton, mineralised endoskarn and vein-type iron ores hosted in marine carbonate intruded by the pluton, were examined using scanning electron microscopy and analysed for major and trace elements using electron microprobe and laser ablation-inductively coupled plasma-mass spectrometry. The field and microscope observation reveals that early-stage magnetite from the Hutouya and Kendekeke deposits occurs as massive or banded assemblages, whereas late- stage magnetite is disseminated or scattered in the ores. Early-stage magnetite contains high contents of Ti, V, Ga, AI and low in Mg and Mn. In contrast, late-stage magnetite is high in Mg, Mn and low in Ti, V, Ga, AI. Most magnetite grains from the Qimantag metallogenic belt deposits except the Kendekeke deposit plot in the ＂ Skarn ＂ field in the Ca＋AI＋Mn vs Ti＋V diagram, far from typical magmatic Fe deposits such as the Damiao and Panzhihua deposits. According to the （MgO＋MnO）- TiO^-AI203 diagram, magnetite grains from the Kaerqueka and Galingge deposits and the No.7 ore body of the Hutouya deposit show typical characteristics of skarn magnetite, whereas magnetite grains from the Kendekeke deposit and the No.2 ore body of the Hutouya deposit show continuous elemental variation from magmatic type to skarn type. This compositional contrast indicates that chemical composition of magnetite is largely controlled by the compositions of magmatic fluids and host rocks of the ores that have reacted with the fluids. Moreover, a combination of petrography and magnetite geochemistry indicates that the formation of those ore deposits in the Qimantag metallogenic belt involved a magmatic-hydrothermal process.

Effects of basicity and temperature on mineralogy and reduction behaviors of high-chromium vanadium-titanium magnetite sinters

The effects of basicity and temperature on the reduction process of Hongge high-chromium vanadium-titanium magnetite(HCVTM)sinter were investigated in this work.The main characterization methods of X-ray fluorescence(XRF),X-ray diffraction(XRD),scanning electron microscope(SEM),and metallographic microscope were employed in this study.In this work,the reduction of HCVTM sinter with different temperature and basicity were experimented.The Fe,FeO,and TiO in reductive samples increase with increasing basicity and temperatures.The increase of basicity and temperature is favorable to the reduction of HCVTM sinter.The Fe phase has out-migration tendency to the surface of sinter while the perovskite and silicate phases have in-migration tendency to the inside of sinter.The reduction degradation index(RDI)decreases while the reduction index(RI)increases with increasing basicity.The RI increases from 67.14%to 82.09%with increasing temperature from 1073 K to 1373 K.

Effect of magnetic pulse pretreatment on grindability of a magnetite ore and its implication on magnetic separation

The pulsed power is a potential means for energy saving and presents an alternative to the conventional mechanical communication for minerals.The effect of magnetic pulse treatment on grindability of a magnetite ore was investigated by grindability tests.The results of the investigation show that the pulsed treatment has little effect on the particle size distribution of the magnetite ore.Significant micro-cracks or fractures are not found by SEM analysis in magnetic pulse treated sample.Magnetic separation of magnetic pulse treated and untreated magnetite ore indicates that iron recovery increases from 81.3% in the untreated sample to 87.7% in the magnetic pulse treated sample,and the corresponding iron grade increases from 42.1% to 44.4%.The results demonstrate that the magnetic pulse treatment does not significantly weaken the mineral grain boundaries or facilitate the liberation of minerals,but is beneficial to magnetic separation.

Influence of Coke Content on Sintering Process of Chromium-containing Vanadium-titanium Magnetite

The sintering of chromium-containing vanadium-titanium magnetite using different coke contents was studied through the sintering pot tests, X-ray diffraction analysis and mineralogical phase analysis. Results showed that, as the coke content increased from 3.2% to 4.4%, the liquid phase and combustion zone thickness increased while the vertical sintering rate and ratio of sintered product decreased. In addition, the combustion ratio of exhaust gas also increased with increasing the coke content, indicating that combustion zone temperature also increased, and the excessive the coke content in the sintering process of vanadiumtitanium magnetite is harmful. As the coke content increased, the magnetite, silicates, and perovskite contents of the sintered ore increased while the contents of hematite and calcium ferrite of sintered ore decreased; drum strength decreased, and reduction degradation properties increased while reduction ability decreased. We found that the appropriate coke content for the sintering process is 3.6 wt%.

Magnetite Quartzite-Type Iron Ores – China's Most Important Current Iron Ore Source

China is abundant in iron-ore resources, with proven ore reserves of 576.62×10^8 t and proven reserves of 210×10^8 t, containing an average iron content of 33%. However, the rich iron-ore reserves of 10.85×10^8 t only account for 1.9% of all proven reserves. China＇s iron-ore resources are characterized by many lean ores and a few rich ones.

Metalizing reduction and magnetic separation of vanadium titano-magnetite based on hot briquetting

To achieve high efficiency utilization of Panzhihua vanadium titano-magnetite, a new process of metalizing reduction and magnetic separation based on hot briquetting is proposed, and factors that affect the cold strength of the hot-briquetting products and the efficiency of reduction and magnetic separation are successively investigated through laboratory experiments. The relevant mechanisms are elucidated on the basis of microstructural observations. Experimental results show that the optimal process parameters for hot briquetting include a hot briquetting temperature of 475°C, a carbon ratio of 1.2, ore and coal particle sizes of less than 74 μm. Additionally, with respect to metalizing reduction and magnetic separation, the rational parameters include a magnetic field intensity of 50 mT, a reduction temperature of 1350°C, a reduction time of 60 min, and a carbon ratio of 1.2. Under these above conditions, the crushing strength of the hot-briquetting agglomerates is 1480 N, and the recovery ratios of iron, vanadium, and titanium are as high as 91.19%, 61.82%, and 85.31%, respectively. The new process of metalizing reduction and magnetic separation based on hot briquetting demonstrates the evident technological advantages of high efficiency separation of iron from other valuable elements in the vanadium titano-magnetite.

Sintering behaviors and consolidation mechanism of high-chromium vanadium and titanium magnetite fines

To achieve high efficiency utilization of high-chromium vanadium-titanium magnetite （V-Ti-Cr） fines, an investigation of V Ti42r fines was conducted using a sinter pot. The chemical composition, particle parameters, and granulation of V-Ti-Cr mixtures were analyzed, and the effects of sintering parameters on the sintering behaviors were investigated. The results indicated that the optimum quicklime dosage, mixture moisture, wetting time, and granulation time for V-Ti-Cr fines are 5wt%, 7.5wt%, 10 min, and 5-8 min, respectively. Meanwhile, the vertical sintering speed, yield, tumbler strength, and productivity gains were shown to be 21.28 mm/min, 60.50wt% , 58.26wt%, and 1.36 t·m^-2·h^-1, respectively. Furthermore, the consolidation mechanism of V-Ti-Cr fines was clarified, revealing that the consolidation of a V-Ti-Cr sinter requires an approximately 14vo1% calcium ferrite liquid-state, an approximately 15vo1% silicate liq- uid-state, a solid-state reaction, and the recrystallization of magnetite. Compared to an ordinary sinter, calcium ferrite content in a V-Ti-Cr sinter is lower, while the perovskite content is higher, possibly resulting in unsatisfactory sinter outcomes.

Optimized use of MgO flux in the agglomeration of high-chromium vanadium–titanium magnetite

The optimized use of MgO flux in the agglomeration of high-chromium vanadium-titanium magnetite was investigated system- atically through sinter and pellet experiments. MgO was added in the form of magnesite. When the content of MgO in the sinter was in- creased from 1.95wt% to 2.63wt%, the low-temperature reduction degradation index increased from 80.57% to 82.71%. When the content of MgO in the pellet was increased from 1.14wt% to 2.40wt%, the reduction swelling index decreased from 15.2% to 8.6%; however, the com- pressive strength of the oxidized pellet decreased dramatically and it was 1985 N with an MgO content of 1.14wt%. This compressive strength does not satisfy the requirements for blast-furnace production. When all of the aforementioned results were taken into account, the sinter with a high MgO content （2.63wt%） matching the pellet with a low MgO content （less than 1.14wt%） was the rational burden structure for smelting high-chromium vanadium-titanium magnetite in blast furnaces.

Three-liquid-phase extraction and separation of V(V) and Cr(VI) from acidic leach solutions of high-chromium vanadium–titanium magnetite

A new method by liquid-liquid-liquid three phase system, consisting of acidified primary amine N1923 （abbreviated as A-N1923）, poly（ethylene glycol） （PEG） and （NH4）2S04 aqueous solution, was suggested for the separation and simultaneous extraction of Ⅴ（Ⅴ） and Cr（Ⅵ） from the acidic leach solutions of high- chromium vanadium-titanium magnetite. Experimental results indicated that Ⅴ（Ⅴ） and Cr（Ⅵ） could be selectively enriched into the A-N1923 organic top phase and PEG-rich middle phase, respectively, while AI（Ⅲ） and other co-existing impurity ions, such as Si（Ⅳ）, Fe（Ⅲ）, Ti（Ⅳ）, Mg（Ⅱ） and Ca（Ⅱ） in acidic leach solutions, could be enriched in the （NH4）2SO4 bottom aqueous phase. During the process for extraction and separation of Ⅴ（Ⅴ） and Cr（Ⅵ）, almost all of impurity ions could be removed. The separation factors between Ⅴ （Ⅴ） and Cr（Ⅵ） could reach 630 and 908, respectively in the organic top phase and PEG middle phase, and yields of recovered Ⅴ（Ⅴ） and Cr（Ⅵ） in the top phase and middle phase respectively were all above 90%. Various effects including aqueous pH, A-N1923 concentration, PEG added amount and （NH4）2SO4 concentration on three-phase partitioning of Ⅴ（Ⅴ） and Cr（Ⅵ） were discussed. It was found that the partition of Cr（Ⅵ） into the PEG-rich middle phase was driven by hydrophobic interaction, while extraction of Ⅴ（Ⅴ） by A-N1923 resulted of anion exchange between NO; and H2V10O4-28. Stripping of Ⅴ（Ⅴ） and Cr（Ⅵ） from the top organic phase and the middle PEG-rich phase were achieved by mixing respectively with NANO3 aqueous solutions and NaOH-（NH4）2SO4 solutions. The present work highlights a new approach for the extraction and purification of V and Cr from the complex multi-metal co-existing acidic leach solutions of high-chromium vanadium-titanium magnetite.

PREPARATION OF IRON CARBIDE FROM MAGNETITE PELLETS BY CO-H_2 MIXTURES REDUCTION

A method of preparing iron carbide by reducing magnetite pellets with H2-CO mixtures is presented. The results show that an over 90 percent conversion ratio of iron carbide can be reached at 973 K and 1073 K under the suitable atmosphere. The reaction process to prepare iron carbide from magnetite pellets can be divided into two stages: reduction of magnetite pellets and carburization of reduction products. The carbon deposition has a great influence on the formation of iron carbide. In order to get a high conversion ratio of iron carbide, the relative weight loss value (m) should be controlled between 0.5 to 0.8.

Reduction mechanism of high-chromium vanadium–titanium magnetite pellets by H_2–CO–CO_2 gas mixtures

The reduction of high-chromium vanadium–titanium magnetite as a typical titanomagnetite containing 0.95wt% V2O5 and 0.61wt% Cr2O3 by H2–CO–CO2 gas mixtures was investigated from 1223 to 1373 K. Both the reduction degree and reduction rate increase with increasing temperature and increasing hydrogen content. At a temperature of 1373 K, an H2/CO ratio of 5/2 by volume, and a reduction time of 40 min, the degree of reduction reaches 95%. The phase transformation during reduction is hypothesized to proceed as follows： Fe2O3 → Fe3O4 → FeO → Fe; Fe9 TiO 15 ＋ Fe2Ti3O9 → Fe2.75Ti0.25O4 → FeT iO 3 → TiO 2;（Cr0.15V0.85）2O3 → Fe2VO4; and Cr1.3Fe0.7O3 → FeC r2O4. The reduction is controlled by the mixed internal diffusion and interfacial reaction at the initial stage; however, the interfacial reaction is dominant. As the reduction proceeds, the internal diffusion becomes the controlling step.

Growth behavior of the magnetite phase in the reduction of hematite via a fluidized bed

To understand the formation and growth mechanism of the magnetite phase during the fluidized reduction of hematite, a high-purity hematite ore was isothermally reduced using a 20vol% CO 80vol% CO2 gas mixture in a micro-fluidized bed to examine the process of the selective conversion of hematite to magnetite. The micro-structural characteristics of the magnetite phase were investigated using scanning electron microscopy (SEM) and the Brunauer, Emmett, and Teller (BET) method, and the thickness of the magnetite layer was measured and evaluated using statistical analysis. The experimental results showed that the fresh magnetite nuclei were dense needles of different lengths, and the original hematite grains became porous after complete reduction to the magnetite phase. The thickness of the mag- netite layer increased with an increase in reduction temperature and reduction time. The growth kinetics of the magnetite layer was investi- gated, and the value of the activation energy E was estimated to be 28.33 kJ/mol.

Microwave assisted grinding of ilmenite ore

The influence of microwave heating on the grinding of Panzhihua ilmenite ore was investigated. Factors that influence the processing are： the microwave exposure time, power density and sample mass. 40 g sample was microwave heated for 30 s with 1 kW of microwave power and followed by water quenching. SEM analysis indicated that intergranular fractures occurred between ores and gangues other than transgranular fractures after microwave treatment, which would liberate minerals from each other effectively. The subsequently magnetic separation trials provided evidence that the recovery rate increased from 44% for raw ore to 72% by microwave treatment.

Wettability and corrosion behavior between alkaline slag from sodium smelting of vanadium-titanium magnetite and refractory substrates

The sodium smelting of vanadium-titanium magnetite can achieve the comprehensive utilization of Fe,V,and Ti.However,the generation of alkaline slag during this process may cause damage to refractory materials.The wettability and corrosion behavior of alkaline slag on three types of refractory(MgO-C,SiC,and high alumina refractory)substrates were investigated at temperatures up to 1200℃.The effects of duration on the wettability of molten slag on SiC substrates were also investigated.Results showed that the high alumina refractory exhibited better wettability with the molten slag than the others,and thus,it is easier to be corroded.The results of scanning electron microscopy coupled with energy dispersive spectroscopy showed that MgO-C and high alumina refractory substrates were severely eroded.There was a visible and regular interfacial reaction layer between the slag and SiC refractory substrate,which was produced by the redox reaction between the metal oxides in the slag and the SiC refractory substrate.With the increase in holding time,the interface layer expands and silico-ferrite phases are generated at the interface.The redox reaction between Fe_(2)O_(3) and SiC substrate is the main reason for the corrosion.By comparing the differences in wettability and corrosion behavior between the alkaline slag from sodium smelting of vanadium-titanium magnetite and MgO-C,SiC and high alumina refractories,it is concluded that SiC refractory has good corrosion resistance to the slag.Iron oxides in the slag accelerate the oxidation rate of SiC refractory.

Enrichment and reconfiguration of titanium-bearing phase in vortex smelting reduction process of vanadium-titanium magnetite

To comprehensively utilize the low-iron high-vanadium-titanium magnetite,a new method of vortex smelting reduction of vanadium-titanium magnetite was proposed,and the enrichment and reconstitution regularity of Ti-bearing phases in the slag was investigated through X-ray fluorescence spectrometry,X-ray photoelectron spectroscopy,X-ray diffraction analysis,and optical microscopy.The phase diagram revealed that the preferential crystallization of MgTi_(2)O_(5) can be achieved by adjusting the CaO,MgO,and TiO_(2) contents of slag.The predominant Ti-bearing phases in the slag obtained from the reduction process are MgxTi_(3_x)O_(5)(0≤x≤1)and CaTiO_(3).FeTiO_(3) is present at carbon-iron ratio(CR)=1.3,while MgTi_(2)O4 and TiC are formed at CR=1.3.The enrichment of TiO_(2) in the slag increases first and then decreases as the CR increases,and at CR=1.1,the enrichment of TiO_(2) in the slag reaches 51.3 wt.%.Additionally,the concentrations of MgxTi_(3_x)O_(5)(0≤x≤1)and CaTiO_(3) in the slag,along with the grain width of MgxTi_(3_x)O_(5)(0≤x≤1),decrease with the increase in CR.