This research explored replacing acrylic core-shell impact modifier （AIM） by silica fume to toughen PVC. 100%, 75%, 50% and 25% of AIM （8 phr） were substituted by silica fume in PVC respectively, and then processe...This research explored replacing acrylic core-shell impact modifier （AIM） by silica fume to toughen PVC. 100%, 75%, 50% and 25% of AIM （8 phr） were substituted by silica fume in PVC respectively, and then processed by dry blending and twin-screw extrusion. Severe silica fume agglomeration was observed by scanning electron microscope （SEM） in the PVC matrix when 8 phr pure silica fume was used and processed by screw speed of 20 rpm. Its tensile strength was thereby reduced by 38% comparing to unmodified PVC. The silica fume was successfully dispersed while the screw speed was slowed down to 10 rpm to give a stronger screw torque and a longer melt residential time in the extruder. The tensile strength was ’recovered’ to a level comparable to unmodified PVC. Impact test were performed on all formulations extruded at 10 rpm screw speed and synergetic toughening effect was found with 50% substitution and it had the impact strength that was comparable to 8 phr pure AIM toughened PVC.展开更多
In this study, the polyacrylate intraocularr lens is irradiated by argon ion which can produce free radicals. In order to obtain better hydrophilic and lower platelets adhesion, monomer vinyl pyrrolidone (NVP) is graf...In this study, the polyacrylate intraocularr lens is irradiated by argon ion which can produce free radicals. In order to obtain better hydrophilic and lower platelets adhesion, monomer vinyl pyrrolidone (NVP) is grafted onto the hydrophobic polyacrylate intraocular lens surface in a certain reaction conditions. Specific changes in intraocular lens are detected by static contact angle (CA), scanning electron microscope (SEM) and light transmittance. The results show that this surface modification can greatly improve its hydrophilic character and surface formation.展开更多
文摘This research explored replacing acrylic core-shell impact modifier （AIM） by silica fume to toughen PVC. 100%, 75%, 50% and 25% of AIM （8 phr） were substituted by silica fume in PVC respectively, and then processed by dry blending and twin-screw extrusion. Severe silica fume agglomeration was observed by scanning electron microscope （SEM） in the PVC matrix when 8 phr pure silica fume was used and processed by screw speed of 20 rpm. Its tensile strength was thereby reduced by 38% comparing to unmodified PVC. The silica fume was successfully dispersed while the screw speed was slowed down to 10 rpm to give a stronger screw torque and a longer melt residential time in the extruder. The tensile strength was ’recovered’ to a level comparable to unmodified PVC. Impact test were performed on all formulations extruded at 10 rpm screw speed and synergetic toughening effect was found with 50% substitution and it had the impact strength that was comparable to 8 phr pure AIM toughened PVC.
基金National Natural Science of Foundation of Chinagrant number:81070716
文摘In this study, the polyacrylate intraocularr lens is irradiated by argon ion which can produce free radicals. In order to obtain better hydrophilic and lower platelets adhesion, monomer vinyl pyrrolidone (NVP) is grafted onto the hydrophobic polyacrylate intraocular lens surface in a certain reaction conditions. Specific changes in intraocular lens are detected by static contact angle (CA), scanning electron microscope (SEM) and light transmittance. The results show that this surface modification can greatly improve its hydrophilic character and surface formation.