Improved Resin Transfer Molding (RTM) technology and equipment were established.Void content and morphology of the 3-D braided preform/phenolic composite were investigated using different RTM processes.The results sho...Improved Resin Transfer Molding (RTM) technology and equipment were established.Void content and morphology of the 3-D braided preform/phenolic composite were investigated using different RTM processes.The results showed that void content of the vacuum and compression co-assisted RTM process was the lowest.Void morphologies of the specimen cross-section were analyzed with metallographic microscope.In traditional RTM process,the crack of cross-section was in evidence.In vacuum assisted RTM process,the void shape was divided into three categories:irregular crack,triangle,rotundity and ellipse.The most voids distributed in resin rich areas and were observed as large void based on equivalent diameter.In compression assisted RTM,vacuum and compression co-assisted RTM process,the polygonal voids mostly existed inter tows.Void size was mainly intermediate and small based equivalent diameter separately.展开更多
Similar diffusion bonding of 1Cr11Ni2W2MoV stainless steel was conducted at different bonding tem- peratures. The interface characteristics and mechanical properties of joints were examined, and the evolution of inter...Similar diffusion bonding of 1Cr11Ni2W2MoV stainless steel was conducted at different bonding tem- peratures. The interface characteristics and mechanical properties of joints were examined, and the evolution of interracial void morphology was analyzed in detail The results showed that there were four typical interfacial void shapes generating sequentially： the large scraggly voids, penny-shaped voids, ellipse voids and rounded voids. The variation of interracial void shape was dominated by surface diffusion, while the reduction of void volume was ascribed to the combined effects of plastic flow of materials around voids, interface diffusion and volume diffusion. Owing to the elimination of void from the bonding interface, the sound joint obtained could exhibit nearly full interracial contact, and present excellent mechanical properties, in which the microhardness and shear strength of joint matched those of base material.展开更多
A model for the morphological evolution of a void under thermal and mechanical loads is established, and the thermodynamics potential of the model is given based on energy principle. Thus, the path and the bifurcation...A model for the morphological evolution of a void under thermal and mechanical loads is established, and the thermodynamics potential of the model is given based on energy principle. Thus, the path and the bifurcation condition of the morphological evolution of the void are described, which gives some insight into the reliability of the interconnect under combined thermal and mechanical loads.展开更多
基金Tianjin Natural Science Foundation of China(No.06YFJ MJC03100,08JCZDJC24500)
文摘Improved Resin Transfer Molding (RTM) technology and equipment were established.Void content and morphology of the 3-D braided preform/phenolic composite were investigated using different RTM processes.The results showed that void content of the vacuum and compression co-assisted RTM process was the lowest.Void morphologies of the specimen cross-section were analyzed with metallographic microscope.In traditional RTM process,the crack of cross-section was in evidence.In vacuum assisted RTM process,the void shape was divided into three categories:irregular crack,triangle,rotundity and ellipse.The most voids distributed in resin rich areas and were observed as large void based on equivalent diameter.In compression assisted RTM,vacuum and compression co-assisted RTM process,the polygonal voids mostly existed inter tows.Void size was mainly intermediate and small based equivalent diameter separately.
基金supported by the National Natural Science Foundation of China (No. 51505386 and No. 51275416)the China Postdoctoral Science Foundation (No. 2014M562447)the Research Fund of the State Key Laboratory of Solidification Processing (NWPU), China (16-BZ-2015)
文摘Similar diffusion bonding of 1Cr11Ni2W2MoV stainless steel was conducted at different bonding tem- peratures. The interface characteristics and mechanical properties of joints were examined, and the evolution of interracial void morphology was analyzed in detail The results showed that there were four typical interfacial void shapes generating sequentially： the large scraggly voids, penny-shaped voids, ellipse voids and rounded voids. The variation of interracial void shape was dominated by surface diffusion, while the reduction of void volume was ascribed to the combined effects of plastic flow of materials around voids, interface diffusion and volume diffusion. Owing to the elimination of void from the bonding interface, the sound joint obtained could exhibit nearly full interracial contact, and present excellent mechanical properties, in which the microhardness and shear strength of joint matched those of base material.
基金the National Natural Science Foundation of China(Nos.10602034,10572088)
文摘A model for the morphological evolution of a void under thermal and mechanical loads is established, and the thermodynamics potential of the model is given based on energy principle. Thus, the path and the bifurcation condition of the morphological evolution of the void are described, which gives some insight into the reliability of the interconnect under combined thermal and mechanical loads.