A series of dodecenylsuccinylated starches( DSSs) with different degree of substitution( DS) were prepared via the esterification of dodencenylsuccinic anhydride with hydrolyzed cornstarch in aqueous dispersion for in...A series of dodecenylsuccinylated starches( DSSs) with different degree of substitution( DS) were prepared via the esterification of dodencenylsuccinic anhydride with hydrolyzed cornstarch in aqueous dispersion for investigating the influences of starch dodecenylsuccinylation upon the performances such as apparent viscosity and surface tension of starch paste, film behaviors,and adhesion to fibers for warp sizing. It was found that the dodecenylsuccinylation was able to reduce the surface tension of cooked starch paste and enhance the adhesion of starch to polyester fibers. It was also capable of depressing the brittleness of native starch and improving the mechanical behaviours such as breaking elongation and work-to-break of starch film. Initial increase in DS level of dodecenylsuccinylation enhanced these positive effects,while excessively increasing the level resulted in marked reduction in tensile strength of starch film and significant decrement in reaction efficiency. X-ray diffraction patterns of starch films showed the dodecenylsuccinates derivatized onto the backbones of starch depressed the degree of crystallinity of starch film. Based on the paste behaviors, adhesion, and film properties, the dodecenylsuccinylation level is recommended in a range of 0. 015-0. 025 for sizing polyester warps.展开更多
A series of poly （ 2-ethylhexyl acrylate-co-acrylic acid ） s （ P （2-EHA-co-AA） ）s with different mole contents of 2-ethylhexyl acrylate （ 2-EHA ） were synthesized through free radical copolymerization in ethan...A series of poly （ 2-ethylhexyl acrylate-co-acrylic acid ） s （ P （2-EHA-co-AA） ）s with different mole contents of 2-ethylhexyl acrylate （ 2-EHA ） were synthesized through free radical copolymerization in ethanol for investigating the influences of copolymer composition upon the performance such as apparent viscosity, film behaviors, and adhesion to fibers for warp sizing. The content of 2-EHA was varied from 80 % to 40 %. The adhesion was estimated by measuring tensile strength and work-to-break of impregnated roving. The film behaviors were evaluated in terms of breaking strength, breaking elongation, work-to-break, and flex- fatigue resistance. It was observed that the viscosity, adhesion, and film behaviors of the copolymers strongly depended on the content of 2-EHA. Excessively increasing or decreasing the content of 2-EHA units incorporated into the copolymeric chains reduces the serviceability of P（2-EHA-co-AA） in warp sizing. The adhesion and film behaviors of the copolymcr reach their maximal values at mole content of 50 % simultaneously. Therefore, the copolymer used as sizing agent should be synthesized under equal mole of 2-EHA and AA in monomer formulation.展开更多
基金the Fund of Anhui Province Science Research Projects,China(No.1106b0105062)the Research Foundation Program of Scientific and Technological Innovation Team of College and University at the Provincial Level of Anhui,China(No.TD200710)
文摘A series of dodecenylsuccinylated starches( DSSs) with different degree of substitution( DS) were prepared via the esterification of dodencenylsuccinic anhydride with hydrolyzed cornstarch in aqueous dispersion for investigating the influences of starch dodecenylsuccinylation upon the performances such as apparent viscosity and surface tension of starch paste, film behaviors,and adhesion to fibers for warp sizing. It was found that the dodecenylsuccinylation was able to reduce the surface tension of cooked starch paste and enhance the adhesion of starch to polyester fibers. It was also capable of depressing the brittleness of native starch and improving the mechanical behaviours such as breaking elongation and work-to-break of starch film. Initial increase in DS level of dodecenylsuccinylation enhanced these positive effects,while excessively increasing the level resulted in marked reduction in tensile strength of starch film and significant decrement in reaction efficiency. X-ray diffraction patterns of starch films showed the dodecenylsuccinates derivatized onto the backbones of starch depressed the degree of crystallinity of starch film. Based on the paste behaviors, adhesion, and film properties, the dodecenylsuccinylation level is recommended in a range of 0. 015-0. 025 for sizing polyester warps.
基金Open Project Program of Key Laboratory of Eco-Textiles,Ministry of Education,China(No.KLET0617)
文摘A series of poly （ 2-ethylhexyl acrylate-co-acrylic acid ） s （ P （2-EHA-co-AA） ）s with different mole contents of 2-ethylhexyl acrylate （ 2-EHA ） were synthesized through free radical copolymerization in ethanol for investigating the influences of copolymer composition upon the performance such as apparent viscosity, film behaviors, and adhesion to fibers for warp sizing. The content of 2-EHA was varied from 80 % to 40 %. The adhesion was estimated by measuring tensile strength and work-to-break of impregnated roving. The film behaviors were evaluated in terms of breaking strength, breaking elongation, work-to-break, and flex- fatigue resistance. It was observed that the viscosity, adhesion, and film behaviors of the copolymers strongly depended on the content of 2-EHA. Excessively increasing or decreasing the content of 2-EHA units incorporated into the copolymeric chains reduces the serviceability of P（2-EHA-co-AA） in warp sizing. The adhesion and film behaviors of the copolymcr reach their maximal values at mole content of 50 % simultaneously. Therefore, the copolymer used as sizing agent should be synthesized under equal mole of 2-EHA and AA in monomer formulation.