Application of reactive acrylate microgels in water-base coatings

Reactive acrylate microgels with different reactive groups such as carboxyl, hydroxide groups had excellent properties such as quick-dry, low viscosity, high adhesion and hardness, which made them extensively used in preparing paints or in coating-modification. Reactive acrylate microgels were prepared by emulsion co-polymerization with zwitterions surfactant, anionic surfactant and nonionic surfactant as co-emulsifier. The water-base baking paints made from reactive acrylate microgels and melamine-formaldehyde resin had excellent combination properties. The aluminium powder can be well-dispersed in the paints. The influences of monomer components on the properties of the water-base baking paints were discussed in this paper. And the baking paints were also compared with the marketing solvent acrylate baking paints. It was found that the water-base acrylate amino baking paints had better combination properties than the organic solvent acrylate baking paints, which means that the water-base baking paints had a bright marketing future.

低毒低挥发性脱漆剂的研制

以甲基丙烯酸甲酯为主溶剂,苯甲醛为助溶剂,有机酸为促进剂,OP-10为表面活性剂,硫脲为缓蚀剂,液体石蜡为封闭剂,制备了一种针对丙烯酸涂层的低毒、低挥发性的脱漆剂。分别研究了主、助溶剂配比,甲酸含量及表面活性剂含量对脱漆剂脱漆效果的影响,同时研究了液体石蜡含量对脱漆剂挥发速度的影响。结果表明,当甲基丙烯酸甲酯的质量分数为65.25%,苯甲醛为21.75%,OP-10为2%,有机酸为2%,硫脲为2.5%,液体石蜡为6%时,所得脱漆剂的脱漆效果好,毒性、挥发性和腐蚀性低。

一种新型镁合金脱漆剂的研制

以苯甲醇为主溶剂,乙烯基乙醚为助溶剂,三乙醇胺为活化剂,十二烷基苯磺酸钠为表面活性剂,添加剂A为缓蚀剂,石蜡为阻挥发剂,甲基纤维素为增稠剂,制备了一种镁合金基体的新型低毒,低腐蚀性的脱漆剂。分别研究了主、助溶剂配比,活化剂、表面活性剂及增稠剂质量分数对脱漆剂脱漆时间的影响,同时研究了缓蚀剂对脱漆效果影响。结果表明,当w(苯甲醇)为60%,w(乙烯基乙醚)为20%,w(三乙醇胺)为5%,w(咪唑)为1.5%,w(十二烷基苯磺酸钠)为5%,w(甲基纤维素)为3%时,所得脱漆剂的脱漆效果好,毒性和腐蚀性低。

环境友好的溶剂型脱漆剂的研究进展

阐述了脱漆剂的发展趋势,侧重介绍了水性脱漆剂、乳液型脱漆剂和低毒低挥发性脱漆剂的配方及优点,并对环保型脱漆剂的发展前景提出了展望。

脱漆剂脱漆速度的主要影响因素分析

脱漆剂脱漆速度的快慢影响其使用推广,影响脱漆速度的因素既有脱漆剂本身,也有使用环境或基体材料等条件。讨论了脱漆剂的主要成分、工作温度以及经不同转化膜处理的金属基材等因素对脱漆剂脱漆速度的影响。结果表明,作为脱漆剂的主溶剂只有与带有羟基、胺基等活性官能团的溶剂复配使用,脱漆速度才能明显提高;加入促进剂可以提高脱漆速度,能够脱除一些强耐腐蚀性的漆膜;铝基氧化膜上的漆膜比铁基转化膜上的漆膜更容易脱除。本研究结果为脱漆剂的应用提供了依据。

溶剂型碱性脱漆剂的研制

研制了一种用于航空发动机零部件脱漆的脱漆剂，该脱漆剂由两层液体组成，上层为油封层，下层为工作液。脱漆时需将工件完全浸没在工作液中，合适的脱漆温度为80～110℃。该脱漆剂具有较宽的使用范围，脱漆效率较高。

船舶用脱漆剂的研究

以苯甲醇为主溶剂,乙醇为助溶剂,羧甲基纤维素作增稠剂,制备了水溶性船舶用脱漆剂。讨论了不同用量的苯甲醇、复合促进剂对脱漆效果的影响,确定了最佳用量,分别为:φ(苯甲醇)=40%,φ(促进剂)=13%。按国家标准将新型脱漆剂与传统脱漆剂对不同漆膜的脱漆效果进行了比较。结果证明,该脱漆剂的脱漆效果优于传统的醇醚型、热碱型脱漆剂,而与二氯甲烷型脱漆剂相当,在安全性方面则优于传统脱漆剂。

适于塑料基材的水溶性脱漆剂研究

电动车塑料外壳回收业发展迅速,但是缺乏高效、低耗的专用脱漆剂。本文根据溶解度参数相近原则和溶剂化原则,设计了适于ABS塑料基体表面不饱和聚酯和丙烯酸酯共聚物涂层的水溶性脱漆剂。以芳香醇为主溶剂,添加一元醇、乙酸和非离子型表面活性剂A作为助剂,通过正交试验获得了水溶性脱漆剂配方。试验结果表明,该脱漆剂的渗透、剥离能力较强,对ABS基材无损伤,在室温下脱漆时间约20 min,2 h内挥发率低于7%,每升溶液可以脱掉表面积为450～500 cm^2的漆膜。

拉链头用水性高效脱漆剂的制备及应用

通过单因素试验考察了不同主溶剂、助溶剂和促进剂对拉链头上聚酯类漆膜的脱漆能力的影响,然后用正交试验确定所选各组分的用量,得到最佳脱漆剂配方为:主溶剂苯甲醛21.28%(质量分数,下同),助溶剂丙三醇24.82%,促进剂[m(甲酸):m(三乙醇胺):m(氢氧化钠):m(水)=4:1:1:4]47.69%,表面活性剂OP-10 6.21%。该水性脱漆剂适用于采用不同工艺(包括滚喷、挂喷和电泳)涂装的拉链头,脱漆效率均为95%以上,并且重复使用10次后,脱漆效率仍能达到95%以上。

食品罐用镀锡钢板的无机碱性脱漆剂研究

根据水解啄理，以NaOH为主溶刹，CTMAB为表面活性剂，尿素为助溶剂，1，2-丙二醇为辅助添加剂，在恒温水浴条件下制备了一种针对食品罐用镀锡钢板的无机碱性脱漆剂。考察了主溶剂、表面活性剂、助溶剂及辅助添加剂的种类、用量以及温度对脱漆效率的影响，同时探讨了脱漆剂的理化性能、综合性能、挥发速率及腐蚀性。结果表明：当NaOH为5．0g，CTMAB为0．3g，尿素为0．6g，1，2-丙二醇为0．2g，在70～75℃时，所得脱漆剂的脱漆效果最高，挥发性和腐蚀性低，3～5min内可使镀锡钢板底色样板漆膜软化、脱落。

脱漆剂的研究进展

介绍了脱漆剂的脱漆原理和分类。综述了国内外脱漆剂的研究现状。详细叙述了脱漆剂配方的确定依据,并对其应用前景提出了展望。

DBE脱漆剂的脱漆性能研究

研究了DBE(二元酸酯及其混合物)环保型脱漆剂的腐蚀性。实验结果表明,该脱漆剂对镀锡钢板的平均腐蚀速率分别为0.121 5 g·m-2·h-1;配制好的脱漆剂敞口放置48 h后,其质量保留率分别为84%。说明该脱漆剂的腐蚀性和挥发性均较小,环保性能稳定,使用寿命较长。扫描电镜(SEM)和能谱分析(EDS)结果表明,DBE脱DBE脱漆剂的脱漆性能研究漆剂在脱漆后金属基材表明仍存在连续的磷化膜,锡元素含量与原镀锡钢板基本保持在同一水平,样板表面锡层受破坏的程度较低,不影响镀锡钢板的二次涂装和利用。

苯甲醇(醛)型脱漆剂使用性能研究

配制以苯甲醇 (醛 )为主溶剂的脱漆剂 ,探讨了其使用温度、增稠剂的用量以及对基材的适应性等。确定了最佳使用温度。适用于垂直面或倾斜面的施工。采用PET包装脱漆剂性能稳定。

用于镀锡钢板的水性脱漆剂的研制

针对用于食品罐的镀锡钢板表面的白涂、金属油墨和罩光清漆样板研制一种水性脱漆剂。当苯甲醇的质量分数为35%、丙二醇碳酸酯质量分数为6%、甲酸质量分数为10%、十六烷基三甲基溴化铵(CTMAB)质量分数为2%、蒸馏水质量分数为47%时,所得脱漆剂脱漆效率最高。该脱漆剂含有一定水组分,挥发性小,不易燃烧。扫描电镜检测表明该脱漆剂对镀锡钢板的腐蚀性较小。

水性脱漆剂脱漆效率影响因素的试验研究

以苯甲醇型水性脱漆剂为研究对象,考察促进剂和表面活性剂类型及用量、脱漆温度、搅拌状态各因素对白涂、金属油墨和罩光漆涂漆镀锡钢板脱漆效率的影响。结果表明,当促进剂甲酸含量为10%(质量分数),表面活性剂十六烷基三甲基溴化铵(CTMAB)含量为2%时,该脱漆剂的脱漆效率可明显提高;60℃时,脱漆速率最快,继续升温,脱漆速率变化不明显;搅拌状态的变化对脱漆效率的影响不大。扫描电镜及X射线能谱分析检测表明该脱漆剂对镀锡钢板的腐蚀性较小。

溶剂型脱漆剂脱漆效率影响因素的探讨

根据“相似相容原理”，制备了一种针对食品罐用镀锡钢板的溶剂型脱漆剂。讨论了表面活性剂、促进剂的选择，以及温度、挥发速率、搅拌时间对脱漆剂效率的影响。结果表明，表面活性剂CTMAB为2％，促进剂乳酸为28％，在80～85℃时搅拌10min，3～5min内可使漆膜软化、脱落，所得脱漆剂的脱漆效果最高，毒性、挥发性和腐蚀性低。红外光谱（FT-IR）分析结果表明，该体系在脱除漆膜的过程中未发生化学反应，脱漆后材料组分基本无变化，脱漆剂可反复利用。

聚氨酯类铜漆包线的水性脱漆剂的研究

文章针对目前国内脱漆剂存在的毒性大、污染严重等问题,开展绿色环保水性铜漆包线脱漆剂的研发工作。实验首先选择目前我国应用最为广泛的苯甲醇及N,N–甲基吡咯烷酮作为脱漆剂的主要成分,再加入助溶剂、活化剂、缓蚀剂、乳化剂、增稠剂等配制出一种聚氨酯类铜漆包线的水性脱漆剂。并通过单因素条件实验考察了溶液成分、各组分剂量、温度梯度以及反应时间等对脱漆剂脱漆效果的影响,确定了较优的脱漆剂组成以及脱漆反应条件。

环境友好的溶剂型脱漆剂的研究进展

本文阐述了脱漆剂的发展趋势,侧重介绍了水性脱漆剂、乳液型脱漆剂和低毒低挥发性脱漆剂的配方及优点,并对环保型脱漆剂的发展前景提出了展望。

食品罐用镀锡钢板的溶剂型脱漆剂的研制

制备了一种针对食品罐用镀锡钢板的溶剂型脱漆剂。采用单因素实验法研究了主溶剂复配比例及含量、十六烷基三甲基溴化铵含量及乳酸含量对脱除效率的影响，同时探讨了脱漆剂的挥发速率和腐蚀性。结果表明，当苯乙醇、无水乙醇、十六烷基三甲基澳化铵、乳酸质量分数分别为21％、49％、2％、28％，温度为80-85℃时，3～5min内可使漆膜软化、脱落，所得脱漆剂的脱漆效率最高，毒性、挥发性和腐蚀性低。

二元酸酯及其混合物脱漆剂的制备及其脱漆效率研究

针对镀锡钢板表面的白涂、金属油墨及罩光清漆漆膜研制出二元酸酯及其混合物(DBE)环保型脱漆剂。实验结果表明,当DBE脱漆剂中各溶剂的质量分数分别为:己二酸二甲酯31.38%、十六烷基三甲基溴化铵5.88%、1,2-丙二醇碳酸酯27.45%、乳酸23.53%、无水乙醇11.76%时,其脱漆效率最高。