Environmentally friendly, polyacrylic-based polyurethane dispersion (PUD) was synthesised using various molar ratios of polycaprolactone, dimethylolpropionic acid and tetramethyl xylene diisocyanate. Synthesis was car...Environmentally friendly, polyacrylic-based polyurethane dispersion (PUD) was synthesised using various molar ratios of polycaprolactone, dimethylolpropionic acid and tetramethyl xylene diisocyanate. Synthesis was carried out in flowing nitrogen atmosphere. The PUD’s preparations are free of NMP (n-methyl pyrrolidone), a toxic processing solvent generally used during the preparation of PUD’s. The performance of the synthesised polyurethane dispersions with varying NCO/OH molar ratio was tested on wood surface. The physical, chemical, thermal and mechanical properties such as viscosity, particle size, chemical resistance, thermal stability and taber abrasion of applied polyurethane dispersion were carried out as a function of NCO/OH molar ratio. The PUD’s preparation with NCO/OH ratio of 1.4 or 1.6 showed better performance as a wood finish and the results are described in the present study.展开更多
A series of nano silica/silicone modified waterborne polyurethane(WPU) have been synthesized from polytetramethylene glycol and isophorone diisocyanate, dihydroxymethyl propionic acid and triethylamine, ethylenediamin...A series of nano silica/silicone modified waterborne polyurethane(WPU) have been synthesized from polytetramethylene glycol and isophorone diisocyanate, dihydroxymethyl propionic acid and triethylamine, ethylenediamine, trimethylolpropane, nano-SiO2 and the silane coupling agent KH550. The effect of the dosage of nano-SiO2 on the WPU-Si membrane and the coated RDX(cyclotrimethylenetrinitramine) particles have been studied in terms of their surface properties, mechanical properties, and thermal stability. The results showed that with the increase of Si content, the stability of the emulsion reduced gradually. The material with more Si content displayed an increased thermodynamic stability, an increased high temperature resistance, an increased tensile strength and a decreased elongation at break. With the increase of Si content, the surface tension of the material decreased, the bibulous rate reduced, and the contact angle increased gradually, so that the surface tension of the polyurethane and RDX are close to each other which could improve the performance of coating.展开更多
The increasing pressure from consumers and policy makers to reduce the use of synthetic polymers,whose production contributes to the depletion of non-renewable resources and are usually non-biodegradable,has prompted ...The increasing pressure from consumers and policy makers to reduce the use of synthetic polymers,whose production contributes to the depletion of non-renewable resources and are usually non-biodegradable,has prompted the efforts to find suitable bio-based sources for the production of polymers.Vegetable oils have been a frequently spotted in this search because they are versatile,highly available and a low cost liquid biosource,which can be used in the synthesis of a wide plethora of different polymers and reactive monomers.Following the same idea of reducing the environmental stress,the traditional polyurethanes that are soluble in organic solvents have been targeted for replacement,particularly in applications such as adhesives and coatings,in which the solvent is released to the atmosphere increasing the air pollution.Instead,waterborne polyurethanes(WBPU),which are polyurethane dispersions(PUD)prepared in aqueous media,release benign water to the atmosphere during use as supported or self-standing films for different applications.In this brief review,the contributions to the development of WBPUs based on vegetable oils are discussed,focusing mainly on the contributions of the last decade.The synthesis of ionic and nonionic PUDs,their characterization and the properties of the resulting dried materials,as well as derived composite materials are considered.展开更多
In this study, to improve hemocompatibility of biomedical materials, a waterborne polyurethane （WPU）haepafin release coating system （WPU/heparin） is fabricated via simply blending biodegradable WPU emulsions with ...In this study, to improve hemocompatibility of biomedical materials, a waterborne polyurethane （WPU）haepafin release coating system （WPU/heparin） is fabricated via simply blending biodegradable WPU emulsions with heparin aqueous solutions. The surface compositions and hydrophilicity of these WPU/heparin blend coatings are characterized by attenuated total reflectance infrared spectroscopy （ATR-FTIR） and water contact angle measurements. These WPU/heparin blend coatings show effectively controlled release of heparin, as determined by the toluidine blue method. Furthermore, the biocompatibility and anticoagulant activity of these blend coatings are evaluated based on the protein adsorption, platelet adhesion, activated partial thromboplastin time （APTT）, thrombin time （TT）, hemolysis, and cytotoxicity. The results indicate that better hemocompatibility and cytocompatilibity are obtained due to blending heparin into this waterborne polyurethane. Thus, the WPU/heparin blend coating system is expected to be valuable for various biomedical applications.展开更多
文摘Environmentally friendly, polyacrylic-based polyurethane dispersion (PUD) was synthesised using various molar ratios of polycaprolactone, dimethylolpropionic acid and tetramethyl xylene diisocyanate. Synthesis was carried out in flowing nitrogen atmosphere. The PUD’s preparations are free of NMP (n-methyl pyrrolidone), a toxic processing solvent generally used during the preparation of PUD’s. The performance of the synthesised polyurethane dispersions with varying NCO/OH molar ratio was tested on wood surface. The physical, chemical, thermal and mechanical properties such as viscosity, particle size, chemical resistance, thermal stability and taber abrasion of applied polyurethane dispersion were carried out as a function of NCO/OH molar ratio. The PUD’s preparation with NCO/OH ratio of 1.4 or 1.6 showed better performance as a wood finish and the results are described in the present study.
基金the financial support by the National Natural Science Foundation of China(No.20973022 and No.11472048)
文摘A series of nano silica/silicone modified waterborne polyurethane(WPU) have been synthesized from polytetramethylene glycol and isophorone diisocyanate, dihydroxymethyl propionic acid and triethylamine, ethylenediamine, trimethylolpropane, nano-SiO2 and the silane coupling agent KH550. The effect of the dosage of nano-SiO2 on the WPU-Si membrane and the coated RDX(cyclotrimethylenetrinitramine) particles have been studied in terms of their surface properties, mechanical properties, and thermal stability. The results showed that with the increase of Si content, the stability of the emulsion reduced gradually. The material with more Si content displayed an increased thermodynamic stability, an increased high temperature resistance, an increased tensile strength and a decreased elongation at break. With the increase of Si content, the surface tension of the material decreased, the bibulous rate reduced, and the contact angle increased gradually, so that the surface tension of the polyurethane and RDX are close to each other which could improve the performance of coating.
基金the Consejo Nacional de Investigaciones Científicas y Técnicas(CONICET,Argentina)(PIP 20170100677)the Fondo para la Investigación Científica y Tecnológica(FONCYT)(PICT-2017-1318)the Universidad Nacional de Mar del Plata(UNMdP,15/G557,ING561/19)and to the Comisión de Investigaciones Científicas de la Provincia de Buenos Aires(CIC)and the Universidad Tecnológica Nacional(UTN)for their financial support.
文摘The increasing pressure from consumers and policy makers to reduce the use of synthetic polymers,whose production contributes to the depletion of non-renewable resources and are usually non-biodegradable,has prompted the efforts to find suitable bio-based sources for the production of polymers.Vegetable oils have been a frequently spotted in this search because they are versatile,highly available and a low cost liquid biosource,which can be used in the synthesis of a wide plethora of different polymers and reactive monomers.Following the same idea of reducing the environmental stress,the traditional polyurethanes that are soluble in organic solvents have been targeted for replacement,particularly in applications such as adhesives and coatings,in which the solvent is released to the atmosphere increasing the air pollution.Instead,waterborne polyurethanes(WBPU),which are polyurethane dispersions(PUD)prepared in aqueous media,release benign water to the atmosphere during use as supported or self-standing films for different applications.In this brief review,the contributions to the development of WBPUs based on vegetable oils are discussed,focusing mainly on the contributions of the last decade.The synthesis of ionic and nonionic PUDs,their characterization and the properties of the resulting dried materials,as well as derived composite materials are considered.
基金financially supported by the National Natural Science Foundation of China(Nos.51173118,51273124 and51273126)the National Science Fund for Distinguished Young Scholars of China(No.51425305)+1 种基金the Youth Science and Technology Innovation Team of Sichuan Province(No.2015TD0001)State Key Laboratory of Polymer Materials Engineering(No.sklpme2014-2-03)
文摘In this study, to improve hemocompatibility of biomedical materials, a waterborne polyurethane （WPU）haepafin release coating system （WPU/heparin） is fabricated via simply blending biodegradable WPU emulsions with heparin aqueous solutions. The surface compositions and hydrophilicity of these WPU/heparin blend coatings are characterized by attenuated total reflectance infrared spectroscopy （ATR-FTIR） and water contact angle measurements. These WPU/heparin blend coatings show effectively controlled release of heparin, as determined by the toluidine blue method. Furthermore, the biocompatibility and anticoagulant activity of these blend coatings are evaluated based on the protein adsorption, platelet adhesion, activated partial thromboplastin time （APTT）, thrombin time （TT）, hemolysis, and cytotoxicity. The results indicate that better hemocompatibility and cytocompatilibity are obtained due to blending heparin into this waterborne polyurethane. Thus, the WPU/heparin blend coating system is expected to be valuable for various biomedical applications.