Recycled powder(RP)is produced as a by-product during the process of recycling construction and demolition(C&D)wastes,presenting a low additional value.Using RP-based solidifying material can not only improve its ...Recycled powder(RP)is produced as a by-product during the process of recycling construction and demolition(C&D)wastes,presenting a low additional value.Using RP-based solidifying material can not only improve its utilization efficiency,but also reduce the cost of commercial solidifying materials.To date,this is the best solidifying material utilized to dispose the original waterworks sludge(OWS)with high moisture contents(60%),and the product could be used to fabricate non-fired bricks.This has become a new environment-friendly technology of“using waste to treat waste”.In this paper,the influence of different particle sizes and dosages of RP on the prepared solidifying material was studied.Besides,unconfined compression strength(UCS),volume stability,chemical composition,and heat of hydration,pore structure of the solidifying material were characterized.Then,non-fired bricks were prepared by using the solidifying material,recycled aggregate,and original waterworks sludge.The UCS and softing coefficient(SC)of the non-fired bricks were evaluated.As a result,the 28-day UCS of the solidifying material with optimal(M30)was 35.40 MPa,which could reach 84.37%of Portland cement(PC).The addition of RP increased the volume stability of the solidifying material.The addition of a large amount of RP reduced the heat flux and cumulative heat release of the solidifying material,while its porosity increased.The UCS of non-fired brick(NF20)in 28 days was 15.19 MPa and the SC after 28 days was 78.35%.In conclusion,the preparation of solidifying material using RP could be a promising approach and has a great potential in disposal of original waterworks sludge.展开更多
The aim of this research is to find substitute barrier materials for natural clay from two kinds of municipal sludge: waterworks sludge(S_w) and dredging sludge(S_d). Laboratory tests were performed firstly to determi...The aim of this research is to find substitute barrier materials for natural clay from two kinds of municipal sludge: waterworks sludge(S_w) and dredging sludge(S_d). Laboratory tests were performed firstly to determine their Atterberg limits and hydraulic conductivity. Based on the results, the use of waterworks sludge was recommended. Then, shear strength tests were performed and it was found the shear resistance property of waterworks sludge is strong enough to maintain slope stability. In order to evaluate the possibility of secondary pollution, the heavy metal contents of waterworks sludge was determined and the results indicated that secondary pollution is unlikely happened. Finally, economic analysis proves that reusing waterworks sludge as barrier will reduce the lost a great for both landfill and waterworks. Based on the results, waterworks sludge was proposed to use and a further long-term simulated landfill test was suggested.展开更多
基金This work was supported by the Jiangsu Provincial Science and Technology Department’s Social Development-Major Science and Technology Demonstration Project(Grant No.BE2018697)the Demonstration Engineering Technology Research Center of Suqian Science and Technology Bureau(Grant No.M201912)a Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions.
文摘Recycled powder(RP)is produced as a by-product during the process of recycling construction and demolition(C&D)wastes,presenting a low additional value.Using RP-based solidifying material can not only improve its utilization efficiency,but also reduce the cost of commercial solidifying materials.To date,this is the best solidifying material utilized to dispose the original waterworks sludge(OWS)with high moisture contents(60%),and the product could be used to fabricate non-fired bricks.This has become a new environment-friendly technology of“using waste to treat waste”.In this paper,the influence of different particle sizes and dosages of RP on the prepared solidifying material was studied.Besides,unconfined compression strength(UCS),volume stability,chemical composition,and heat of hydration,pore structure of the solidifying material were characterized.Then,non-fired bricks were prepared by using the solidifying material,recycled aggregate,and original waterworks sludge.The UCS and softing coefficient(SC)of the non-fired bricks were evaluated.As a result,the 28-day UCS of the solidifying material with optimal(M30)was 35.40 MPa,which could reach 84.37%of Portland cement(PC).The addition of RP increased the volume stability of the solidifying material.The addition of a large amount of RP reduced the heat flux and cumulative heat release of the solidifying material,while its porosity increased.The UCS of non-fired brick(NF20)in 28 days was 15.19 MPa and the SC after 28 days was 78.35%.In conclusion,the preparation of solidifying material using RP could be a promising approach and has a great potential in disposal of original waterworks sludge.
文摘The aim of this research is to find substitute barrier materials for natural clay from two kinds of municipal sludge: waterworks sludge(S_w) and dredging sludge(S_d). Laboratory tests were performed firstly to determine their Atterberg limits and hydraulic conductivity. Based on the results, the use of waterworks sludge was recommended. Then, shear strength tests were performed and it was found the shear resistance property of waterworks sludge is strong enough to maintain slope stability. In order to evaluate the possibility of secondary pollution, the heavy metal contents of waterworks sludge was determined and the results indicated that secondary pollution is unlikely happened. Finally, economic analysis proves that reusing waterworks sludge as barrier will reduce the lost a great for both landfill and waterworks. Based on the results, waterworks sludge was proposed to use and a further long-term simulated landfill test was suggested.