Microstructure and Wear/corrosion Resistance of Stainless Steel Laser-alloyed with Mn+W_(2)C, Mn+NiWC and Mn+SiC

In-situ formed high Mn steel coating reinforced by carbides was formed by laser surface alloying(LSA).Laser alloyed layers on 1Cr18Ni9Ti steel with Mn+W_(2)C(specimen A),Mn+NiWC(specimen B)and Mn+SiC(specimen C)powders were fabricated to improve the wear and corrosion behavior of 1Cr18Ni9Ti steel blades in high speed mixers.Microstructure evolution,phases,element distribution,microhardness,wear and corrosion behavior of the laser alloyed layers were investigated.Results indicated that high Mn steel matrix composites with undissolved W_(2)C,WC and other in-situ formed carbides were formed by LSA with Mn+W_(2)C and Mn+NiWC while SiC totally dissolved into the high Mn matrix when adding Mn+SiC.Ni as the binding phase in Ni-WC powder decreased the crack sensitivity of the alloyed layer as compared with the addition of W_(2)C powder.An improvement in average microhardness was achieved in the matrix in specimen A,B and C,with the value of 615,602 and 277 HV_(0.5),while that of the substrate was 212 HV_(0.5).The increase of microhardness,wear and corrosion resistance is highly corelated to microstructure,formed phases,type and content of carbides,micro-hardness and toughness of the alloyed layers.

Enhanced wear resistance,antibacterial performance,and biocompatibility using nanotubes containing nano-Ag and bioceramics in vitro

A good Ti-based joint implant should prevent stress shielding and achieve good bioactivity and anti-infection performance.To meet these requirements,the low-elastic-modulus alloy—Ti–35Nb–2Ta–3Zr—was used as the substrate,and functional coatings that contained bioceramics and Ag ions were prepared for coating on TiO_(2)nanotubes(diameter:(80±20)nm and(150±40)nm)using anodization,deposition,and spin-coating methods.The effects of the bioceramics(nano-β-tricalcium phosphate,microhydroxyapatite(micro-HA),and meso-CaSiO_(3))and Ag nanoparticles(size:(50±20)nm)on the antibacterial activity and the tribocorrosion,corrosion,and early in vitro osteogenic behaviors of the nanotubes were investigated.The tribocorrosion and corrosion results showed that the wear rate and corrosive rate were highly dependent on the features of the nanotube surface.Micro-HA showed great wear resistance with a wear rate of(1.26±0.06)×10^(−3)mm^(3)/(N·m)due to adhesive and abrasivewear.Meso-CaSiO_(3)showed enhanced cell adhesion,proliferation,and alkaline phosphatase activity.The coatings that contained nano-Ag exhibited good antibacterial activity with an antibacterial rate of≥89.5%against Escherichia coli.These findings indicate that hybrid coatings may have the potential to accelerate osteogenesis.

Reactive HVOF sprayed TiN-matrix composite coating and its corrosion and wear resistance properties

TiN-matrix composite coating was prepared on 45# steel by reactive high-velocity oxy-fuel （HVOF） spraying. Its microstructure, phase composition, micro-hardness, corrosion resistance in 3.5% NaC1 solution and wear resistance were analyzed. The results suggest that the TiN-matrix composite coating is well bonded with the substrate. The micro-hardness measured decreases with the increase of applied test loads. And the micro-hardness of the coating under heavy loads is relatively high. The TiN-matrix composite coating exhibits an excellent corrosion resistance in 3.5% NaC1 solution. The corrosion potential of coating is positive and the passivation zone is broad, which indicates that the TiN-matrix composite coating is stable in the electrolyte and provides excellent protection to the substrate. The wear coefficient of the coating under all loads maintains at 0.49-0.50. The wear mechanism of the coating is revealed to be three-body abrasive wear. Yet the failure forms of TiN-matrix composite coating under different loads have an obvious difference. The failure form of coating under light loads is particle spallation due to the stress concentration while that of coating under heavy loads is crackin~ between inter-lamellae.

Microstructure,mechanical properties and dry wear resistance of β-type Ti-15Mo-xNb alloys for biomedical applications

In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb（x=5,10,15 and 20 in %） alloys were investigated.The dry wear resistance of β-type Ti-15Mo-xNb alloys against Gr15 ball was investigated on CJS111A ball-disk wear instrument.Experimental results indicate that crystal structure and morphology of the Ti-15Mo-xNb alloys are sensitive to their Nb contents.Ti-15Mo-xNb alloys match those for β phase peaks and no any phases are found.The Vickers hardness values of all the Ti-15Mo-xNb alloys are higher than HV200.The compression yield strength of the Ti-15Mo-5Nb alloy is the lowest and that of the Ti-15Mo-10Nb alloy is the highest.For all the Ti-15Mo-xNb alloys,the friction coefficient is not constant but takes a higher value.In dry condition,SEM study reveals deep parallel scars on the wear surfaces of all the Ti-15Mo-xNb alloys under different loads.The friction coefficient of the Ti-15Mo-5Nb alloy under 1 N is the lowest.The wear principal mechanism for Ti-15Mo-xNb alloys is adhesive wear.

Effects of slurry pack cementation temperature on microstructure and wear resistance of Ti-Al co-deposited coating on copper plated nickel layer

In order to improve the wear resistance properties of copper substrate, a layer of electroplated nickel was firstly deposited on copper substrate, subsequently these electroplated specimens were treated by slurry pack cementation process with a slurry pack cementation mixture composed of TiO2 as titanizing source, pure Al powder as aluminzing source and also a reducer for titanizing, an activator of NH4Cl and albumen （egg white） as cohesive agent. The Ti-Al coating was fabricated on the surface of electro-deposited nickel layer on copper matrix followed by the slurry pack cementation process. The effects of slurry pack cementation temperature on the microstructures and wear resistance of Ti-Al coating were studied. The results show that the microstructure of the coating changed from NiAl＋Ni3（Ti,Al） to NiAl ＋Ni3（Ti,Al）＋Ni4Ti3 to Ni4Ti3＋NiAl, and to NiAl＋Ni3（Ti,Al）＋NiTi with slurry pack cementation temperature ranging from 800 ℃ to 950 ℃ in 12 h. The friction coefficient of Ti-Al coating decreased and the hardness increased with increasing the slurry pack cementation temperature. The minimum friction coefficient was 1/3 and the minimum hardness was 5 times larger than that of pure copper.

HARDNESS PROPERTY AND WEAR RESISTANCE OF Al_2O_(3P)/ Zn-Al COMPOSITE

The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.

Greatly enhanced corrosion/wear resistances of epoxy coating for Mg alloy through a synergistic effect between functionalized graphene and insulated blocking layer

The poor corrosion and wear resistances of Mg alloys seriously limit their potential applications in various industries.The conventional epoxy coating easily forms many intrinsic defects during the solidification process,which cannot provide sufficient protection.In the current study,we design a double-layer epoxy composite coating on Mg alloy with enhanced anti-corrosion/wear properties,via the spin-assisted assembly technique.The outer layer is functionalized graphene(FG)in waterborne epoxy resin(WEP)and the inner layer is Ce-based conversion(Ce)film.The FG sheets can be homogeneously dispersed within the epoxy matrix to fill the intrinsic defects and improve the barrier capability.The Ce film connects the outer layer with the substrate,showing the transition effect.The corrosion rate of Ce/WEP/FG composite coating is 2131 times lower than that of bare Mg alloy,and the wear rate is decreased by~90%.The improved corrosion resistance is attributed to the labyrinth effect(hindering the penetration of corrosive medium)and the obstruction of galvanic coupling behavior.The synergistic effect derived from the FG sheet and blocking layer exhibits great potential in realizing the improvement of multi-functional integration,which will open up a new avenue for the development of novel composite protection coatings of Mg alloys.

Ultra wear resistant TiC-Fe coating prepared by high efficient and economic plasma cladding method

The key components of engineering machinery frequently failed due to working in the high load and high wear operating envir-onment.And the performance of the Fe-based alloy coatings typically employed need to be improved for fulfilling the service requirements.Herein,a TiC strengthened Fe-based alloy cladding layer,named TiC-Fe coating,was designed and prepared by plasma cladding technology.The frictional wear performance of coating under various loads was tested.The wear morphology of the coating was observed,and its wear mechanism was examined.The results indicated that the TiC-Fe coating was well formed and metallurgically bonded to the Q345C substrate.Its microstructure mainly consisted of Fe-Cr solid solution,α-Fe phase,(Fe,Cr)_(7)C_(3) phase and TiC phase.The coating exhibited an average microhardness of 980 HV0.2,which was about 5.4 times that of the Q345C substrate.The wear mass loss of the TiC-Fe coatings was much smaller than that of the Q345C substrate,which indicated that the wear resistance of the Q345C coating was superior to the substrate,and the wear mechanism of the coating was mainly attributed to the abrasive wear.

Ghrelin regulates insulin resistance by targeting insulin-like growth factor-1 receptor via miR-455-5p in hepatic cells

Objective: To explore the mechanism by which ghrelin regulates insulin sensitivity through modulation of miR-455-5p in hepatic cells. Methods: HepG2 cells were treated with or without DAG (1 μM). Glucose consumption, intracellular glycogen content, phosphorylation of PI3K and Akt stimulated by insulin, expression of miR-455-5p, as well as IGF-1R protein level were analyzed. In addition, bioinformatic analysis, dual luciferase reporter assay, miR- 455-5p mimic or inhibitor treatment was conducted to investigate the molecular mechanisms. Results: High glucose treatment upregulated miR-455-5p expression but reduced glucose consumption and glycogen content. DAG reversed the effect of high glucose on glucose metabolism, increased protein level of IGF-1R and phosphorylation of PI3K/Akt stimulated by insulin, as well as downregulated miR-455-5p expression. Bioinformatic analysis indicated IGF-1R was the target of miR-455-5p. Dual luciferase reporter assay, as well as transfection with miR-455-5p mimic/inhibitor confirmed that DAG activated IGF-1R/PI3K/Akt signaling via inhibiting miR-455-5p. Conclusion: DAG improves insulin resistance via miR-455-5p- mediated activation of IGF-1R/PI3K/Akt system, suggesting that suppression of miR-455-5p or activation of DAG may be potential targets for T2DM therapy.

CATHODIC PROCESS AND WEAR RESISTANCE OF ELECTRO-DEPOSITED RE-Ni-W-P-SiC COMPOSITE COATING

Cathodic deposition current density of the composite coatings increases when SiC par-ticles and rare earth (RE) were added in the bath, which is profitable for Ni- W-P alloy to deposit in the cathod, forming Ni-W-P-SiC and RE-Ni-W-P-SiC composite coatings. On the contrary, the addition of PTFE in the bath decreases cathodic deposition current density of the coatings. The current density increases a little when the amount of RE is 7-9g/l; however, the current density increases greatly when the amount of RE is increased to 11-13g/l. Bui ij the amount of RE is raised further, the current density decreases. Hardness and wear resistance of RE-Ni-W-P-SiC composite coating have been studied, and the results show that the hardness and wear resistance of RE-Ni-W-P-SiC composite coating increase with increasing heat treatment tempera-ture, which reach peak values at 400℃; while the hardness and wear resistance of the coating decrease with the rise of heat treated temperature continuously.

Wear and corrosion resistance of laser-cladded Fe-based composite coatings on AISI 4130 steel

The wear and corrosion resistance of Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） and Fe_（77.3）Cr_（15.8）Ni_（3.9）Mo_（1.1）Mn_（0.5）C_（0.2）Si_（1.2） coatings laser-cladded on AISI 4130 steel were studied.The coatings possess excellent wear and corrosion resistance despite the absence of expensive yttrium,tungsten,and cobalt and very little molybdenum.The microstructure mainly consists of dendrites and eutectic phases,such as duplex（γ＋α）-Fe and the Fe–Cr（Ni）solid solution,confirmed via energy dispersive spectrometry and X-ray diffraction.The cladded Fe-based coatings have lower coefficients of friction,and narrower and shallower wear tracks than the substrate without the cladding,and the main wear mechanism is mild abrasive wear.Electrochemical test results suggest that the soft Fe_（72.2）Cr_（16.8）Ni_（7.3）Mo_（1.6）Mn_（0.7）C_（0.2）Si_（1.2） coating with high Cr and Ni concentrations has high passivation resistance,low corrosion current,and positive corrosion potential,providing a better protective barrier layer to the AISI 4130 steel against corrosion.

Effects of nano-Al_2O_3 and nano-ZrO_2 on the microstructure, behavior and abrasive wear resistance of WC-8Co cemented carbide

WC-8wt.% Co cemented carbides with varied nano-Al 2 O 3 and nano-ZrO 2 contents were prepared respectively following conventional powder metallurgical procedures. Effects of nano-Al 2 O 3 and nano-ZrO 2 on the microstructure, behavior, and abrasive wear resistance were investigated. The result shows that a finer and more homogenous microstructure can be achieved by increasing nano-Al 2 O 3 , and increasing nano-ZrO 2 makes the microstructure more refined. Nano-Al 2 O 3 and nano-ZrO 2 could both help to give increased hardness. Transverse rupture strength is higher if the above nano-oxides are doped appropriately, whereas excess addition is deleterious. Abrasive wear resistance presents different variations with respect to increasing nano-Al 2 O 3 and nano-ZrO 2 . By contrast, increasing nano-ZrO 2 enhances the abrasive wear resistance more effectively than increasing nano-Al 2 O 3 . The influence of the two nano-oxides contents on the abrasive wear resistance does not almost vary with wear time, and the optimum addition level of nano-Al 2 O 3 in WC-8% Co cemented carbide is 0.3 wt.% from the stand of abrasive wear resistance. In addition, both of the nano-oxides can retard the increase of wear rate in long-term abrasive wear.

Effects of Y_2O_3 on the microstructure and wear resistance of cobalt-based alloy coatings deposited by plasma transferred arc process

Cobalt-based alloys with different Y2O3 contents were deposited on Q235A-carbon steel using plasma transferred arc （PTA） welding machine. The effect of Y2O3 on the microstructure and wear resistance properties of the cobait-based alloys were investigated using an optical microscope, a scanning electron microscope （SEM）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. It was found that a cobalt-based solid solution with a face-centered cubic crystal structure was presented accompanied by the secondary phase M7C3 with a hexagonal crystal structure in the Y2O3-free cobalt-based alloy coating. Several stacking faults exist in the cobalt-based solid solution. The addition of Y2O3 leads to the existence of the Y2O3 phase in the Y2O3-modified coatings. Though stacking fault exists in the Y2O3-modified coatings, its density increases. The addition of Y2O3 can refine the microstructure and can increase the wear resistance properties when its contents are less than or equal to 0.8 wt.%. However, further increase of its contents will lead to the agglomeration of undissolved Y2O3 particles at the γ-Co grain boundary, and will lead to a coarse microstructure and lower wear resistance properties.

Effects of additives on corrosion and wear resistance of micro-arc oxidation coatings on TiAl alloy

Ceramic coating was deposited on TiAl alloy substrate by micro-arc oxidation(MAO)in a silicate-aluminate electrolyte solution with additives including sodium citrate,graphite and sodium tungstate.The microstructures and compositions were analyzed by SEM,EDX and XRD.The corrosion and wear properties of the coatings were investigated by potentiodynamic polarization and ball-on-disc wear test,respectively.The results show that the MAO coatings consist of WO3,Ti2O3,graphite and Al2O3 besides Al2TiO5 and Al2SiO5.With additives in the electrolyte,the working voltage at the micro-arc discharge stage decreases,and the ceramic coating gets smoother and more compact.The corrosion current density of MAO coating is much lower than that of TiAl substrate.It can be reduced from 9.81×10-8A/cm 2to 3.02×10-10A/cm 2 .The MAO coatings composed of hard Al2O3,WO3 and Ti2O3 obviously improve the wear resistance of TiAl alloy.The wear rate is-3.27×10-7g/(N·m).

Improvement of wear and corrosion resistance of AZ91 magnesium alloy by applying Ni-SiC nanocomposite coating via pulse electrodeposition

To improve the surface properties of AZ91 magnesium alloy, Ni-SiC nanocomposite coatings with various SiC contents were pulse electrodeposited in modified Watts baths containing SiC nano-particles with the concentration of 0-15 g/L. The morphology of the coatings was studied by scanning electron microscope （SEM）. The SiC content of the coatings was measured by energy dispersive spectroscopy （EDS） analyzer. Microhardness measurement of the coatings showed up to 600% enhancement for the sample produced from the bath with 15 g/L SiC. The corrosion behavior of the coated AZ91 alloy was investigated by potentiodynamic polarization method. The results reveal a significant improvement in the corrosion resistance, that is, the corrosion current density decreases from 0.13 mA/cm2 for uncoated specimen to 1.74x10-6 mA/cm2 for the sample coated from the bath containing 15 g/L SiC and the corrosion potential increases from -1.6 V for uncoated specimen to -0.31 V for the sample coated from the bath. The wear resistance of both coated and uncoated samples was evaluated by pin-on-disc tribotester. The results show that the wear volume loss of coated sample is 8 times less than the bare alloy.

Wear and corrosion resistance and electroplating characteristics of electrodeposited Cr-SiC nano-composite coatings

Cr-SiC nanocomposite coatings with various contents of SiC nanoparticles were prepared by electrodeposition in optimized Cr plating bath containing different concentrations of SiC nanoparticles. Direct current electrocodeposition technique was used to deposit chromium layers with and without SiC nanoparticles on mild carbon steel. The effects of current density, stirring rate and concentration of nanoparticles in the plating bath were investigated. Scanning electron microscopy was used to study surface morphology. Energy dispersive analysis technique was used to verify the presence of SiC nanoparticles in the coated layers. The corrosion behaviors of coatings were investigated by potentiodynamic polarization and electrochemical impedance spectroscopy methods in 0.05 mol/L HCl, 1 mol/L NaOH and 3.5% NaCl （mass fraction）, respectively. Microhardness measurements and pin-on- disc tribometer technique were used to investigate the wear behavior of the coatings.

Effect of molybdenum on the microstructure and wear resistance of hypoeutectic Fe-Cr-B-C hardfacing alloys

Hypoeutectic Fe-Cr-B-C hardfacing alloys with different molybdenum( Mo) contents( The design content was 0,2,3. 3 and 4. 5 wt. %,respectively) were deposited using the flux-cored wire by means of metal active gas arc welding. The effects of Mo on the refinement of microstructures,eutectic microstructure changes and improvement of wear resistance were investigated. The main results were shown as follows: the added Mo could increase the volume fraction of eutectic microstructure and reduce the size of coarse primary austenite as well as the volume fraction. The carboboride of M3( B,C) could be observed in hypoeutectic Fe-Cr-B-C hardfacing alloys at the Mo design content of ≤2. 0 wt. %,while that of M23( B,C)6was formed when 3. 3 wt. % Mo was added.Additionally,the wear resistance of alloys was increased with the increase in Mo content. Specifically,the highest wear resistance of alloys was achieved at 4. 5 wt. % Mo design content,which was 113. 7% higher than that in alloys without Mo.

Electron-beam Treatment of Tungsten-free TiC/NiCr Cermet Ⅰ:Influence of Subsurface Layer Microstructure on Resistance to Wear during Cutting of Metals

An experimental investigation were performed on the effect of the impulse electron-beam irradiation upon microstruc-ture of the surface layer and on wear resistance of a cutting tool for sintered TiC/NiCr cermet. The results showed that the surface electron-beam treatment of the TiC/NiCr cermet is an efficient method for investigating the mi-crostructure and phase composition in the surface layer of the powder composite and there are optimal regimes of electron-beam treatment, which ensure a substantial increase in the resistance of the cermet to wear during cutting of metals.

Effects of Mo and Zr on Microstructure,Mechanical Properties and Wear Resistance of Fe-Al Based Alloys

In this work the microstructure, mechanical properties and wear resistance of Fe-Al based alloys with various alloying elements were studied. The microstructures were examined by optical and scanning electron microscopy （SEM） equipped with an energy dispersive X-ray spectroscope （EDS）. Two types of alloys were prepared by vacuum arc melting. One is Fe-28Al based alloys （D03 structured） with and without alloying elements such as Mo and Zr. The other one is Fe-35Al based alloys （B2 structured） produced with the same manner. For both types of alloys, Mo addition had found to exhibit an equiaxed microstructure, while dendritic structure was observed to show the effect of Zr addition. These microstructural features were more evinced with increasing content of alloying element. Concerning the mechanical properties and wear resistance, Fe-35Al based alloys were superior to Fe-28Al based alloys over the whole temperature range investigated.

Effect of nano-size nickel particles on wear resistance and high temperature oxidation resistance of ultrafine ceramic coating

In order to improve the wear resistance and high temperature oxidation resistance of titanium and titanium alloy, the high temperature ultra fine ceramic coating containing nano-size nickel particles was prepared by flow coat method on the surface of industrially pure titanium TB1-0. The effects of nano-size nickel particles on the wear resistance and high temperature oxidation resistance of coating substrate system were investigated through oxidation kinetics experiment and wear resistance test. The morphologies of the specimens were examined by means of optical microscopy, scanning electron microscopy and X-ray diffraction. The results show that the high temperature ultra fine ceramic coating has notable protection effect on industrially pure titanium TB1-0 from oxidation. The oxidation and wear resistance properties of the coating can be effectively improved by adding nano-size nickel particles. The oxidative mass gain of the specimen decreases from 11.33 mg·cm-2 to 5.25 mg·cm-2 and the friction coefficient decreases from 1.1 to 0.6 by adding nano-size nickel particles, and the coating containing 10% （mass fraction） nano-size nickel shows the optimum properties.