To make clear the wear conditions of ATM (Automatic Teller Machine) tribosystem when servicing in Chi- nese sand dust environment, abrasive wear of two kinds of polymer tapes specified for ATM, PI (Polyimide) and PEN ...To make clear the wear conditions of ATM (Automatic Teller Machine) tribosystem when servicing in Chi- nese sand dust environment, abrasive wear of two kinds of polymer tapes specified for ATM, PI (Polyimide) and PEN (Polyethylene-2, 6-naphthalenedicarboxylate), was investigated in simulated sand dust environment with ATM tape-scraper tribosystem under various conditions of loads and sliding distances. The surface profiles of worn tape were measured with a surface profiler in order to calculating the wear cross-section areas and the wear volumes. The specific wear rates of polymer tapes were calculated under load conditions of 0.6, 1 and 1.5 N, and wear mechanisms were in- vestigated with optical topography photos. As main results, the specific wear rates show stage variations in the wear process and the wear resistance of polymer tape shows good relationship with the mechanical deformation factors. In consideration of the service life, four wear models are generalized according to the magnitude of specific wear rates, which include no wear, mild wear, normal wear and severe wear model and the corresponding wear mechanisms for the four wear models are discussed with typical worn topographies. Based on the wear models and corresponding wear mechanisms, the abrasive wear maps of two polymer tapes servicing in sand dust environments are concluded for its industrial applications.展开更多
In this research, the effect of precipitation hardening on the tribological behavior of the ZK60Gd/SiC composite was studied. For this purpose, ZK60Gd alloy containing with 5 and 10 wt% SiC were produced with stir cas...In this research, the effect of precipitation hardening on the tribological behavior of the ZK60Gd/SiC composite was studied. For this purpose, ZK60Gd alloy containing with 5 and 10 wt% SiC were produced with stir casting method. The microstructure characterization of the samples showed the wide distributions of Mg_(7)Zn_(3) and Gd(Mg_(0.5)Zn_(0.5)) precipitates were formed during casting. The results of hardness measurement after precipitation hardening at different temperatures showed that the hardness peck was obtained at 175 ℃. The wear tests with different loads(10, 40, 60, 90, and 120 N) and velocities(0.1, 0.3, 0.6, and 0.9 m/s) were performed on the as-cast and heat treated sample at 125, 175, and 225 for 12 h. Between the different precipitation hardening conditions, the precipitation hardened samples at 175 ℃ had the highest hardness values and least wear rate. The sample containing 10% reinforcement had the least wear rate between the unreinforced alloy and the composites. The results showed that abrasive, adhesive, delamination, MML, and fatigue wear mechanisms were the dominant wear mechanisms for the composite samples. In contrast, the dominant wear mechanism for the unreinforced samples was abrasive, adhesive,delamination, MML, and plastic deformation.展开更多
基金Project 59974030 supported by National Natural Science Foundation of China and by Mechanical Engineering Research Laboratory, Hitachi Ltd of Japan
文摘To make clear the wear conditions of ATM (Automatic Teller Machine) tribosystem when servicing in Chi- nese sand dust environment, abrasive wear of two kinds of polymer tapes specified for ATM, PI (Polyimide) and PEN (Polyethylene-2, 6-naphthalenedicarboxylate), was investigated in simulated sand dust environment with ATM tape-scraper tribosystem under various conditions of loads and sliding distances. The surface profiles of worn tape were measured with a surface profiler in order to calculating the wear cross-section areas and the wear volumes. The specific wear rates of polymer tapes were calculated under load conditions of 0.6, 1 and 1.5 N, and wear mechanisms were in- vestigated with optical topography photos. As main results, the specific wear rates show stage variations in the wear process and the wear resistance of polymer tape shows good relationship with the mechanical deformation factors. In consideration of the service life, four wear models are generalized according to the magnitude of specific wear rates, which include no wear, mild wear, normal wear and severe wear model and the corresponding wear mechanisms for the four wear models are discussed with typical worn topographies. Based on the wear models and corresponding wear mechanisms, the abrasive wear maps of two polymer tapes servicing in sand dust environments are concluded for its industrial applications.
文摘In this research, the effect of precipitation hardening on the tribological behavior of the ZK60Gd/SiC composite was studied. For this purpose, ZK60Gd alloy containing with 5 and 10 wt% SiC were produced with stir casting method. The microstructure characterization of the samples showed the wide distributions of Mg_(7)Zn_(3) and Gd(Mg_(0.5)Zn_(0.5)) precipitates were formed during casting. The results of hardness measurement after precipitation hardening at different temperatures showed that the hardness peck was obtained at 175 ℃. The wear tests with different loads(10, 40, 60, 90, and 120 N) and velocities(0.1, 0.3, 0.6, and 0.9 m/s) were performed on the as-cast and heat treated sample at 125, 175, and 225 for 12 h. Between the different precipitation hardening conditions, the precipitation hardened samples at 175 ℃ had the highest hardness values and least wear rate. The sample containing 10% reinforcement had the least wear rate between the unreinforced alloy and the composites. The results showed that abrasive, adhesive, delamination, MML, and fatigue wear mechanisms were the dominant wear mechanisms for the composite samples. In contrast, the dominant wear mechanism for the unreinforced samples was abrasive, adhesive,delamination, MML, and plastic deformation.