Pure copper plates were coated by Ni-TiC dipulse current plating method. The effects of adding different concentration（ranging from 0.5 g/L to 3.0 g/L） of attapulgite nano particles to the plating bath on the surfac...Pure copper plates were coated by Ni-TiC dipulse current plating method. The effects of adding different concentration（ranging from 0.5 g/L to 3.0 g/L） of attapulgite nano particles to the plating bath on the surface morphology, wear resistance, and oxidation resistance of Ni/TiC/Attapulgite nano-composite coatings were investigated. The experimental results show that the composite coating is flat and compact with adding 3.0 g/L in the bath, and the coating preferred orientation is changed from the planes（111） to（200）. The coefficient of the composite coatings decreases from 0.68 to 0.18 with increasing content of attapulgite in the bath, a mixed mode of adhesive-abrasive wear occurs for all coatings, and the wear mechanism shows a transition from adhesive-abrasive to predominantly abrasive wear mechanism when the concentration of attapulgite is beyond 1.5 g/L in electrolyte. The oxidation resistance of composite coatings is the best prepared when adding attapulgite particles at 0.5 g/L in the bath, the oxide mainly consists of a NiO phase by X-ray analysis.展开更多
A novel approach to produce an intermetallic composite coating was put forward.The microstructure,microhardness,and dry-sliding wear behavior of the composite coating were investigated using X-ray diffraction （XRD）,...A novel approach to produce an intermetallic composite coating was put forward.The microstructure,microhardness,and dry-sliding wear behavior of the composite coating were investigated using X-ray diffraction （XRD）,scanning electron microscopy （SEM）,energy dispersive spectrum （EDS） analysis,microhardness test,and ball-on-disc wear experiment.XRD results indicate that some new phases FeAl,Fe0.23Ni0.77Al,and Ni3Al exit in the composite coating with the Al2O3 addition.SEM results show that the coating is bonded with carbon steel metallurgically and exhibits typical rapid directional solidification structures.The Cr7C3 carbide and intermetallic compounds co-reinforced composite coating has a high average hardness and exhibits an excellent wear resistance under dry-sliding wear test compared with the Cr7C3 carbide-reinforced composite coating.The formation mechanism of the intermetallic compounds was also investigated.展开更多
基金Founded by the National Natural Youth Science Fundation of China(51301086)the Scientific Research Fund of Nanjing Institute of Technology Doctoral(N20130222 and CKJB201205)the Nanjing Institute of Technology,China
文摘Pure copper plates were coated by Ni-TiC dipulse current plating method. The effects of adding different concentration（ranging from 0.5 g/L to 3.0 g/L） of attapulgite nano particles to the plating bath on the surface morphology, wear resistance, and oxidation resistance of Ni/TiC/Attapulgite nano-composite coatings were investigated. The experimental results show that the composite coating is flat and compact with adding 3.0 g/L in the bath, and the coating preferred orientation is changed from the planes（111） to（200）. The coefficient of the composite coatings decreases from 0.68 to 0.18 with increasing content of attapulgite in the bath, a mixed mode of adhesive-abrasive wear occurs for all coatings, and the wear mechanism shows a transition from adhesive-abrasive to predominantly abrasive wear mechanism when the concentration of attapulgite is beyond 1.5 g/L in electrolyte. The oxidation resistance of composite coatings is the best prepared when adding attapulgite particles at 0.5 g/L in the bath, the oxide mainly consists of a NiO phase by X-ray analysis.
文摘A novel approach to produce an intermetallic composite coating was put forward.The microstructure,microhardness,and dry-sliding wear behavior of the composite coating were investigated using X-ray diffraction （XRD）,scanning electron microscopy （SEM）,energy dispersive spectrum （EDS） analysis,microhardness test,and ball-on-disc wear experiment.XRD results indicate that some new phases FeAl,Fe0.23Ni0.77Al,and Ni3Al exit in the composite coating with the Al2O3 addition.SEM results show that the coating is bonded with carbon steel metallurgically and exhibits typical rapid directional solidification structures.The Cr7C3 carbide and intermetallic compounds co-reinforced composite coating has a high average hardness and exhibits an excellent wear resistance under dry-sliding wear test compared with the Cr7C3 carbide-reinforced composite coating.The formation mechanism of the intermetallic compounds was also investigated.