This paper was to develop a weft-knitted stent coated by a drug-loaded electro-spun fibrous membrane and then investigate its morphology, mechanical properties and in vitro drug release property. This work was started...This paper was to develop a weft-knitted stent coated by a drug-loaded electro-spun fibrous membrane and then investigate its morphology, mechanical properties and in vitro drug release property. This work was started by weft-knitting of an inner layer of such stent using polydioxanone( PDO) and silkfilament.Subsequently,5-fluorouracil( 5-FU) and curcumin( CUR) ioaded silk fibroin( SF) membranes were coated on the surface of the weftknitted stent using electro-spinning technique to endow the drug delivery function of the stent. The results show that the radial compression strength and circumferential expanding strength can reach above( 9. 1 ± 0. 4) cN/cm^2 and( 205. 0 ± 0. 2) c N/mm,respectively. The drug releasing behaviors can be sustained for 400 h. It is concluded that the stents have potential application as anintestinal stent in the future.展开更多
The work investigated surface and mechanical properties of untreated and treated three-layered weftknitted spacer fabrics.In order to optimize the mechanical properties of weft-knitted spacer fabrics,silica aerogels(S...The work investigated surface and mechanical properties of untreated and treated three-layered weftknitted spacer fabrics.In order to optimize the mechanical properties of weft-knitted spacer fabrics,silica aerogels(SAs)coating was employed.Scanning electron microscopy(SEM)images of untreated and treated spacer fabrics were analyzed to ensure the presence of SAs on the coated spacer fabrics.The basic properties of uncoated and coated weftknitted spacer fabrics were studied and compared.Tensile strength and initial modulus were studied according to the GB/T3923 test standard YG026 MB-250 by testing machine.Moreover,compression properties of spacer fabrics were also tested by HD026 G test instrument.In this testing,work of compression,the linearity of compression,recovery work of compression and other parameters were calculated from stress and strain curves.It was found that SAs coating has a significant influence on the mechanical properties of weftknitted spacer fabrics.The statistical analysis also verified the significant performance(P value smaller than 0.05)of treated fabric samples at the 0.05 level.展开更多
In this paper the significance analysis has been made of the factors influencing the yarn appearing of single plated weft-knit fabrics knitted on large diameter machine by a mathematical statistical method. By means o...In this paper the significance analysis has been made of the factors influencing the yarn appearing of single plated weft-knit fabrics knitted on large diameter machine by a mathematical statistical method. By means of orthogonal test and variance analysis, it is known that the feeding tension is the significant factor influencing the yarn appearance and the ground yarn tension should be larger than the face yarn tension. Through comparison, it is also known that the drawing off force should be regulated suitably, the carrier should be near the first closed needle, and the sinker should be out late slightly.展开更多
基金National Natural Science Foundation of China(No.51603140)Natural Science Foundation of Jiangsu Province,China(No.BK20150372)+2 种基金University Science Research Project of Jiangsu Province,China(No.16KJB540003)Key Industry Technology Innovation,Science and Technology Project of Suzhou,China(No.SYG201638)Sino-Germany Joint Project,China(No.GZ1094)
文摘This paper was to develop a weft-knitted stent coated by a drug-loaded electro-spun fibrous membrane and then investigate its morphology, mechanical properties and in vitro drug release property. This work was started by weft-knitting of an inner layer of such stent using polydioxanone( PDO) and silkfilament.Subsequently,5-fluorouracil( 5-FU) and curcumin( CUR) ioaded silk fibroin( SF) membranes were coated on the surface of the weftknitted stent using electro-spinning technique to endow the drug delivery function of the stent. The results show that the radial compression strength and circumferential expanding strength can reach above( 9. 1 ± 0. 4) cN/cm^2 and( 205. 0 ± 0. 2) c N/mm,respectively. The drug releasing behaviors can be sustained for 400 h. It is concluded that the stents have potential application as anintestinal stent in the future.
文摘The work investigated surface and mechanical properties of untreated and treated three-layered weftknitted spacer fabrics.In order to optimize the mechanical properties of weft-knitted spacer fabrics,silica aerogels(SAs)coating was employed.Scanning electron microscopy(SEM)images of untreated and treated spacer fabrics were analyzed to ensure the presence of SAs on the coated spacer fabrics.The basic properties of uncoated and coated weftknitted spacer fabrics were studied and compared.Tensile strength and initial modulus were studied according to the GB/T3923 test standard YG026 MB-250 by testing machine.Moreover,compression properties of spacer fabrics were also tested by HD026 G test instrument.In this testing,work of compression,the linearity of compression,recovery work of compression and other parameters were calculated from stress and strain curves.It was found that SAs coating has a significant influence on the mechanical properties of weftknitted spacer fabrics.The statistical analysis also verified the significant performance(P value smaller than 0.05)of treated fabric samples at the 0.05 level.
文摘In this paper the significance analysis has been made of the factors influencing the yarn appearing of single plated weft-knit fabrics knitted on large diameter machine by a mathematical statistical method. By means of orthogonal test and variance analysis, it is known that the feeding tension is the significant factor influencing the yarn appearance and the ground yarn tension should be larger than the face yarn tension. Through comparison, it is also known that the drawing off force should be regulated suitably, the carrier should be near the first closed needle, and the sinker should be out late slightly.