Composition and service properties of high - strength low-alloyed steels with 590-980 MPa yield strength,which find an application in Russia, Belorus,Ukraine and other countries of the former USSR in manufacture of w...Composition and service properties of high - strength low-alloyed steels with 590-980 MPa yield strength,which find an application in Russia, Belorus,Ukraine and other countries of the former USSR in manufacture of welded structures of a powerful mining and transport machinery, are given. Electrodes and wires for main processes of arc welding of these steels have been devel- oped on the basis of a rational use of different systems of alloying (08KhN2GM,08KhNG2M, and also economical systems of type 10G25, ect. ). Main approaches to the technological provess- es of manufacture of structures of high - strength steels are formulated.They are mainly directed to the weakening of de offect of the factors which contribute to a delayed fracture of joints (diffusive hydrogen,unfavourable rates of cooling,level of residual stresses). When there are no stress concentrators (and at a low level of residual stresses) the welded joints of these steels have a good resistance to fatigue and brittle fractures.As a rule, they are prevented with the help of the known approaches.It is shown that in addition to them and due to a proper selection of conditions of welding the life of welded joints of the high - strength steels can be 1. 2 - 1. 4 times in- creased.展开更多
Effects of molten state of ultrasonic welded joints of plastics on their strength were investigated. Physical parameters such as temperature, viscosity and thickness of melting layers of plastic material joints were m...Effects of molten state of ultrasonic welded joints of plastics on their strength were investigated. Physical parameters such as temperature, viscosity and thickness of melting layers of plastic material joints were measured and analyzed. Results show that when the welding vibration amplitude and pressure increase, the temperature increases, the viscosity decreases, and the thickness of molten layer decreases. The microstructure of weld fusion zone was observed by using an optical microscope. It was found that there is strong orientation along transverse direction in the microstructure of fusion zone. Testing results show that the mechanics performance of welded joints are obviously anisotropic, and strongly affected by the thickness of molten layer and the extent of orientation.展开更多
文摘Composition and service properties of high - strength low-alloyed steels with 590-980 MPa yield strength,which find an application in Russia, Belorus,Ukraine and other countries of the former USSR in manufacture of welded structures of a powerful mining and transport machinery, are given. Electrodes and wires for main processes of arc welding of these steels have been devel- oped on the basis of a rational use of different systems of alloying (08KhN2GM,08KhNG2M, and also economical systems of type 10G25, ect. ). Main approaches to the technological provess- es of manufacture of structures of high - strength steels are formulated.They are mainly directed to the weakening of de offect of the factors which contribute to a delayed fracture of joints (diffusive hydrogen,unfavourable rates of cooling,level of residual stresses). When there are no stress concentrators (and at a low level of residual stresses) the welded joints of these steels have a good resistance to fatigue and brittle fractures.As a rule, they are prevented with the help of the known approaches.It is shown that in addition to them and due to a proper selection of conditions of welding the life of welded joints of the high - strength steels can be 1. 2 - 1. 4 times in- creased.
基金the National Natural Science Foundation of China (No.59675054) andNational Key Laboratory of Advanced Welding Production Techn
文摘Effects of molten state of ultrasonic welded joints of plastics on their strength were investigated. Physical parameters such as temperature, viscosity and thickness of melting layers of plastic material joints were measured and analyzed. Results show that when the welding vibration amplitude and pressure increase, the temperature increases, the viscosity decreases, and the thickness of molten layer decreases. The microstructure of weld fusion zone was observed by using an optical microscope. It was found that there is strong orientation along transverse direction in the microstructure of fusion zone. Testing results show that the mechanics performance of welded joints are obviously anisotropic, and strongly affected by the thickness of molten layer and the extent of orientation.