A two-step leaching method in combination of acid and ethylene diaminetetraacetic acid disodium (EDTA-Na2) was applied to extract metals such as Cd,Cu,Fe,Pb and Zn from a zinc smelting slag. The results show that the ...A two-step leaching method in combination of acid and ethylene diaminetetraacetic acid disodium (EDTA-Na2) was applied to extract metals such as Cd,Cu,Fe,Pb and Zn from a zinc smelting slag. The results show that the extraction rates of Cd,Cu,Fe and Zn in slag reach 88.3%,54.1%,69.6% and 54.7%,respectively,while the extraction rate of Pb is only 0.05% leached with 1.25 mol/L sulfuric acid under the conditions of the ratio of slag to liquid of 100 g/L,65 °C and 120 r/min for 2 h. However,Pb extraction rate from 1.25 mol/L sulfuric acid leached residue reaches as high as 66.5% by using 0.1 mol/L EDTA-Na2 solution. The results indicate that two-step sequential extraction procedure combining 1.25 mol/L sulfuric acid and 0.1 mol/L EDTA-Na2 solution can extensively extract Cd,Cu,Fe,Pb and Zn from zinc smelting slag.展开更多
Germanium(Ge),a waste residue leaching from zinc(Zn)smelting process,has potential cementitious properties and could be recycled as a cement supplement activated by chemical reagents.In this work,a test was conducted ...Germanium(Ge),a waste residue leaching from zinc(Zn)smelting process,has potential cementitious properties and could be recycled as a cement supplement activated by chemical reagents.In this work,a test was conducted to determine the hydration properties of Ge slag-cement-based composites with Ge slag(GS)/ordinary Portland cement(PC)contents of 0wt%,5wt%,10wt%,15wt%,20wt%,and 25wt% and water-to-binder ratio(w/b)of 0.4.The activators Ca(OH)2,AlCl3,NaAlO2,and Na2CO3 were mixed under 1wt%,2wt%,3wt%,and 4wt% dosages of GS weight.The composition and microstructure of the hydration products were investigated by the combined approaches of X-ray diffraction(XRD),thermogravimetry-differential scanning calorimetry(TG-DSC),scanning electron microscopy(SEM),and energy-dispersive X-ray spectroscopy(EDS).First,the GS cementitious property is attributed to the high content of CaSO4·2H2O.Second,the activators affected the acceleration performance in the following order:NaAlO2,Na2CO3,AlCl3,and Ca(OH)2.More importantly,the 28-day unconfined compressive strength(UCS)is 45.34 MPa at the optimum formula of 0.6wt% NaAlO2,15wt% GS,and 85wt% PC,which is 9.16% higher than the control.Thus,NaAlO2 is beneficial for the ettringite(AFt)generation,resulting in the C-S-H structure compaction.However,the Zn^2+ residue inhibited the AFt formation,representing an important challenge to the strength growth with curing age.Consequently,the GS could be recycled as a supplement to the cement under the activator NaAlO2.展开更多
An efficient approach for lead extraction from waste funnel glass through the lead smelting process has been proposed. To clarify the effect of funnel glass addition on the degradation of magnesia-chromite refractorie...An efficient approach for lead extraction from waste funnel glass through the lead smelting process has been proposed. To clarify the effect of funnel glass addition on the degradation of magnesia-chromite refractories by ZnO-containing fayalite slag, the corrosion behavior of magnesia-chromite refractories in lead smelting slags with different funnel glass additions from 0wt% to 40wt% was tested. Scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) was used to acquire the microstructural information of the worn refractory samples. Experimental results showed that the corrosion of magnesia-chromite refractory consisted predominantly of the dissolution of MgO into slag. ZnO and FeO reacted with periclase and chromite to form (Zn,Fe,Mg)O solid solution and (Zn,Fe,Mg)(Fe,Al,Cr)2O4 spinel, respectively. With the addition of funnel glass, the solubility of MgO increased whereas ZnO levels remained stable, thereby resulting in a reduced Mg content and an elevated Zn and Fe content in the (Zn,Fe,Mg)O solid solution and the (Zn,Fe,Mg)(Fe,Al,Cr)2O4 spinel. Considering the stability of the (Zn,Fe,Mg)O solid solution layer and the penetration depth of the slag, the optimal funnel glass addition for lead smelting was found to be 20wt%.展开更多
基金Project(2011SK3262) supported by Science and Technology Program of Hunan Province,China
文摘A two-step leaching method in combination of acid and ethylene diaminetetraacetic acid disodium (EDTA-Na2) was applied to extract metals such as Cd,Cu,Fe,Pb and Zn from a zinc smelting slag. The results show that the extraction rates of Cd,Cu,Fe and Zn in slag reach 88.3%,54.1%,69.6% and 54.7%,respectively,while the extraction rate of Pb is only 0.05% leached with 1.25 mol/L sulfuric acid under the conditions of the ratio of slag to liquid of 100 g/L,65 °C and 120 r/min for 2 h. However,Pb extraction rate from 1.25 mol/L sulfuric acid leached residue reaches as high as 66.5% by using 0.1 mol/L EDTA-Na2 solution. The results indicate that two-step sequential extraction procedure combining 1.25 mol/L sulfuric acid and 0.1 mol/L EDTA-Na2 solution can extensively extract Cd,Cu,Fe,Pb and Zn from zinc smelting slag.
基金financially supported by the National Natural Science Foundation of China (Nos. 51701094, 51834001, and 51574013)the key projects for the prevention and control of major accidents in safety production, China (No. Henan-0005-2016AQ)the Plan for Scientific Innovation Talent of Henan Province (No. 194200510010)
文摘Germanium(Ge),a waste residue leaching from zinc(Zn)smelting process,has potential cementitious properties and could be recycled as a cement supplement activated by chemical reagents.In this work,a test was conducted to determine the hydration properties of Ge slag-cement-based composites with Ge slag(GS)/ordinary Portland cement(PC)contents of 0wt%,5wt%,10wt%,15wt%,20wt%,and 25wt% and water-to-binder ratio(w/b)of 0.4.The activators Ca(OH)2,AlCl3,NaAlO2,and Na2CO3 were mixed under 1wt%,2wt%,3wt%,and 4wt% dosages of GS weight.The composition and microstructure of the hydration products were investigated by the combined approaches of X-ray diffraction(XRD),thermogravimetry-differential scanning calorimetry(TG-DSC),scanning electron microscopy(SEM),and energy-dispersive X-ray spectroscopy(EDS).First,the GS cementitious property is attributed to the high content of CaSO4·2H2O.Second,the activators affected the acceleration performance in the following order:NaAlO2,Na2CO3,AlCl3,and Ca(OH)2.More importantly,the 28-day unconfined compressive strength(UCS)is 45.34 MPa at the optimum formula of 0.6wt% NaAlO2,15wt% GS,and 85wt% PC,which is 9.16% higher than the control.Thus,NaAlO2 is beneficial for the ettringite(AFt)generation,resulting in the C-S-H structure compaction.However,the Zn^2+ residue inhibited the AFt formation,representing an important challenge to the strength growth with curing age.Consequently,the GS could be recycled as a supplement to the cement under the activator NaAlO2.
基金financially supported by the National Key R&D Program of China (No. 2018YFC1902004)the National Natural Science Foundation of China (No. U1608254)+1 种基金the Project for Guangdong Collaborative Innovation and Platform Environment Building (No. 2017B090904035)the Special Project for Key Laboratory of Guangdong Science and Technology Department, China (No. 2017B030314046)
文摘An efficient approach for lead extraction from waste funnel glass through the lead smelting process has been proposed. To clarify the effect of funnel glass addition on the degradation of magnesia-chromite refractories by ZnO-containing fayalite slag, the corrosion behavior of magnesia-chromite refractories in lead smelting slags with different funnel glass additions from 0wt% to 40wt% was tested. Scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM-EDS) was used to acquire the microstructural information of the worn refractory samples. Experimental results showed that the corrosion of magnesia-chromite refractory consisted predominantly of the dissolution of MgO into slag. ZnO and FeO reacted with periclase and chromite to form (Zn,Fe,Mg)O solid solution and (Zn,Fe,Mg)(Fe,Al,Cr)2O4 spinel, respectively. With the addition of funnel glass, the solubility of MgO increased whereas ZnO levels remained stable, thereby resulting in a reduced Mg content and an elevated Zn and Fe content in the (Zn,Fe,Mg)O solid solution and the (Zn,Fe,Mg)(Fe,Al,Cr)2O4 spinel. Considering the stability of the (Zn,Fe,Mg)O solid solution layer and the penetration depth of the slag, the optimal funnel glass addition for lead smelting was found to be 20wt%.