The effect of Eu-substitution on the density and thermoelectric properties of ternary sulfide Ce3-xEuxS4 (0≤x≤0.8) compacts was investigated. Ce3-xEuxS4 powders were prepared via the sulfurization of the oxide usi...The effect of Eu-substitution on the density and thermoelectric properties of ternary sulfide Ce3-xEuxS4 (0≤x≤0.8) compacts was investigated. Ce3-xEuxS4 powders were prepared via the sulfurization of the oxide using CS2 gas at 1473 K. The pressureless sintered Ce3-xEuxS4 compacts in the atmosphere were crystallized in the T-phase. The density of the Ce3-xEuxS4 compacts increased with the increasing of Eu-substitution. Eu-substitution yielded a higher Seebeck coefficient and lower electrical resistivity. The highest value of the thermoelectric power factor of 1.41×10^-4 W/K^2m was obtained for the Ce2.2Eu0.8S4 compact at 673 K. It indicated that Eu-substitution was effective for improving thermoelectric properties of Ce3-xEuxS4.展开更多
In order to confirm the relationship between the luminescence and the ratio of Ce3+/Ce4+ more clearly, a series of YAG:Ce3+ (Yttrium Aluminum Garnet, Y2.94Al5O12:0.06Ce3+) phosphors were pre- pared under different sin...In order to confirm the relationship between the luminescence and the ratio of Ce3+/Ce4+ more clearly, a series of YAG:Ce3+ (Yttrium Aluminum Garnet, Y2.94Al5O12:0.06Ce3+) phosphors were pre- pared under different sintering atmosphere. A semi-quantitative analysis based on X-ray photoe-lectron spectroscopy (XPS) was introduced to study the mole ratio of Ce3+/Ce4+ in the as-synthesized YAG:Ce3+ phosphors. The results indicated that the percentage of Ce3+/(Ce3+ + Ce4+) reached 88.46% under the reduction atmosphere. The emission intensity of YAG:Ce3+ phosphors was in-creased significantly with the increasing of Ce3+ concentration.展开更多
ZHOU Bai-Bin *,1,2 WEI Yong-De 1 LI Zhong-Hua 1 ( 1 Department of Applied Chemistry,Ha rbin Institute of Technology £?Harbin£±£ì£°£°£°£±£(c)( 2 Department of Chemistry,Harbin Norm...ZHOU Bai-Bin *,1,2 WEI Yong-De 1 LI Zhong-Hua 1 ( 1 Department of Applied Chemistry,Ha rbin Institute of Technology £?Harbin£±£ì£°£°£°£±£(c)( 2 Department of Chemistry,Harbin Normal University£?Harbin£±£ì£°£°£?£°£(c) The air-solid interface reaction of Ce,Lu with K10 H 3[Gd (SiMo 4 W£*O£3£1£(c) 2]through chemistry-heated permeation is reported for the fi rst time£(r)The permeated complex is characterized by ICP and the result shows tha t the mini mum Ce,Lu can permeate into the inner sph ere of K 10 H £3 £?Gd £¨SiMo £′ W £* O £3£1 £(c) 2]The IR ,XRD patterns give the eviden ce that after permeation the comple x still keeps the Keggin structure,howe ver,its crystal structure is different from the complex before permeation£(r)The cond uctivity of the permeated complex has been measured with the four-electr ode method and the data show that the co nductivity of the complex after permeation is 10 6 times higher than that of the sample before permeation and reaches £′£(r)84 6×10 -1 S·cm -1 £(r)These indicate that the permeated c omplex is a good solid electrolyte and further appli cations are also expected£(r)展开更多
Atom economy of the process of rare earth separation by using fluoride was discussed in this paper.We compared the atomic economic characters between the processes of vitriolic composite salt and fluoride,then stated ...Atom economy of the process of rare earth separation by using fluoride was discussed in this paper.We compared the atomic economic characters between the processes of vitriolic composite salt and fluoride,then stated that changing present rare earth producing process by green chemistry and technology transformation was the best way to make our rare earth manufacture prosperous.展开更多
基金supported by the National Natural Science Foundation of China (20501023)the National "863" Project Foundation of China (2004AA001340)the Nature Science Foundation of Guangdong for Doctorial Training base (5300527)
文摘The effect of Eu-substitution on the density and thermoelectric properties of ternary sulfide Ce3-xEuxS4 (0≤x≤0.8) compacts was investigated. Ce3-xEuxS4 powders were prepared via the sulfurization of the oxide using CS2 gas at 1473 K. The pressureless sintered Ce3-xEuxS4 compacts in the atmosphere were crystallized in the T-phase. The density of the Ce3-xEuxS4 compacts increased with the increasing of Eu-substitution. Eu-substitution yielded a higher Seebeck coefficient and lower electrical resistivity. The highest value of the thermoelectric power factor of 1.41×10^-4 W/K^2m was obtained for the Ce2.2Eu0.8S4 compact at 673 K. It indicated that Eu-substitution was effective for improving thermoelectric properties of Ce3-xEuxS4.
文摘In order to confirm the relationship between the luminescence and the ratio of Ce3+/Ce4+ more clearly, a series of YAG:Ce3+ (Yttrium Aluminum Garnet, Y2.94Al5O12:0.06Ce3+) phosphors were pre- pared under different sintering atmosphere. A semi-quantitative analysis based on X-ray photoe-lectron spectroscopy (XPS) was introduced to study the mole ratio of Ce3+/Ce4+ in the as-synthesized YAG:Ce3+ phosphors. The results indicated that the percentage of Ce3+/(Ce3+ + Ce4+) reached 88.46% under the reduction atmosphere. The emission intensity of YAG:Ce3+ phosphors was in-creased significantly with the increasing of Ce3+ concentration.
文摘ZHOU Bai-Bin *,1,2 WEI Yong-De 1 LI Zhong-Hua 1 ( 1 Department of Applied Chemistry,Ha rbin Institute of Technology £?Harbin£±£ì£°£°£°£±£(c)( 2 Department of Chemistry,Harbin Normal University£?Harbin£±£ì£°£°£?£°£(c) The air-solid interface reaction of Ce,Lu with K10 H 3[Gd (SiMo 4 W£*O£3£1£(c) 2]through chemistry-heated permeation is reported for the fi rst time£(r)The permeated complex is characterized by ICP and the result shows tha t the mini mum Ce,Lu can permeate into the inner sph ere of K 10 H £3 £?Gd £¨SiMo £′ W £* O £3£1 £(c) 2]The IR ,XRD patterns give the eviden ce that after permeation the comple x still keeps the Keggin structure,howe ver,its crystal structure is different from the complex before permeation£(r)The cond uctivity of the permeated complex has been measured with the four-electr ode method and the data show that the co nductivity of the complex after permeation is 10 6 times higher than that of the sample before permeation and reaches £′£(r)84 6×10 -1 S·cm -1 £(r)These indicate that the permeated c omplex is a good solid electrolyte and further appli cations are also expected£(r)
文摘Atom economy of the process of rare earth separation by using fluoride was discussed in this paper.We compared the atomic economic characters between the processes of vitriolic composite salt and fluoride,then stated that changing present rare earth producing process by green chemistry and technology transformation was the best way to make our rare earth manufacture prosperous.