Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nano...Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.展开更多
The solubilities of Cs 2 SO 4 -C 2 H 5 OH-H 2 O ternary system at 30℃and 50℃have been studied using microe-quipment for solubility determination.There appears two phases,alcoh olic phase,water phase in the liquid ph...The solubilities of Cs 2 SO 4 -C 2 H 5 OH-H 2 O ternary system at 30℃and 50℃have been studied using microe-quipment for solubility determination.There appears two phases,alcoh olic phase,water phase in the liquid phase.The solubilities of Cs 2 SO 4 in water,C 2 H 5 OH and mixed solvent have been determ ined.The phase diagram indicated that C 2 H 5 OH might be salted out by Cs 2 SO 4 from this system and the equilibrium solid phase is Cs 2 SO 4 .展开更多
The new mixed borates with formula(Rb 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O and Cs 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O)were prepared by reaction Rb (Cs )-borate aqueous solution with CaCl 2 .Two kinds of compounds w...The new mixed borates with formula(Rb 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O and Cs 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O)were prepared by reaction Rb (Cs )-borate aqueous solution with CaCl 2 .Two kinds of compounds were characterized by chemical analysis,X-ray powder dif fraction,FT-IR spectra and thermal analysis.展开更多
PhCH2)3Sn·(O2CC5H4N)·(H2O)]n was synthesized by the reaction of 4-pyridine car-boxylic acid with the tribenzyltin o xide and was characterized by IR,1 H NMR and MS.Its crystal structure was determined by X-r...PhCH2)3Sn·(O2CC5H4N)·(H2O)]n was synthesized by the reaction of 4-pyridine car-boxylic acid with the tribenzyltin o xide and was characterized by IR,1 H NMR and MS.Its crystal structure was determined by X-ray single crystal diffraction.The crystal belongs to monoclinic.The space group P21 /c with unit cell parameters a=1.2241(8)nm,b=0.9660(6)nm,c=2.3708(15)nm,β=102.722(12)°,V=2.734(3)nm3,Z =4,Dc=1.298g·cm-3 .In crystal,the tin atom rendered five-coordinate in a trigo nal bipyramidal structure which is b ridged by 4-pyridine carboxy-late into one-dimensional chain polymers.展开更多
Two new Gd Ⅲ complexes with nitrilotriacetic acid(nta) and trans-1,2-cyclohexanediaminetetraacetic acid(Cydta) ligands were synthesized. Their crystal structures were determined by single-crystal X-ray structure anal...Two new Gd Ⅲ complexes with nitrilotriacetic acid(nta) and trans-1,2-cyclohexanediaminetetraacetic acid(Cydta) ligands were synthesized. Their crystal structures were determined by single-crystal X-ray structure analyses. The crystal data are as follows: K 3[Gd Ⅲ(nta) 2·(H 2O)]·6H 2O, monoclinic system, C2/c space group, a=1.534 81(15) nm, b=1.292 05(12) nm, c=2.610 8(3) nm, β=96.244(2)°, V=5.146 7(9) nm 3, Z=8, M=776.87, D c=2.005 g/cm 3, μ= 3.149 mm -1 and \{F(000)=\}3 080, R=0.024 5, wR=0.064 3 for 4 455 unique reflections and R= 0.028 9, wR=0.067 2 for all 10 305 reflections. The Gd ⅢN 2O 7 part in the [Gd Ⅲ(nta) 2(H 2O)] 3- anion is a pseudo-monocapped square antiprismatic nine-coordination structure.(NH 4)[Gd Ⅲ(Cydta)(H 2O) 2]·5H 2O, triclinic system, P1 space group, a=0.866 2(3) nm, b=1.006 7(3) nm, c= 1.444 8(5) nm, α= 88.282(5)°, β=75\^190(5)°, γ=88.317(4)°, V=1.217 2(7) nm 3, Z=2, M=643.69, D c=1.756 g/cm 3, μ=2.798 mm -1 and F(000)=650, R=0.030 3, wR=0.080 9 for 4 273 unique reflections and R=0.033 2, wR=0.082 5 for all 5 062 reflections. The Gd ⅢN 2O 6 part in the [Gd Ⅲ(Cydta)(H 2O) 2] - anion has a pseudo-square antiprismatic eight-coordination structure.展开更多
The two new compounds Cs5EuCl8· 14H2O(5∶ 1 type) and Cs2EuCl5· 4H2O(2∶ 1 type) were found and synthesized from CsCl EuCl3 11% HCl H2O quaternary systems by phase equilibrium method, and were characterized ...The two new compounds Cs5EuCl8· 14H2O(5∶ 1 type) and Cs2EuCl5· 4H2O(2∶ 1 type) were found and synthesized from CsCl EuCl3 11% HCl H2O quaternary systems by phase equilibrium method, and were characterized and measured by ultra violet absorption spectrometry and fluorescence spectrum. The results show that upconversion spectrum exhibit at 590nm and 610nm exited at 790nm, and the upconversion intensity increases with the EuCl3 ratio increasing in CsCl.展开更多
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.
文摘Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.
文摘The solubilities of Cs 2 SO 4 -C 2 H 5 OH-H 2 O ternary system at 30℃and 50℃have been studied using microe-quipment for solubility determination.There appears two phases,alcoh olic phase,water phase in the liquid phase.The solubilities of Cs 2 SO 4 in water,C 2 H 5 OH and mixed solvent have been determ ined.The phase diagram indicated that C 2 H 5 OH might be salted out by Cs 2 SO 4 from this system and the equilibrium solid phase is Cs 2 SO 4 .
文摘The new mixed borates with formula(Rb 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O and Cs 2 Ca [B 4 O 5 (OH) 4 ] 2 ·8H 2 O)were prepared by reaction Rb (Cs )-borate aqueous solution with CaCl 2 .Two kinds of compounds were characterized by chemical analysis,X-ray powder dif fraction,FT-IR spectra and thermal analysis.
文摘PhCH2)3Sn·(O2CC5H4N)·(H2O)]n was synthesized by the reaction of 4-pyridine car-boxylic acid with the tribenzyltin o xide and was characterized by IR,1 H NMR and MS.Its crystal structure was determined by X-ray single crystal diffraction.The crystal belongs to monoclinic.The space group P21 /c with unit cell parameters a=1.2241(8)nm,b=0.9660(6)nm,c=2.3708(15)nm,β=102.722(12)°,V=2.734(3)nm3,Z =4,Dc=1.298g·cm-3 .In crystal,the tin atom rendered five-coordinate in a trigo nal bipyramidal structure which is b ridged by 4-pyridine carboxy-late into one-dimensional chain polymers.
文摘Two new Gd Ⅲ complexes with nitrilotriacetic acid(nta) and trans-1,2-cyclohexanediaminetetraacetic acid(Cydta) ligands were synthesized. Their crystal structures were determined by single-crystal X-ray structure analyses. The crystal data are as follows: K 3[Gd Ⅲ(nta) 2·(H 2O)]·6H 2O, monoclinic system, C2/c space group, a=1.534 81(15) nm, b=1.292 05(12) nm, c=2.610 8(3) nm, β=96.244(2)°, V=5.146 7(9) nm 3, Z=8, M=776.87, D c=2.005 g/cm 3, μ= 3.149 mm -1 and \{F(000)=\}3 080, R=0.024 5, wR=0.064 3 for 4 455 unique reflections and R= 0.028 9, wR=0.067 2 for all 10 305 reflections. The Gd ⅢN 2O 7 part in the [Gd Ⅲ(nta) 2(H 2O)] 3- anion is a pseudo-monocapped square antiprismatic nine-coordination structure.(NH 4)[Gd Ⅲ(Cydta)(H 2O) 2]·5H 2O, triclinic system, P1 space group, a=0.866 2(3) nm, b=1.006 7(3) nm, c= 1.444 8(5) nm, α= 88.282(5)°, β=75\^190(5)°, γ=88.317(4)°, V=1.217 2(7) nm 3, Z=2, M=643.69, D c=1.756 g/cm 3, μ=2.798 mm -1 and F(000)=650, R=0.030 3, wR=0.080 9 for 4 273 unique reflections and R=0.033 2, wR=0.082 5 for all 5 062 reflections. The Gd ⅢN 2O 6 part in the [Gd Ⅲ(Cydta)(H 2O) 2] - anion has a pseudo-square antiprismatic eight-coordination structure.
文摘The two new compounds Cs5EuCl8· 14H2O(5∶ 1 type) and Cs2EuCl5· 4H2O(2∶ 1 type) were found and synthesized from CsCl EuCl3 11% HCl H2O quaternary systems by phase equilibrium method, and were characterized and measured by ultra violet absorption spectrometry and fluorescence spectrum. The results show that upconversion spectrum exhibit at 590nm and 610nm exited at 790nm, and the upconversion intensity increases with the EuCl3 ratio increasing in CsCl.