{1012¯}twins were introduced into the magnesium(Mg)plate AZ31 via pre-rolling along its transverse direction.The plates,both with and without the pre-induced{1012¯}twins,were subjected to uniaxial tension al...{1012¯}twins were introduced into the magnesium(Mg)plate AZ31 via pre-rolling along its transverse direction.The plates,both with and without the pre-induced{1012¯}twins,were subjected to uniaxial tension along different directions.Using crystal plasticity modeling,we found that the strengthening effect of the pre-induced{1012¯}twins on the macroscopic flow stress primarily arised from the increased slip resistance caused by the boundaries,rather than the orientation hardening due to the twinning reorientation(although the latter did make its contribution in some specific loading directions).Besides,the pre-existing{1012¯}twins were found,by both experiments and simulation,to promote the activity of prismatic and pyramidal<c+a>in the parent matrix of the material.Further analysis showed that the enhanced non-basal slip activity is related to the{1012¯}twin boundaries’low micro Hall-Petch slope ratios of non-basal slips to basal slip.With the critical resolved shear stress(CRSS)obtained from crystal plasticity modeling and the orientation data from EBSD,a probability-based slip transfer model was proposed.The model predicts higher slip transfer probabilities and thus lower strain concentration tendencies at{1012¯}twin boundaries than that at grain boundaries,which agrees with the experimental observation that the strain localization was primarily associated with the latter.The present findings are helpful scientifically,in deepening our understanding of how the pre-induced{1012¯}twins affect the strength and slip activity of Mg alloys,and technologically,in guiding the design of the pre-strain protocol of Mg alloys.展开更多
A large number of anomalous extension twins,with low or even negative twinning Schmid factors,were found to nucleate and grow in a strongly textured Mg-1Al alloy during tensile deformation along the extruded direction...A large number of anomalous extension twins,with low or even negative twinning Schmid factors,were found to nucleate and grow in a strongly textured Mg-1Al alloy during tensile deformation along the extruded direction.The deformation mechanisms responsible for this behaviour were investigated through in-situ electron back-scattered diffraction,grain reference orientation deviation,and slip trace-modified lattice rotation.It was found that anomalous extension twins nucleated mainly at the onset of plastic deformation at or near grain boundary triple junctions.They were associated with the severe strain incompatibility between neighbour grains as a result from the differentbasal slip-induced lattice rotations.Moreover,the anomalous twins were able to grow with the applied strain due to the continuous activation ofbasal slip in different neighbour grains,which enhanced the strain incompatibility.These results reveal the complexity of the deformation mechanisms in Mg alloys at the local level when deformed along hard orientations.展开更多
Interactions of solute atoms in biodegradable zinc alloys and their effect on alloy mechanical properties have been less investigated.In this work,the interactions between the common solutes(Li,Mg,Mn,Cu,and Ag)used in...Interactions of solute atoms in biodegradable zinc alloys and their effect on alloy mechanical properties have been less investigated.In this work,the interactions between the common solutes(Li,Mg,Mn,Cu,and Ag)used in the biodegradable Zn alloys,including a solute-solute pair with the same element or with two different elements,are investigated based on first-principles calculations.It is found that the energetically favorable configuration is the third nearest-neighboring for most solute-solute pairs in the bulk lattice because of the relatively strong electronic interaction between solute and Zn atoms or the relatively small local elastic deformation associated with the configuration.Considering that interfacial cleavage is a key fracture mode of zinc,the segregation ability of these solutes and their effect on the{1012}twin boundary cohesion are also examined.The result shows that Li tends to fully occupy its preferred site in the twin boundary,while Mg,Mn,Cu,or Ag has a concentration limitation in the twin boundary.The twin boundary cohesion can be significantly enhanced by the segregation of Mn,followed by Cu and Ag,because of the contribution of their d states close to the Fermi level.Furthermore,the co-segregation ability of two solute atoms in the twin boundary increases with increasing the binding tendency of these two solute atoms in the boundary.Mn and Li or Mg show a relatively strong co-segregation ability in the twin boundary.Adding Mn to Zn-Li or Zn-Mg alloys can significantly enhance the resistance to fracture of twin boundaries.展开更多
Natural disaster risk monitoring is an important task for disaster prevention and reduction.In the case of immovable cultural relics,however,the feedback mechanism,risk factors,monitoring logic,and monitoring indicato...Natural disaster risk monitoring is an important task for disaster prevention and reduction.In the case of immovable cultural relics,however,the feedback mechanism,risk factors,monitoring logic,and monitoring indicators of natural disaster risk monitoring are complex.How to achieve intelligent perception and monitoring of natural disaster risk for immovable cultural relics has always been a focus and a challenge for researchers.Based on the analysis of the concepts and issues related to the natural disaster risk of immovable cultural relics,this paper proposes a framework for natural disaster risk monitoring for immovable cultural relics based on the digital twin.This framework focuses on risk monitoring,including the physical entities of natural disaster risk for immovable cultural relics,monitoring indicators,and virtual entity construction.A platform for monitoring the natural disaster risk of immovable cultural relics is proposed.Using the Puzhou Ancient City Site as a test bed,the proposed concept can be used for monitoring the natural disaster risk of immovable cultural relics at different scales.展开更多
目前主流工业机器人为封闭式控制结构,存在不开源、二次开发难的问题,因此设计一种基于TwinCAT3(the windows control and automation technology)的跨平台、可移植性好的机器人控制系统架构。该架构包含视觉、运动控制和算法集成与仿...目前主流工业机器人为封闭式控制结构,存在不开源、二次开发难的问题,因此设计一种基于TwinCAT3(the windows control and automation technology)的跨平台、可移植性好的机器人控制系统架构。该架构包含视觉、运动控制和算法集成与仿真控制模块,采用倍福自动化设备规范(automation device specification,ADS)通信技术和实时工业以太网总线技术(ethernet for control automation technology,EtherCAT),建立以计算机(personal computer,PC)和倍福控制器为EtherCAT主站,控制多组从站执行器的一主多从工作模式。该模式结合离线与在线控制、集成数字孪生技术,完成虚拟样机与物理样机的联动;采用开源可扩展架构,便于视觉算法、智能算法等算法集成。经实验验证,此架构具有拓展性好、实时性强的特点。展开更多
Twinning is widely recognized as an effective and cost-efficient method for controlling the microstructure and properties of wrought magnesium(Mg)alloys.Specifically,twins play a crucial role in initiating dynamic rec...Twinning is widely recognized as an effective and cost-efficient method for controlling the microstructure and properties of wrought magnesium(Mg)alloys.Specifically,twins play a crucial role in initiating dynamic recrystallization(DRX),while twin regions experience rapid recrystallization during static recrystallization(SRX).The activation of twinning can lead to changes in lattice orientation,significantly impacting the final texture in Mg alloys.The active roles of twinning are influenced by various factors during the activation process,and the mobility of twin boundaries(TB)can be amplified by stress effects,dislocation interactions,and thermal effects.Conversely,annealing treatments that involve proper segregation or precipitation on TBs serve to stabilize them,restraining their motion.Events such as segregation may also alter the twinning propensity in Magnesium-rare earth(Mg-RE)alloys.While{10–11}contraction twins(CT)and{10–11}-{10–12}double twins(DT)can promote dynamic recrystallization(DRX),they also pose a risk as potential sources of voids and cracks.Additionally,understanding the nucleation and growth mechanisms of twinning is crucial,and these aspects are briefly reviewed in this article.Considering the factors mentioned above,this article summarizes the recent research progress in this field,shedding light on advancements in recent eras.展开更多
The rapid development of 5G/6G and AI enables an environment of Internet of Everything(IoE)which can support millions of connected mobile devices and applications to operate smoothly at high speed and low delay.Howeve...The rapid development of 5G/6G and AI enables an environment of Internet of Everything(IoE)which can support millions of connected mobile devices and applications to operate smoothly at high speed and low delay.However,these massive devices will lead to explosive traffic growth,which in turn cause great burden for the data transmission and content delivery.This challenge can be eased by sinking some critical content from cloud to edge.In this case,how to determine the critical content,where to sink and how to access the content correctly and efficiently become new challenges.This work focuses on establishing a highly efficient content delivery framework in the IoE environment.In particular,the IoE environment is re-constructed as an end-edge-cloud collaborative system,in which the concept of digital twin is applied to promote the collaboration.Based on the digital asset obtained by digital twin from end users,a content popularity prediction scheme is firstly proposed to decide the critical content by using the Temporal Pattern Attention(TPA)enabled Long Short-Term Memory(LSTM)model.Then,the prediction results are input for the proposed caching scheme to decide where to sink the critical content by using the Reinforce Learning(RL)technology.Finally,a collaborative routing scheme is proposed to determine the way to access the content with the objective of minimizing overhead.The experimental results indicate that the proposed schemes outperform the state-of-the-art benchmarks in terms of the caching hit rate,the average throughput,the successful content delivery rate and the average routing overhead.展开更多
Machine tools,often referred to as the“mother machines”of the manufacturing industry,are crucial in developing smart manufacturing and are increasingly becoming more intelligent.Digital twin technology can promote m...Machine tools,often referred to as the“mother machines”of the manufacturing industry,are crucial in developing smart manufacturing and are increasingly becoming more intelligent.Digital twin technology can promote machine tool intelligence and has attracted considerable research interest.However,there is a lack of clear and systematic analyses on how the digital twin technology enables machine tool intelligence.Herein,digital twin modeling was identified as an enabling technology for machine tool intelligence based on a comparative study of the characteristics of machine tool intelligence and digital twin.The review then delves into state-of-the-art digital twin modelingenabled machine tool intelligence,examining it from the aspects of data-based modeling and mechanism-data dual-driven modeling.Additionally,it highlights three bottleneck issues facing the field.Considering these problems,the architecture of a digital twin machine tool(DTMT)is proposed,and three key technologies are expounded in detail:Data perception and fusion technology,mechanism-data-knowledge hybrid-driven digital twin modeling and virtual-real synchronization technology,and dynamic optimization and collaborative control technology for multilevel parameters.Finally,future research directions for the DTMT are discussed.This work can provide a foundation basis for the research and implementation of digital-twin modeling-enabled machine tool intelligence,making it significant for developing intelligent machine tools.展开更多
In this study, a three dimensional(3D) numerical model of six-degrees-of-freedom(6DOF) is applied to simulate the water entries of twin spheres side-by-side at different lateral distances and time intervals.The turbul...In this study, a three dimensional(3D) numerical model of six-degrees-of-freedom(6DOF) is applied to simulate the water entries of twin spheres side-by-side at different lateral distances and time intervals.The turbulence structure is described using the shear-stress transport k-ω(SST k-ω) model, and the volume of fluid(VOF) method is used to track the complex air-liquid interface. The motion of spheres during water entry is simulated using an independent overset grid. The numerical model is verified by comparing the cavity evolution results from simulations and experiments. Numerical results reveal that the time interval between the twin water entries evidently affects cavity expansion and contraction behaviors in the radial direction. However, this influence is significantly weakened by increasing the lateral distance between the two spheres. In synchronous water entries, pressure is reduced on the midline of two cavities during surface closure, which is directly related to the cavity volume. The evolution of vortexes inside the two cavities is analyzed using a velocity vector field, which is affected by the lateral distance and time interval of water entries.展开更多
Digital Twin(DT)supports real time analysis and provides a reliable simulation platform in the Internet of Things(IoT).The creation and application of DT hinges on amounts of data,which poses pressure on the applicati...Digital Twin(DT)supports real time analysis and provides a reliable simulation platform in the Internet of Things(IoT).The creation and application of DT hinges on amounts of data,which poses pressure on the application of Artificial Intelligence(AI)for DT descriptions and intelligent decision-making.Federated Learning(FL)is a cutting-edge technology that enables geographically dispersed devices to collaboratively train a shared global model locally rather than relying on a data center to perform model training.Therefore,DT can benefit by combining with FL,successfully solving the"data island"problem in traditional AI.However,FL still faces serious challenges,such as enduring single-point failures,suffering from poison attacks,lacking effective incentive mechanisms.Before the successful deployment of DT,we should tackle the issues caused by FL.Researchers from industry and academia have recognized the potential of introducing Blockchain Technology(BT)into FL to overcome the challenges faced by FL,where BT acting as a distributed and immutable ledger,can store data in a secure,traceable,and trusted manner.However,to the best of our knowledge,a comprehensive literature review on this topic is still missing.In this paper,we review existing works about blockchain-enabled FL and visualize their prospects with DT.To this end,we first propose evaluation requirements with respect to security,faulttolerance,fairness,efficiency,cost-saving,profitability,and support for heterogeneity.Then,we classify existing literature according to the functionalities of BT in FL and analyze their advantages and disadvantages based on the proposed evaluation requirements.Finally,we discuss open problems in the existing literature and the future of DT supported by blockchain-enabled FL,based on which we further propose some directions for future research.展开更多
The mechanical behavior and microstructural evolution of an Fe-30Mn-3Al-3Si twinninginduced plasticity(TWIP)steel processed using warm forging was investigated.It is found that steel processed via warm forging improve...The mechanical behavior and microstructural evolution of an Fe-30Mn-3Al-3Si twinninginduced plasticity(TWIP)steel processed using warm forging was investigated.It is found that steel processed via warm forging improves comprehensive mechanical properties compared to the TWIP steel processed via cold rolling,with a high tensile strength(R_(m))of 793 MPa,a yield strength(R_(P))of 682 MPa,an extremely large R_(P)/R_(m)ratio as high as 0.86 as well as an excellent elongation rate of 46.8%.The microstructure observation demonstrates that steel processed by warm forging consists of large and elongated grains together with fine,equiaxed grains.Complicated micro-defect configurations were also observed within the steel,including dense dislocation networks and a few coarse deformation twins.As the plastic deformation proceeds,the densities of dislocations and deformation twins significantly increase.Moreover,a great number of slip lines could be observed in the elongated grains.These findings reveal that a much more dramatic interaction between microstructural defect and dislocations glide takes place in the forging sample,wherein the fine and equiaxed grains propagated dislocations more rapidly,together with initial defect configurations,are responsible for enhanced strength properties.Meanwhile,larger,elongated grains with more prevalently activated deformation twins result in high plasticity.展开更多
基金supported by the National Natural Science Foundation of China(grant numbers 51801147,51790482,51722104,51625103,and 51621063)the National Key Re-search and Development Program of China(grant number 2017YFB0702301)the International Joint Laboratory for Micro/Nano Manufacturing and Measurement Technologies.
文摘{1012¯}twins were introduced into the magnesium(Mg)plate AZ31 via pre-rolling along its transverse direction.The plates,both with and without the pre-induced{1012¯}twins,were subjected to uniaxial tension along different directions.Using crystal plasticity modeling,we found that the strengthening effect of the pre-induced{1012¯}twins on the macroscopic flow stress primarily arised from the increased slip resistance caused by the boundaries,rather than the orientation hardening due to the twinning reorientation(although the latter did make its contribution in some specific loading directions).Besides,the pre-existing{1012¯}twins were found,by both experiments and simulation,to promote the activity of prismatic and pyramidal<c+a>in the parent matrix of the material.Further analysis showed that the enhanced non-basal slip activity is related to the{1012¯}twin boundaries’low micro Hall-Petch slope ratios of non-basal slips to basal slip.With the critical resolved shear stress(CRSS)obtained from crystal plasticity modeling and the orientation data from EBSD,a probability-based slip transfer model was proposed.The model predicts higher slip transfer probabilities and thus lower strain concentration tendencies at{1012¯}twin boundaries than that at grain boundaries,which agrees with the experimental observation that the strain localization was primarily associated with the latter.The present findings are helpful scientifically,in deepening our understanding of how the pre-induced{1012¯}twins affect the strength and slip activity of Mg alloys,and technologically,in guiding the design of the pre-strain protocol of Mg alloys.
基金supported by the project(MAD2DCM)-IMDEA Materials funded by Comunidad de Madrid and by the Recovery,Transformation and Resilience Plan and by NextGenerationEU from the European Union,and by the María de Maeztu seal of excellence from the Spanish Research Agency(CEX2018-000800-M)Mr.B.Yang wishes to express his gratitude for the support of the China Scholarship Council(202106370122).
文摘A large number of anomalous extension twins,with low or even negative twinning Schmid factors,were found to nucleate and grow in a strongly textured Mg-1Al alloy during tensile deformation along the extruded direction.The deformation mechanisms responsible for this behaviour were investigated through in-situ electron back-scattered diffraction,grain reference orientation deviation,and slip trace-modified lattice rotation.It was found that anomalous extension twins nucleated mainly at the onset of plastic deformation at or near grain boundary triple junctions.They were associated with the severe strain incompatibility between neighbour grains as a result from the differentbasal slip-induced lattice rotations.Moreover,the anomalous twins were able to grow with the applied strain due to the continuous activation ofbasal slip in different neighbour grains,which enhanced the strain incompatibility.These results reveal the complexity of the deformation mechanisms in Mg alloys at the local level when deformed along hard orientations.
基金The authors acknowledge the financial support from the Australian Research Council(No.DP190102373)This work was supported by computational resources provided by the Australian Gov-ernment through National Computational Infrastructure(Raijin)and Pawsey supercomputing centre(Magnus)under the National Computational Merit Allocation Scheme(NCMAS).
文摘Interactions of solute atoms in biodegradable zinc alloys and their effect on alloy mechanical properties have been less investigated.In this work,the interactions between the common solutes(Li,Mg,Mn,Cu,and Ag)used in the biodegradable Zn alloys,including a solute-solute pair with the same element or with two different elements,are investigated based on first-principles calculations.It is found that the energetically favorable configuration is the third nearest-neighboring for most solute-solute pairs in the bulk lattice because of the relatively strong electronic interaction between solute and Zn atoms or the relatively small local elastic deformation associated with the configuration.Considering that interfacial cleavage is a key fracture mode of zinc,the segregation ability of these solutes and their effect on the{1012}twin boundary cohesion are also examined.The result shows that Li tends to fully occupy its preferred site in the twin boundary,while Mg,Mn,Cu,or Ag has a concentration limitation in the twin boundary.The twin boundary cohesion can be significantly enhanced by the segregation of Mn,followed by Cu and Ag,because of the contribution of their d states close to the Fermi level.Furthermore,the co-segregation ability of two solute atoms in the twin boundary increases with increasing the binding tendency of these two solute atoms in the boundary.Mn and Li or Mg show a relatively strong co-segregation ability in the twin boundary.Adding Mn to Zn-Li or Zn-Mg alloys can significantly enhance the resistance to fracture of twin boundaries.
基金National Natural Science Foundation of China(Nos.42171444,42301516)Beijing Natural Science Foundation Project-Municipal Education Commission Joint Fund Project(No.KZ202110016021)Beijing Municipal Education Commission Scientific Research Project-Science and Technology Plan General Project(No.KM202110016005).
文摘Natural disaster risk monitoring is an important task for disaster prevention and reduction.In the case of immovable cultural relics,however,the feedback mechanism,risk factors,monitoring logic,and monitoring indicators of natural disaster risk monitoring are complex.How to achieve intelligent perception and monitoring of natural disaster risk for immovable cultural relics has always been a focus and a challenge for researchers.Based on the analysis of the concepts and issues related to the natural disaster risk of immovable cultural relics,this paper proposes a framework for natural disaster risk monitoring for immovable cultural relics based on the digital twin.This framework focuses on risk monitoring,including the physical entities of natural disaster risk for immovable cultural relics,monitoring indicators,and virtual entity construction.A platform for monitoring the natural disaster risk of immovable cultural relics is proposed.Using the Puzhou Ancient City Site as a test bed,the proposed concept can be used for monitoring the natural disaster risk of immovable cultural relics at different scales.
文摘目前主流工业机器人为封闭式控制结构,存在不开源、二次开发难的问题,因此设计一种基于TwinCAT3(the windows control and automation technology)的跨平台、可移植性好的机器人控制系统架构。该架构包含视觉、运动控制和算法集成与仿真控制模块,采用倍福自动化设备规范(automation device specification,ADS)通信技术和实时工业以太网总线技术(ethernet for control automation technology,EtherCAT),建立以计算机(personal computer,PC)和倍福控制器为EtherCAT主站,控制多组从站执行器的一主多从工作模式。该模式结合离线与在线控制、集成数字孪生技术,完成虚拟样机与物理样机的联动;采用开源可扩展架构,便于视觉算法、智能算法等算法集成。经实验验证,此架构具有拓展性好、实时性强的特点。
基金supported by the National Natural Science Foundation of China(No.U22A20187,No.52271147,No.12261160364).
文摘Twinning is widely recognized as an effective and cost-efficient method for controlling the microstructure and properties of wrought magnesium(Mg)alloys.Specifically,twins play a crucial role in initiating dynamic recrystallization(DRX),while twin regions experience rapid recrystallization during static recrystallization(SRX).The activation of twinning can lead to changes in lattice orientation,significantly impacting the final texture in Mg alloys.The active roles of twinning are influenced by various factors during the activation process,and the mobility of twin boundaries(TB)can be amplified by stress effects,dislocation interactions,and thermal effects.Conversely,annealing treatments that involve proper segregation or precipitation on TBs serve to stabilize them,restraining their motion.Events such as segregation may also alter the twinning propensity in Magnesium-rare earth(Mg-RE)alloys.While{10–11}contraction twins(CT)and{10–11}-{10–12}double twins(DT)can promote dynamic recrystallization(DRX),they also pose a risk as potential sources of voids and cracks.Additionally,understanding the nucleation and growth mechanisms of twinning is crucial,and these aspects are briefly reviewed in this article.Considering the factors mentioned above,this article summarizes the recent research progress in this field,shedding light on advancements in recent eras.
基金supported by the National Key Research and Development Program of China under Grant No.2019YFB1802800the National Natural Science Foundation of China under Grant No.62002055,62032013,61872073,62202247.
文摘The rapid development of 5G/6G and AI enables an environment of Internet of Everything(IoE)which can support millions of connected mobile devices and applications to operate smoothly at high speed and low delay.However,these massive devices will lead to explosive traffic growth,which in turn cause great burden for the data transmission and content delivery.This challenge can be eased by sinking some critical content from cloud to edge.In this case,how to determine the critical content,where to sink and how to access the content correctly and efficiently become new challenges.This work focuses on establishing a highly efficient content delivery framework in the IoE environment.In particular,the IoE environment is re-constructed as an end-edge-cloud collaborative system,in which the concept of digital twin is applied to promote the collaboration.Based on the digital asset obtained by digital twin from end users,a content popularity prediction scheme is firstly proposed to decide the critical content by using the Temporal Pattern Attention(TPA)enabled Long Short-Term Memory(LSTM)model.Then,the prediction results are input for the proposed caching scheme to decide where to sink the critical content by using the Reinforce Learning(RL)technology.Finally,a collaborative routing scheme is proposed to determine the way to access the content with the objective of minimizing overhead.The experimental results indicate that the proposed schemes outperform the state-of-the-art benchmarks in terms of the caching hit rate,the average throughput,the successful content delivery rate and the average routing overhead.
基金Supported by Tianjin Municipal University Science and Technology Development Foundation of China(Grant No.2021KJ176).
文摘Machine tools,often referred to as the“mother machines”of the manufacturing industry,are crucial in developing smart manufacturing and are increasingly becoming more intelligent.Digital twin technology can promote machine tool intelligence and has attracted considerable research interest.However,there is a lack of clear and systematic analyses on how the digital twin technology enables machine tool intelligence.Herein,digital twin modeling was identified as an enabling technology for machine tool intelligence based on a comparative study of the characteristics of machine tool intelligence and digital twin.The review then delves into state-of-the-art digital twin modelingenabled machine tool intelligence,examining it from the aspects of data-based modeling and mechanism-data dual-driven modeling.Additionally,it highlights three bottleneck issues facing the field.Considering these problems,the architecture of a digital twin machine tool(DTMT)is proposed,and three key technologies are expounded in detail:Data perception and fusion technology,mechanism-data-knowledge hybrid-driven digital twin modeling and virtual-real synchronization technology,and dynamic optimization and collaborative control technology for multilevel parameters.Finally,future research directions for the DTMT are discussed.This work can provide a foundation basis for the research and implementation of digital-twin modeling-enabled machine tool intelligence,making it significant for developing intelligent machine tools.
基金China Academy of Launch Vehicle Technology(Grant No.CALT-2022-03)Science and Technology on Underwater Information and Control Laboratory(Grant No.2021-JCJQ-LB-030-05).
文摘In this study, a three dimensional(3D) numerical model of six-degrees-of-freedom(6DOF) is applied to simulate the water entries of twin spheres side-by-side at different lateral distances and time intervals.The turbulence structure is described using the shear-stress transport k-ω(SST k-ω) model, and the volume of fluid(VOF) method is used to track the complex air-liquid interface. The motion of spheres during water entry is simulated using an independent overset grid. The numerical model is verified by comparing the cavity evolution results from simulations and experiments. Numerical results reveal that the time interval between the twin water entries evidently affects cavity expansion and contraction behaviors in the radial direction. However, this influence is significantly weakened by increasing the lateral distance between the two spheres. In synchronous water entries, pressure is reduced on the midline of two cavities during surface closure, which is directly related to the cavity volume. The evolution of vortexes inside the two cavities is analyzed using a velocity vector field, which is affected by the lateral distance and time interval of water entries.
基金supported in part by the National Natural Science Foundation of China under Grant 62072351in part by the Academy of Finland under Grant 308087,Grant 335262,Grant 345072,and Grant 350464+1 种基金in part by the Open Project of Zhejiang Lab under Grant 2021PD0AB01in part by the 111 Project under Grant B16037.
文摘Digital Twin(DT)supports real time analysis and provides a reliable simulation platform in the Internet of Things(IoT).The creation and application of DT hinges on amounts of data,which poses pressure on the application of Artificial Intelligence(AI)for DT descriptions and intelligent decision-making.Federated Learning(FL)is a cutting-edge technology that enables geographically dispersed devices to collaboratively train a shared global model locally rather than relying on a data center to perform model training.Therefore,DT can benefit by combining with FL,successfully solving the"data island"problem in traditional AI.However,FL still faces serious challenges,such as enduring single-point failures,suffering from poison attacks,lacking effective incentive mechanisms.Before the successful deployment of DT,we should tackle the issues caused by FL.Researchers from industry and academia have recognized the potential of introducing Blockchain Technology(BT)into FL to overcome the challenges faced by FL,where BT acting as a distributed and immutable ledger,can store data in a secure,traceable,and trusted manner.However,to the best of our knowledge,a comprehensive literature review on this topic is still missing.In this paper,we review existing works about blockchain-enabled FL and visualize their prospects with DT.To this end,we first propose evaluation requirements with respect to security,faulttolerance,fairness,efficiency,cost-saving,profitability,and support for heterogeneity.Then,we classify existing literature according to the functionalities of BT in FL and analyze their advantages and disadvantages based on the proposed evaluation requirements.Finally,we discuss open problems in the existing literature and the future of DT supported by blockchain-enabled FL,based on which we further propose some directions for future research.
基金Funded by the National Natural Science Foundation of China(Nos.51701206 and 51671187)the Shanxi Natural Science Foundation(No.2019JQ-833)+2 种基金the Anhui Natural Science Foundation(1808085QE166)the Special Scientific Research Project of Shanxi Education Committee(No.19JQ0974)the Doctoral Research Initiation Project of Yan’an University(No.YDBD2018-21)。
文摘The mechanical behavior and microstructural evolution of an Fe-30Mn-3Al-3Si twinninginduced plasticity(TWIP)steel processed using warm forging was investigated.It is found that steel processed via warm forging improves comprehensive mechanical properties compared to the TWIP steel processed via cold rolling,with a high tensile strength(R_(m))of 793 MPa,a yield strength(R_(P))of 682 MPa,an extremely large R_(P)/R_(m)ratio as high as 0.86 as well as an excellent elongation rate of 46.8%.The microstructure observation demonstrates that steel processed by warm forging consists of large and elongated grains together with fine,equiaxed grains.Complicated micro-defect configurations were also observed within the steel,including dense dislocation networks and a few coarse deformation twins.As the plastic deformation proceeds,the densities of dislocations and deformation twins significantly increase.Moreover,a great number of slip lines could be observed in the elongated grains.These findings reveal that a much more dramatic interaction between microstructural defect and dislocations glide takes place in the forging sample,wherein the fine and equiaxed grains propagated dislocations more rapidly,together with initial defect configurations,are responsible for enhanced strength properties.Meanwhile,larger,elongated grains with more prevalently activated deformation twins result in high plasticity.