电力铁塔用18 mm厚160角钢Q420C(/%:≤0.20C,1.00~1.70Mn,≤0.55Si,≤0.035S,≤0.035P,0.02~0.20V,≥0.015Als)的冶金流程为80 t BOF-LF-CC-车制工艺。利用光学显微镜、SEM以及能谱分析仪对热轧角钢角部裂纹进行了分析,结果表明,裂纹周...电力铁塔用18 mm厚160角钢Q420C(/%:≤0.20C,1.00~1.70Mn,≤0.55Si,≤0.035S,≤0.035P,0.02~0.20V,≥0.015Als)的冶金流程为80 t BOF-LF-CC-车制工艺。利用光学显微镜、SEM以及能谱分析仪对热轧角钢角部裂纹进行了分析,结果表明,裂纹周围存在脱碳层及铁素体膜,裂纹处发现S富集及在晶界析出的AlN破坏了钢基体的连续性;得出连铸振痕谷底的夹渣、成分偏析,热应力和弯曲矫直应力导致了角钢沿晶界开裂。通过降低[N]至0.008 0%,控制Als 0.017%~0.022%,Mn/S≥80,钢水过热度≥25℃,保护渣牯度0.73 Pa·s,矫直温度≥950℃等工艺措施,使连铸坯的优质品率由原25.78%提高至85%,有效地降低了角钢角部裂纹的发生。展开更多
永钢高压气瓶钢4147(/%:0.46~0.50C,0.15~0.35Si,0.8~1.0Mn,≤0.015P,≤0.008S,0.85~1.10Cr,0.15~0.25Mo,0.02~0.04Al)的冶炼工艺为110 t EBT电弧炉-LF-VD-Φ500 mm圆坯连铸。通过使用炉料80%铁水+20%废钢,控制(Pb+As+Sn+Sb+Bi)≤150...永钢高压气瓶钢4147(/%:0.46~0.50C,0.15~0.35Si,0.8~1.0Mn,≤0.015P,≤0.008S,0.85~1.10Cr,0.15~0.25Mo,0.02~0.04Al)的冶炼工艺为110 t EBT电弧炉-LF-VD-Φ500 mm圆坯连铸。通过使用炉料80%铁水+20%废钢,控制(Pb+As+Sn+Sb+Bi)≤150×10^(-6),EAF终点[C]≥0.08%,终点[P]≤0.006%,并在出钢过程加1.0 kg/t Al;以及采用LF精炼合成渣(/%:40~55CaO,20~30Al_2O_3,≤6MgO,≤4.0SiO_2,≤1.5FeO),成品硫含量≤0.002%,T[O]≤17×10^(-6),[N]≤32×10^(-6),[H]≤0.9×10^(-6),(Pb+Sn+Sb+As+Bi)≤0.013 7%;连铸圆坯中心疏松、缩孔≤1.5级,轧材各类夹杂物均≤0.5级,满足高压气瓶钢质量要求。展开更多