α″phase-assisted nucleation to obtain ultrafineαprecipitates for designing high-strength near-βtitanium alloys

The diffusion-multiple method was used to determine the composition of Ti−6Al−4V−xMo−yZr alloy(0.45<x<12,0.5<y<14,wt.%),which can obtain an ultrafine α phase.Results show that Ti−6Al−4V−5Mo−7Zr alloy can obtain an ultrafineαphase by using the α″phase assisted nucleation.The bimodal microstructure obtained with the heat-treatment process can confer the alloy with a good balance between the strength and plasticity.The deformation mechanism is the dislocation slip and the{1101}twinning in the primary α phase.The strengthening mechanism is α/β interface strengthening.The interface of(0001)α/(110)β has a platform−step structure,whereas(1120)α/(111)βinterface is flat with no steps.

Microstructure and mechanical properties of cast and heat treated Ti-6.55Al-3.41Mo-1.77Zr alloy

α＋βtitanium alloy with a composition of Ti-6.55Al-3.41Mo-1.77Zr （mass fraction,%） was cast into bars in a graphite mould using vacuum induction skull melting furnace （ISM）. The cast bars were hot swaged at 700 °C and then heat treated by two different regimes which resulted in fine and coarse lamella structures, respectively. The grain size of the as-cast structure was estimated to be 660 μm and the swaged samples obtained a very fine grain size in the range of 50 μm. The overall best combination of hardness, tensile properties, and wear resistance of theα＋βtitanium alloy was achieved by heat treating the samples at 1050 °C for getting fine lamellar structure. The maximum compression strength was reported for the heat treated samples at 800 °C with coarse lamella structure. The minimum wear rate was reported for the heat treated samples with fine lamellar structure and the maximum wear rate was obtained for as-cast samples due to its coarse and heterogeneity microstructure.

Effect of Different Sizes of α Phase on Tensile Properties of Metastable β Titanium Alloy Ti-5.5Cr-5Al-4Mo-3Nb-2Zr

To study the relationship between the microstructure and tensile properties of the novel metastable β titanium alloy Ti-5.5Cr-5Al-4Mo-3Nb-2Zr,a heat treatment process of ABFCA(solid solution in α+βregion with subsequent furnace cooling followed by aging treatment finally)was designed,by which α phases of different sizes can be precipitated in the β matrix.The results show that the microstructure obtained by this heat treatment process is composed of primary α(α_(p))phase,submicro rod-like α(α_(r))phase and secondary α(α_(s))phase.The alloy with multi-scale α phase has an excellent balance between strength and ductility.The elongation is about 18.3% at the ultimate tensile strength of 1125.4 MPa.The relationship between the strength of the alloy and the α phase was established.The strength of the alloy is proportional to the power of‒1/2 of the average spacing and width of α phase.The α_(s) phase with a smaller size and phase spacing can greatly improve the strength of the alloy by hindering dislocation slip.The transmission electron microscope analysis shows that there is a large amount of dislocation accumulation at the α/β interfaces,and many deformation twins are found in the α_(p) phase after tensile deformation.When the dislocation slip is hindered,twins occur at the stress concentration location,and twins can initiate some dislocations that are difficult to slip.Meanwhile,the plastic strain is distributed uniformly among the α_(p),α_(r),α_(s) phases and β matrix,thereby enhancing the ductility of the alloy.

Influence of anodization conditions on deposition of hydroxyapatite onα/βTi alloys for osseointegration:Atomic force microscopy analysis

Integrating titanium-based implants with the surrounding bone tissue remains challenging.This study aims to explore the impact of different anodization voltages(20−80 V)on the surface topography of two-phase(α/β)Ti alloys and to produce TiO_(2) films with enhanced bone formation abilities.Scanning electron microscopy coupled with energy dispersive spectroscopy(SEM−EDS)and atomic force microscopy(AFM)were applied to investigate the morphological,chemical,and surface topography of the prepared alloys and to confirm the growth of hydroxyapatite(HA)on their surfaces.Results disclosed that the surface roughness of TiO_(2) films formed on Ti−6Al−7Nb alloys was superior to that of Ti−6Al−4V alloys.Ti−6Al−7Nb alloy anodized at 80 V had the highest yields of HA after immersion in simulated body fluid with enhanced HA surface coverage.The developed HA layer had a mean thickness of(128.38±18.13)μm,suggesting its potential use as an orthopedic implantable material due to its promising bone integration and,hence,remarkable stability inside the human body.