Electrocatalysts with high activity and long-term durability are vital toward large-scale hydrogen pro-duction from electrocatalytic water splitting.Here,the self-supported electrode(FeO_(χ)H_(y)@Ni_(3)B/NF)with hier...Electrocatalysts with high activity and long-term durability are vital toward large-scale hydrogen pro-duction from electrocatalytic water splitting.Here,the self-supported electrode(FeO_(χ)H_(y)@Ni_(3)B/NF)with hierarchical heterostructure was simply prepared by using Ni_(3)B chunks grown on nickel foam as sub-strate to in situ form vertical FeO_(χ)H_(y)nanosheets.Such hybrid shows efficient oxygen evolution reaction activity with overpotentials as low as 267 and 249 mV at 100 mA cm^(-2)in 1 M KOH solution and 30 wt%KOH solution,respectively.Meanwhile,it also exhibits excellent catalytic stability,sustaining catalysis at 500 mA cm^(-2)in 1 M KOH solution for 200 h,and even for 200 h at 1000 mA cm^(-2)in 30 wt%KOH solution.Further experimental results reveal that the FeO_(χ)H_(y)@Ni_(3)B/NF is endowed with superhydrophilic and superaerophobic surface properties,which not only provide more mass transport channels,as well as facilitated the diffusion of reaction intermediates and gas bubbles.Also,it holds faster reaction kinetics,more accessible active sites and accelerated electron transfer rates due to strong synergistic interactions attheheterogeneous interface.展开更多
The high temperature phase a-Ba3Y(BO3)3 was synthesized by Czochralski method, and its crystal structure has been determined by single-crystal X-ray diffraction. It crystallizes in the trigonal system, space group 3R ...The high temperature phase a-Ba3Y(BO3)3 was synthesized by Czochralski method, and its crystal structure has been determined by single-crystal X-ray diffraction. It crystallizes in the trigonal system, space group 3R with a = 13.028(2), c = 9.4992(2) ? V = 1396.1(5) ?, Ba3YB3O9, Mr = 677.36, Z = 6, Dc = 4.834 g/cm3, l(MoKa) = 0.71073 ? m = 18.721 mm-1, F(000) = 1764, the final R = 0.0718 and wR = 0.1640 for 1199 observed reflections with I > 2s(I). In this structure two alternate nonequivalent Y atoms form one-dimensional chains bridged by the Ba atoms with BO3 triangles which link Y(1) and Y(2), respectively. The Ba atom is surrounded by nine O atoms belonging to six BO3 triangles.展开更多
基金supported by the National Natural Science Foundation of China (12234018,52101256,51872115)
文摘Electrocatalysts with high activity and long-term durability are vital toward large-scale hydrogen pro-duction from electrocatalytic water splitting.Here,the self-supported electrode(FeO_(χ)H_(y)@Ni_(3)B/NF)with hierarchical heterostructure was simply prepared by using Ni_(3)B chunks grown on nickel foam as sub-strate to in situ form vertical FeO_(χ)H_(y)nanosheets.Such hybrid shows efficient oxygen evolution reaction activity with overpotentials as low as 267 and 249 mV at 100 mA cm^(-2)in 1 M KOH solution and 30 wt%KOH solution,respectively.Meanwhile,it also exhibits excellent catalytic stability,sustaining catalysis at 500 mA cm^(-2)in 1 M KOH solution for 200 h,and even for 200 h at 1000 mA cm^(-2)in 30 wt%KOH solution.Further experimental results reveal that the FeO_(χ)H_(y)@Ni_(3)B/NF is endowed with superhydrophilic and superaerophobic surface properties,which not only provide more mass transport channels,as well as facilitated the diffusion of reaction intermediates and gas bubbles.Also,it holds faster reaction kinetics,more accessible active sites and accelerated electron transfer rates due to strong synergistic interactions attheheterogeneous interface.
基金the Key Project of Science and Technology of Fujian province (2001H107) and National Natural Science Foundation of China (N0. 59972037)
文摘The high temperature phase a-Ba3Y(BO3)3 was synthesized by Czochralski method, and its crystal structure has been determined by single-crystal X-ray diffraction. It crystallizes in the trigonal system, space group 3R with a = 13.028(2), c = 9.4992(2) ? V = 1396.1(5) ?, Ba3YB3O9, Mr = 677.36, Z = 6, Dc = 4.834 g/cm3, l(MoKa) = 0.71073 ? m = 18.721 mm-1, F(000) = 1764, the final R = 0.0718 and wR = 0.1640 for 1199 observed reflections with I > 2s(I). In this structure two alternate nonequivalent Y atoms form one-dimensional chains bridged by the Ba atoms with BO3 triangles which link Y(1) and Y(2), respectively. The Ba atom is surrounded by nine O atoms belonging to six BO3 triangles.