Precursor foam based Co incorporated α-Fe<sub>2</sub>O<sub>3</sub> (AFC) was successfully synthesized at 600℃ calcination temperature by simple solution method using PVA. The formation of α-...Precursor foam based Co incorporated α-Fe<sub>2</sub>O<sub>3</sub> (AFC) was successfully synthesized at 600℃ calcination temperature by simple solution method using PVA. The formation of α-Fe<sub>2</sub>O<sub>3</sub> nanoparticles was confirmed by X-ray diffraction measurement and reduction in crystallite size was found after cobalt incorporation. Field emission scanning electron microscopy revealed the existence of pyramidal shaped iron oxide in AFC. FTIR and Raman spectra also confirmed the presence of α-Fe<sub>2</sub>O<sub>3</sub>. Photocatalytic activity study showed that the cobalt incorporated α-Fe<sub>2</sub>O<sub>3</sub> was better photocatalyst than pure α-Fe<sub>2</sub>O<sub>3</sub>. The cobalt incorporated iron oxide nanoparticles could be used for drug delivery application and this simple preparation method could be adopted for the synthesis of other transition metal oxides.展开更多
Y2O3： Er^3＋, Yb^3＋ nanoparticles were synthesized by a homogeneous precipitation method without and with different concentrations of EDTA 2Na. Upconversion luminescence spectra of the samples were studied under 980...Y2O3： Er^3＋, Yb^3＋ nanoparticles were synthesized by a homogeneous precipitation method without and with different concentrations of EDTA 2Na. Upconversion luminescence spectra of the samples were studied under 980 nm laser excitation. The results of XRD showed that the obtained Y2O3：Er^3＋,Yb^3＋ nanoparticles were of a cubic structure. The average crystallite sizes calculated were in the range of 28-40 nm. Green and red upconversion emission were observed, and attributed to ^2H11/2,^4S3/2→^4I15/2 and ^4F9/2→^4I15/2 transitions of the ion, respectively. The ratio of the intensity of green emission to that of red emission drastically changed with a change in the EDTA 2Na concentration. In the sample synthesized without EDTA, the relative intensity of the green emission was weaker than that of the red emission. The relative intensities of green emission increased with the increased amount of EDTA 2Na used. The possible upconversion luminescence mechanisms were discussed.展开更多
In recent decades, many additives with different characteristics have been applied to strengthen and toughen Al2O3-based ceramic cutting tool materials. Among them, SiC whiskers and SiC nanoparticles showed excellent ...In recent decades, many additives with different characteristics have been applied to strengthen and toughen Al2O3-based ceramic cutting tool materials. Among them, SiC whiskers and SiC nanoparticles showed excellent performance in improving the material properties. While no attempts have been made to add SiC whiskers and SiC nanoparticles together into the ceramic matrix and the synergistically toughening effects of them have not been studied. An Al2O3-SiCw-SiC np advanced ceramic cutting tool material is fabricated by adding both one-dimensional SiC whiskers and zero-dimensional SiC nanoparticles into the Al2O3 matrix with an effective dispersing and mixing process. The composites with 25 vol% SiC whiskers and 25 vol% SiC nanoparticles alone are also investegated for comparison purposes. Results show that the Al2O3-SiCw-SiCnp composite with both 20 vo1% SiC whiskers and 5 vol% SiC nanoparticles additives have much improved mechanical properties. The flexural strength of Al2O3-SiCw-SiCnp is 730＋ 95 MPa and fracture toughness is 5.6 ± 0.6 MPa.m1/2. The toughening and strengthening mechanisms of SiC whiskers and nanoparticles are studied when they are added either individually or in combination. It is indicated that when SiC whiskers and nanoparticles are added together, the grains are further refined and homogenized, so that the microstructure and fracture mode ratio is modified. The SiC nanoparticles are found helpful to enhance the toughening effects of the SiC whiskers. The proposed research helps to enrich the types of ceramic cutting tool and is benefit to expand the application range of ceramic cutting tool.展开更多
The Fe3O4@SiO2 composite nanoparticles were obtained from as-synthesized magnetite (Fe3O4) nanoparticles through the modified St?ber method. Then, the Fe3O4 nanoparticles and Fe3O4@SiO2 composite nanoparticles were ch...The Fe3O4@SiO2 composite nanoparticles were obtained from as-synthesized magnetite (Fe3O4) nanoparticles through the modified St?ber method. Then, the Fe3O4 nanoparticles and Fe3O4@SiO2 composite nanoparticles were characterized by means of X-ray diffraction (XRD), Raman spectra, scanning electron microscope (SEM) and vibrating sample magnetometer (VSM). Recently, the studies focus on how to improve the dispersion of composite particle and achieve good magnetic performance. Hence effects of the volume ratio of tetraethyl orthosilicate (TEOS) and magnetite colloid on the structural, morphological and magnetic properties of the composite nanoparticles were systematically investi-gated. The results revealed that the Fe3O4@SiO2 had better thermal stability and dispersion than the magnetite nanoparticles. Furthermore, the particle size and magnetic property of the Fe3O4@SiO2 composite nanoparticles can be adjusted by changing the volume ratio of TEOS and magnetite colloid.展开更多
Using density functional theory,noncovalent interactions and four mechanisms of covalent functionalization of capecitabine anticancer drug onto γ-Fe2O3 nanoparticles have been investigated.Quantum molecular descripto...Using density functional theory,noncovalent interactions and four mechanisms of covalent functionalization of capecitabine anticancer drug onto γ-Fe2O3 nanoparticles have been investigated.Quantum molecular descriptors of noncovalent configurations were studied.It was specified that binding of capecitabine onto γ-Fe2O3 nanoparticles is thermodynamically suitable.Hardness and the gap of energy between LUMO and HOMO of capecitabine are higher than the noncovalent configurations,showing the reactivity of capecitabine increases in the presence of γ-Fe2O3 nanoparticles.Capecitabine can bond to γ-Fe2O3 nanoparticles through OH（k1 mechanism）,NH（k2 mechanism）,CO（k3 mechanism） and F（k4 mechanism） groups.The activation energies,activation enthalpies and activation Gibbs free energies of these reactions were calculated.It was specified that the k1 and k2 mechanisms are under thermodynamic control and k3 and k4 under kinetic control.These results could be generalized to other similar drugs.展开更多
Nanocomposites of PAn-DBSA/γ-Fe 2O 3 with electrical and ferromagnetic behavior(σ= 2.18×10 -3-5.00×10 -5 S/cm, M s=3.7-16.6 m 2·A/kg, H c=8 805.2-9 133.1 A/m) were prepared by a chemical modification-...Nanocomposites of PAn-DBSA/γ-Fe 2O 3 with electrical and ferromagnetic behavior(σ= 2.18×10 -3-5.00×10 -5 S/cm, M s=3.7-16.6 m 2·A/kg, H c=8 805.2-9 133.1 A/m) were prepared by a chemical modification-redoping method in a neutral medium. The products were characterized by TEM, XRD, UV-Vis, four-probe method, and magnetometer. The results indicate that the electrical and magnetic properties of the nanocomposites strongly depend on γ-Fe 2O 3 content. With the increase of γ-Fe 2O 3 content, the electrical conductivity is decreased and saturation magnetization is increased.展开更多
Cubic and ellipsoide ultrafine monodispersed hematite colloidal particles wereprepared by hydrothermal reaction from Fe（OH）3 get in the presence of Sn4+ ions. Thenumbers of nuclei increase with the concentration of ...Cubic and ellipsoide ultrafine monodispersed hematite colloidal particles wereprepared by hydrothermal reaction from Fe（OH）3 get in the presence of Sn4+ ions. Thenumbers of nuclei increase with the concentration of Sn4+ ions. The initial concentrationof Fe（OH）3 gel might approach to 0.5 mol.L- 1. The products were characterized by TEMand XRD.展开更多
文摘Precursor foam based Co incorporated α-Fe<sub>2</sub>O<sub>3</sub> (AFC) was successfully synthesized at 600℃ calcination temperature by simple solution method using PVA. The formation of α-Fe<sub>2</sub>O<sub>3</sub> nanoparticles was confirmed by X-ray diffraction measurement and reduction in crystallite size was found after cobalt incorporation. Field emission scanning electron microscopy revealed the existence of pyramidal shaped iron oxide in AFC. FTIR and Raman spectra also confirmed the presence of α-Fe<sub>2</sub>O<sub>3</sub>. Photocatalytic activity study showed that the cobalt incorporated α-Fe<sub>2</sub>O<sub>3</sub> was better photocatalyst than pure α-Fe<sub>2</sub>O<sub>3</sub>. The cobalt incorporated iron oxide nanoparticles could be used for drug delivery application and this simple preparation method could be adopted for the synthesis of other transition metal oxides.
基金the Foundation for the University by Educational Department of Liaoning (05L337)Key Laboratory of Rare Earth Chemistry and Physics, Chinese Academy of Sciences
文摘Y2O3： Er^3＋, Yb^3＋ nanoparticles were synthesized by a homogeneous precipitation method without and with different concentrations of EDTA 2Na. Upconversion luminescence spectra of the samples were studied under 980 nm laser excitation. The results of XRD showed that the obtained Y2O3：Er^3＋,Yb^3＋ nanoparticles were of a cubic structure. The average crystallite sizes calculated were in the range of 28-40 nm. Green and red upconversion emission were observed, and attributed to ^2H11/2,^4S3/2→^4I15/2 and ^4F9/2→^4I15/2 transitions of the ion, respectively. The ratio of the intensity of green emission to that of red emission drastically changed with a change in the EDTA 2Na concentration. In the sample synthesized without EDTA, the relative intensity of the green emission was weaker than that of the red emission. The relative intensities of green emission increased with the increased amount of EDTA 2Na used. The possible upconversion luminescence mechanisms were discussed.
基金Supported by National Natural Science Foundation of China(Grant No.51175305)
文摘In recent decades, many additives with different characteristics have been applied to strengthen and toughen Al2O3-based ceramic cutting tool materials. Among them, SiC whiskers and SiC nanoparticles showed excellent performance in improving the material properties. While no attempts have been made to add SiC whiskers and SiC nanoparticles together into the ceramic matrix and the synergistically toughening effects of them have not been studied. An Al2O3-SiCw-SiC np advanced ceramic cutting tool material is fabricated by adding both one-dimensional SiC whiskers and zero-dimensional SiC nanoparticles into the Al2O3 matrix with an effective dispersing and mixing process. The composites with 25 vol% SiC whiskers and 25 vol% SiC nanoparticles alone are also investegated for comparison purposes. Results show that the Al2O3-SiCw-SiCnp composite with both 20 vo1% SiC whiskers and 5 vol% SiC nanoparticles additives have much improved mechanical properties. The flexural strength of Al2O3-SiCw-SiCnp is 730＋ 95 MPa and fracture toughness is 5.6 ± 0.6 MPa.m1/2. The toughening and strengthening mechanisms of SiC whiskers and nanoparticles are studied when they are added either individually or in combination. It is indicated that when SiC whiskers and nanoparticles are added together, the grains are further refined and homogenized, so that the microstructure and fracture mode ratio is modified. The SiC nanoparticles are found helpful to enhance the toughening effects of the SiC whiskers. The proposed research helps to enrich the types of ceramic cutting tool and is benefit to expand the application range of ceramic cutting tool.
文摘The Fe3O4@SiO2 composite nanoparticles were obtained from as-synthesized magnetite (Fe3O4) nanoparticles through the modified St?ber method. Then, the Fe3O4 nanoparticles and Fe3O4@SiO2 composite nanoparticles were characterized by means of X-ray diffraction (XRD), Raman spectra, scanning electron microscope (SEM) and vibrating sample magnetometer (VSM). Recently, the studies focus on how to improve the dispersion of composite particle and achieve good magnetic performance. Hence effects of the volume ratio of tetraethyl orthosilicate (TEOS) and magnetite colloid on the structural, morphological and magnetic properties of the composite nanoparticles were systematically investi-gated. The results revealed that the Fe3O4@SiO2 had better thermal stability and dispersion than the magnetite nanoparticles. Furthermore, the particle size and magnetic property of the Fe3O4@SiO2 composite nanoparticles can be adjusted by changing the volume ratio of TEOS and magnetite colloid.
文摘Using density functional theory,noncovalent interactions and four mechanisms of covalent functionalization of capecitabine anticancer drug onto γ-Fe2O3 nanoparticles have been investigated.Quantum molecular descriptors of noncovalent configurations were studied.It was specified that binding of capecitabine onto γ-Fe2O3 nanoparticles is thermodynamically suitable.Hardness and the gap of energy between LUMO and HOMO of capecitabine are higher than the noncovalent configurations,showing the reactivity of capecitabine increases in the presence of γ-Fe2O3 nanoparticles.Capecitabine can bond to γ-Fe2O3 nanoparticles through OH（k1 mechanism）,NH（k2 mechanism）,CO（k3 mechanism） and F（k4 mechanism） groups.The activation energies,activation enthalpies and activation Gibbs free energies of these reactions were calculated.It was specified that the k1 and k2 mechanisms are under thermodynamic control and k3 and k4 under kinetic control.These results could be generalized to other similar drugs.
文摘Nanocomposites of PAn-DBSA/γ-Fe 2O 3 with electrical and ferromagnetic behavior(σ= 2.18×10 -3-5.00×10 -5 S/cm, M s=3.7-16.6 m 2·A/kg, H c=8 805.2-9 133.1 A/m) were prepared by a chemical modification-redoping method in a neutral medium. The products were characterized by TEM, XRD, UV-Vis, four-probe method, and magnetometer. The results indicate that the electrical and magnetic properties of the nanocomposites strongly depend on γ-Fe 2O 3 content. With the increase of γ-Fe 2O 3 content, the electrical conductivity is decreased and saturation magnetization is increased.
文摘Cubic and ellipsoide ultrafine monodispersed hematite colloidal particles wereprepared by hydrothermal reaction from Fe（OH）3 get in the presence of Sn4+ ions. Thenumbers of nuclei increase with the concentration of Sn4+ ions. The initial concentrationof Fe（OH）3 gel might approach to 0.5 mol.L- 1. The products were characterized by TEMand XRD.