The adsorption method has the advantages of low cost,high efficiency,and environmental friendliness in treating fluorinated wastewater,and the adsorbent material is the key.This study combines the inherent anion-excha...The adsorption method has the advantages of low cost,high efficiency,and environmental friendliness in treating fluorinated wastewater,and the adsorbent material is the key.This study combines the inherent anion-exchange adsorption properties of layered double hydroxides(LDHs).Self-supported porous adsorbent materials loaded with AFm and AFt were prepared from a composite cementitious system consisting of calcium aluminate cement(CAC)and flue gas desulfurization gypsum(FGDG)by chemical foaming technique.The mineral composition of the adsorbent material was characterized by X-ray diffraction(XRD)and Scanning electron microscopy(SEM).Through the static adsorption experiment,the adsorption effect of the mineral composition of the adsorbent on fluoride ions was deeply analyzed,and the adsorption mechanism was revealed.XRD and SEM showed that the main hydration phases of the composite cementitious system consisting of CAC and FGDG are AFm,AFt,AH_(3),and CaSO_(4)·2H_(2)O.FGDG accelerates the hydration process of CAC and inhibits the transformation of AFt to AFm.The AFt content increased,and the AFm content decreased or even disappeared as the amount of FGDG increased.Static adsorption experiment results showed that AFm and AFt in adsorbent materials could significantly enhance the adsorption of fluoride ions.The adsorption of F^(−)in aqueous solution by PAG tends more towards monolayer adsorption with a theoretical maximum capacity of 108.70 mg/g and is similar to the measured value of 112.77 mg/g.展开更多
In this paper,the solid waste desulfurization gypsum produced by coal-fired power plants was used as a raw material to prepare calcium sulfate whiskers with high application prospects.Calcium sulfate whiskers with uni...In this paper,the solid waste desulfurization gypsum produced by coal-fired power plants was used as a raw material to prepare calcium sulfate whiskers with high application prospects.Calcium sulfate whiskers with uniform morphology and high aspect ratio can be prepared by hydrothermal method in sulfuric acid solution.A new process of desulfurization gypsum activated by high-energy grinding to reduce the reaction temperature and sulfuric acid concentration was developed.Through the comparison of product morphology,the best grinding time was determined to be 3.5 h.The mechanism of desulfurization gypsum through physical–chemical coupling to reduce energy consumption was clarified.The activation of desulfurization gypsum by grinding and the acidic environment provided by the sulfuric acid solution made the calcium sulfate solution reached rapid saturation and accelerated the nucleation rate.By calculating the conversion and crystallization rate of calcium sulfate whiskers,it was found that there were obvious"autocatalytic"kinetic characteristics during the crystallization process.展开更多
The feasibility of flue gas desulphurization (FGD) as concrete admixture was studied. A combined concrete admixture of the thermally-treated FGD gypsum and slag powder was explored. The FGD gypsum was roasted at 200...The feasibility of flue gas desulphurization (FGD) as concrete admixture was studied. A combined concrete admixture of the thermally-treated FGD gypsum and slag powder was explored. The FGD gypsum was roasted at 200℃ for 60 min and then mixed with the slag powder to form FGD gypsum-slag powder combined admixture in which the SO3 content was 3.5wt%. Cement was partially and equivalently replaced by slag powder alone or FGD gypsum-slag powder, at concentration of 25wt%, 40wt%, and 50wt%, respectively. The setting times, hydration products, total porosity and pore size distributions of the paste were determined. The compressive strength and drying shrinkage of cement mortar and concrete were also tested. The experimental results show that, in the presence of FGD gypsum, the setting times are much slower than those of pastes in the absence of FGD gypsum. The combination of FGD gypsum and slag powder provides synergistic benefits above that of slag powder alone. The addition of FGD gypsum provides benefit by promoting ettringite formation and forms a compact microstructure, increasing the compressive strength and reduces the drying shrinkage of cement mortar and concrete.展开更多
The freezing acidolysis solution of the nitric acid-phosphate fertilizer process has a high calcium content,which makes it difficult to produce fine phosphate and high water-soluble phosphate fertilizer products.Here,...The freezing acidolysis solution of the nitric acid-phosphate fertilizer process has a high calcium content,which makes it difficult to produce fine phosphate and high water-soluble phosphate fertilizer products.Here,based on the potential crystallization principle of calcium sulfate in NH_(4)NO_(3)-H_(3)PO_(4)-H_(2)O,the deep decalcification(i.e.calcium removal)technology to achieveα-high-strength gypsum originated from freezing acidolysis-solutions has been firstly proposed and investigated.Typically,calcium can be removed from the factory-provided freezing acidolysis-solution by neutralizing it with ammonia,followed by the addition of ammonium sulfate solution.As a result,the formation of calcium sulfate in the reaction system undergoes the nucleation and growth of CaSO_(4)·2H_(2)O(DH),as well as its dissolution and crystallization into short columnarα-CaSO_(4)·0.5H_(2)O(α-HH).Remarkably,with the molar ratio of SO_(4)^(2-)/Ca^(2+)at 1.8,the degree of neutralization(NH_(3)/HNO_(3) molar ratio)at 1.7,the reaction temperature of 94℃,and the reaction time of 300 min,the decalcification rate can reach 86.89%,of which the high-strengthα-CaSO_(4)·0.5H_(2)O(α-HH)will be obtained.Noteworthy,the deep decalcification product meets the standards for the production of fine phosphates and highly water-soluble phosphate fertilizers.Consequently,the 2 h flexural strength ofα-HH is 5.3 MPa and the dry compressive strength is 36.8 MPa,which is up to the standard of commercialα-HH.展开更多
This work aimed to use oyster shell powder (OSP) as the partial replacement of Ag/TiO2 particle to obtain multifunctional β-hemihydrate gypsum.Thus,the β-hemihydrate gypsum was mixed with different contents of OSP a...This work aimed to use oyster shell powder (OSP) as the partial replacement of Ag/TiO2 particle to obtain multifunctional β-hemihydrate gypsum.Thus,the β-hemihydrate gypsum was mixed with different contents of OSP and Ag/TiO2 particle.Antibacterial and MB removal experiments were conducted to assess the antibacterial characteristic and photocatalytic activity of β-hemihydrate gypsum with Ag/TiO2 particle and OSP.Besides,the formaldehyde degradation test was carried out to evaluate its formaldehyde removal ratio.Moreover,their setting times,compressive and flexural strengths at 1,3,and 28 days were comparatively analyzed.The experimental results prove that the composite use of OSP and Ag/TiO2 particle provide feasible multifunction for the β-hemihydrate gypsum.They can further improve the bactericidal rates and exhibit extra MB removal ratios compared with the gypsum plasters with single Ag/TiO2 particle.Besides,they can increase the formaldehyde degradation ratios,and this promotion is related to the introduction of Ag/TiO2 particle.However,OSP delays the initial setting time but promotes the final setting time of β-hemihydrate gypsum,and Ag/TiO2 particle hardly affects the setting times.Furthermore,OSP reduces the strengths of plasters at 1,3,and 28 days.But in general,the composite addition of OSP and Ag/TiO2 particle increase the compressive and flexural strengths of gypsum plasters at 1,3,and 28 days.These results provide theoretical guidance for the recycling of OSP and the preparation of gypsum-based products with antibacterial and formaldehyde degradation capabilities.展开更多
Flue gas desulfurization gypsum and clover planting alleviated the soil salinization stress.Soil pH and total phosphorus affected the bacterial communi-ties.Total phosphorus affected the fungal communities.Flue gas de...Flue gas desulfurization gypsum and clover planting alleviated the soil salinization stress.Soil pH and total phosphorus affected the bacterial communi-ties.Total phosphorus affected the fungal communities.Flue gas desulfurization gypsum and clover planting improved jujube quality.The coastal area of Shandong Province,characterized by coastal saline tidal soil,is one of the main production areas of winter jujube in China.However,the low soil fertility and poor soil structure in jujube orchard restricted the development of the jujube industry.The objectives of this study were to 1)evaluate the effect of application of flue gas desulfurization(FGD)gypsum and clover planting on soil quality improvement and soil microbial community structure of jujube orchard;2)investigate the effects of two measures on the nutrition and quality of winter jujube.The results showed that FGD gypsum reduced the soil total salt content by 65.6%,and clover planting increased the soil organic matter content by 30.7%,which effectively alleviated the soil salinization stress and improved the soil structure.Soil pH and total phosphorus(TP)were the main determinants influencing bacterial community composition,and TP was the dominant factor of the fungal community composition in the saline-alkali soils.Meanwhile,FGD gypsum addition and clover planting significantly increased the sugar degree and Vc content of winter jujube,thus improved jujube quality,and further contributed to the ecological sustainable development of winter jujube industry.展开更多
The synergistic impact of mechanical ball milling and flue gas desulfurization(FGD)gypsum on the dealkalization of bauxite residue was investigated through integrated analyses of solution chemistry,mineralogy,and micr...The synergistic impact of mechanical ball milling and flue gas desulfurization(FGD)gypsum on the dealkalization of bauxite residue was investigated through integrated analyses of solution chemistry,mineralogy,and microtopography.The results showed a significant decrease in Na_(2)O content(>30 wt.%)of FGD gypsum-treated bauxite residue after 30 min of mechanical ball milling.Mechanical ball milling resulted in differentiation of the elemental distribution,modification of the minerals in crystalline structure,and promotion in the dissolution of alkaline minerals,thus enhancing the acid neutralization capacity of bauxite residue.5 wt.%FGD gypsum combined with 30 min mechanical ball milling was optimal for the dealkalization of bauxite residue.展开更多
基金Supported by the National High Technology Research and Development Program of China(2006AA06Z385) the Science Foundation of Wuhan University of Science and Technology(2008RC06)
基金supported by the National Natural Science Foundation of China(No.52279138)supported by Scientific Research Project of Shanxi Province(2018SF-367).
文摘The adsorption method has the advantages of low cost,high efficiency,and environmental friendliness in treating fluorinated wastewater,and the adsorbent material is the key.This study combines the inherent anion-exchange adsorption properties of layered double hydroxides(LDHs).Self-supported porous adsorbent materials loaded with AFm and AFt were prepared from a composite cementitious system consisting of calcium aluminate cement(CAC)and flue gas desulfurization gypsum(FGDG)by chemical foaming technique.The mineral composition of the adsorbent material was characterized by X-ray diffraction(XRD)and Scanning electron microscopy(SEM).Through the static adsorption experiment,the adsorption effect of the mineral composition of the adsorbent on fluoride ions was deeply analyzed,and the adsorption mechanism was revealed.XRD and SEM showed that the main hydration phases of the composite cementitious system consisting of CAC and FGDG are AFm,AFt,AH_(3),and CaSO_(4)·2H_(2)O.FGDG accelerates the hydration process of CAC and inhibits the transformation of AFt to AFm.The AFt content increased,and the AFm content decreased or even disappeared as the amount of FGDG increased.Static adsorption experiment results showed that AFm and AFt in adsorbent materials could significantly enhance the adsorption of fluoride ions.The adsorption of F^(−)in aqueous solution by PAG tends more towards monolayer adsorption with a theoretical maximum capacity of 108.70 mg/g and is similar to the measured value of 112.77 mg/g.
基金supported by the State Key Laboratory of Mineral Processing Science and Technology Open Fund(BGRIMM-KJSKL-2017-16)Liaoning Provincial Department of Education Youth Project(LJ2017QL028)Coal Resource Safety Mining and Clean Utilization Engineering Research Center Open Fund(LNTU15KF18)。
文摘In this paper,the solid waste desulfurization gypsum produced by coal-fired power plants was used as a raw material to prepare calcium sulfate whiskers with high application prospects.Calcium sulfate whiskers with uniform morphology and high aspect ratio can be prepared by hydrothermal method in sulfuric acid solution.A new process of desulfurization gypsum activated by high-energy grinding to reduce the reaction temperature and sulfuric acid concentration was developed.Through the comparison of product morphology,the best grinding time was determined to be 3.5 h.The mechanism of desulfurization gypsum through physical–chemical coupling to reduce energy consumption was clarified.The activation of desulfurization gypsum by grinding and the acidic environment provided by the sulfuric acid solution made the calcium sulfate solution reached rapid saturation and accelerated the nucleation rate.By calculating the conversion and crystallization rate of calcium sulfate whiskers,it was found that there were obvious"autocatalytic"kinetic characteristics during the crystallization process.
基金Funded by the National Natural Science Foundation of China(Nos.51208370,51172164)the Doctoral Program of Higher Education of China(No.20110072120046)+1 种基金the Fundamental Research Funds for the Central Universities(No.0500219170)the Opening Measuring Fund of LargeApparatus of Tongji University(No.0002012011)
文摘The feasibility of flue gas desulphurization (FGD) as concrete admixture was studied. A combined concrete admixture of the thermally-treated FGD gypsum and slag powder was explored. The FGD gypsum was roasted at 200℃ for 60 min and then mixed with the slag powder to form FGD gypsum-slag powder combined admixture in which the SO3 content was 3.5wt%. Cement was partially and equivalently replaced by slag powder alone or FGD gypsum-slag powder, at concentration of 25wt%, 40wt%, and 50wt%, respectively. The setting times, hydration products, total porosity and pore size distributions of the paste were determined. The compressive strength and drying shrinkage of cement mortar and concrete were also tested. The experimental results show that, in the presence of FGD gypsum, the setting times are much slower than those of pastes in the absence of FGD gypsum. The combination of FGD gypsum and slag powder provides synergistic benefits above that of slag powder alone. The addition of FGD gypsum provides benefit by promoting ettringite formation and forms a compact microstructure, increasing the compressive strength and reduces the drying shrinkage of cement mortar and concrete.
基金supported by the National Key Research and Development Program of China(2018YFC1900206-2)Science&Technology Plan Projects of Guizhou Province(Qiankehe Service Enterprises[2018]4011)Science and Technology Support Plan Project of Guizhou Provincial:Qiankehe Support[2021]General 487。
文摘The freezing acidolysis solution of the nitric acid-phosphate fertilizer process has a high calcium content,which makes it difficult to produce fine phosphate and high water-soluble phosphate fertilizer products.Here,based on the potential crystallization principle of calcium sulfate in NH_(4)NO_(3)-H_(3)PO_(4)-H_(2)O,the deep decalcification(i.e.calcium removal)technology to achieveα-high-strength gypsum originated from freezing acidolysis-solutions has been firstly proposed and investigated.Typically,calcium can be removed from the factory-provided freezing acidolysis-solution by neutralizing it with ammonia,followed by the addition of ammonium sulfate solution.As a result,the formation of calcium sulfate in the reaction system undergoes the nucleation and growth of CaSO_(4)·2H_(2)O(DH),as well as its dissolution and crystallization into short columnarα-CaSO_(4)·0.5H_(2)O(α-HH).Remarkably,with the molar ratio of SO_(4)^(2-)/Ca^(2+)at 1.8,the degree of neutralization(NH_(3)/HNO_(3) molar ratio)at 1.7,the reaction temperature of 94℃,and the reaction time of 300 min,the decalcification rate can reach 86.89%,of which the high-strengthα-CaSO_(4)·0.5H_(2)O(α-HH)will be obtained.Noteworthy,the deep decalcification product meets the standards for the production of fine phosphates and highly water-soluble phosphate fertilizers.Consequently,the 2 h flexural strength ofα-HH is 5.3 MPa and the dry compressive strength is 36.8 MPa,which is up to the standard of commercialα-HH.
基金Funded by the National Natural Science Foundation of China(51878479)。
文摘This work aimed to use oyster shell powder (OSP) as the partial replacement of Ag/TiO2 particle to obtain multifunctional β-hemihydrate gypsum.Thus,the β-hemihydrate gypsum was mixed with different contents of OSP and Ag/TiO2 particle.Antibacterial and MB removal experiments were conducted to assess the antibacterial characteristic and photocatalytic activity of β-hemihydrate gypsum with Ag/TiO2 particle and OSP.Besides,the formaldehyde degradation test was carried out to evaluate its formaldehyde removal ratio.Moreover,their setting times,compressive and flexural strengths at 1,3,and 28 days were comparatively analyzed.The experimental results prove that the composite use of OSP and Ag/TiO2 particle provide feasible multifunction for the β-hemihydrate gypsum.They can further improve the bactericidal rates and exhibit extra MB removal ratios compared with the gypsum plasters with single Ag/TiO2 particle.Besides,they can increase the formaldehyde degradation ratios,and this promotion is related to the introduction of Ag/TiO2 particle.However,OSP delays the initial setting time but promotes the final setting time of β-hemihydrate gypsum,and Ag/TiO2 particle hardly affects the setting times.Furthermore,OSP reduces the strengths of plasters at 1,3,and 28 days.But in general,the composite addition of OSP and Ag/TiO2 particle increase the compressive and flexural strengths of gypsum plasters at 1,3,and 28 days.These results provide theoretical guidance for the recycling of OSP and the preparation of gypsum-based products with antibacterial and formaldehyde degradation capabilities.
基金supported by the Forestry Science and Technology Innovation Project of Shandong Province(grant number 2019LY009)the National Key Basic Research Program of China(grant number2021YFD190090101).
文摘Flue gas desulfurization gypsum and clover planting alleviated the soil salinization stress.Soil pH and total phosphorus affected the bacterial communi-ties.Total phosphorus affected the fungal communities.Flue gas desulfurization gypsum and clover planting improved jujube quality.The coastal area of Shandong Province,characterized by coastal saline tidal soil,is one of the main production areas of winter jujube in China.However,the low soil fertility and poor soil structure in jujube orchard restricted the development of the jujube industry.The objectives of this study were to 1)evaluate the effect of application of flue gas desulfurization(FGD)gypsum and clover planting on soil quality improvement and soil microbial community structure of jujube orchard;2)investigate the effects of two measures on the nutrition and quality of winter jujube.The results showed that FGD gypsum reduced the soil total salt content by 65.6%,and clover planting increased the soil organic matter content by 30.7%,which effectively alleviated the soil salinization stress and improved the soil structure.Soil pH and total phosphorus(TP)were the main determinants influencing bacterial community composition,and TP was the dominant factor of the fungal community composition in the saline-alkali soils.Meanwhile,FGD gypsum addition and clover planting significantly increased the sugar degree and Vc content of winter jujube,thus improved jujube quality,and further contributed to the ecological sustainable development of winter jujube industry.
基金the National Natural Science Foundation of China(Nos.42177391,42077379)the Natural Science Foundation of Hunan Province,China(No.2022JJ20060)+1 种基金the Central South University Innovation-driven Research Program,China(No.2023CXQD065)the Fundamental Research Funds for the Central Universities of Central South University,China(No.2023ZZTS0800).
文摘The synergistic impact of mechanical ball milling and flue gas desulfurization(FGD)gypsum on the dealkalization of bauxite residue was investigated through integrated analyses of solution chemistry,mineralogy,and microtopography.The results showed a significant decrease in Na_(2)O content(>30 wt.%)of FGD gypsum-treated bauxite residue after 30 min of mechanical ball milling.Mechanical ball milling resulted in differentiation of the elemental distribution,modification of the minerals in crystalline structure,and promotion in the dissolution of alkaline minerals,thus enhancing the acid neutralization capacity of bauxite residue.5 wt.%FGD gypsum combined with 30 min mechanical ball milling was optimal for the dealkalization of bauxite residue.