In this work,a two-step metal organic chemical vapor deposition(MOCVD)method was applied for growingβ-Ga_(2)O_(3) film on c-plane sapphire.Optimized buffer layer growth temperature(T_(B))was found at 700℃ and theβ-...In this work,a two-step metal organic chemical vapor deposition(MOCVD)method was applied for growingβ-Ga_(2)O_(3) film on c-plane sapphire.Optimized buffer layer growth temperature(T_(B))was found at 700℃ and theβ-Ga_(2)O_(3) film with full width at half maximum(FWHM)of 0.66°was achieved.A metal−semiconductor−metal(MSM)solar-blind photodetector(PD)was fabricated based on theβ-Ga_(2)O_(3) film.Ultrahigh responsivity of 1422 A/W@254 nm and photo-to-dark current ratio(PDCR)of 10^(6) at 10 V bias were obtained.The detectivity of 2.5×10^(15) Jones proved that the photodetector has outstanding performance in detecting weak signals.Moreover,the photodetector exhibited superior wavelength selectivity with rejection ratio(R_(250 nm)/R_(400 nm))of 105.These results indicate that the two-step method is a promising approach for preparation of high-qualityβ-Ga_(2)O_(3)films for high-performance solar-blind photodetectors.展开更多
High qualityβ-Ga_(2)O_(3)single crystal nanobelts with length of 2−3 mm and width from tens of microns to 132μm were synthesized by carbothermal reduction method.Based on the grown nanobelt with the length of 600μm...High qualityβ-Ga_(2)O_(3)single crystal nanobelts with length of 2−3 mm and width from tens of microns to 132μm were synthesized by carbothermal reduction method.Based on the grown nanobelt with the length of 600μm,the dual-Schottky-junctions coupling device(DSCD)was fabricated.Due to the electrically floating Ga_(2)O_(3)nanobelt region coupling with the double Schottky-junctions,the current I_(S2)increases firstly and rapidly reaches into saturation as increase the voltage V_(S2).The saturation current is about 10 pA,which is two orders of magnitude lower than that of a single Schottky-junction.In the case of solar-blind ultraviolet(UV)light irradiation,the photogenerated electrons further aggravate the coupling physical mechanism in device.I_(S2)increases as the intensity of UV light increases.Under the UV light of 1820μW/cm^(2),I_(S2)quickly enters the saturation state.At V_(S2)=10 V,photo-to-dark current ratio(PDCR)of the device reaches more than 104,the external quantum efficiency(EQE)is 1.6×10^(3)%,and the detectivity(D*)is 7.5×10^(12)Jones.In addition,the device has a very short rise and decay times of 25−54 ms under different positive and negative bias.DSCD shows unique electrical and optical control characteristics,which will open a new way for the application of nanobelt-based devices.展开更多
In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The...In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).展开更多
The Ga_(2)O_(3) films are deposited on the Si and quartz substrates by magnetron sputtering, and annealing. The effects of preparation parameters(such as argon–oxygen flow ratio, sputtering power, sputtering time and...The Ga_(2)O_(3) films are deposited on the Si and quartz substrates by magnetron sputtering, and annealing. The effects of preparation parameters(such as argon–oxygen flow ratio, sputtering power, sputtering time and annealing temperature)on the growth and properties(e.g., surface morphology, crystal structure, optical and electrical properties of the films) are studied by x-ray diffractometer(XRD), scanning electron microscope(SEM), and ultraviolet-visible spectrophotometer(UV-Vis). The results show that the thickness, crystallization quality and surface roughness of the β-Ga_(2)O_(3) film are influenced by those parameters. All β-Ga_(2)O_(3) films show good optical properties. Moreover, the value of bandgap increases with the enlarge of the percentage of oxygen increasing, and decreases with the increase of sputtering power and annealing temperature, indicating that the bandgap is related to the quality of the film and affected by the number of oxygen vacancy defects. The I–V curves show that the Ohmic behavior between metal and β-Ga_(2)O_(3) films is obtained at 900℃. Those results will be helpful for the further research of β-Ga_(2)O_(3) photoelectric semiconductor.展开更多
Theβ-Ga_(2)O_(3)films with different thicknesses are prepared by an atomic layer deposition system.The influence of film thickness on the crystal quality is obvious,indicating that the thicker films perform better cr...Theβ-Ga_(2)O_(3)films with different thicknesses are prepared by an atomic layer deposition system.The influence of film thickness on the crystal quality is obvious,indicating that the thicker films perform better crystal quality,which is verified from x-ray diffraction(XRD)and scanning electron microscope(SEM)results.The Ga_(2)O_(3)-based solar blind photodetectors with different thicknesses are fabricated and studied.The experimental results show that the responsivity of the photodetectors increases exponentially with the increase of the film thickness.The photodetectors with inter-fingered structure based on 900 growth cyclesβ-Ga_(2)O_(3)active layers(corresponding film thickness of 58 nm)exhibit the best performances including a low dark current of 134 fA,photo-to-dark current ratio of 1.5×10^(7),photoresponsivity of 1.56 A/W,detectivity of 2.77×10^(14)Jones,and external quantum efficiency of 764.49%at a bias voltage of 10 V under 254-nm DUV illumination.The photoresponse rejection ratio(R_(254)/R_(365))is up to 1.86×10^(5).In addition,we find that the photoelectric characteristics also depend on the finger spacing of the MSM structure.As the finger spacing decreases from 50μm to10μW,the photoresponsivity,detectivity,and external quantum efficiency increase significantly.展开更多
We investigated the influence of the growth temperature, O_(2) flow, molar ratio between Ga_(2)O_(3) powder and graphite powder on the structure and morphology of the films grown on the c-plane sapphire(0001) substrat...We investigated the influence of the growth temperature, O_(2) flow, molar ratio between Ga_(2)O_(3) powder and graphite powder on the structure and morphology of the films grown on the c-plane sapphire(0001) substrates by a carbothermal reduction method. Experimental results for the heteroepitaxial growth of β-Ga_(2)O_(3) illustrate that β-Ga_(2)O_(3) growth by the carbothermal reduction method can be controlled. The optimal result was obtained at a growth temperature of 1050 °C. The fastest growth rate of β-Ga_(2)O_(3) films was produced when the O_(2) flow was 20 sccm. To guarantee that β-Ga_(2)O_(3) films with both high-quality crystal and morphology properties, the ideal molar ratio between graphite powder and Ga_(2)O_(3) powder should be set at 10 : 1.展开更多
基金This work was supported by the National Key Research and Development Program of China(Grant No.2020YFB2206103)。
文摘In this work,a two-step metal organic chemical vapor deposition(MOCVD)method was applied for growingβ-Ga_(2)O_(3) film on c-plane sapphire.Optimized buffer layer growth temperature(T_(B))was found at 700℃ and theβ-Ga_(2)O_(3) film with full width at half maximum(FWHM)of 0.66°was achieved.A metal−semiconductor−metal(MSM)solar-blind photodetector(PD)was fabricated based on theβ-Ga_(2)O_(3) film.Ultrahigh responsivity of 1422 A/W@254 nm and photo-to-dark current ratio(PDCR)of 10^(6) at 10 V bias were obtained.The detectivity of 2.5×10^(15) Jones proved that the photodetector has outstanding performance in detecting weak signals.Moreover,the photodetector exhibited superior wavelength selectivity with rejection ratio(R_(250 nm)/R_(400 nm))of 105.These results indicate that the two-step method is a promising approach for preparation of high-qualityβ-Ga_(2)O_(3)films for high-performance solar-blind photodetectors.
基金supported by Natural Science Basic Research Program in Shaanxi Province of China(No.2023-JCYB-574)National Natural Science Foundation of China(No.62204203).
文摘High qualityβ-Ga_(2)O_(3)single crystal nanobelts with length of 2−3 mm and width from tens of microns to 132μm were synthesized by carbothermal reduction method.Based on the grown nanobelt with the length of 600μm,the dual-Schottky-junctions coupling device(DSCD)was fabricated.Due to the electrically floating Ga_(2)O_(3)nanobelt region coupling with the double Schottky-junctions,the current I_(S2)increases firstly and rapidly reaches into saturation as increase the voltage V_(S2).The saturation current is about 10 pA,which is two orders of magnitude lower than that of a single Schottky-junction.In the case of solar-blind ultraviolet(UV)light irradiation,the photogenerated electrons further aggravate the coupling physical mechanism in device.I_(S2)increases as the intensity of UV light increases.Under the UV light of 1820μW/cm^(2),I_(S2)quickly enters the saturation state.At V_(S2)=10 V,photo-to-dark current ratio(PDCR)of the device reaches more than 104,the external quantum efficiency(EQE)is 1.6×10^(3)%,and the detectivity(D*)is 7.5×10^(12)Jones.In addition,the device has a very short rise and decay times of 25−54 ms under different positive and negative bias.DSCD shows unique electrical and optical control characteristics,which will open a new way for the application of nanobelt-based devices.
基金Funded by the Youth Backbone Teacher Training Plan in University of Henan Province(No.21220028)Science and Technology Research Project of Henan Province(No.242102321066)+2 种基金Natural Science Foundation of Henan Province(No.232300420312)Henan University of Technology Young Backbone Teacher Training Plan(No.21421260)the Innovation Training Program for College Students in Henan Province(No.202310463046)。
文摘In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).
基金Project supported by the Science and Technology Major Project of Shanxi Province,China (Grant No.20181102013)the “1331 Project” Engineering Research Center of Shanxi Province,China (Grant No.PT201801)the Natural Science Foundation of Shanxi Province,China (Grant No.201801D221131)。
文摘The Ga_(2)O_(3) films are deposited on the Si and quartz substrates by magnetron sputtering, and annealing. The effects of preparation parameters(such as argon–oxygen flow ratio, sputtering power, sputtering time and annealing temperature)on the growth and properties(e.g., surface morphology, crystal structure, optical and electrical properties of the films) are studied by x-ray diffractometer(XRD), scanning electron microscope(SEM), and ultraviolet-visible spectrophotometer(UV-Vis). The results show that the thickness, crystallization quality and surface roughness of the β-Ga_(2)O_(3) film are influenced by those parameters. All β-Ga_(2)O_(3) films show good optical properties. Moreover, the value of bandgap increases with the enlarge of the percentage of oxygen increasing, and decreases with the increase of sputtering power and annealing temperature, indicating that the bandgap is related to the quality of the film and affected by the number of oxygen vacancy defects. The I–V curves show that the Ohmic behavior between metal and β-Ga_(2)O_(3) films is obtained at 900℃. Those results will be helpful for the further research of β-Ga_(2)O_(3) photoelectric semiconductor.
基金Project supported by the Natural Science Basic Research Program of Shaanxi Province,China(Grant No.2022JQ-701)the Scientific Research Program Funded by Shaanxi Provincial Education Department,China(Grant No.21JK0919)。
文摘Theβ-Ga_(2)O_(3)films with different thicknesses are prepared by an atomic layer deposition system.The influence of film thickness on the crystal quality is obvious,indicating that the thicker films perform better crystal quality,which is verified from x-ray diffraction(XRD)and scanning electron microscope(SEM)results.The Ga_(2)O_(3)-based solar blind photodetectors with different thicknesses are fabricated and studied.The experimental results show that the responsivity of the photodetectors increases exponentially with the increase of the film thickness.The photodetectors with inter-fingered structure based on 900 growth cyclesβ-Ga_(2)O_(3)active layers(corresponding film thickness of 58 nm)exhibit the best performances including a low dark current of 134 fA,photo-to-dark current ratio of 1.5×10^(7),photoresponsivity of 1.56 A/W,detectivity of 2.77×10^(14)Jones,and external quantum efficiency of 764.49%at a bias voltage of 10 V under 254-nm DUV illumination.The photoresponse rejection ratio(R_(254)/R_(365))is up to 1.86×10^(5).In addition,we find that the photoelectric characteristics also depend on the finger spacing of the MSM structure.As the finger spacing decreases from 50μm to10μW,the photoresponsivity,detectivity,and external quantum efficiency increase significantly.
基金supported by the National Natural Science Foundation of China under Grant 62104024, Grant 11875097, Grant 12075045, Grant 11975257, Grant 11961141014, and Grant 62074146the Fundamental Research Funds for the Central Universities under Grant DUT19RC (3)074the Natural Science Foundation of Liaoning Province under Grant 2021MS124, Grant 2022020474JH2/1013。
文摘We investigated the influence of the growth temperature, O_(2) flow, molar ratio between Ga_(2)O_(3) powder and graphite powder on the structure and morphology of the films grown on the c-plane sapphire(0001) substrates by a carbothermal reduction method. Experimental results for the heteroepitaxial growth of β-Ga_(2)O_(3) illustrate that β-Ga_(2)O_(3) growth by the carbothermal reduction method can be controlled. The optimal result was obtained at a growth temperature of 1050 °C. The fastest growth rate of β-Ga_(2)O_(3) films was produced when the O_(2) flow was 20 sccm. To guarantee that β-Ga_(2)O_(3) films with both high-quality crystal and morphology properties, the ideal molar ratio between graphite powder and Ga_(2)O_(3) powder should be set at 10 : 1.