Rolling texture development in a dual-phase Mg-Li alloy:The role of temperature

Dual-phase Mg-Li alloys sheets were rolled at four different temperatures ranging from liquid nitrogen to 300℃to explore effect of rolling temperature on texture and mechanical properties of the material.Crystal plasticity simulation was utilized to illustrate the influence of slip activity on rolling texture development.The results show that the rolling texture is largely depended on deformation temperature.Unlike commercial Mg alloys,the critical resolved shear stress of basal slip inα-Mg phase of Mg-Li alloy decreased more significantly by increasing temperature compared to that of pyramidal<c+a>slip.Enhancement of basal slip by increasing temperature triggered a decrease of split angle of basal poles for the double-peak texture.Prismaticslip largely enhanced by increasing temperature upon 200℃,which induced a wider orientation spread along the transverse direction.For theβ-Li phase,the promotion of{110}<111>slip system at elevated temperature triggered the enhancement of{211}<110>and{111}<211>texture components.The cryo-rolled sample exhibited the highest strength compared to the others due to a strong hardening behavior at this temperature.A two-stage hardening behavior was observed in these as-rolled dual-phase alloys.Strain transition at phase boundaries could be the reason for appearance of this two-stage hardening.

Layer thickness dependent plastic deformation mechanism in Ti/TiCu dual-phase nano-laminates

Crystalline/amorphous nanolaminate is an effective strategy to improve the mechanical properties of metallic materials,but the underlying deformation mechanism is still under the way of exploring.Here,the mechanical properties and plastic deformation mechanism of Ti/TiCu dual-phase nanolaminates(DPNLs)with different layer thicknesses are investigated using molecular dynamics simulations.The results indicate that the influence of the layer thickness on the plastic deformation mechanism in crystalline layer is negligible,while it affects the plastic deformation mechanism of amorphous layers distinctly.The crystallization of amorphous TiCu is exhibited in amorphous parts of the Ti/TiCu DPNLs,which is inversely proportional to the layer thickness.It is observed that the crystallization of the amorphous TiCu is a process driven by stress and heat.Young's moduli for the Ti/TiCu DPNLs are higher than those of composite material due to the amorphous/crystalline interfaces.Furthermore,the main plastic deformation mechanism in crystalline part:grain reorientation,transformation from hexagonal-close-packed-Ti to face-centered cubic-Ti and body-centered cubic-Ti,has also been displayed in the present work.The results may provide a guideline for design of high-performance Ti and its alloy.

Criterion of gas and solid dual-phase flow atomization crash in molten metal

A self-invented atomization process, in which molten metal is atomized into powder by a high-velocity gas stream carrying solid particles as the atomization medium, was introduced. The characteristics of powders prepared by common gas atomization and dual-phase flow atomization under similar conditions were compared. The experimental results show that the dual-phase flow-atomized powders have average particle sizes that are one-half that of the common gas-atomized particles;additionally, they possess a finer microstructure and higher cooling rate under the same atomization gas pressure and the same gas flow. The Weber number in the crash criteria of liquid atomization is adopted to measure the crash ability of the atomization media. The Weber number of the dual-phase flow atomization medium is the sum of that of the gas and the solid particles. Furthermore, the critical equation of the crash model in dual-phase flow atomization is established, and the main regularities associated with this process were analyzed.

Numerical simulation on the microstress and microstrain of low Si-Mn-Nb dual-phase steel

According to the stress-strain curves of single-phase martensite and single-phase ferrite steels,whose compositions are similar to those of martensite and ferrite in low Si-Mn-Nb dual-phase steel,the stress-strain curve of the low Si-Mn-Nb dual-phase steel was simulated using the finite element method（FEM）.The simulated result was compared with the measured one and they fit closely with each other, which proves that the FE model is correct.Based on the FE model,the microstress and microstrain of the dual-phase steel were analyzed. Meanwhile,the effective factors such as the volume fraction of martensite and the yield stress ratio between martensite and ferrite phases on the stress-strain curves of the dual-phase steel were simulated,too.The simulated results indicate that for the low Si-Mn-Nb dual-phase steel, the maximum stress occurs in the martensite region,while the maximum strain occurs in the ferrite one.The effect of the volume fraction of martensite（fm） and the yield stress ratio on the stress-strain curve of the dual-phase steel is small in the elastic part,while it is obvious in the plastic part.In the plastic part of this curve,the strain decreases with the increase of f_M,while it decreases with the decrease of the yield stress ratio.

Microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels

The microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels were studied by scanning electron microscopy （SEM）, transmission electron microscopy （TEM）, and tensile test. The results show that Si can promote the transformation of austenite （γ） to ferrite （α）, enlarge the （α＋γ） region, and increase the aging stability of martensite by inhibiting carbide precipitation. Adding Cr leads to the formation of retained austenite and martensite/austenite （M/A） constituents, as well as the decomposi- tion of martensite during the overaging stage. Both of the steels show higher initial strain-hardening rates and two-stage strain-hardening characteristics. The C-Mn-Si-Nb steel shows the higher strain-hardening rate than the C-Mn-Cr-Nb steel in the first stage; however, there is no significant difference in the second stage. Although the tensile strength and elongation of the two steels both exceed 1000 MPa and 15%, respectively, the comprehensive mechanical properties of the C-Mn-Si-Nb steel are superior.

Effect of hot-dip galvanizing processes on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel

A C–Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s(process A) or rapidly cooled to 350°C and then reheated to 450°C(process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel(DP600) was investigated using optical microscopy, scanning electron microscopy(SEM), transmission electron microscopy(TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength(YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient(n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength(UTS) and elongation(A80) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties(YS = 362 MPa, UTS = 638 MPa, A_(80) = 24.3%, n = 0.17) was obtained via process A.

Effects of pre-strain and baking parameters on the microstructure and bake-hardening behavior of dual-phase steel

In a typical process, C-Mn steel was annealed at 800℃ for 180 s, and then cooled rapidly to obtain the ferrite-martensite microstructure. After pre-straining, the specimens were baked and the corresponding bake-hardening （BH） values were determined as a function of pre-strain, baking temperature, and baking time. The influences ofpre-strain, baking temperature and baking time on the microstructure evolution and bake-hardening behavior of the dual-phase steel were investigated systematically. It was found that the BH value apparently increased with an increase in pre-strain in the range from 0 to 1%; however, increasing pre-strain from 1% to 8% led to a decrease in the BH value. Furthermore, an increase in baking temperature favored a gradual improvement in the BH value because of the formation of Cottrell atmosphere and the precipitation of carbides in both the ferrite and martensite phases. The BH value reached a maximum of 110 MPa at a baking temperature of 300℃. Moreover, the BH value enhanced significantly with increasing baking time from 10 to 100 min.

Tensile strength prediction of dual-phase Al0.6CoCrFeNi high-entropy alloys

The evolution of the microstructure and tensile properties of dual-phase Al0.6CoCrFeNi high-entropy alloys(HEAs)subjected to cold rolling was investigated.The homogenized Al0.6CoCrFeNi alloys consisted of face-centered-cubic and body-centered-cubic phases,presenting similar mechanical behavior as the as-cast state.The yield and tensile strengths of the alloys could be dramatically enhanced to^1205 MPa and^1318 MPa after 50%rolling reduction,respectively.A power-law relationship was discovered between the strain-hardening exponent and rolling reduction.The tensile strengths of this dual-phase HEA with different cold rolling treatments were predicted,mainly based on the Hollomon relationship,by the strain-hardening exponent,and showed good agreement with the experimental results.

Oxygen permeability and CO_2-tolerance of Ce_(0.8)Gd_(0.2)O_(2-δ)-Ln BaCo_2O_(5+δ) dual-phase membranes

A series of oxygen permeable dual-phase composite oxides 60 wt% Ce0.8Gd0.2O2-δ-40 wt% LnBaCo2O5＋δ （CGO-LBCO, Ln = La, Pr, Nd, Sin, Gd and Y） were synthesized through a sol-gel route and effects of the Ln3＋ cations on their phase structure, oxygen permeability and chemical stability against CO2 were investigated systemically by XRD, SEM, TG-DSC and oxygen permeation experiments. XRD patterns reveal that the larger Ln3＋ cations （La3＋, Pr3＋ and Nd3＋） successfully stabilized the double-layered perovskite structure of sintered LBCO, while the smaller ones （Sm3＋, Gd3＋, and Y3＋） resulted in the partial decomposition of LBCO with some impurities formed. CGO-PBCO yields the highest oxygen permeation flux, reaching 2.8× 10^-7 mol.s-1.cm-2 at 925 ℃ with 1 mm thickness under air/He gradient. The TG-DSC profiles in 20 mol% CO2/N2 and oxygen permeability experiments with CO2 as sweep gas show that CGO-YBCO demonstrates the best chemical stability against CO2, possibly due to its minimum basicity. The stable oxygen permeation flux of CGO-YBCO under CO2 atmosphere reveals its potential application in the oxy-fuel combustion route for CO2 capture.

Effect of intercritical annealing on microstructure,mechanical properties,and work-hardening behavior of ultrahigh-strength dual-phase steels with different silicon contents

In this study,three kinds of dual-phase(DP) steels were used to investigate the influence of silicon content and intercritical annealing temperature on their microstructures,mechanical properties,and work-hardening behaviors. By adding silicon and matching the critical annealing temperature,a new DP steel(1.0Si and intercritically annealed at 790 ℃) that exhibits an excellent combination of ultrahigh strength and adequate ductility was obtained. Variations in the strength,elongation,and fracture mechanism of the specimens with respect to different intercritical annealing temperatures were correlated to microstructural features. With an increase in the silicon content,there is no significant change in the martensitic band structure or ferrite morphology. At the same annealing temperature,the yield strength and yield strength ratio of the specimens decreased,but at different annealing temperatures,the tensile strength was reduced. The Hollomon analysis results indicate that the workhardening behavior obeys a two-stage work-hardening mechanism. With an increasing intercritical annealing temperature,the "transition strain"shifts to the left,and with an increasing silicon content,the "transition strain"shifts to the right. The surface exhibits ductile fractures characterized by a high density of microvoid dimples. With an increase in the silicon content,the average dimple size on the fracture surface decreases and the plasticity of the material increases.

Effect of Holding Time on the Microstructure and Mechanical Properties of Dual-Phase Steel during Intercritical Annealing

Continuous annealing simulation tests were conducted by using a continuous annealing thermomechanical simulator. Holding times of 5, 60, 180, and 480 seconds for an intercritical annealing temperature of 820℃ were adopted to investigate the evolution of the mierostructure and mechanical properties of ferrite-bainite dual-phase steel. The ferrite-bainite dual-phase steel was characterized by high strength and low yield ratio due to the presence of the constituents （polygonal ferrite, bainite, martensite and retained austenite） of the steel microstructure. Specimen 3 exhibits the highest value of A50 （7.67%） and a product of Rm × A50 （10453MPa%） after a 180s holding. This is likely attributed to the presence of a C-enriched retained anstenite in the microstructure. And the effect of martensite islands and carbide precipitate is thought to be able to contribute in strengthening the present steel. It is expected that equilibrium of anstenite fraction would be reached for reasonable intercritical holding period, regardless of the heating temperature. The results suggest that long increasing holding times may not be needed because the major phase of the microstructure does not change very significantly. It is favorable for industrial production of DP steels to shorten holding times. Key words： ferrite-bainite dual-phase steel; holding time; martensite islands; mechanical properties

Corrosion behavior of tempered dual-phase steel embedded in concrete

Dual-phase （DP） steels with different martensite contents were obtained by appropriate heat treatment of an SAE1010 structural carbon steel, which was cheap and widely used in the construction industry. The corrosion behavior of DP steels in concrete was investigated under various tempering conditions. Intercritical annealing heat treatment was applied to the reinforcing steel to obtain DP steels with different contents of martensite. These DP steels were tempered at 200, 300, and 400℃ for 45 min and then cooled to room temperature. Corrosion experiments were conducted in two stages. In the first stage, the corrosion potential of DP steels embedded in concrete was measured every day for a period of 30 d based on the ASTM C 876 standard. In the second stage, the anodic and cathodic polarization values of these steels were obtained and subsequently the corrosion currents were determined with the aid of cathodic polarization curves. It was observed that the amount of second phase had a definite effect on the corrosion behavior of the DP steel embedded in concrete. As a result of this study, it is found that the corrosion rate of the DP steel increases with an increase in the amount of martensite.

Effect of microvoids on microplasticity behavior of dual-phase titanium alloy under high cyclic loading(Ⅰ):Crystal plasticity analysis

A crystal plasticity finite element(CPFE)model was established and 2D simulations were carried out to study the relationship between microvoids and the microplasticity deformation behavior of the dual-phase titanium alloy under high cyclic loading.Results show that geometrically necessary dislocations(GND)tend to accumulate around the microvoids,leading to an increment of average GND density.The influence of curvature in the tip plastic zone(TPZ)on GND density is greater than that of the size of the microvoid.As the curvature in TPZ and the size of the microvoid increase,the cumulative shear strain(CSS)in the primaryα,secondaryα,andβphases increases.Shear deformation in the prismatic slip system is dominant in the primaryαphase.As the distance between the microvoids increases,the interactive influence of the microvoids on the cumulative shear strain decreases.

Tailoring phase fractions of T'and η' phases in dual-phase strengthened Al−Zn−Mg−Cu alloy via ageing treatment

Hardness tests and transmission electron microscopy were used to investigate the strategy of tailoring the phase fraction of precipitates in an Al-Zn-Mg-Cu alloy strengthened by T’ and η’ phases. Different phase fractions of T’ and η’ phases are presented in samples subjected to either single or two stages of ageing treatments at 120 and 150 ℃.For both types of ageing, the precipitation of η’ phase is found to be promoted by ageing at lower temperature and its phase fraction increases with prolonging ageing time at 120 ℃;whereas the phase fractions of T’ and η’ phases almost remain constant during ageing at 150 ℃. Besides, the strain fields produced by T’ and η’ phases were analyzed by using the geometric phase analysis technique, and on a macroscale the contributions of T’ and η’ phases to precipitation strengthening have been quantitatively predicted by combining the size, phase fraction and number density of precipitates.

Effects of overaging temperature on the microstructure and properties of 600MPa cold-rolled dual-phase steel

C–Mn steels prepared by annealing at 800°C for 120 s and overaging at 250–400°C were subjected to pre-straining（2%） and baking treatments（170°C for 20 min） to measure their bake-hardening（BH_2） values. The effects of overaging temperature on the microstructure, mechanical properties, and BH_2 behavior of 600 MPa cold-rolled dual-phase（DP） steel were investigated by optical microscopy, scanning electron microscopy, and tensile tests. The results indicated that the martensite morphology exhibited less variation when the DP steel was overaged at 250–350°C. However, when the DP steel was overaged at 400°C, numerous non-martensite and carbide particles formed and yield-point elongation was observed in the tensile curve. When the overaging temperature was increased from 250 to 400°C, the yield strength increased from 272 to 317 MPa, the tensile strength decreased from 643 to 574 MPa, and the elongation increased from 27.8% to 30.6%. Furthermore, with an increase in overaging temperature from 250 to 400°C, the BH_2 value initially increases and then decreases. The maximum BH_2 value of 83 MPa was observed for the specimen overaged at 350°C.

Plastic Deformation Mechanism of Dual-phase Steel at Different Strain Rates

The mechanical properties of dual-phase steel (DP1000) over the strain rate range of 10^-3-10^3 s^-1 were studied using an electronic universal testing machine and a high-speed tensile testing machine.The plastic deformation mechanism was investigated from the perspectives of the strain rate sensitivity index,activation volume and dynamic factors.The results show that the tensile strength and yield strength of DP1000 increase as the strain rate increases.The elongation increases without any change after fracture,and then decreased rapidly when the strain rate reaches 103 s^-1.The true strain curves of DP1000 show three stages:the point of instability decreases in the strain range of 10^-3-10^-1 s^-1;the instability point increases between 100-5×10^2 s^-1;above 5×10^2 s^-1,and the instability strain becomes smaller again.The plastic deformation mechanism of the DP was determined by the competitive contributions of work hardening (strain hardening,strain rate hardening) and softening effects due to the adiabatic temperature rise.

Microstructure evolution and mechanical properties of 1000 MPa cold rolled dual-phase steel

The microstructure evolution of 1 000 MPa cold rolled dual-phase (DP) steel at the initial heating stages of the continuous annealing process was analyzed. The effects of different overaging temperatures on the microstructures and mechanical properties of 1 000 MPa cold rolled DP steel were investigated using a Gleeble-3500 thermal/mechanical simulator. The experimental results show that ferrite recovery and recrystallization, pearlite dissolution and austenite nucleation and growth take place in the annealing process of ultra-high strength cold rolled DP steel. When being annealed at 800 ℃ for 80 s, the tensile strength and total elongation of DP steel can reach 1 150 MPa and 13%, respectively. The microstructure of DP steel mainly consists of a mixture of ferrite and martensite. The steel exhibits low yield strength and continuous yielding which is commonly attributed to mobile dislocations introduced during cooling process from the intercritical annealing temperature.

CHARACTERISTICS OF MARTENSITIC TRANSFORMATION IN DUAL-PHASE STEELS

A theorectical expression for the driving force and M_(?) point of martensitic transformation has been proposed.The M_(?) values using this expression are in good agreement with that obtained experimentally.It was found that the values of M_(?) and M_(?) are not only related to the carbon content in martensite,but also to the volume fraction of ferrite.

The Study of Dual-phase Steel after Cyclic Deformation at Various Strain Amplitudes

Low cycle fatigue tests under plastic strain control were carried out with a dual-phase steel containing 23 Vol.-％ martensite. Specimens hardened rapidly at first few cycles followed by a slight softening to saturation stages when cycled at higher strain amplitudes, whereas at lower strain amplitudes the specimens presented continually hardening for a long time until saturation. TEM examination of the saturation dislocation structures show that clusters, parallel walls and cells were found at low, medium and high strain amplitude, respectively. It also has been found that the martensite/ferrite interfaces did not affect the dislocation structures signi- ficantly when a specimen was fatigued at lower strain amplitude. However, the dislocation struc- ture adjacent to the two-phase boundary is dif- ferent to some extent from that in the remote regions in the ferrite when a higher strain amplitude is applied.

EFFECT OF CRACK CLOSURE ON SLOW PROPAGATION IN DUAL-PHASE STEEL

The effect of ferrite content in ferrite-martensite dual-phase steel on the initiation and prop- agation of fatigue crack and the plastic deformation at crack tip has been studied.In the range of ferrite content from 24.2 to 41.5％,the optimum seems to be 33.8％,of which the crack ini- tiation will be prolonged,the threshold value increased,the propagation rate decreased and the closure stress intensity factor increased.As the propagation force is described by effective stress intensity factor,three steels with various ferrite contents will show the same propagation behaviour on da/dN vs △ K_(eff)curve.It is shown that the closure effect increases with the decrease in △K at the fatigue crack tip.When △K equals to △K_(th),the closure effect reaches a maximum value of0.7 in a dual-phase steel with 33.8％ferrite.