The preparation process of γ-A12O3 nanofiltration membranes were studied by N2 absorption and desorption test and retention rate vs thickness gradient curve method. It was found that template and thermal treatment we...The preparation process of γ-A12O3 nanofiltration membranes were studied by N2 absorption and desorption test and retention rate vs thickness gradient curve method. It was found that template and thermal treatment were key factors for controlling pore size and its distribution. Under the optimized experimental conditions, the BJH (Barret-Joyner-Halenda) desorption average pore diameter, BJH desorption cumulative volume of pores and BET (Brunauer-Emmett-Teller) surface area of obtained membranes were about 3.9 nm, 0.33 cm3/g and 245 m2/g respectively, the pore size distribution was very narrow. Pore size decreased with the increasing of thickness and no evident change after the dense top layer was formed. The optimum thickness can be controlled by retention rate vs thickness gradient curve method.展开更多
γ-Al2O3 membranes were successfidly deposited on the top of porous α-Al2O3 support by sol-gel process and characterized by means of XRD , SEM, N2 adsorption and gas permeation. The γ-Al2O3 membranes, free of pin-h...γ-Al2O3 membranes were successfidly deposited on the top of porous α-Al2O3 support by sol-gel process and characterized by means of XRD , SEM, N2 adsorption and gas permeation. The γ-Al2O3 membranes, free of pin-holes and cracks, adhere tightly to the supports and have a thlekness of about 7μm. When sintered at 400 ℃ , γ-Al2O3 membranes have a rutrrow pore size distribution, with a pore diameter of 3.6nm, and the transport of both H2 and CO2 in supported γ-Al2O3 membrane is governed by Knudsen mechanism, with H2 permeance of 3.3× 10^-6 molm^-2Pa^-1s^-1 and H2/ CO2 permselectivity close to the ideal Knudsen value at 50 ℃ . The γ-Al2O3 membranes are suitable for being used as the substrates of microparoas membranes .展开更多
Spinel lithium manganese oxide ion-sieves have been considered the most promising adsorbents to extract Li^+ from brines and sea water.Here,we report a lithium ion-sieve which was successfully loaded onto tubular α-A...Spinel lithium manganese oxide ion-sieves have been considered the most promising adsorbents to extract Li^+ from brines and sea water.Here,we report a lithium ion-sieve which was successfully loaded onto tubular α-Al2 O3 ceramic substrates by dipping crystallization and post-calcination method.The lithium manganese oxide Li4 Mn5 O(12)was first synthesized onto tubular α-Al2 O3 ceramic substrates as the ion-sieve precursor(i.e.L-AA),and the corresponding lithium ion-sieve(i.e.H-AA) was obtained after acid pickling.The chemical and morphological properties of the ion-sieve were confirmed by X-ray diffraction(XRD) and scanning electron microscopy(SEM).Both L-AA and H-AA showed characteristic peaks of α-Al2 O3 and cubic phase Li4 Mn5 O(12) and the peaks representing cubic phase could still exist after pickling.The lithium manganese oxide Li4 Mn5 O(12) could be uniformly loaded not only on the surface of α-Al2 O3 ubstrates but also inside the pores.Moreover,we found that the equilibrium adsorption capacity of H-AA was 22.9 mg·g^-1.After 12 h adsorption,the adsorption balance was reached.After 5 cycles of adsorption,the adsorption capacity of H-AA was 60.88% of the initial adsorption capacity.The process of H-AA adsorption for Li^+correlated with pseudo-second order kinetic model and Langmuir model.Adsorption thermodynamic parameters regarding enthalpy(△N), Gibbs free energy(△G) and entropy(AS) were calculated.For the dynamic adsorptiondesorption process of H-AA,the H-AA exhibited excellent adsorption performance to Li^+ with the Li^+ dynamic adsorption capacity of 9.74 mg·g^-1 and the Mn^2+dissolution loss rate of 0.99%.After 3 dynamic adsorption-desorption cycles,80% of the initial dynamic adsorption capacity was still kept.展开更多
This paper reports that the transmission of O6＋ ions with energy of 150keV through capillaries in an uncoated Al2O3 membrane was measured, and agreements with previously reported results in general angular distributi...This paper reports that the transmission of O6＋ ions with energy of 150keV through capillaries in an uncoated Al2O3 membrane was measured, and agreements with previously reported results in general angular distribution of the transmitted ions and the transmission fractions as a function of the tilt angle well fitted to Gaussian-like functions were observed. Due tousing an uncoated capillary membrane, our φc is larger than that using a gold-coated one with a smaller value of Ep/q, which suggests a larger equilibrium charge Q∞ in our experiment. The observed special width variation with time and a larger width than that using a smaller Ep/q were qualitatively explained by using mean-field classical transport theory based on a classical-trajectory Monte Carlo simulation.展开更多
文摘The preparation process of γ-A12O3 nanofiltration membranes were studied by N2 absorption and desorption test and retention rate vs thickness gradient curve method. It was found that template and thermal treatment were key factors for controlling pore size and its distribution. Under the optimized experimental conditions, the BJH (Barret-Joyner-Halenda) desorption average pore diameter, BJH desorption cumulative volume of pores and BET (Brunauer-Emmett-Teller) surface area of obtained membranes were about 3.9 nm, 0.33 cm3/g and 245 m2/g respectively, the pore size distribution was very narrow. Pore size decreased with the increasing of thickness and no evident change after the dense top layer was formed. The optimum thickness can be controlled by retention rate vs thickness gradient curve method.
文摘γ-Al2O3 membranes were successfidly deposited on the top of porous α-Al2O3 support by sol-gel process and characterized by means of XRD , SEM, N2 adsorption and gas permeation. The γ-Al2O3 membranes, free of pin-holes and cracks, adhere tightly to the supports and have a thlekness of about 7μm. When sintered at 400 ℃ , γ-Al2O3 membranes have a rutrrow pore size distribution, with a pore diameter of 3.6nm, and the transport of both H2 and CO2 in supported γ-Al2O3 membrane is governed by Knudsen mechanism, with H2 permeance of 3.3× 10^-6 molm^-2Pa^-1s^-1 and H2/ CO2 permselectivity close to the ideal Knudsen value at 50 ℃ . The γ-Al2O3 membranes are suitable for being used as the substrates of microparoas membranes .
基金This work was financially supported by National Key Research and Development Program(2018YFE0203502),ChinaPrimary Research and Development Plan ofJiangsu Province(BE2019117),China and National Students'Platform for Innovation and Entrepreneurship Training(201910291051Z),China.
文摘Spinel lithium manganese oxide ion-sieves have been considered the most promising adsorbents to extract Li^+ from brines and sea water.Here,we report a lithium ion-sieve which was successfully loaded onto tubular α-Al2 O3 ceramic substrates by dipping crystallization and post-calcination method.The lithium manganese oxide Li4 Mn5 O(12)was first synthesized onto tubular α-Al2 O3 ceramic substrates as the ion-sieve precursor(i.e.L-AA),and the corresponding lithium ion-sieve(i.e.H-AA) was obtained after acid pickling.The chemical and morphological properties of the ion-sieve were confirmed by X-ray diffraction(XRD) and scanning electron microscopy(SEM).Both L-AA and H-AA showed characteristic peaks of α-Al2 O3 and cubic phase Li4 Mn5 O(12) and the peaks representing cubic phase could still exist after pickling.The lithium manganese oxide Li4 Mn5 O(12) could be uniformly loaded not only on the surface of α-Al2 O3 ubstrates but also inside the pores.Moreover,we found that the equilibrium adsorption capacity of H-AA was 22.9 mg·g^-1.After 12 h adsorption,the adsorption balance was reached.After 5 cycles of adsorption,the adsorption capacity of H-AA was 60.88% of the initial adsorption capacity.The process of H-AA adsorption for Li^+correlated with pseudo-second order kinetic model and Langmuir model.Adsorption thermodynamic parameters regarding enthalpy(△N), Gibbs free energy(△G) and entropy(AS) were calculated.For the dynamic adsorptiondesorption process of H-AA,the H-AA exhibited excellent adsorption performance to Li^+ with the Li^+ dynamic adsorption capacity of 9.74 mg·g^-1 and the Mn^2+dissolution loss rate of 0.99%.After 3 dynamic adsorption-desorption cycles,80% of the initial dynamic adsorption capacity was still kept.
基金supported by the National Natural Science Foundation of China(Grant No 10775063)
文摘This paper reports that the transmission of O6＋ ions with energy of 150keV through capillaries in an uncoated Al2O3 membrane was measured, and agreements with previously reported results in general angular distribution of the transmitted ions and the transmission fractions as a function of the tilt angle well fitted to Gaussian-like functions were observed. Due tousing an uncoated capillary membrane, our φc is larger than that using a gold-coated one with a smaller value of Ep/q, which suggests a larger equilibrium charge Q∞ in our experiment. The observed special width variation with time and a larger width than that using a smaller Ep/q were qualitatively explained by using mean-field classical transport theory based on a classical-trajectory Monte Carlo simulation.