Precisely refining the electronic structure of electrocatalysts represents a powerful approach to further optimize the electrocatalytic performance.Herein,we demonstrate an ingenious d-d orbital hybridization concept ...Precisely refining the electronic structure of electrocatalysts represents a powerful approach to further optimize the electrocatalytic performance.Herein,we demonstrate an ingenious d-d orbital hybridization concept to construct Mo-doped Co_(9)S_(8) nanorod arrays aligned on carbon cloth(CC)substrate(abbreviated as Mo-Co_(9)S_(8)@CC hereafter)as a high-efficiency bifunctional electrocatalyst toward water electrolysis.It has experimentally and theoretically validated that the 4d-3d orbital coupling between Mo dopant and Co site can effectively optimize the H_(2)O activation energy and lower H^(*)adsorption energy barrier,thereby leading to enhanced hydrogen evolution reaction(HER)and oxygen evolution reaction(OER)activities.Thanks to the unique electronic and geometrical advantages,the optimized Mo-Co_(9)S_(8)@CC with appropriate Mo content exhibits outstanding bifunctional performance in alkaline solution,with the overpotentials of 75 and 234 mV for the delivery of a current density of 10 mA cm^(-2),small Tafel slopes of 53.8 and 39.9 mV dec~(-1)and long-term stabilities for at least 32 and 30 h for HER and OER,respectively.More impressively,a water splitting electrolylzer assembled by the self-supported Mo-Co_(9)S_(8)@CC electrode requires a low cell voltage of 1.53 V at 10 mA cm^(-2)and shows excellent stability and splendid reversibility,demonstrating a huge potential for affordable and scalable electrochemical H_(2) production.The innovational orbital hybridization strategy for electronic regulation herein provides an inspirable avenue for developing progressive electrocatalysts toward new energy systems.展开更多
Heterostructured BiOI@La（OH）3 nanorod photocatalysts were prepared by a facile chemical impregnation method.The enhanced visible light absorption and charge carrier separation can be simultaneously realized after th...Heterostructured BiOI@La（OH）3 nanorod photocatalysts were prepared by a facile chemical impregnation method.The enhanced visible light absorption and charge carrier separation can be simultaneously realized after the introduction of BiOI particles into La（OH）3 nanorods.The BiOI@La（OH）3 composites were applied for visible light photocatalytic oxidization of NO in air and exhibited an enhanced activity compared with BiOI and pure La（OH）3 nanorods.The results show that the energy levels between the La（OH）3 and BiOI phases matched well with each other,thus forming a heterojunctioned BiOI@La（OH）3 structure.This band structure matching could promote the separation and transfer of photoinduced electron-hole pairs at the interface,resulting in enhanced photocatalytic performance under visible light irradiation.The photocatalytic performance of BiOI@La（OH）3 is shown to be dependent on the mass ratio of BiOI to La（OH）3.The highest photocatalytic performance can be achieved when the mass ratio of BiOI to La（OH）3 is controlled at 1.5.A further increase of the mass ratio of BiOI weakened the redox abilities of the photogenerated charge carriers.A new photocatalytic mechanism for BiOI@La（OH）3 heterostructures is proposed,which is directly related to the efficient separation of photogenerated charge carriers by the heterojunction.Importantly,the as-prepared BiOI@La（OH）3 heterostructures exhibited a high photochemical stability after multiple reaction runs.Our findings demonstrate that BiOI is an effective component for the formation of a heterostructure with the properties of a wide bandgap semiconductor,which is of great importance for extending the light absorption and photocatalytic activity of wide bandgap semiconductors into visible light region.展开更多
Oleic acid (denoted as OA) surface-caped lanthanum borate nanorods, abbreviated as OA/LaBO3·H2O, were prepared via hydrothermal method. The microstructures of the as-prepared OA/LaBO3·H2O nanorods were chara...Oleic acid (denoted as OA) surface-caped lanthanum borate nanorods, abbreviated as OA/LaBO3·H2O, were prepared via hydrothermal method. The microstructures of the as-prepared OA/LaBO3·H2O nanorods were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. The friction and wear properties of OA/LaBO3·H2O nanorods in rapeseed oil were evaluated with a four-ball tribo-tester. The results show that the as-prepared OA/LaBO3·H2O nanorods are hydrophobic and display nanorods morphology with uniform diameter of about 50 nm and length of up to 500 nm. In the meantime, OA/LaBO3·H2O nanorods can obviously improve the anti-wear and friction-reducing capacities of rapeseed oil, and the optimal anti-wear and friction-reducing properties of rapeseed oil were obtained at an OA/LaBO3·H2O content of 1% (mass fraction).展开更多
GaN nanorods are successfully synthesized on Si（111） substrates with magnetron sputtering through ammoniating Ga2O3/Co films at 950℃. X-ray diffraction, scanning electron microscopy, high-resolution transmission el...GaN nanorods are successfully synthesized on Si（111） substrates with magnetron sputtering through ammoniating Ga2O3/Co films at 950℃. X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy,and Fourier-transform infrared spectroscopy are used to characterize the samples. The results demonstrate that the nanorods are single-crystal GaN with a hexagonal wurtzite structure and possess relatively smooth surfaces. The growth mechanism of GaN nanorods is also discussed.展开更多
ZnO nanorod arrays （NRs） were synthesized on the fluorine-doped SnO2 transparent conductive glass （FTO） by a simple chemical bath deposition （CBD） method combined with alkali-etched method in potassium hydroxide...ZnO nanorod arrays （NRs） were synthesized on the fluorine-doped SnO2 transparent conductive glass （FTO） by a simple chemical bath deposition （CBD） method combined with alkali-etched method in potassium hydroxide （KOH） solution. X-ray diffraction （XRD）, scanning electron microscopy （SEM） and current-voltage （I-V） curve were used to characterize the structure, morphologies and optoelectronic properties. The results demonstrated that ZnO NRs had wurtzite structures, the morphologies and photovoltaic properties of ZnO NRs were closely related to the concentration of KOH and etching time, well-aligned and uniformly distributed ZnO NRs were obtained after etching with 0.1 mol/L KOH for 1 h. ZnO NRs treated by KOH had been proved to have superior photovoltaic properties compared with high density ZnO NRs. When using ZnO NRs etched with 0.1 mol/L KOH for 1 h as the anode of solar cell, the conversion efficiency, short circuit current and open circuit voltage, compared with the unetched ZnO NRs, increased by 0.71%, 2.79 mA and 0.03 V, respectively.展开更多
MnxNi0.5-xZn0.5Fe2O4 nanorods were successfully synthesized by the thermal treatment of rod-like precursors that were fabricated by the co-precipitation of Mn2＋, Ni2＋, and Fe2＋ in the lye. The phase, morphology, an...MnxNi0.5-xZn0.5Fe2O4 nanorods were successfully synthesized by the thermal treatment of rod-like precursors that were fabricated by the co-precipitation of Mn2＋, Ni2＋, and Fe2＋ in the lye. The phase, morphology, and particle diameter were examined by the X-ray diffraction and transmission electron microscopy. The magnetic properties of the samples were studied using a vibrating sample magnetometer. nanorods with a diameter of 35 nm and an The results indicated that pure Ni0.5-xZn0.5Fe2O4 aspect ratio of 15 were prepared. It was found that the diametei of the MnxNi0.5-xZn0.5Fe2O4（0≤x≤0.5） samples increased, the length and the aspect .ratio decreased, with an increase in x value. When x=0.5, the diameter and the aspect ratio of the sample reached up to 50 nm and 7-8, respectively. The coercivity of the samples first increased and then decreased with the increase in the x value. The coercivity of the samples again increased when the x value was higher than 0.4. When x=0.5, the coercivity of the MnxNi0.5-xZn0.5Fe2O4 sample reached the maximal value （134.3 Oe） at the calcination temperature of 600 ℃. The saturation magnetization of the samples first increased and then. decreased with the increase in the x value. When x=0.2, the saturation magnetizat：ion of the sample reached the maximal value （68.5 emu/g） at the calcination temperature of 800 ℃.展开更多
基金financially supported by the National Natural Science Foundation of China(21972068,22072067,22232004)the High-level Talents Project of Jinling Institute of Technology(jit-b-202164)。
文摘Precisely refining the electronic structure of electrocatalysts represents a powerful approach to further optimize the electrocatalytic performance.Herein,we demonstrate an ingenious d-d orbital hybridization concept to construct Mo-doped Co_(9)S_(8) nanorod arrays aligned on carbon cloth(CC)substrate(abbreviated as Mo-Co_(9)S_(8)@CC hereafter)as a high-efficiency bifunctional electrocatalyst toward water electrolysis.It has experimentally and theoretically validated that the 4d-3d orbital coupling between Mo dopant and Co site can effectively optimize the H_(2)O activation energy and lower H^(*)adsorption energy barrier,thereby leading to enhanced hydrogen evolution reaction(HER)and oxygen evolution reaction(OER)activities.Thanks to the unique electronic and geometrical advantages,the optimized Mo-Co_(9)S_(8)@CC with appropriate Mo content exhibits outstanding bifunctional performance in alkaline solution,with the overpotentials of 75 and 234 mV for the delivery of a current density of 10 mA cm^(-2),small Tafel slopes of 53.8 and 39.9 mV dec~(-1)and long-term stabilities for at least 32 and 30 h for HER and OER,respectively.More impressively,a water splitting electrolylzer assembled by the self-supported Mo-Co_(9)S_(8)@CC electrode requires a low cell voltage of 1.53 V at 10 mA cm^(-2)and shows excellent stability and splendid reversibility,demonstrating a huge potential for affordable and scalable electrochemical H_(2) production.The innovational orbital hybridization strategy for electronic regulation herein provides an inspirable avenue for developing progressive electrocatalysts toward new energy systems.
基金supported by the National Key Research and Development Project (2016YFC0204702)the National Natural Science Foundation of China (51478070, 21501016, 51108487)+2 种基金the Innovative Research Team of Chongqing (CXTDG201602014)the Natural Science Foundation of Chongqing (cstc2016jcyjA0481)Youth Innovation Promotion Association of Chinese Academy of Sciences (2015316)~~
文摘Heterostructured BiOI@La（OH）3 nanorod photocatalysts were prepared by a facile chemical impregnation method.The enhanced visible light absorption and charge carrier separation can be simultaneously realized after the introduction of BiOI particles into La（OH）3 nanorods.The BiOI@La（OH）3 composites were applied for visible light photocatalytic oxidization of NO in air and exhibited an enhanced activity compared with BiOI and pure La（OH）3 nanorods.The results show that the energy levels between the La（OH）3 and BiOI phases matched well with each other,thus forming a heterojunctioned BiOI@La（OH）3 structure.This band structure matching could promote the separation and transfer of photoinduced electron-hole pairs at the interface,resulting in enhanced photocatalytic performance under visible light irradiation.The photocatalytic performance of BiOI@La（OH）3 is shown to be dependent on the mass ratio of BiOI to La（OH）3.The highest photocatalytic performance can be achieved when the mass ratio of BiOI to La（OH）3 is controlled at 1.5.A further increase of the mass ratio of BiOI weakened the redox abilities of the photogenerated charge carriers.A new photocatalytic mechanism for BiOI@La（OH）3 heterostructures is proposed,which is directly related to the efficient separation of photogenerated charge carriers by the heterojunction.Importantly,the as-prepared BiOI@La（OH）3 heterostructures exhibited a high photochemical stability after multiple reaction runs.Our findings demonstrate that BiOI is an effective component for the formation of a heterostructure with the properties of a wide bandgap semiconductor,which is of great importance for extending the light absorption and photocatalytic activity of wide bandgap semiconductors into visible light region.
基金Project(50975282)supported by the National Natural Science Foundation of China
文摘Oleic acid (denoted as OA) surface-caped lanthanum borate nanorods, abbreviated as OA/LaBO3·H2O, were prepared via hydrothermal method. The microstructures of the as-prepared OA/LaBO3·H2O nanorods were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. The friction and wear properties of OA/LaBO3·H2O nanorods in rapeseed oil were evaluated with a four-ball tribo-tester. The results show that the as-prepared OA/LaBO3·H2O nanorods are hydrophobic and display nanorods morphology with uniform diameter of about 50 nm and length of up to 500 nm. In the meantime, OA/LaBO3·H2O nanorods can obviously improve the anti-wear and friction-reducing capacities of rapeseed oil, and the optimal anti-wear and friction-reducing properties of rapeseed oil were obtained at an OA/LaBO3·H2O content of 1% (mass fraction).
文摘GaN nanorods are successfully synthesized on Si（111） substrates with magnetron sputtering through ammoniating Ga2O3/Co films at 950℃. X-ray diffraction, scanning electron microscopy, high-resolution transmission electron microscopy,and Fourier-transform infrared spectroscopy are used to characterize the samples. The results demonstrate that the nanorods are single-crystal GaN with a hexagonal wurtzite structure and possess relatively smooth surfaces. The growth mechanism of GaN nanorods is also discussed.
基金Project (21171027) supported by the National Natural Science Foundation of ChinaProject (K1001020-11) supported by the Science and Technology Key Project of Changsha City, ChinaProject ([2010]70) supported by Science and Technology Innovative Research Team in Higher Educational Institutions of Hunan Province, China
文摘ZnO nanorod arrays （NRs） were synthesized on the fluorine-doped SnO2 transparent conductive glass （FTO） by a simple chemical bath deposition （CBD） method combined with alkali-etched method in potassium hydroxide （KOH） solution. X-ray diffraction （XRD）, scanning electron microscopy （SEM） and current-voltage （I-V） curve were used to characterize the structure, morphologies and optoelectronic properties. The results demonstrated that ZnO NRs had wurtzite structures, the morphologies and photovoltaic properties of ZnO NRs were closely related to the concentration of KOH and etching time, well-aligned and uniformly distributed ZnO NRs were obtained after etching with 0.1 mol/L KOH for 1 h. ZnO NRs treated by KOH had been proved to have superior photovoltaic properties compared with high density ZnO NRs. When using ZnO NRs etched with 0.1 mol/L KOH for 1 h as the anode of solar cell, the conversion efficiency, short circuit current and open circuit voltage, compared with the unetched ZnO NRs, increased by 0.71%, 2.79 mA and 0.03 V, respectively.
文摘MnxNi0.5-xZn0.5Fe2O4 nanorods were successfully synthesized by the thermal treatment of rod-like precursors that were fabricated by the co-precipitation of Mn2＋, Ni2＋, and Fe2＋ in the lye. The phase, morphology, and particle diameter were examined by the X-ray diffraction and transmission electron microscopy. The magnetic properties of the samples were studied using a vibrating sample magnetometer. nanorods with a diameter of 35 nm and an The results indicated that pure Ni0.5-xZn0.5Fe2O4 aspect ratio of 15 were prepared. It was found that the diametei of the MnxNi0.5-xZn0.5Fe2O4（0≤x≤0.5） samples increased, the length and the aspect .ratio decreased, with an increase in x value. When x=0.5, the diameter and the aspect ratio of the sample reached up to 50 nm and 7-8, respectively. The coercivity of the samples first increased and then decreased with the increase in the x value. The coercivity of the samples again increased when the x value was higher than 0.4. When x=0.5, the coercivity of the MnxNi0.5-xZn0.5Fe2O4 sample reached the maximal value （134.3 Oe） at the calcination temperature of 600 ℃. The saturation magnetization of the samples first increased and then. decreased with the increase in the x value. When x=0.2, the saturation magnetizat：ion of the sample reached the maximal value （68.5 emu/g） at the calcination temperature of 800 ℃.