Micro-alloying of Mg,ranged from 30 to 70 ppm,may improve the high temperature ductility,stress rupture,especially,certain important mechanical properties,such as cyclic stress rupture,creep/fatigue interaction and cr...Micro-alloying of Mg,ranged from 30 to 70 ppm,may improve the high temperature ductility,stress rupture,especially,certain important mechanical properties,such as cyclic stress rupture,creep/fatigue interaction and crack propagation rate.The quantity, morphology and distribution of δ-phase may obviously influence the notched cyclic stress rup- ture life.The relevant microstructure shows that the Mg may also influence to certain extent on the feature of δ-phase.Thus,to keep the Mg and δ-phase under control may further im- prove the mechanical properties of alloy GH169.展开更多
The relationship between the γ/(γ+δ) boundary temperature Tδ of austenitic steels and the equivalent weights of [Crl and [Ni] and the variation rule of the δ phase volume with the temperature are studied With th...The relationship between the γ/(γ+δ) boundary temperature Tδ of austenitic steels and the equivalent weights of [Crl and [Ni] and the variation rule of the δ phase volume with the temperature are studied With the aid of computer,the regressives expression derived from the experimental results are Tδ(℃) = T4 -21.2[Cr] +15.8[Ni]-223. Vδ(%)=0.715 exp 0.015(T-Tδ).展开更多
A stable δ- and β-bismuth trioxide was prepared at room temperature by vacuum vapor-phase oxidation. The average crystal size of products was 14.6 nm (by XRD), the d(0.5) value was in the range from 62 nm to 69 nm, ...A stable δ- and β-bismuth trioxide was prepared at room temperature by vacuum vapor-phase oxidation. The average crystal size of products was 14.6 nm (by XRD), the d(0.5) value was in the range from 62 nm to 69 nm, and geometric standard deviation(GSD) was from 1.42 to 1.64. The results show that δ-Bi2O3 is formed when quenching rates is rapid and β-Bi2O3 is formed when it is slow. The size of grains increases with rising reaction temperature, flow rate of carrier gas, residual pressure of system and longer growing time of grains.展开更多
文摘Micro-alloying of Mg,ranged from 30 to 70 ppm,may improve the high temperature ductility,stress rupture,especially,certain important mechanical properties,such as cyclic stress rupture,creep/fatigue interaction and crack propagation rate.The quantity, morphology and distribution of δ-phase may obviously influence the notched cyclic stress rup- ture life.The relevant microstructure shows that the Mg may also influence to certain extent on the feature of δ-phase.Thus,to keep the Mg and δ-phase under control may further im- prove the mechanical properties of alloy GH169.
文摘The relationship between the γ/(γ+δ) boundary temperature Tδ of austenitic steels and the equivalent weights of [Crl and [Ni] and the variation rule of the δ phase volume with the temperature are studied With the aid of computer,the regressives expression derived from the experimental results are Tδ(℃) = T4 -21.2[Cr] +15.8[Ni]-223. Vδ(%)=0.715 exp 0.015(T-Tδ).
基金Project(03SSY4056) supported by the Bureau of Science and Technology of Hunan Province, China Project(04C034) supported by the Bureau of Education of Hunan Province, China
文摘A stable δ- and β-bismuth trioxide was prepared at room temperature by vacuum vapor-phase oxidation. The average crystal size of products was 14.6 nm (by XRD), the d(0.5) value was in the range from 62 nm to 69 nm, and geometric standard deviation(GSD) was from 1.42 to 1.64. The results show that δ-Bi2O3 is formed when quenching rates is rapid and β-Bi2O3 is formed when it is slow. The size of grains increases with rising reaction temperature, flow rate of carrier gas, residual pressure of system and longer growing time of grains.